CN104559390A - Synthetic latex paint powder - Google Patents
Synthetic latex paint powder Download PDFInfo
- Publication number
- CN104559390A CN104559390A CN201510037008.XA CN201510037008A CN104559390A CN 104559390 A CN104559390 A CN 104559390A CN 201510037008 A CN201510037008 A CN 201510037008A CN 104559390 A CN104559390 A CN 104559390A
- Authority
- CN
- China
- Prior art keywords
- powder
- latex paint
- synthetic latex
- emulsion paint
- silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to synthetic latex paint powder and belongs to the technical field of coating. The synthetic latex paint powder comprises the following components in percentage by weight: 10% of titanium dioxide, 8% of barium sulphate, 5% of shell powder, 10% of talcum powder, 2% of aluminium silicate, 16% of kaolin, 39% of heavy calcium carbonate, 8% of wollastonite in powder, 0.2% of a dry powder levelling agent, 0.8% of a dry powder dispersing agent, 0.15% of lithium magnesium silicate and 0.85% of aluminium magnesium silicate. The provided synthetic latex paint powder can be used for effectively improving the properties of the coating and also has a strong ultraviolet ray absorbing and shielding effect, and the adopted raw materials are available, so that the production cost is low, the environmental friendliness is realized, and the stability of the synthetic latex paint powder is extremely high.
Description
Technical field
The present invention relates to a kind of emulsion paint composite powder, belong to technical field of coatings.
Background technology
Emulsion paint is through the development of decades, and it has many advantages compared with other coating, and easy construction, dried coating film are fast, good permeability, water-tolerant.These advantages people due to emulsion paint generally adopt and make emulsion paint obtain significant progress in recent years in indoor and outdoor decoration, along with the development with emulsion paint technology that improves constantly of living standards of the people, Minstry of Housing and Urban-Rural Development of People Republic of China (MOHURD), State Administration for Quality Supervision and Inspection and Quarantine has promulgated the standard and statute of a series of control IAQ (indoor air quality), people are more careful to selecting of upholstery environment friendly emulsion paint, domestic and international Development and Production has gone out some environment-friendly type emulsion paints and has improved air, have developed again now the emulsion paint of some functions, as: mildew-proof latex paint, the environment-friendly type emulsion paints such as absorbing carbon dioxide emulsion paint, these emulsion paints can improve indoor environmental quality to a certain extent, but but reduce other use propertieies of emulsion paint accordingly, production cost is higher simultaneously, stability is not strong, use that can not be relieved safely when people's use.
Summary of the invention
For the deficiency that prior art exists, the invention provides that a kind of shield effectiveness is good, stability is high and the emulsion paint composite powder of environmental protection.
The present invention is achieved by the following technical solutions: a kind of emulsion paint composite powder, be made up of titanium dioxide, barium sulfate, oyster shell whiting, talcum powder, pure aluminium silicate, kaolin, water-ground limestone, wollastonite powder, dry powder flow agent, dry powder dispersion agent, lithium magnesium silicate and neusilin
Its moiety and part by weight following (weight percent):
Further, described talcum powder is hydrous magnesium silicate.
Further, described wollastonite powder is Calucium Silicate powder.
Compared with prior art, the invention has the beneficial effects as follows: emulsion paint composite powder provided by the invention effectively can not only improve coating property, strong absorption, shielding effect can also be had to ultraviolet, the raw material used all easily obtains, therefore production cost is lower, and the stability of environmental protection and product is high.
Embodiment
In order to make those skilled in the art can further understand feature of the present invention and technology contents, the present invention will be described by following preferred embodiment.
Take: titanium dioxide 10%, barium sulfate 8%, oyster shell whiting 5%, talcum powder 10%, pure aluminium silicate 2%, kaolin 16%, water-ground limestone 39%, wollastonite powder 8%, dry powder flow agent 0.2, dry powder dispersion agent 0.8%, lithium magnesium silicate 0.15%, neusilin 0.85%, put into after above-mentioned each component dosage successively in reactor, fully mix, be mixed into emulsion state with 1000-1800 high-speed stirring, fillingly obtain emulsion paint composite powder.
Titanium dioxide has superior whiteness, tinting strength, opacifying power, weathering resistance, thermotolerance and chemical stability, and there is no toxicity, the emulsion paint adding titanium dioxide is bright in luster, opacifying power is high, strong coloring force, and the physical strength of paint film and sticking power high, the generation of crackle can be prevented, prevent simultaneously ultraviolet and moisture through, extend the work-ing life of paint film; Barium sulfate controls the viscosity of emulsion paint, strengthens bright in color and stability; Oyster shell whiting and lithium magnesium silicate can strengthen the ability that emulsion paint purifies air, and absorption obnoxious flavour, regulates humidity; Water-ground limestone, kaolin and talcum powder can increase weathering resistance and the wear resistance of emulsion paint; Neusilin can improve the volatility of emulsion paint; Dry powder flow agent makes emulsion paint surface form very thin unimolecular layer, makes to have good wettability between emulsion paint and coated article, thus overcomes film coated surface, opens beautiful non-uniform face form the disadvantages such as lockhole due to surface.
In sum, be only preferred embodiment of the present invention, not be used for limiting scope of the invention process, all equalizations of doing according to shape, structure, feature and the spirit described in the claims in the present invention scope change and modify, and all should be included in right of the present invention.
Claims (3)
1. an emulsion paint composite powder, is characterized in that: be made up of titanium dioxide, barium sulfate, oyster shell whiting, talcum powder, pure aluminium silicate, kaolin, water-ground limestone, wollastonite powder, dry powder flow agent, dry powder dispersion agent, lithium magnesium silicate and neusilin,
Its moiety and part by weight following (weight percent):
2. a kind of emulsion paint composite powder according to claim 1, is characterized in that: described talcum powder is hydrous magnesium silicate.
3. a kind of emulsion paint composite powder according to claim 1, is characterized in that: described wollastonite powder is Calucium Silicate powder.