CN104884660B - 渗碳用钢 - Google Patents

渗碳用钢 Download PDF

Info

Publication number
CN104884660B
CN104884660B CN201380067800.9A CN201380067800A CN104884660B CN 104884660 B CN104884660 B CN 104884660B CN 201380067800 A CN201380067800 A CN 201380067800A CN 104884660 B CN104884660 B CN 104884660B
Authority
CN
China
Prior art keywords
steel
carburizing
content
contents
concentration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201380067800.9A
Other languages
English (en)
Chinese (zh)
Other versions
CN104884660A (zh
Inventor
小山达也
久保田学
吉田卓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of CN104884660A publication Critical patent/CN104884660A/zh
Application granted granted Critical
Publication of CN104884660B publication Critical patent/CN104884660B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/06—Surface hardening
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C8/00—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C8/06—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases
    • C23C8/08—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases only one element being applied
    • C23C8/20—Carburising
    • C23C8/22—Carburising of ferrous surfaces
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
  • Heat Treatment Of Articles (AREA)
CN201380067800.9A 2012-12-28 2013-12-25 渗碳用钢 Active CN104884660B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012288131 2012-12-28
JP2012-288131 2012-12-28
PCT/JP2013/084708 WO2014104113A1 (ja) 2012-12-28 2013-12-25 浸炭用鋼

Publications (2)

Publication Number Publication Date
CN104884660A CN104884660A (zh) 2015-09-02
CN104884660B true CN104884660B (zh) 2017-03-15

Family

ID=51021191

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201380067800.9A Active CN104884660B (zh) 2012-12-28 2013-12-25 渗碳用钢

Country Status (4)

Country Link
JP (1) JP5862802B2 (ja)
KR (1) KR101745224B1 (ja)
CN (1) CN104884660B (ja)
WO (1) WO2014104113A1 (ja)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105349897A (zh) * 2015-11-10 2016-02-24 宁波市鸿博机械制造有限公司 一种钢制滑阀
CN105420456A (zh) * 2015-11-10 2016-03-23 宁波市鸿博机械制造有限公司 一种泵轴的制备方法
CN105420467A (zh) * 2015-11-10 2016-03-23 宁波市鸿博机械制造有限公司 一种钢制滑阀的制备方法
CN105443545A (zh) * 2015-11-18 2016-03-30 宁波金鹏高强度紧固件有限公司 一种长螺母
CN105420474A (zh) * 2015-11-18 2016-03-23 宁波金鹏高强度紧固件有限公司 一种长螺母的加工方法
CN105671434A (zh) * 2016-03-19 2016-06-15 上海大学 一种含镁钙硫的20MnCr易切削齿轮钢及其制备方法
CN106399847B (zh) * 2016-06-15 2018-05-22 山东钢铁股份有限公司 一种车轴轴头用钢及其制备方法
CN107760983B (zh) * 2016-08-18 2019-03-01 江苏鼎泰工程材料有限公司 一种低合金超高强度钢及其铸件的生产方法
CN107604253A (zh) * 2017-08-30 2018-01-19 东风商用车有限公司 一种高淬透性Mn‑Cr系列渗碳钢
CN110218949A (zh) * 2019-07-12 2019-09-10 东北大学 利用微合金化提高渗碳温度的方法和低碳钢的表面渗碳方法
CN111979494B (zh) * 2020-08-28 2021-11-12 东风商用车有限公司 一种薄壁内齿圈用含Ti渗碳钢、其制造方法及薄壁内齿圈成型方法
CN112593166B (zh) * 2020-12-22 2022-05-03 河南中原特钢装备制造有限公司 超高强度高韧性合金结构钢及其冶炼工艺
CN113462986B (zh) * 2021-07-16 2022-08-16 鞍钢股份有限公司 2000MPa环保耐热农机用钢及其制造方法
CN117089771B (zh) * 2023-10-19 2023-12-15 北京科技大学 镁碲复合微合金化齿轮钢

