CN104864079B - 一种汽车用变速箱箱体 - Google Patents

一种汽车用变速箱箱体 Download PDF

Info

Publication number
CN104864079B
CN104864079B CN201510215110.4A CN201510215110A CN104864079B CN 104864079 B CN104864079 B CN 104864079B CN 201510215110 A CN201510215110 A CN 201510215110A CN 104864079 B CN104864079 B CN 104864079B
Authority
CN
China
Prior art keywords
parts
upper box
lower box
temperature
incubated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510215110.4A
Other languages
English (en)
Other versions
CN104864079A (zh
Inventor
周兰兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Boao Zongheng Network Technology Co ltd
Nanjing Shoucheng Mechanical and Electrical Co.,Ltd.
Original Assignee
Shengzhou City Magic Network Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shengzhou City Magic Network Technology Co Ltd filed Critical Shengzhou City Magic Network Technology Co Ltd
Priority to CN201510215110.4A priority Critical patent/CN104864079B/zh
Priority to CN201710782695.7A priority patent/CN107723490A/zh
Publication of CN104864079A publication Critical patent/CN104864079A/zh
Application granted granted Critical
Publication of CN104864079B publication Critical patent/CN104864079B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，铝合金的成分简单，对该成分的铝合金进行钝化的表面处理工序，避免出现任何表面黑点等问题，使获得表面整洁。

