CN104893044A - Rubber floor and process technology thereof - Google Patents
Rubber floor and process technology thereof Download PDFInfo
- Publication number
- CN104893044A CN104893044A CN201510283919.0A CN201510283919A CN104893044A CN 104893044 A CN104893044 A CN 104893044A CN 201510283919 A CN201510283919 A CN 201510283919A CN 104893044 A CN104893044 A CN 104893044A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- floor covering
- rubber floor
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber floor and a process technology thereof. The floor is prepared from the raw materials in parts by weight of 50-160 parts of chloroprene rubber, 50-200 parts of fluorinated silicone rubber, 60-150 parts of EPDM rubber, 4-12 parts of nano zinc oxide, 4-12 parts of nano calcium carbonate, 1-5 parts of stearic acid, 10-25 parts of magnesium hydrate, 2-6 parts of aluminum phosphate, 2-12 parts of magnesium silicate, 2-10 parts of sodium silicate, 4-18 parts of mica powder, 2-12 parts of silicon carbide, 1-5 parts of anti-aging agent, 1-10 parts of calcium carbonate, 1-7 parts of hydroxyl silicone oil, 1-6 parts of hydrogen silicone oil, 1-5 parts of white carbon black, 1-5 parts of simethicone, 1-5 parts of phthalic acid dibutyl ester, 1-5 parts of N- tertiary butyl-2 benzothiazole sulfonamide and 1-5 parts of 2-mercaptoimidazoline. According to the rubber floor and the process technology thereof, chloroprene rubber is taken as a main raw material, and fluororubber and nano materials are added, so that the fire resistance, oil resistance, wear resistance and corrosion resistance of the rubber floor are extremely improved, the rubber floor can play a certain role in fire, and thus person and property damages can be reduced; and the use time is longer and the life is longer.
Description
Technical field
The present invention relates to floor manufacture field, be specifically related to a kind of rubber floor covering and complete processing thereof.
Background technology
Rubber floor covering is natural rubber, the floor made by macromolecular material of synthetic rubber and other composition, developed country's application is very general abroad for rubber floor covering, the particularly comparatively busy area of public area and traffic, as drome, railway station, subway platform, museum, hotel, office building, cinema, department stores, school, hospital, kindergarten etc., at west european developed country, annual consumption is all at millions of square metres, produce in China and use rubber floor covering to be just rose in recent years, but tempo and consumption sharply increase, and every year with 20% speed increase, therefore the complete processing constantly improving rubber floor covering is correct selection to meet the different demands in market.Invention describes a kind of rubber floor covering and complete processing thereof; take chloroprene rubber as main raw material; with the addition of viton and nano material; greatly improve the fire performance of rubber floor covering, oil resistance, wear resisting property and corrosion resistance nature; rubber floor covering is made to play certain provide protection in a fire; reduce the injury of personal property, and duration of service is more lasting, the life-span is longer.
Summary of the invention
For the deficiencies in the prior art, the object of the present invention is to provide a kind of rubber floor covering and complete processing thereof.
The technical problem that the present invention solves can realize by the following technical solutions: a kind of rubber floor covering, obtained by following raw material: chloroprene rubber 50-160, trifluoropropyl siloxane 50-200, terpolymer EP rubber 60-150, nano zine oxide 4-12, nano-calcium carbonate 4-12, stearic acid 1-5, magnesium hydroxide 10-25, aluminum phosphate 2-6, Magnesium Silicate q-agent 2-12, water glass 2-10, mica powder 4-18, silicon carbide 2-12, anti-aging agent 1-5, calcium carbonate 1-10, hydroxy silicon oil 1-7, hydrogen silicone oil 1-6, white carbon black 1-5, dimethyl silicone oil 1-5, dibutyl phthalate 1-5, the N-tertiary butyl-2 benzothiazole sulphenamide 1-5, 2-thiol group tetrahydroglyoxaline 1-5.
Preferably, described anti-aging agent is that N-phenyl-α-aniline mixes obtained with N-N '-diphenyl-p-phenylenediamine in 2:1 ratio.
