CN104861807A - Interior wall coating and preparation method thereof - Google Patents
Interior wall coating and preparation method thereof Download PDFInfo
- Publication number
- CN104861807A CN104861807A CN201510277280.5A CN201510277280A CN104861807A CN 104861807 A CN104861807 A CN 104861807A CN 201510277280 A CN201510277280 A CN 201510277280A CN 104861807 A CN104861807 A CN 104861807A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- wall coating
- antiseptic
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an interior wall coating. The interior wall coating comprises the following components in parts by weight: 100-300 parts of water, 160-240 parts of titanium dioxide, 60-90 parts of calcium carbonate powder, 3-6 parts of a dispersing agent, 2-5 parts of an antifoaming agent, 160-240 parts of an acrylic emulsion, 4-6 parts of ethyl alcohol, 3-7 parts of a fire retardant, 2-4 parts of an antiseptic and antibiotic agent and 1-3 parts of a plant extract. The interior wall coating is lower in cost, the preparation process is simple, the effects of insect expelling and disinfecting can be achieved by the plant extract, and the interior wall coating smells fresh; the interior wall coating does not contain toxic substances such as formaldehyde, benzene and ammonia, the zero emission of volatile toxic substances is achieved, the own advantages and the mutual synergistic flame retardant effect of inorganic fire retardants are played to the greatest extent by using all components in the fire retardants cooperatively, the flame retardant temperature of the coating can be improved, a good fire retardant effect can be achieved, all components in the antiseptic and antibiotic agent play a role cooperatively, and a better antiseptic effect can be achieved.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of interior wall coating and preparation method.
Background technology
Along with the fast development of paint industry, coating is built, decoration industry widely uses, various interior wall coating emerges in an endless stream, manufacturers attracts the eye of human consumer in color, material and safety, its price mostly costly, existing interior wall coating, in use, usually easily there is following problem: use single fire retardant, flame retardant effect is bad, there is great fire safety evaluating hidden danger, separately, its its anti-corrosive antibacterial of existing coating is poor, or agricultural chemicals type mould inhibitor is added in employing in coating, is detrimental to health.
Summary of the invention
For the defect existed in prior art, the object of this invention is to provide a kind of interior wall coating and preparation method.
Described a kind of interior wall coating, is characterized in that this coating is made up of the component of following weight part: water 100-300 part, titanium dioxide 160-240 part, Paris white 60-90 part, dispersion agent 3-6 part, defoamer 2-5 part, ACRYLIC EMULSION 160-240 part, fire retardant 3-7 part, antiseptic and antibiotic agent 2-4 part, plant milk extract 1-3 part.
Described a kind of interior wall coating, is characterized in that described coating is made up of the component of following weight part: water 150-250 part, titanium dioxide 180-220 part, Paris white 70-80 part, dispersion agent 4-5 part, defoamer 3-4 part, ACRYLIC EMULSION 180-220 part, ethanol 4-6, fire retardant 4-6 part, antiseptic and antibiotic agent 2-4 part, plant milk extract 1-3 part.
Described a kind of interior wall coating, is characterized in that described coating is made up of the component of following weight part: 200 parts, water, titanium dioxide 200 parts, Paris white 75 parts, dispersion agent 4 parts, defoamer 4 parts, ACRYLIC EMULSION 200 parts, ethanol 5 parts, fire retardant 5 parts, antiseptic and antibiotic agent 3 parts, plant milk extract 2 parts.
Described a kind of interior wall coating, it is characterized in that described plant milk extract is the alcohol extract of following composition, chrysanthemum, lavandula angustifolia, peppermint, soybean, castor-oil plant, each component proportions is: chrysanthemum: lavandula angustifolia: peppermint: soybean: castor-oil plant=1:1:1:2:2.
Described a kind of interior wall coating, is characterized in that described fire retardant is the mixture of magnesium hydroxide, aluminium hydroxide, ferric oxide, zinc borate, and the weight ratio of each composition is magnesium hydroxide: aluminium hydroxide: ferric oxide: zinc borate=1:1:0.5:0.2.
