CN104893111A - Low temperature low toxicity resistant rubber - Google Patents
Low temperature low toxicity resistant rubber Download PDFInfo
- Publication number
- CN104893111A CN104893111A CN201510208727.3A CN201510208727A CN104893111A CN 104893111 A CN104893111 A CN 104893111A CN 201510208727 A CN201510208727 A CN 201510208727A CN 104893111 A CN104893111 A CN 104893111A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- low temperature
- agent
- low toxicity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention belongs to the rubber technical field, and discloses low temperature low toxicity resistant rubber, the low temperature low toxicity resistant rubber comprises the following raw materials by weight: 55-65 parts of ethylene-propylene-diene monomer, 35-45 parts of natural rubber, 24-28 parts of polyvinyl chloride (PVC), 30-40 parts of calcium carbonate, 2.5-4.5 parts of a cold-resistant agent, 0.1-0.3 part of paraffin wax, 1.2-1.5 parts of a promoter, 3-4 parts of polyethylene glycol (peg), 1.5-2.5 parts of glyceryl monostearate, 0.2-0.3 part of an antioxidant, 4-5 parts of a calcium zinc stabilizer, 1-1.5 parts of a plasticizer, 0.5-1.5 parts of a vulcanizing agent and 3-5 parts of a foaming agent. The polyvinyl chloride and other raw materials are added into the ethylene-propylene-diene monomer to improve the shortcoming of single formula in the prior art, tensile strength is high, ductility is good, and the low temperature low toxicity resistant rubber has good low temperature resistance, good comprehensive mechanical properties, and low toxicity to human body.
Description
Technical field
the invention belongs to field of rubber technology, specifically a kind of low temperature resistant low toxicity rubber.
Background technology
Along with the concern of people to health and the development of refrigerator industry, the requirement of people to refrigerator part is more and more higher.Refrigerator door sealing strip requires that mechanical property, resistance to migration are qualified, also requires human body low toxicity.
Terpolymer EP rubber has resistance to oxidation, ozone-resistant and erosion-resistant ability, and it has fabulous vulcanization characteristics, and in rubber, terpolymer EP rubber has minimum proportion, and it can absorb a large amount of fillers and oil, but little on self performance impact.
Summary of the invention
The object of the present invention is to provide a kind of low temperature resistant low toxicity rubber.
Object of the present invention can be achieved through the following technical solutions:
Low temperature resistant low toxicity rubber, this rubber is made up of the raw material of following weight part: terpolymer EP rubber 55-65 part, natural rubber 35-45 part, polyvinyl chloride 24-28 part, calcium carbonate 30-40 part, cold-resistant agent 2.5-4.5 part, paraffin 0.1-0.3 part, promotor 1.2-1.5 part, polyoxyethylene glycol 3-4 part, glyceryl monostearate 1.5-2.5 part, oxidation inhibitor 0.2-0.3 part, calcium zinc stabilizer 4-5 part, softening agent 1-1.5 part, vulcanizing agent 0.5-1.5 part, whipping agent 3-5 part.
The present invention is preferably made up of the raw material of following weight part: terpolymer EP rubber 58 parts, natural rubber 32 parts, polyvinyl chloride 26 parts, 34 parts, calcium carbonate, cold-resistant agent 3.5 parts, 0.2 part, paraffin, promotor 1.5 parts, polyoxyethylene glycol 3.5 parts, glyceryl monostearate 2 parts, 0.3 part, oxidation inhibitor, calcium zinc stabilizer 4.5 parts, 1.5 parts, softening agent, vulcanizing agent 1 part, whipping agent 4 parts.
Described vulcanizing agent is dicumyl peroxide.
Beneficial effect of the present invention: the present invention adds the raw materials such as polyvinyl chloride in terpolymer EP rubber, improves the shortcoming of single formula in prior art, and its tensile strength is high, good-extensibility, has good resistance to low temperature, and comprehensive mechanical property is good, to human body low toxicity.
