CN104846528A - Pima cotton and flax blended yarn jacquard knitting shell fabric - Google Patents
Pima cotton and flax blended yarn jacquard knitting shell fabric Download PDFInfo
- Publication number
- CN104846528A CN104846528A CN201510188346.3A CN201510188346A CN104846528A CN 104846528 A CN104846528 A CN 104846528A CN 201510188346 A CN201510188346 A CN 201510188346A CN 104846528 A CN104846528 A CN 104846528A
- Authority
- CN
- China
- Prior art keywords
- bamboo vinegar
- blended yarn
- flax
- dry
- seconds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to knitting shell fabric, in particular to Pima cotton and flax blended yarn jacquard knitting shell fabric. The shell fabric is formed by weaving 60-80 wt% Pima cotton and 20-40 wt% flax blended yarn; the twist degree of the blended yarn is larger than 900 T/m, and the fineness degree of the blended yarn is larger than 60s; the weaving technology of the knitting shell fabric comprises the steps: conducting flax degumming, blend fiber combining, pre-drawing, lap forming and doubling, combing, spooling, twist setting, blended yarn manufacturing, blended yarn union dyeing and knitting; weaving the dyed blended yarn in an SES series imported computer flat knitting machine, wherein the density of the knitting shell fabric is controlled to be PA not less than 75 column/5 cm and PB not less than 80 row/5 cm; conducting after treatment, wherein after treatment is conducted to the shell fabric with a polyether modified macromolecule polysiloxane finishing agent. The shell fabric has the advantages of being skin protecting, antibacterial, breathable, moisture absorbing, fresh, perspiring, comfortable to wear, crease resistant, stiff and easy to wash.
Description
Technical field
The present invention relates to a kind of knit fabric, particularly relate to a kind of Pima cotton and flax blended spinning jacquard knitting fabric.
Background technology
The general designation of the cotton extra long staple ELS that is of the best quality of Pima, superfine product is cotton than general cotton long 35%, cotton speciality=1-3/8 cun of suede.Pima cotton is a kind of superfine product extra long staple, and the knitwear be made up of this fiber have frivolous, soft, comfortable, the effect such as chafe, is not thus widely used in knitting underskirt product, but the defect such as yielding when this series products to exist when wear stiffness difference and washs.
CN102704108B (2014-9-10) discloses the spinning process of a kind of cotton fiber and numb Sai Er fibre blending yarn, but the fabric panel performance that the method is produced still haves much room for improvement.
Summary of the invention
The object of this invention is to provide a kind of frivolous softness, washing not yielding, wear the cotton and flax blended spinning jacquard knitting fabric of the good Pima of stiffness.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
A kind of Pima cotton and flax blended spinning jacquard knitting fabric, it is cotton by 60-80wt%Pima, 20-40wt% linen blend weaving yarns forms; The twist >900T/m of described blended yarn, fineness >60s;
The weaving process of described knit fabric comprises:
(1) flax degumming;
(2) blend fibre combination, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn;
(3) blended yarn Tone-on-Tone Dyeing;
(4) knitting: the blended yarn after described dyeing to be weaved at SES series import Computerized flat knitting machine, controls the density PA >=75 file/5cm of knit fabric; PB >=80 line/5cm;
(5) Final finishing: the agent of polyether-modified polyphosphazene polymer siloxane finishing is to fabric Final finishing.
Fabric panel density of the present invention:
Lateral density PA: the coil wale number in the 5cm of row direction;
Density PB: number walked crosswise by the coil in coil file direction 5cm;
The present invention twists with the fingers high pima cotton/flax blended spinning blended weave and the corresponding Tone-on-Tone Dyeing technique of blended yarn by high, and highly dense weaving process and corresponding polyether-modified polyphosphazene polymer functional polyorganosiloxane arrange and specifically weave, maintaining, the cotton product of Pima is comfortable, outside the features such as moisture absorption, taking full advantage of linen fibre has powerful high, soft, fineness is good, conduct electricity weak, water suction aproll is fast, the features such as expansion rate is large, select Pima combination that is cotton and linen fibre can improve the spinnability of flax blended spinning and the number of blended yarn simultaneously, improve the skin care improved to skin when product is worn further simultaneously, temperature adjustment function.Product of the present invention have skin care, antibacterial, gas permeability, hygroscopicity, salubrious property and perspire, comfortable and easy to wear, crease-resistant well-pressed, easily the multinomial feature such as to wash, compared with traditional cotton class knit fabric, be especially applicable to the exploitation of clothing knitted product in high-grade cotton class.