Described a kind of interior wall coating, is characterized in that described antiseptic and antibiotic agent is the mixture of ethyl p-hydroxybenzoate and propylben, and both weight ratios are ethyl p-hydroxybenzoate: propylben=1:0.5.
The preparation method of described a kind of interior wall coating, is characterized in that adopting following steps:
1) measure chrysanthemum, lavandula angustifolia, peppermint, soybean, castor-oil plant by formula, mixing after pulverizing, soaks one week with under the alcohol at normal temperature of 75%, and leach liquor concentrates, plant milk extract of pulverizing to obtain after drying, for subsequent use;
2) part water, dispersion agent and part defoamer are joined in reaction unit to stir and disperse;
3) in reaction unit, continuation interpolation titanium dioxide, Paris white, fire retardant, antiseptic and antibiotic agent, ethanol stir, and are milled to fineness of materials at below 50um;
4) in reaction unit, continue to add ACRYLIC EMULSION, the defoamer of surplus and plant milk extract in reaction unit, stir, add water adjusting viscosity, crosses 200 mesh sieves.
The preparation method of described a kind of interior wall coating, is characterized in that step 2) in mixing speed be 750-850 rev/min, disperse 40 minutes; In step 3), mixing speed is 800-1000 rev/min, and churning time is 30 minutes; Step 4) stirs 40 minutes under rotating speed is the condition of 700 revs/min, and adjusting viscosity is to 90-110KU.
In the present invention, ethanol working concentration is 75%; adopt the coating that the inventive method and formula obtain; construction proportioning is coating: water=100:(100-20); obtained coating gas mould is plentiful; possess good decoration functions and protection of environment function; all have good effect at smell, environmental protection, aspect of performance, smell is pure and fresh, can not the obnoxious flavour such as emitting formaldehyde, benzene, ammonia, TVOC.
A kind of interior wall coating of the present invention and preparation method thereof, cost is lower, preparation technology is simple, and plant milk extract can play good expelling parasite, sterilization efficacy, and smell is pure and fresh simultaneously; Product of the present invention is not containing toxic substances such as formaldehyde, benzene, ammonia, volatile toxic substance reaches zero release, in fire retardant each composition with the use of, the respective advantage of inorganic combustion inhibitor and mutual cooperative flame retardant effect are farthest brought into play, and the resistance combustion temperature of coating can be improved, good flame retardant effect can be played, mutually work in coordination with between each composition in antiseptic and antibiotic agent and play a role, guarantee to reach better preservative effect.
Embodiment
The present invention is described in further detail below in conjunction with embodiment.
Embodiment 1
Joining in reactor by 150kg water, 4kg dispersion agent, 2kg defoamer, is under the condition of 750-850 rev/min at rotating speed, disperses 40 minutes; Adding the titanium dioxide of 200kg, 75kg Paris white, 5kg fire retardant, 3kg antiseptic and antibiotic agent, 5kg ethanol again, is churning time 30 minutes under the condition of 800-1000 rev/min at rotating speed, crosses sand milling to fineness of materials at below 50um; Adding the pure acrylic latex of 200kg, 2kg defoamer, 2kg plant milk extract again in reactor, is stir 40 minutes under the condition of 700 revs/min at rotating speed; The water adjusting viscosity of last 50kg, makes its viscosity at normal temperatures for (90-110) KU, is qualified product after crossing 200 mesh sieves, carries out encapsulation preservation.
Wherein, each weight ratio of constituents of fire retardant is magnesium hydroxide: aluminium hydroxide: ferric oxide: zinc borate=1:1:0.5:0.2; The weight ratio of each composition of antiseptic and antibiotic agent is ethyl p-hydroxybenzoate: propylben=1:0.5.
The preparation of plant milk extract: take chrysanthemum 1kg, lavandula angustifolia 1kg, peppermint 1kg, soybean 2kg, castor-oil plant 2kg, mixing after pulverizing, soaks one week with under the alcohol at normal temperature of 75%, and leach liquor concentrates, plant milk extract of pulverizing to obtain after drying.
