CN104862470A - 一种缩短球团焙烧时间的方法 - Google Patents

一种缩短球团焙烧时间的方法 Download PDF

Info

Publication number
CN104862470A
CN104862470A CN201510242423.9A CN201510242423A CN104862470A CN 104862470 A CN104862470 A CN 104862470A CN 201510242423 A CN201510242423 A CN 201510242423A CN 104862470 A CN104862470 A CN 104862470A
Authority
CN
China
Prior art keywords
green
pellet
pullets
added
ball
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510242423.9A
Other languages
English (en)
Other versions
CN104862470B (zh
Inventor
唐文博
饶家庭
黎静文
张志强
习鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pangang Group Panzhihua Iron and Steel Research Institute Co Ltd
Original Assignee
Pangang Group Panzhihua Iron and Steel Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pangang Group Panzhihua Iron and Steel Research Institute Co Ltd filed Critical Pangang Group Panzhihua Iron and Steel Research Institute Co Ltd
Priority to CN201510242423.9A priority Critical patent/CN104862470B/zh
Publication of CN104862470A publication Critical patent/CN104862470A/zh
Application granted granted Critical
Publication of CN104862470B publication Critical patent/CN104862470B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种缩短球团焙烧时间的方法，方法步骤如下：a.将膨润土和矿粉加入混匀机里，用混匀机对其混匀5min，b.将混匀后的物料的一半加入圆盘造球机里面，开启圆盘造球机加入质量含量1％-2％的高锰酸钙溶液，待造球机里面的混合料母球出现后，逐步将剩下的物料加入造球机里面，c.待生球造好后，将生球取出并装于刚玉坩埚里，放入预热炉内，预热45min后将球团移入球团焙烧炉内进行焙烧，d.焙烧完毕后将球团取出置于空气中冷却。与现有焙烧球团方法相比，本发明通过在造生球时加的水里面加入高猛酸钙，在焙烧过程中通过高猛酸钙的分解反应释放出的氧气来提高球团的氧化度，以缩短焙烧时间来提高球团产量。