Description

一种汽车用变速箱箱体
技术领域
本发明涉一种汽车用变速箱箱体，属于汽车配件技术领域。
背景技术
在世界汽车市场的激烈竞争中，各国都在向高质量、高可靠性、重量轻、节能、低成本方向发展。在材料方面表现为轻量化，用铝合金代替部分钢(铁)件，以达到汽车向高质量、低成本的发展的要求；在工艺方面表现为科学性，用先进工艺取代传统的工艺以达到提高毛坯精度，减少加工余量，减少原材料消耗，降低成本的目的。要进一步扩大铝合金材料在汽车结构和动力总成系统的运用，现有的铝合金铸件的制备方法和制造工艺已难以满足这一要求。
发明内容
本发明就是针对上述问题而提出的一种工艺简单、成本低、耐蚀性性良好的变速箱箱体。
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12-13﹪、Zn：9-10﹪、Fe：4-5﹪，Si：2-3﹪、Ti：1-2﹪、Ni 0.7-0.8﹪、Cu：0.5-0.6﹪、Mn：0.2-0.3﹪、Zr：0.07-0.08﹪、Y：0.03-0.04﹪、Mo ：0.05-0.06﹪，Ca：0.06-0.07﹪，Ag：0.08-0.09﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵10-15份，硝酸10-13份，硫酸镍5-10份，氯化铈2-3份，硫酸1-4份，高锰酸钾1-2份，水25-35份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛20-30份，氧化锆10-20份，碳化铬 5-10份，碳化钛 1-3份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂50-60份，纳米级氧化铝10-15份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇30-40份，得到最终的箱体。
所述的一种汽车用变速箱箱体，铝合金化学组成为（重量百分比）：Mg：12﹪、Zn：9﹪、Fe：4﹪，Si：2﹪、Ti：1﹪、Ni 0.7﹪、Cu：0.5﹪、Mn：0.2﹪、Zr：0.07﹪、Y：0.03﹪、Mo ：0.05﹪，Ca：0.06﹪，Ag：0.08﹪，余量为Al以及不可避免的杂质。
所述的一种汽车用变速箱箱体，铝合金化学组成为（重量百分比）：Mg： 13﹪、Zn：10﹪、Fe： 5﹪，Si： 3﹪、Ti： 2﹪、Ni 0.8﹪、Cu： 0.6﹪、Mn： 0.3﹪、Zr： 0.08﹪、Y：0.04﹪、Mo ： 0.06﹪，Ca： 0.07﹪，Ag： 0.09﹪，余量为Al以及不可避免的杂质。
所述的一种汽车用变速箱箱体，铝合金化学组成为（重量百分比）：Mg：12.5﹪、Zn：9.5﹪、Fe：4.5﹪，Si：2.5﹪、Ti：1.5﹪、Ni 0.75﹪、Cu：0.55﹪、Mn：0.25﹪、Zr：0.075﹪、Y：0.035﹪、Mo ：0.055﹪，Ca：0.065﹪，Ag：0.085﹪，余量为Al以及不可避免的杂质。
所述的一种汽车用变速箱箱体，氧化钛系陶瓷材料层包括（重量）：氧化钛20份，氧化锆10份，碳化铬 5份，碳化钛 1份。
所述的一种汽车用变速箱箱体，氧化钛系陶瓷材料层包括（重量）：氧化钛30份，氧化锆20份，碳化铬10份，碳化钛3份。
所述的一种汽车用变速箱箱体，氧化钛系陶瓷材料层包括（重量）：氧化钛25份，氧化锆15份，碳化铬 7份，碳化钛 2份。
所述的一种汽车用变速箱箱体，所述涂料包括（重量）：环氧改性有机硅树脂50份，纳米级氧化铝10份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇30份。
所述的一种汽车用变速箱箱体，所述涂料包括（重量）：环氧改性有机硅树脂60份，纳米级氧化铝15份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇40份。
所述的一种汽车用变速箱箱体，所述涂料包括（重量）：环氧改性有机硅树脂55份，纳米级氧化铝13份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇35份。
一种汽车用变速箱箱体及其制造方法，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12-13﹪、Zn：9-10﹪、Fe：4-5﹪，Si：2-3﹪、Ti：1-2﹪、Ni 0.7-0.8﹪、Cu：0.5-0.6﹪、Mn：0.2-0.3﹪、Zr：0.07-0.08﹪、Y：0.03-0.04﹪、Mo ：0.05-0.06﹪，Ca：0.06-0.07﹪，Ag：0.08-0.09﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵10-15份，硝酸10-13份，硫酸镍5-10份，氯化铈2-3份，硫酸1-4份，高锰酸钾1-2份，水25-35份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛20-30份，氧化锆10-20份，碳化铬 5-10份，碳化钛 1-3份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂50-60份，纳米级氧化铝10-15份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇30-40份，得到最终的箱体。
上述发明内容相对于现有技术的有益效果在于：1）铝合金的成分简单；2）对该成分的铝合金进行钝化的表面处理工序，避免出现任何表面黑点等问题，使获得表面整洁；3）因箱体内表面长期接触变速箱油，会对其内表面造成损伤，通过在铝合金箱体内表面涂覆氧化钛系涂层，提高耐蚀性能。4）对箱体外表面形成有机涂层有效提高耐候抗污性能。
具体实施方式
为了对本发明的技术特征、目的和效果有更加清楚的理解，现详细说明本发明的具体实施方式。
实施例1
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12﹪、Zn：9﹪、Fe：4﹪，Si：2﹪、Ti：1﹪、Ni 0.7﹪、Cu：0.5﹪、Mn：0.2﹪、Zr：0.07﹪、Y：0.03﹪、Mo：0.05﹪，Ca：0.06﹪，Ag：0.08﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵10份，硝酸10份，硫酸镍5份，氯化铈2份，硫酸1份，高锰酸钾1份，水25份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛20份，氧化锆10份，碳化铬 5份，碳化钛 1份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂50份，纳米级氧化铝10份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇30份，得到最终的箱体。
实施例2
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg： 13﹪、Zn： 10﹪、Fe： 5﹪，Si： 3﹪、Ti： 2﹪、Ni 0.8﹪、Cu： 0.6﹪、Mn： 0.3﹪、Zr： 0.08﹪、Y：0.04﹪、Mo ： 0.06﹪，Ca： 0.07﹪，Ag： 0.09﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵15份，硝酸13份，硫酸镍10份，氯化铈3份，硫酸4份，高锰酸钾2份，水35份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛30份，氧化锆20份，碳化铬10份，碳化钛3份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂60份，纳米级氧化铝15份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇40份，得到最终的箱体。
实施例3
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12.5﹪、Zn：9.5﹪、Fe：4.5﹪，Si：2.5﹪、Ti：1.5﹪、Ni 0.75﹪、Cu：0.55﹪、Mn：0.25﹪、Zr：0.075﹪、Y：0.035﹪、Mo ：0.055﹪，Ca：0.065﹪，Ag：0.085﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵13份，硝酸12份，硫酸镍7份，氯化铈2.5份，硫酸3份，高锰酸钾1.5份，水30份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛25份，氧化锆15份，碳化铬 7份，碳化钛 2份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂55份，纳米级氧化铝13份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇35份，得到最终的箱体。
实施例4
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12.3﹪、Zn：9.2﹪、Fe：4.1﹪，Si：2.4﹪、Ti：1.2﹪、Ni 0.71﹪、Cu：0.51﹪、Mn：0.23﹪、Zr：0.074﹪、Y：0.033﹪、Mo ：0.054﹪，Ca：0.064﹪，Ag：0.083﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵12份，硝酸11份，硫酸镍6份，氯化铈2.2份，硫酸1.3份，高锰酸钾1.1份，水27份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛23份，氧化锆14份，碳化铬 7份，碳化钛 1.2份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂52份，纳米级氧化铝11份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇32份，得到最终的箱体。
实施例5
一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12.7﹪、Zn：9.9﹪、Fe：4.7﹪，Si：2.6﹪、Ti：1.7﹪、Ni 0.78﹪、Cu：0.58﹪、Mn：0.29﹪、Zr：0.077﹪、Y：0.038﹪、Mo ：0.058﹪，Ca：0.067﹪，Ag：0.086﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵14份，硝酸12份，硫酸镍9份，氯化铈2.8份，硫酸3份，高锰酸钾1.8份，水32份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛28份，氧化锆19份，碳化铬 9份，碳化钛 2.8份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂58份，纳米级氧化铝14份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇39份，得到最终的箱体。