As preferably, described Final finishing is included in the agent of polyether-modified polyphosphazene polymer siloxane finishing and passes through with speed of a motor vehicle 30-35m/min, and described polyether-modified polyphosphazene polymer siloxane finishing agent adopts the block polyether polysiloxanes finishing agent of terminal hydroxy group end-blocking and the containing hydrogen silicone oil of low hydrogen content to be composited.
That form high molecular by the reaction arranging process hydroxyl and si-h bond, that there is polyethers section polysiloxanes, improve the stiffness of product, and give fabric softness, the function such as smooth, comfortable and hydrophilic, and make the stiffness that product has softness, smooth and anti-fluffing and anti-pilling function improves Project Product further, and give fabric softness, the function such as smooth, comfortable and hydrophilic.
As preferably, the hydrogen content of described containing hydrogen silicone oil is 1.6-3wt%.
As preferably, described weaving process carries out jacquard weave after being also included in described Final finishing, and described jacquard weave comprises first time loose formula ovens dry, cut pile, the loose formula of second time are dried, the flower pattern half tone of making chromatography.
By jacquard process, Pima cotton and the flax blended spinning extremely refreshing concavo-convex jacquard knitting fabric of type can be prepared.
As preferably, the bake out temperature that the first time pine formula in described jacquard weave step is dried is 130-140 DEG C, and drying time is 5-9min; The bake out temperature that the loose formula of second time is dried is 70-90 DEG C, and drying time is 15-22min; Described cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone of described making chromatography comprises the flower pattern half tone making chromatography of 100-120 order twine.
As preferably, described weaving process carries out bamboo vinegar process after being also included in flax degumming, described bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20-40min in bamboo vinegar treatment fluid tossa being immersed in 40-50 DEG C, the process of secondary bamboo vinegar is 10-30min in secondary bamboo vinegar treatment fluid tossa being immersed in 55-80 DEG C, a described bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20-30g/L, described secondary bamboo vinegar treatment fluid is the bamboo vinegar of weight ratio 1:0.1-0.2:60-100, the mixed solution of ethylenediamine tetra-acetic acid and water composition.
As preferably, described blended yarn Tone-on-Tone Dyeing carries out chromatography after being included in dispersion pad-dry-cure dyeing, and described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography.
As preferably, described dispersion pad-dry-cure dyeing is two baths dyeing, first pads DISPERSE DYES dye liquor at 175 DEG C-180 DEG C, then carries out drying, wax baking, reduction cleaning, washes, soaps, washes, dries; Pad reducing dye dye liquor again, then carry out reduction cleaning, washing, oxidation, wash, soap, wash, dry, pad chlorine again and wash promoting agent, oven dry, described DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R.
As preferably; the concrete grammar of described dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 40%-65%; then dry 30 seconds-60 seconds at 60 DEG C-80 DEG C, bake 45 seconds-60 seconds at 100 DEG C-120 DEG C, then adopt concentration to be that the caustic soda of 25-30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning; carry out successively again washing, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then concentration is adopted to be that the caustic soda of 25-30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying.
Detailed description of the invention
embodiment one
(1) flax degumming;
(2) 60wt%Pima cotton, the combination of 40wt% linen blend, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn; The twist 1000T/m of obtained blended yarn, fineness 70s;
(3) blended yarn Tone-on-Tone Dyeing: carry out chromatography after dispersion pad-dry-cure dyeing, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 40%; then dry 30 seconds at 60 DEG C; 45 seconds are baked at 100 DEG C; adopt concentration to be that the caustic soda of 25g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 85 DEG C of temperature 45 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%, then concentration is adopted to be that the caustic soda of 25g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of temperature 45 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R;
(4) knitting: weaved at SES series import Computerized flat knitting machine by the blended yarn after described dyeing, the density PA controlling knit fabric is 75 files/5cm; PB is 80 lines/5cm;
(5) Final finishing: pass through with speed of a motor vehicle 30m/min in the agent of polyether-modified polyphosphazene polymer siloxane finishing, the block polyether polysiloxanes finishing agent of described polyether-modified polyphosphazene polymer siloxane finishing agent employing terminal hydroxy group end-blocking and hydrogen content are that the containing hydrogen silicone oil of 1.6wt% is composited;
(6) jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 130 DEG C, and drying time is 5min; The bake out temperature that the loose formula of second time is dried is 70 DEG C, and drying time is 15min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 100 order twines.