Embodiment 2
Joining in reactor by 200kg water, 6kg dispersion agent, 1kg defoamer, is under the condition of 750-850 rev/min at rotating speed, disperses 40 minutes; Adding the titanium dioxide of 240kg, 60kg Paris white, 3kg fire retardant, 4kg antiseptic and antibiotic agent, 6kg ethanol again, is churning time 30 minutes under the condition of 800-1000 rev/min at rotating speed, crosses sand milling to fineness of materials at below 50um; Adding the pure acrylic latex of 160kg, 1kg defoamer, 1kg plant milk extract again in reactor, is stir 40 minutes under the condition of 700 revs/min at rotating speed; The water adjusting viscosity of last 100kg, makes its viscosity at normal temperatures for (90-110) KU, is qualified product after crossing 200 mesh sieves, carries out encapsulation preservation.
Wherein, each weight ratio of constituents of fire retardant is magnesium hydroxide: aluminium hydroxide: ferric oxide: zinc borate=1:1:0.5:0.2; The weight ratio of each composition of antiseptic and antibiotic agent is ethyl p-hydroxybenzoate: propylben=1:0.5.
The preparation of plant milk extract: take chrysanthemum 1kg, lavandula angustifolia 1kg, peppermint 1kg, soybean 2kg, castor-oil plant 2kg, mixing after pulverizing, soaks one week with under the alcohol at normal temperature of 75%, and leach liquor concentrates, plant milk extract of pulverizing to obtain after drying.
Embodiment 3
Joining in reactor by 120kg water, 5kg dispersion agent, 1.5kg defoamer, is under the condition of 750-850 rev/min at rotating speed, disperses 40 minutes; Adding the titanium dioxide of 220kg, 70kg Paris white, 6kg fire retardant, 2kg antiseptic and antibiotic agent, 4kg ethanol again, is churning time 30 minutes under the condition of 800-1000 rev/min at rotating speed, crosses sand milling to fineness of materials at below 50um; Adding the pure acrylic latex of 180kg, 1.5kg defoamer, 3kg plant milk extract again in reactor, is stir 40 minutes under the condition of 700 revs/min at rotating speed; The water adjusting viscosity of last 30kg, makes its viscosity at normal temperatures for (90-110) KU, is qualified product after crossing 200 mesh sieves, carries out encapsulation preservation.
Wherein, each weight ratio of constituents of fire retardant is magnesium hydroxide: aluminium hydroxide: ferric oxide: zinc borate=1:1:0.5:0.2; The weight ratio of each composition of antiseptic and antibiotic agent is ethyl p-hydroxybenzoate: propylben=1:0.5.
The preparation of plant milk extract: take chrysanthemum 1kg, lavandula angustifolia 1kg, peppermint 1kg, soybean 2kg, castor-oil plant 2kg, mixing after pulverizing, soaks one week with under the alcohol at normal temperature of 75%, and leach liquor concentrates, plant milk extract of pulverizing to obtain after drying.
Through test; the concrete proportioning that fire retardant adopts the present invention to fill a prescription; its flame retardant properties is optimum; resistance combustion temperature reaches the highest, and nearby object high-temp combustion time, this coating also can absorb the moisture in air; effectively can protect cavity and stop spreading of flame; the concrete proportioning that antiseptic and antibiotic agent adopts the present invention to fill a prescription, its anti-fungi performance is optimum, and the coating of the present invention's formula is low, nonflammable, color is soft, brushing is convenient.
experimental example:adopt each embodiment coating prepared by formula of the present invention and method, carry out each side index and performance test with traditional coating, the results are shown in Table 1.
Table 1
Test item | Embodiment 1-3 | Traditional Architecture Decoration coating |
Smell | Smell is pure and fresh, nature | Smell is pungent |
Paint film appearance | White, soft not dazzling, paint film is water-fast, acidproof, alkaline-resisting, anti-yellowing change, to go mouldy, there is texture and fullness ratio | Micro-yellow, paint film easily turn to be yellow, mildew |
Paint film property | The use of fire retardant, greatly can improve resistance combustion temperature, antiseptic and antibiotic agent is anti-mildew, keeps indoor temperature and humidity balance | Do not possess any function |
Duration of service after brushing | With brush with use | Use about brushing rear venting two weeks |
Water tolerance | 108h is without exception | 48h is without exception |
Alkali resistance | 96h is without exception | 36h is without exception |
Existing coating products is no more than the limits of harmful substances standard of national regulation mostly, but more or less all containing certain objectionable impurities in coating products, and the coating products that formula of the present invention and preparation method produce, the content of objectionable impurities is all examined and is not measured, and detected result is in table 2.
Table 2
Claims (8)
1. an interior wall coating, is characterized in that this coating is made up of the component of following weight part: water 100-300 part, titanium dioxide 160-240 part, Paris white 60-90 part, dispersion agent 3-6 part, defoamer 2-5 part, ACRYLIC EMULSION 160-240 part, ethanol 4-6 part, fire retardant 3-7 part, antiseptic and antibiotic agent 2-4 part, plant milk extract 1-3 part.
2. a kind of interior wall coating according to claim 1, is characterized in that described coating is made up of the component of following weight part: water 150-250 part, titanium dioxide 180-220 part, Paris white 70-80 part, dispersion agent 4-5 part, defoamer 3-4 part, ACRYLIC EMULSION 180-220 part, ethanol 4-6, fire retardant 4-6 part, antiseptic and antibiotic agent 2-4 part, plant milk extract 1-3 part.
3. a kind of interior wall coating according to claim 1, is characterized in that described coating is made up of the component of following weight part: 200 parts, water, titanium dioxide 200 parts, Paris white 75 parts, dispersion agent 4 parts, defoamer 4 parts, ACRYLIC EMULSION 200 parts, ethanol 5 parts, fire retardant 5 parts, antiseptic and antibiotic agent 3 parts, plant milk extract 2 parts.
4. a kind of interior wall coating according to claim 1 or 2 or 3, it is characterized in that described plant milk extract is the alcohol extract of following composition, chrysanthemum, lavandula angustifolia, peppermint, soybean, castor-oil plant, each component proportions is: chrysanthemum: lavandula angustifolia: peppermint: soybean: castor-oil plant=1:1:1:2:2.
5. a kind of interior wall coating according to claim 1 or 2 or 3, is characterized in that described fire retardant is the mixture of magnesium hydroxide, aluminium hydroxide, ferric oxide, zinc borate, and the weight ratio of each composition is magnesium hydroxide: aluminium hydroxide: ferric oxide: zinc borate=1:1; 0.5:0.2.
6. a kind of interior wall coating according to claim 1 or 2 or 3, is characterized in that described antiseptic and antibiotic agent is the mixture of ethyl p-hydroxybenzoate and propylben, and both weight ratios are ethyl p-hydroxybenzoate: propylben=1:0.5.
7. the preparation method of a kind of interior wall coating as claimed in claim 1, is characterized in that adopting following steps:
1) measure chrysanthemum, lavandula angustifolia, peppermint, soybean, castor-oil plant by formula, mixing after pulverizing, soaks one week with under the alcohol at normal temperature of 75%, and leach liquor concentrates, plant milk extract of pulverizing to obtain after drying, for subsequent use;
2) part water, dispersion agent and part defoamer are joined in reaction unit to stir and disperse;
3) in reaction unit, continuation interpolation titanium dioxide, Paris white, fire retardant, antiseptic and antibiotic agent, ethanol stir, and are milled to fineness of materials at below 50um;
4) in reaction unit, continue to add ACRYLIC EMULSION, the defoamer of surplus and plant milk extract in reaction unit, stir, add water adjusting viscosity, crosses 200 mesh sieves.
8. the preparation method of a kind of interior wall coating according to claim 7, is characterized in that step 2) in mixing speed be 750-850 rev/min, disperse 40 minutes; In step 3), mixing speed is 800-1000 rev/min, and churning time is 30 minutes; Step 4) stirs 40 minutes under rotating speed is the condition of 700 revs/min, and adjusting viscosity is to 90-110KU.