Claims (1)

1.一种汽车用变速箱箱体，包括下箱体和与下箱体相连的上箱体，上箱体和下箱体内表面涂覆有氧化钛系陶瓷材料层，上箱体和下箱体外表面涂覆环氧改性有机硅树脂系涂料，
所述上箱体和下箱体为铝合金材质，铝合金化学组成为（重量百分比）：Mg：12-13﹪、Zn：9-10﹪、Fe：4-5﹪，Si：2-3﹪、Ti：1-2﹪、Ni 0.7-0.8﹪、Cu：0.5-0.6﹪、Mn：0.2-0.3﹪、Zr：0.07-0.08﹪、Y：0.03-0.04﹪、Mo ：0.05-0.06﹪，Ca：0.06-0.07﹪，Ag：0.08-0.09﹪，余量为Al以及不可避免的杂质；
上箱体和下箱体的制备方法：包括以下步骤：按照上述铝合金化学成分配料，先将铝锭加入到熔炼炉中，炉温控制在720℃，待铝锭熔化后，铝液温度升到730℃加入镁铝中间合金，后将炉温升高到735℃加入锌铝中间合金；后将炉温升高到740℃加入铁铝中间合金和纯硅；后将炉温升高到745℃加入其他合金元素，后炉温升高到760℃，加入精炼净化剂，精炼净化剂加入量为炉料量的0.8％，搅拌40分钟，静置60分钟，待渣与金属液分离，扒渣，后加入覆盖剂，静置30分钟后再次扒渣，之后对上箱体和下箱体分别进行浇注；浇注温度为740℃；得到的上箱体和下箱体进行热处理：首先将上箱体和下箱体进行加热升温至560℃，升温速率50℃/小时，保温2小时，之后进行淬火处理，淬火介质为水，淬火后将上箱体和下箱体从室温加热至500℃，升温速率100℃/小时，保温7小时，后降温至300℃，降温速率50℃/小时，保温3小时，后再次降温至200℃，降温速率50℃/小时，保温9小时，后空冷至室温，所述精炼净化剂包括：氯化铝60％，硝酸铝20％，氯化钾10％，硝酸钠5％， 氯化锰5％；所述覆盖剂包括：硫酸铝40％，硫酸钡20％，氯化钠10％；铝氟酸钠10％；氧化铝10％，氟化钠10％，覆盖剂总加入量为炉料量的0.8％，
之后对上箱体和下箱体表面进行钝化处理，其中：钝化液组成为（重量）：硫酸铵10-15份，硝酸10-13份，硫酸镍5-10份，氯化铈2-3份，硫酸1-4份，高锰酸钾1-2份，水25-35份；
之后对上箱体和下箱体内表面进行涂覆氧化钛系陶瓷材料；通过涂覆在内表面形成氧化钛系陶瓷材料层，氧化钛系陶瓷材料层厚度0.5mm，氧化钛系陶瓷材料层包括（重量）：氧化钛20-30份，氧化锆10-20份，碳化铬 5-10份，碳化钛 1-3份，将涂覆后的上箱体和下箱体进行加热，升温至400℃，升温速率200℃/小时，保温5小时，后降温至300℃，降温速率50℃/小时，保温5小时，后再次降温至150℃，降温速率50℃/小时，保温8小时，后空冷至室温，
之后对上箱体和下箱体外表面进行涂覆环氧改性有机硅树脂系涂料；所述涂料包括（重量）：环氧改性有机硅树脂55份，纳米级氧化铝13份，氧化铈5份，氧化钴5份，硅酸钠20份，乙二胺5份， 二甲苯10份，膨润土3份，氧化硼3份，磷酸锌1份，乙醇30-40份，得到最终的箱体。
CN201510215110.4A 2015-04-30 2015-04-30 一种汽车用变速箱箱体 Expired - Fee Related CN104864079B (zh)