embodiment two
(1) flax degumming;
(2) 80wt%Pima cotton, the combination of 20wt% linen blend, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn; The twist 1200T/m of obtained blended yarn, fineness 80s;
(3) blended yarn Tone-on-Tone Dyeing: carry out chromatography after dispersion pad-dry-cure dyeing, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 65%; then dry 60 seconds at 80 DEG C; 60 seconds are baked at 120 DEG C; adopt concentration to be that the caustic soda of 30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 95 DEG C of temperature 60 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 65%, then concentration is adopted to be that the caustic soda of 30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 95 DEG C of temperature 60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R;
(4) knitting: the blended yarn after described dyeing to be weaved at SES series import Computerized flat knitting machine, controls the density PA85 file/5cm of knit fabric; PB90 line/5cm;
(5) Final finishing: pass through with speed of a motor vehicle 35m/min in the agent of polyether-modified polyphosphazene polymer siloxane finishing, the block polyether polysiloxanes finishing agent of described polyether-modified polyphosphazene polymer siloxane finishing agent employing terminal hydroxy group end-blocking and hydrogen content are that the containing hydrogen silicone oil of 3wt% is composited;
(6) jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 140 DEG C, and drying time is 9min; The bake out temperature that the loose formula of second time is dried is 90 DEG C, and drying time is 22min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 120 order twines.
embodiment three
(1) flax degumming;
(2) 70wt%Pima cotton, the combination of 30wt% linen blend, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn; The twist 1100T/m of obtained blended yarn, fineness 100s;
(3) blended yarn Tone-on-Tone Dyeing: carry out chromatography after dispersion pad-dry-cure dyeing, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 55%; then dry 30 seconds-60 seconds at 70 DEG C; 50 seconds are baked at 110 DEG C; adopt concentration to be that the caustic soda of 28g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 90 DEG C of temperature 50 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 48%, then concentration is adopted to be that the caustic soda of 28g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 90 DEG C of temperature 50 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R;
(4) knitting: the blended yarn after described dyeing to be weaved at SES series import Computerized flat knitting machine, controls the density PA88 file/5cm of knit fabric; PB88 line/5cm;
(5) Final finishing: pass through with speed of a motor vehicle 33m/min in the agent of polyether-modified polyphosphazene polymer siloxane finishing, the block polyether polysiloxanes finishing agent of described polyether-modified polyphosphazene polymer siloxane finishing agent employing terminal hydroxy group end-blocking and hydrogen content are that the containing hydrogen silicone oil of 2.6wt% is composited;
(6) jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 135 DEG C, and drying time is 6min; The bake out temperature that the loose formula of second time is dried is 80 DEG C, and drying time is 15-22min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 110 order twines.
Embodiment four
With embodiment one, bamboo vinegar process is carried out after being also included in flax degumming unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20min in bamboo vinegar treatment fluid tossa being immersed in 40 DEG C, the process of secondary bamboo vinegar is 10min in secondary bamboo vinegar treatment fluid tossa being immersed in 55 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.1:60, ethylenediamine tetra-acetic acid and water composition.
Embodiment five
With embodiment two, bamboo vinegar process is carried out after being also included in flax degumming unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 40min in bamboo vinegar treatment fluid tossa being immersed in 50 DEG C, the process of secondary bamboo vinegar is 30min in secondary bamboo vinegar treatment fluid tossa being immersed in 80 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 30g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.2:100, ethylenediamine tetra-acetic acid and water composition.
Embodiment six
With embodiment two, bamboo vinegar process is carried out after being also included in flax degumming unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 30min in bamboo vinegar treatment fluid tossa being immersed in 45 DEG C, the process of secondary bamboo vinegar is 20min in secondary bamboo vinegar treatment fluid tossa being immersed in 60 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 25g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.12:80, ethylenediamine tetra-acetic acid and water composition.
Comparative example one
With embodiment one, unlike 50wt%Pima is cotton, 50wt% linen blend combination, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn; The twist 800T/m of obtained blended yarn, fineness 50s.
Comparative example two
With embodiment two, weave at SES series import Computerized flat knitting machine unlike by the blended yarn after dyeing, control the density PA 60 files/5cm of knit fabric; PB 70 lines/5cm; The finishing agent that Final finishing adopts is antistatic additive SN.
In two steps, the first step is evaluation feel style to hand feel evaluation, comprises the performances such as flexibility, fluffy, smooth, elasticity, active, stiffness; Second step is rating, and feel grading is divided into 5 grades, and 1 grade the poorest, and 5 grades best, and evaluation result is averaged.
