CN104877628A - 一种防水沥青密封胶及其制备方法 - Google Patents
一种防水沥青密封胶及其制备方法 Download PDFInfo
- Publication number
- CN104877628A CN104877628A CN201510256488.9A CN201510256488A CN104877628A CN 104877628 A CN104877628 A CN 104877628A CN 201510256488 A CN201510256488 A CN 201510256488A CN 104877628 A CN104877628 A CN 104877628A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- stir
- sealant
- seal gum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防水沥青密封胶,涉及密封胶技术领域,由以下重量份的原料制成:聚丙烯80-100份、三元乙丙橡胶50-60份、甲基丙烯酸8-10份、对苯二酚25-35份、苯乙烯弹性体50-60份、硅氧烷乳液8-10份、增稠剂7-9份、炭黑20-30份、滑石粉20-30份、催化剂0.5-0.7份。本发明的有益效果是:本发明工艺流程简洁,原料配比合理,采用的均为无毒无害的化学产品制作,制备的密封胶,使用效果好,防水、耐光、耐腐蚀,同时具备耐低温和耐高温的作用,可有效的使用在建筑中,使用效果明显,无污染,使用寿命长,市场价值高,便于推广及使用。
Description
技术领域
本发明涉及密封胶技术领域,具体涉及一种防水沥青密封胶及其制备方法。
背景技术
密封胶是指引随密封面形状而变形,不易流淌,有一定粘结性的密封材料,是用来填充构形间隙、以起到密封作用的胶粘剂,具有防泄漏、防水、防振动及隔音、隔热等作用,通常以沥青物、天然树脂或合成树脂、天然橡胶或合成橡胶等干性或非干性的粘稠物为基料,配合滑石粉、白土、炭黑、钛白粉和石棉等惰性填料,再加入增塑剂、溶剂、固化剂、促进剂等制成,密封胶的功能有很多,更具不同的功能会有这不同配方及制备的方法,目前市面上存在的密封胶,其产品质量并不好,弹性差,同时使用时间久后,容易变形,特别是用于建筑的密封胶,要求的性能要更加强劲,拉伸度很差,容易变形,回弹性差,容易腐蚀,并不能保证建筑上使用。
发明内容:
本发明所要解决的技术问题在于提供一种配方合理,抗拉伸强度高,耐候性强的防水沥青密封胶及其制备方法。
本发明所要解决的技术问题采用以下技术方案来实现:
一种防水沥青密封胶,其特征在于:由以下组分的原料制成:
沥青75-85份、环烷油40-50份、二甲苯10-20份、松香水25-35份、氧化锌3-5份、环氧蓖麻油20-30份、环氧树脂20-30份、酚醛树脂活性粘土20-30份、滑石粉20-30份、催化剂0.3-0.5份。
各原料的优选组分为:沥青80份、环烷油45份、二甲苯15份、松香水30份、氧化锌4份、环氧蓖麻油25份、环氧树脂25份、酚醛树脂活性粘土25份、滑石粉25份、催化剂0.4份。
所述的催化剂为四甲基丁二胺。
本发明的另一个目的是提供一种制备本发明防水沥青密封胶的方法,其特征在于包括以下步骤:
a、选用一搅拌罐,将原料中的沥青、环烷油、二甲苯、松香水、氧化锌加入其中,搅拌混合均匀后得到混合料A;
b、选用一搅拌反应釜,将原料中的环氧蓖麻油和环氧树脂加入其中,然后加热至80-90℃后,搅拌反应10-15min;
c、将步骤a搅拌后的原料取出,加入步骤b内的反应釜内,再次加入催化剂,混合再次搅拌15-20min;