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003034843A (ja) * 2001-05-14 2003-02-07 Sanyo Special Steel Co Ltd 高強度肌焼鋼および高強度肌焼鋼部品
JP2006307271A (ja) * 2005-04-27 2006-11-09 Kobe Steel Ltd 耐結晶粒粗大化特性と冷間加工性に優れた軟化焼鈍の省略可能な肌焼用鋼およびその製法
JP2011042859A (ja) * 2009-08-24 2011-03-03 Sumitomo Metal Ind Ltd 耐食性厚板用低合金鋼の連続鋳造方法及び連続鋳造鋳片
CN102149839A (zh) * 2009-03-27 2011-08-10 新日本制铁株式会社 渗碳淬火性优异的碳钢板及其制造方法
CN102341520A (zh) * 2010-03-19 2012-02-01 新日本制铁株式会社 表层硬化处理用钢及表层硬化钢部件及其制造方法

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2014019908A (ja) * 2012-07-18 2014-02-03 Nippon Steel & Sumitomo Metal 防食被覆鋼材

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003034843A (ja) * 2001-05-14 2003-02-07 Sanyo Special Steel Co Ltd 高強度肌焼鋼および高強度肌焼鋼部品
JP2006307271A (ja) * 2005-04-27 2006-11-09 Kobe Steel Ltd 耐結晶粒粗大化特性と冷間加工性に優れた軟化焼鈍の省略可能な肌焼用鋼およびその製法
CN102149839A (zh) * 2009-03-27 2011-08-10 新日本制铁株式会社 渗碳淬火性优异的碳钢板及其制造方法
JP2011042859A (ja) * 2009-08-24 2011-03-03 Sumitomo Metal Ind Ltd 耐食性厚板用低合金鋼の連続鋳造方法及び連続鋳造鋳片
CN102341520A (zh) * 2010-03-19 2012-02-01 新日本制铁株式会社 表层硬化处理用钢及表层硬化钢部件及其制造方法

Also Published As

Publication number Publication date
CN104884660A (zh) 2015-09-02
WO2014104113A1 (ja) 2014-07-03
JP5862802B2 (ja) 2016-02-16
KR101745224B1 (ko) 2017-06-08
KR20150086365A (ko) 2015-07-27
JPWO2014104113A1 (ja) 2017-01-12

Similar Documents

Publication Publication Date Title
CN104884660B (zh) 渗碳用钢
CN105899697B (zh) 渗碳钢部件的制造方法和渗碳钢部件
JP5099276B1 (ja) 面疲労強度に優れたガス浸炭鋼部品、ガス浸炭用鋼材およびガス浸炭鋼部品の製造方法
CN102770570B (zh) 表面硬化钢和渗碳材料
EP2562283B1 (en) Steel part having excellent in temper softening resistance
WO2011111269A1 (ja) 低サイクル曲げ疲労強度に優れた浸炭鋼部品
JP5558887B2 (ja) 低サイクル疲労強度に優れるＴｉ、Ｂ添加鋼を用いた高強度部品の製造方法
JP4941252B2 (ja) 動力伝達部品用肌焼鋼
WO2013146124A1 (ja) 転動疲労特性に優れた軸受用鋼材およびその製造方法
JP2007308772A (ja) 浸炭部品およびその製造方法
CN109689911A (zh) 表面硬化钢及其制造方法以及齿轮部件的制造方法
JP4964001B2 (ja) 低サイクル疲労強度に優れた歯車
JP4384592B2 (ja) 高温浸炭特性と熱間鍛造性に優れた浸炭用圧延鋼材
JP2009068065A (ja) 面圧疲労強度と衝撃強度及び曲げ疲労強度に優れたはだ焼鋼
EP3040437A1 (en) Mechanical structural component and method for manufacturing same
KR20150074645A (ko) 고탄소침탄강 소재 및 이를 이용한 기어 제조방법
WO2020138432A1 (ja) 鋼材
JP5077814B2 (ja) シャフト及びその製造方法
JPH10259450A (ja) 低サイクル疲労強度の優れた肌焼鋼
JP2020002447A (ja) 浸炭部材
JP3607583B2 (ja) 動力伝達部品用鋼および動力伝達部品
JP2023163967A (ja) 棒鋼及び浸炭焼入れ部品
JP2024016809A (ja) 鋼材、及び、機械構造用部品
JP2022055308A (ja) 浸炭鋼およびその製造方法
JP2024016808A (ja) 鋼材、及び、浸炭機械構造用部品

Legal Events

Date Code Title Description
PB01 Publication
EXSB Decision made by sipo to initiate substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CP01 Change in the name or title of a patent holder

Address after: Tokyo, Japan

Patentee after: Nippon Iron & Steel Corporation

Address before: Tokyo, Japan

Patentee before: Nippon Steel Corporation

CP01 Change in the name or title of a patent holder