The bamboo charcoal fibre face fabric performance comparison of table 3 embodiment and comparative example
After testing, the embodiment of the present invention one-embodiment six product content of formaldehyde :≤75ppm; Color fastness to water: >=3 grades; Color fastness to washing: >=3 grades; Colour fastness to rubbing (unlubricated friction): >=3 grades, colour fastness to rubbing (wet and rub): >=2-3 level, ecological criteria meets GB18401.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this description, as long as but be all subject to the protection of Patent Law in right of the present invention.
Claims (9)
1. Pima cotton and a flax blended spinning jacquard knitting fabric, is characterized in that: it is cotton by 60-80wt%Pima, 20-40wt% linen blend weaving yarns forms; The twist >900T/m of described blended yarn, fineness >60s;
The weaving process of described knit fabric comprises:
(1) flax degumming;
(2) blend fibre combination, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn;
(3) blended yarn Tone-on-Tone Dyeing;
(4) knitting: the blended yarn after described dyeing to be weaved at SES series import Computerized flat knitting machine, controls the density PA >=75 file/5cm of knit fabric; PB >=80 line/5cm;
(5) Final finishing: the agent of polyether-modified polyphosphazene polymer siloxane finishing is to fabric Final finishing.
2. a kind of Pima cotton according to claim 1 and flax blended spinning jacquard knitting fabric, it is characterized in that: described Final finishing is included in the agent of polyether-modified polyphosphazene polymer siloxane finishing and passes through with speed of a motor vehicle 30-35m/min, described polyether-modified polyphosphazene polymer siloxane finishing agent adopts the block polyether polysiloxanes finishing agent of terminal hydroxy group end-blocking and the containing hydrogen silicone oil of low hydrogen content to be composited.
3. a kind of Pima cotton according to claim 2 and flax blended spinning jacquard knitting fabric, is characterized in that: the hydrogen content of described containing hydrogen silicone oil is 1.6-3wt%.
4. a kind of Pima cotton according to claim 1 and flax blended spinning jacquard knitting fabric, it is characterized in that: described weaving process carries out jacquard weave after being also included in described Final finishing, described jacquard weave comprises the flower pattern half tone of first time loose formula oven dry, cut pile, the loose formula oven dry of second time, making chromatography.
5. a kind of Pima cotton according to claim 4 and flax blended spinning jacquard knitting fabric, is characterized in that: the bake out temperature that the first time pine formula in described jacquard weave step is dried is 130-140 DEG C, and drying time is 5-9min; The bake out temperature that the loose formula of second time is dried is 70-90 DEG C, and drying time is 15-22min; Described cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone of described making chromatography comprises the flower pattern half tone making chromatography of 100-120 order twine.
6. a kind of Pima cotton according to claim 3 or 5 and flax blended spinning jacquard knitting fabric, it is characterized in that: described weaving process carries out bamboo vinegar process after being also included in flax degumming, described bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20-40min in bamboo vinegar treatment fluid tossa being immersed in 40-50 DEG C, the process of secondary bamboo vinegar is 10-30min in secondary bamboo vinegar treatment fluid tossa being immersed in 55-80 DEG C, a described bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20-30g/L, described secondary bamboo vinegar treatment fluid is the bamboo vinegar of weight ratio 1:0.1-0.2:60-100, the mixed solution of ethylenediamine tetra-acetic acid and water composition.
7. a kind of Pima cotton according to claim 6 and flax blended spinning jacquard knitting fabric, it is characterized in that: described blended yarn Tone-on-Tone Dyeing carries out chromatography after being included in dispersion pad-dry-cure dyeing, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography.
8. a kind of Pima cotton according to claim 7 and flax blended spinning jacquard knitting fabric; it is characterized in that: described dispersion pad-dry-cure dyeing is two bath dyeing; first pad DISPERSE DYES dye liquor at 175 DEG C-180 DEG C, then carry out drying, wax baking, reduction cleaning, wash, soap, wash, dry; Pad reducing dye dye liquor again, then carry out reduction cleaning, washing, oxidation, wash, soap, wash, dry, pad chlorine again and wash promoting agent, oven dry, described DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R.
9. a kind of Pima cotton according to claim 8 and flax blended spinning jacquard knitting fabric, it is characterized in that: the concrete grammar of described dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then dry 30 seconds-60 seconds at 60 DEG C-80 DEG C, 45 seconds-60 seconds are baked at 100 DEG C-120 DEG C, concentration is adopted to be that the caustic soda of 25-30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, wash successively again, basic soap lotion DF-5 is adopted to soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, dry, one bath terminates, then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then concentration is adopted to be that the caustic soda of 25-30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying.