CN104891920A - 一种抗冻粉煤灰砖及其制作方法 - Google Patents

一种抗冻粉煤灰砖及其制作方法 Download PDF

Info

Publication number
CN104891920A
CN104891920A CN201510227102.1A CN201510227102A CN104891920A CN 104891920 A CN104891920 A CN 104891920A CN 201510227102 A CN201510227102 A CN 201510227102A CN 104891920 A CN104891920 A CN 104891920A
Authority
CN
China
Prior art keywords
fly ash
minutes
flyash
minute
brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510227102.1A
Other languages
English (en)
Inventor
刘林
魏克山
朱志远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510227102.1A priority Critical patent/CN104891920A/zh
Publication of CN104891920A publication Critical patent/CN104891920A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种抗冻粉煤灰砖及其制作方法，制作时向粉煤灰、赤泥、废石膏、粘土、硅藻土中加入18-20份水加热至80-85℃，在200-230r/min的转速下搅拌20-22分钟，得到混合浆料，将混合浆料放入球磨机中研磨10-15分钟后，干燥制粒，得到粉状物料，将沥青加热融化，加入粉状物料、羧甲基纤维素、增塑剂搅拌4-6分钟后，放入制砖模中在-2~-5℃放置30-35分钟，得到抗冻粉煤灰砖。本发明制作工艺简单，充分利用废弃自然资源，制作出的粉煤灰砖具有重量较轻，保温隔热的优点，还具有较强的抗冻性能，在温度较低的环境下也能使用。

Description

一种抗冻粉煤灰砖及其制作方法
技术领域
本发明属于工程建材材料技术领域，具体涉及一种抗冻粉煤灰砖及其制作方法。
背景技术
粉煤灰砖的主要原材料是粉煤灰、石灰、石膏、电石渣、电石泥等工业废弃固态物。 以粉煤灰、石灰为主要原料，掺加适量石膏和骨料经胚料制备，压制成型，高压或常压蒸汽养护而成的实心粉煤灰砖，粉煤灰砖可用于工业与民用建筑的墙体和基础，但现有技术中加工出的粉煤灰砖并不能在易受冻融和干湿交替的环境下使用，同时，在长期受热，受急冷急热和有酸性介质侵蚀的部位也不能使用。
发明内容
为解决现有技术中粉煤灰砖在一些特殊环境下使用受限的缺点，本发明提供一种抗冻粉煤灰砖及其制作方法。
本发明采用的技术方案为：一种抗冻粉煤灰砖，其由以下重量份数的原料组成：
粉煤灰25-28份、沥青10-12份、赤泥5-8份、废石膏3-6份、粘土10-12份、羧甲基纤维素1-2份、硅藻土2-4份、增塑剂0.5-0.8份；
按组成份量称取各原料，向粉煤灰、赤泥、废石膏、粘土、硅藻土中加入18-20份水加热至80-85℃，在200-230r/min的转速下搅拌20-22分钟，得到混合浆料，将混合浆料放入球磨机中研磨10-15分钟后，干燥制粒，得到粉状物料，将沥青加热融化，加入粉状物料、羧甲基纤维素、增塑剂搅拌4-6分钟后，放入制砖模中在-2~-5℃放置30-35分钟，得到抗冻粉煤灰砖。
本发明制作工艺简单，充分利用废弃自然资源，制作出的粉煤灰砖具有重量较轻，保温隔热的优点，还具有较强的抗冻性能，在温度较低的环境下也能使用。
具体实施方式
取粉煤灰25份、沥青10份、赤泥5份、废石膏3份、粘土10份、羧甲基纤维素1份、硅藻土2份、增塑剂0.5份；
按组成份量称取各原料，向粉煤灰、赤泥、废石膏、粘土、硅藻土中加入18份水加热至80℃，在200r/min的转速下搅拌20分钟，得到混合浆料，将混合浆料放入球磨机中研磨10分钟后，干燥制粒，得到粉状物料，将沥青加热融化，加入粉状物料、羧甲基纤维素、增塑剂搅拌4分钟后，放入制砖模中在-2℃放置30分钟，得到抗冻粉煤灰砖。

Claims (1)

1.一种抗冻粉煤灰砖，其特征在于，其由以下重量份数的原料组成：
粉煤灰25-28份、沥青10-12份、赤泥5-8份、废石膏3-6份、粘土10-12份、羧甲基纤维素1-2份、硅藻土2-4份、增塑剂0.5-0.8份；
按组成份量称取各原料，向粉煤灰、赤泥、废石膏、粘土、硅藻土中加入18-20份水加热至80-85℃，在200-230r/min的转速下搅拌20-22分钟，得到混合浆料，将混合浆料放入球磨机中研磨10-15分钟后，干燥制粒，得到粉状物料，将沥青加热融化，加入粉状物料、羧甲基纤维素、增塑剂搅拌4-6分钟后，放入制砖模中在-2~-5℃放置30-35分钟，得到抗冻粉煤灰砖。
CN201510227102.1A 2015-05-07 2015-05-07 一种抗冻粉煤灰砖及其制作方法 Pending CN104891920A (zh)