Embodiment
Be described in further detail the present invention below in conjunction with specific embodiment, raw material used herein all commercially can be bought and obtain, and " part " described in embodiment is " kg ".
Embodiment 1
Low temperature resistant low toxicity rubber: terpolymer EP rubber 58 parts of getting the raw materials ready, natural rubber 32 parts, polyvinyl chloride 26 parts, 34 parts, calcium carbonate, cold-resistant agent 3.5 parts, 0.2 part, paraffin, promotor 1.5 parts, polyoxyethylene glycol 3.5 parts, glyceryl monostearate 2 parts, 0.3 part, oxidation inhibitor, calcium zinc stabilizer 4.5 parts, 1.5 parts, softening agent, dicumyl peroxide 1 part, whipping agent 4 parts.
Above-mentioned raw materials high-temperature stirring is even, and enter Banbury mixer banburying, mixing 15-20min, extrudes through twin screw extruder, namely obtains the low temperature resistant low toxicity rubber of the present invention.
Embodiment 2
Terpolymer EP rubber 55 parts, natural rubber 45 parts, polyvinyl chloride 24 parts, 40 parts, calcium carbonate, cold-resistant agent 2.5 parts, 0.1 part, paraffin, promotor 1.2 parts, polyoxyethylene glycol 3 parts, glyceryl monostearate 1.5 parts, 0.3 part, oxidation inhibitor, calcium zinc stabilizer 4 parts, 1 part, softening agent, vulcanizing agent 1.5 parts, whipping agent 3 parts.
Above-mentioned raw materials high-temperature stirring is even, and enter Banbury mixer banburying, mixing 15min, extrudes through twin screw extruder, namely obtains the low temperature resistant low toxicity rubber of the present invention.
Embodiment 3
Terpolymer EP rubber 65 parts, natural rubber 35 parts, polyvinyl chloride 28 parts, 30 parts, calcium carbonate, cold-resistant agent 4.5 parts, 0.3 part, paraffin, promotor 1.5 parts, polyoxyethylene glycol 4 parts, glyceryl monostearate 2.5 parts, 0.2 part, oxidation inhibitor, calcium zinc stabilizer 5 parts, 1.5 parts, softening agent, dicumyl peroxide 0.5 part, whipping agent 5 parts.
Above-mentioned raw materials high-temperature stirring is even, and enter Banbury mixer banburying, mixing 15min, extrudes through twin screw extruder, namely obtains the low temperature resistant low toxicity rubber of the present invention.
Above content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (3)
1. low temperature resistant low toxicity rubber, is characterized in that: this rubber is made up of the raw material of following weight part: terpolymer EP rubber 55-65 part, natural rubber 35-45 part, polyvinyl chloride 24-28 part, calcium carbonate 30-40 part, cold-resistant agent 2.5-4.5 part, paraffin 0.1-0.3 part, promotor 1.2-1.5 part, polyoxyethylene glycol 3-4 part, glyceryl monostearate 1.5-2.5 part, oxidation inhibitor 0.2-0.3 part, calcium zinc stabilizer 4-5 part, softening agent 1-1.5 part, vulcanizing agent 0.5-1.5 part, whipping agent 3-5 part.
2. low temperature resistant low toxicity rubber according to claim 1, is characterized in that: this rubber is made up of the raw material of following weight part: terpolymer EP rubber 58 parts, natural rubber 32 parts, polyvinyl chloride 26 parts, 34 parts, calcium carbonate, cold-resistant agent 3.5 parts, 0.2 part, paraffin, promotor 1.5 parts, polyoxyethylene glycol 3.5 parts, glyceryl monostearate 2 parts, 0.3 part, oxidation inhibitor, calcium zinc stabilizer 4.5 parts, 1.5 parts, softening agent, vulcanizing agent 1 part, whipping agent 4 parts.
3. low temperature resistant low toxicity rubber according to claim 1 and 2, is characterized in that: described vulcanizing agent is dicumyl peroxide.