Description

一种缩短球团焙烧时间的方法
技术领域
本发明涉及一种钢铁冶金技术领域，尤其涉及一种缩短球团焙烧时间的方法。
背景技术
钢铁冶金技术领域中，焙烧球团进行造生球时都是采用水喷洒在造球机内的矿粉上，焙烧球团氧化度不高，球团焙烧时间长，提高球团产量不高，加入其他成分又易影响球团质量及性能指标。
发明内容
本发明的目的就在于提供一种解决上述问题，通过在造生球时加的水里面加入高猛酸钙，在焙烧过程中通过高猛酸钙的分解反应释放出的氧气来提高焙烧球团氧化度的方法。
为了实现上述目的，本发明采用的技术方案是：一种缩短球团焙烧时间的方法，方法步骤如下：
a.将膨润土和矿粉加入混匀机里，用混匀机对其混匀5min，
b.将混匀后的物料的一半加入圆盘造球机里面，开启圆盘造球机加入质量含量1％-2％的高锰酸钙溶液，待造球机里面的混合料母球出现后，逐步将剩下的物料加入造球机里面，，使得造成的生球里面含有高锰酸钙，在高温焙烧的过程中，高锰酸钙分解为氧化锰、氧化钙和氧气反应式CaMnO4→CaO+MnO+O2↑；
c.待生球造好后，将生球取出并装于刚玉坩埚里，放入预热炉内，预热45min后将球团移入球团焙烧炉内进行焙烧，
d.焙烧完毕后将球团取出置于空气中冷却。
作为优选，增加球团的氧势，提高球团氧化度，在保证球团质量不下降的前提下可以有效缩短球团焙烧时间，提高球团产量，再将造好的生球进行球团焙烧。
作为优选，所述矿粉与膨润土的配料比为98％白马精矿、2％膨润土。
作为优选，步骤b中，通过喷洒高锰酸钙溶液将生球水分控制在9％-9.5％范围内，生球粒度控制在8-10mm范围内，将水分控制在此范围内时，生球抗压强度和落下强度较好，而生球粒度则影响焙烧时间和球团的强度，选择8-10mm的范围，可以保证焙烧出的球团强度能满足高炉生产需要，同时不需要太长的焙烧时间，而且制造此粒度生球较易控制。
作为优选，步骤c中，进行球团焙烧时先进行预热，预热温度为800℃，预热时间45min，生球在300～800℃的温度下被氧化，生成Fe2O3微晶，新生成的Fe2O3微晶具有高度的迁移能力，促使微晶长大形成连接桥(又称Fe2O3微晶键)，将生球中各颗粒互相粘结起来，预热时间为根据实际情况和经验选取。
作为优选，步骤c中，所述球团焙烧的温度为1250℃，当预热后的球团在氧化性气氛中加热到1000-1300℃时，Fe2O3的微晶才能够再结晶，长成相互紧密连成一片的赤铁矿晶体，这时球团强度才能达到最高。。
与现有技术相比，本发明的优点在于：通过在造生球时加的水里面加入高猛酸钙，在焙烧过程中通过高猛酸钙的分解反应释放出的氧气来提高球团的氧化度，增加球团的氧势，提高球团氧化度，在保证球团质量不下降的前提下可以有效缩短球团焙烧时间，提高球团产量。
具体实施方式
下面将对本发明作进一步说明。
实施例：一种缩短球团焙烧时间的方法，将膨润土和矿粉总重为10kg加入混匀机里，用混匀机对其混匀5min，将混匀后的物料的一半一次性加入圆盘造球机里面，开启圆盘造球机开始加高锰酸钙溶液，等造球机里面的混合料母球出现后，逐步将剩下的混合料加入造球机里面，等生球造好后，将生球取出并装于刚玉坩埚里，放入预热炉内，预热45min后将球团移入球团焙烧炉内进行焙烧，焙烧完毕后将球团取出置于空气中冷却，待球团冷却完全后，测定球团的强度。
分别配制1％、1.3％、1.7％和2％高锰酸钙溶液，使用水(作为基准)和前述溶液分别制造生球，生球配比为98％白马精矿+2％膨润土，控制生球水分在9％-9.5％范围内，生球粒度在8-10mm范围内，控制球团预热温度为800℃，预热时间均为45min，球团焙烧温度为1250℃，焙烧时间分别为60min(水)、56min(1％高锰酸钙溶液)、54min(1.3％高锰酸钙溶液)、52min(1.7％高锰酸钙溶液)、51min(2％高锰酸钙溶液)，并对焙烧好的球团检测其抗压强度和球团矿成分，结果如下：
球团矿成分
抗压强度
结果表明：使用高猛酸钙溶液代替水制造的生球，经过焙烧，可以有效降低球团矿的FeO含量，提高球团的氧化度，并且在保证球团矿抗压强度不降低的情况下，最多缩短球团焙烧时间15％，可以有效缩短球团焙烧时间，提高球团焙烧效率。
以上对本发明所提供的一种提高焙烧球团氧化度的方法进行了详尽介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，对本发明的变更和改进将是可能的，而不会超出附加权利要求所规定的构思和范围，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (5)

1.一种缩短球团焙烧时间的方法，其特征在于，方法步骤如下：
a.将膨润土和矿粉加入混匀机里，用混匀机对其混匀5min，
b.将混匀后的物料的一半加入圆盘造球机里面，开启圆盘造球机加入质量含量1％-2％的高锰酸钙溶液，待造球机里面的混合料母球出现后，逐步将剩下的物料加入造球机里面，
c.待生球造好后，将生球取出并装于刚玉坩埚里，放入预热炉内，预热45min后将球团移入球团焙烧炉内进行焙烧，
d.焙烧完毕后将球团取出置于空气中冷却。
2.根据权利要求1所述的一种缩短球团焙烧时间的方法，其特征在于：所述矿粉与膨润土的配料比为98％白马精矿、2％膨润土。
3.根据权利要求1所述的一种缩短球团焙烧时间的方法，其特征在于：步骤b中通过喷洒高锰酸钙溶液将生球水分控制在9％-9.5％范围内，生球粒度控制在8-10mm范围内。
4.根据权利要求1所述的一种缩短球团焙烧时间的方法，其特征在于：步骤c中，进行球团焙烧时先进行预热，预热温度为800℃，预热时间45min。
5.根据权利要求1所述的一种缩短球团焙烧时间的方法，其特征在于：步骤c中，所述球团焙烧的温度为1250℃。
CN201510242423.9A 2015-05-13 2015-05-13 一种缩短球团焙烧时间的方法 Active CN104862470B (zh)