d、待上述步骤c搅拌结束后,将原料中的酚醛树脂活性粘土、滑石粉加入,持续搅拌2-3h后,停止搅拌,自然冷却后,出料,计量包装。
本发明的有益效果是:本发明工艺流程简洁,原料配比合理,采用的均为无毒无害的化学产品制作,制备的密封胶,使用效果好,防水、耐光、耐腐蚀,同时具备耐低温和耐高温的作用,可有效的使用在建筑中,使用效果明显,无污染,使用寿命长,市场价值高,便于推广及使用。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
一种防水沥青密封胶,其特征在于:由以下组分的原料制成:
沥青75-85kg、环烷油40-50kg、二甲苯10-20kg、松香水25-35kg、氧化锌3-5kg、环氧蓖麻油20-30kg、环氧树脂20-30kg、酚醛树脂活性粘土20-30kg、滑石粉20-30kg、四甲基丁二胺0.3-0.5kg。
制备方法如下:
a、选用一搅拌罐,将原料中的沥青、环烷油、二甲苯、松香水、氧化锌加入其中,搅拌混合均匀后得到混合料A;
b、选用一搅拌反应釜,将原料中的环氧蓖麻油和环氧树脂加入其中,然后加热至80-90℃后,搅拌反应10-15min;
c、将步骤a搅拌后的原料取出,加入步骤b内的反应釜内,再次加入四甲基丁二胺,混合再次搅拌15-20min;
d、待上述步骤c搅拌结束后,将原料中的酚醛树脂活性粘土、滑石粉加入,持续搅拌2-3h后,停止搅拌,自然冷却后,出料,计量包装。
实施例2
一种防水沥青密封胶,由以下组分的原料制成:
沥青80kg、环烷油45kg、二甲苯15kg、松香水30kg、氧化锌4kg、环氧蓖麻油25kg、环氧树脂25kg、酚醛树脂活性粘土25kg、滑石粉25kg、四甲基丁二胺0.4kg。
制备方法如下:
a、选用一搅拌罐,将原料中的沥青、环烷油、二甲苯、松香水、氧化锌加入其中,搅拌混合均匀后得到混合料A;
b、选用一搅拌反应釜,将原料中的环氧蓖麻油和环氧树脂加入其中,然后加热至80-90℃后,搅拌反应10-15min;
c、将步骤a搅拌后的原料取出,加入步骤b内的反应釜内,再次加入四甲基丁二胺,混合再次搅拌15-20min;
d、待上述步骤c搅拌结束后,将原料中的酚醛树脂活性粘土、滑石粉加入,持续搅拌2-3h后,停止搅拌,自然冷却后,出料,计量包装。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种防水沥青密封胶,其特征在于:由以下组分的原料制成:
聚丙烯80-100份、三元乙丙橡胶50-60份、甲基丙烯酸8-10份、对苯二酚25-35份、苯乙烯弹性体50-60份、硅氧烷乳液8-10份、增稠剂7-9份、炭黑20-30份、滑石粉20-30份、催化剂0.5-0.7份。
2.根据权利要求1所述的一种防水沥青密封胶,其特征在于:各原料的优选组分为:各原料的优选组分为:沥青80份、环烷油45份、二甲苯15份、松香水30份、氧化锌4份、环氧蓖麻油25份、环氧树脂25份、酚醛树脂活性粘土25份、滑石粉25份、催化剂0.4份。
3.根据权利要求1所述的一种防水沥青密封胶,其特征在于:所述的催化剂为四甲基丁二胺。
4.一种制备权利要求1和2中任意一种防水沥青密封胶的方法,其特征在于,包括以下步骤:
a、选用一搅拌罐,将原料中的沥青、环烷油、二甲苯、松香水、氧化锌加入其中,搅拌混合均匀后得到混合料A;
b、选用一搅拌反应釜,将原料中的环氧蓖麻油和环氧树脂加入其中,然后加热至80-90℃后,搅拌反应10-15min;
c、将步骤a搅拌后的原料取出,加入步骤b内的反应釜内,再次加入催化剂,混合再次搅拌15-20min;
d、待上述步骤c搅拌结束后,将原料中的酚醛树脂活性粘土、滑石粉加入,持续搅拌2-3h后,停止搅拌,自然冷却后,出料,计量包装。