A complete processing for rubber floor covering, described processes step is:
(1) weighing: take the raw material making rubber floor covering by allocation sheet;
(2) batch mixing: the raw material that step (1) takes is mixed;
(3) shaping: step (2) mixed raw material to be inserted sulfidization molding in the mould of the injector of setting thickness;
(4) demoulding: obtain the rubber plate with setting thickness;
(5) cut: by desired length and width, the rubber plate that step (4) is obtained is cut into rubber floor covering.
Beneficial effect is: the present invention is a kind of rubber floor covering and complete processing thereof; take chloroprene rubber as main raw material; with the addition of viton and nano material; greatly improve the fire performance of rubber floor covering, oil resistance, wear resisting property and corrosion resistance nature; rubber floor covering is made to play certain provide protection in a fire; reduce the injury of personal property, and duration of service is more lasting, the life-span is longer.
Embodiment
The following detailed description of the preferred embodiment of the present invention.
The embodiment of a kind of rubber floor covering of the present invention and complete processing thereof: a kind of rubber floor covering, obtained by following raw material: chloroprene rubber 50-160, trifluoropropyl siloxane 50-200, terpolymer EP rubber 60-150, nano zine oxide 4-12, nano-calcium carbonate 4-12, stearic acid 1-5, magnesium hydroxide 10-25, aluminum phosphate 2-6, Magnesium Silicate q-agent 2-12, water glass 2-10, mica powder 4-18, silicon carbide 2-12, anti-aging agent 1-5, calcium carbonate 1-10, hydroxy silicon oil 1-7, hydrogen silicone oil 1-6, white carbon black 1-5, dimethyl silicone oil 1-5, dibutyl phthalate 1-5, the N-tertiary butyl-2 benzothiazole sulphenamide 1-5, 2-thiol group tetrahydroglyoxaline 1-5.Described anti-aging agent is that N-phenyl-α-aniline mixes obtained with N-N '-diphenyl-p-phenylenediamine in 2:1 ratio.A complete processing for rubber floor covering, described processes step is: (1) weighing: take the raw material making rubber floor covering by allocation sheet; (2) batch mixing: the raw material that step (1) takes is mixed; (3) shaping: step (2) mixed raw material to be inserted sulfidization molding in the mould of the injector of setting thickness; (4) demoulding: obtain the rubber plate with setting thickness; (5) cut: by desired length and width, the rubber plate that step (4) is obtained is cut into rubber floor covering.
After above-mentioned processing step; obtain rubber floor covering; it take chloroprene rubber as main raw material; with the addition of viton and nano material; greatly improve the fire performance of rubber floor covering, oil resistance, wear resisting property and corrosion resistance nature, make rubber floor covering play certain provide protection in a fire, reduce the injury of personal property; and duration of service is more lasting, the life-span is longer.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize specification sheets of the present invention to do equivalent structure or the conversion of equivalent flow process, or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a rubber floor covering, it is characterized in that, obtained by following raw material: chloroprene rubber 50-160, trifluoropropyl siloxane 50-200, terpolymer EP rubber 60-150, nano zine oxide 4-12, nano-calcium carbonate 4-12, stearic acid 1-5, magnesium hydroxide 10-25, aluminum phosphate 2-6, Magnesium Silicate q-agent 2-12, water glass 2-10, mica powder 4-18, silicon carbide 2-12, anti-aging agent 1-5, calcium carbonate 1-10, hydroxy silicon oil 1-7, hydrogen silicone oil 1-6, white carbon black 1-5, dimethyl silicone oil 1-5, dibutyl phthalate 1-5, the N-tertiary butyl-2 benzothiazole sulphenamide 1-5, 2-thiol group tetrahydroglyoxaline 1-5.
2. a kind of rubber floor covering according to claim 1, is characterized in that, described anti-aging agent is that N-phenyl-α-aniline mixes obtained with N-N '-diphenyl-p-phenylenediamine in 2:1 ratio.
3. the complete processing of a kind of rubber floor covering as claimed in claim 1, is characterized in that, described processes step is:
(1) weighing: take the raw material making rubber floor covering by allocation sheet;
(2) batch mixing: the raw material that step (1) takes is mixed;
(3) shaping: step (2) mixed raw material to be inserted sulfidization molding in the mould of the injector of setting thickness;
(4) demoulding: obtain the rubber plate with setting thickness;
(5) cut: by desired length and width, the rubber plate that step (4) is obtained is cut into rubber floor covering.