CN104846527A - Environment-friendly wool and SRN fiber blending jacquard warm-keeping knitted fabric - Google Patents
Environment-friendly wool and SRN fiber blending jacquard warm-keeping knitted fabric Download PDFInfo
- Publication number
- CN104846527A CN104846527A CN201510188123.7A CN201510188123A CN104846527A CN 104846527 A CN104846527 A CN 104846527A CN 201510188123 A CN201510188123 A CN 201510188123A CN 104846527 A CN104846527 A CN 104846527A
- Authority
- CN
- China
- Prior art keywords
- srn
- bamboo vinegar
- fabric
- dry
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to knitted fabrics, in particular to an environment-friendly wool and SRN fiber blending jacquard warm-keeping knitted fabric. The weaving process of the knitted fabric includes the step of conducting blending and combing of 60wt%-80wt% of wool and 20wt%-40wt% of SRN fibers, pre-drawing, lap forming and doubling, carding, spooling and twist setting to obtain blended yarn; the step of conducting blended yarn union dyeing sequentially including the procedures of single-face singeing, scouring and bleaching, sizing, mercerizing, dispersed thermosol dyeing and topping, wherein gas singeing is specifically adopted in the single-face singeing process, singeing is conducted twice at the front sides of two burners, the travel speed is 80 m/min-85 m/min, topping is conducted after dispersed thermosol dyeing, and reactive dye or indanthrene dye is adopted for topping; the step of conducing weaving, wherein the dyed blended yarn is woven into the fabric through an MACH-2 sheet forming computerized flat knitting machine, and the two faces of the fabric are of different structures; the step of conducting aftertreatment, wherein a hyperbranched polyether amidogen modified polysiloxane finishing agent is adopted for conducting aftertreatment on the fabric. The fabric has the advantages of being soft, fluffy, capable of keeping warm and having tender luster, anti-pilling, anti-wrinkling, stiff, smooth, quick-drying and anti-ultraviolet.
Description
Technical field
The present invention relates to a kind of knit fabric, particularly relate to a kind of environment-friendly type wool and SRN fiber blend jacquard weave thermal protection knitted fabric.
Background technology
Adopt high-performance fiber, in conjunction with the fibrous material with environmental benefit, exploitation high added value low-carbon ecological textiles is the target that current textile industry is pursued.Wool fibre elastic recovery is good, has the good characteristics such as high-hydroscopicity, warmth retention property, durability, but also exist fracture strength low, easily the defect such as to go mouldy.
CN201390846Y (2010-1-27) discloses a kind of knitted double-sided fabric, and its front is bird's eye, but this fabric panel performance still haves much room for improvement.
Summary of the invention
The object of this invention is to provide a kind of soft, fluffy, warming, gloss is soft, ANTIPILLING, crease-resistant well-pressed, the anti-ultraviolet environment-friendly type wool of quick-drying and SRN fiber blend jacquard weave thermal protection knitted fabric.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
A kind of environment-friendly type wool and SRN fiber blend jacquard weave thermal protection knitted fabric,
The weaving process of described knit fabric comprises:
60-80wt% wool, 20-40wt%SRN fiber blend combine, pre-drawing, and bar is also rolled up, combing, winder, and dead twist makes blended yarn;
Blended yarn Tone-on-Tone Dyeing: comprise step successively: one side is singed, boil drift, sizing, mercerising, dispersion pad-dry-cure dyeing and chromatography; Described one side singeing specifically gas singeing, two burner fronts singe twice, speed of a motor vehicle 80-85m/min be included in dispersion pad-dry-cure dyeing after carry out, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography;
Knitting: the fabric blended yarn after described dyeing being weaved two sides different structure at the complete shaping Computerized flat knitting machine of MACH-2;
Final finishing: hyperbranched polyether amino modified polysiloxane finishing agent is to fabric Final finishing.
SRN(Sorona) fiber is the high-performance environment-friendly fiber type of du pont company's exploitation, this fiber is except having the premium properties of conventional ptt fiber, have more production process clean environment firendly, the advantages such as energy resource consumption is few, CO2 emission is few, simultaneously recyclable, can be recycled.Both fibers are carried out the advantage that blending can play respective fiber, obviously can improve elasticity and the wrinkle resistance of conventional hair/terylene fabric.
The present invention is by wool Tone-on-Tone Dyeing technique, the knitting corresponding to SRN fiber blend yarn blended weave and blended yarn, and hyperbranched polyether amino modified polysiloxane finishing agent, production two sides has the fabric of different pattern structure, to the skin care of skin, temperature adjustment function when further raising improves product wrinkle resistance, shape-retaining ability and wears, enhanced products is hydrophilic, soft, fluffy, plentiful, without prodding and itching feeling function.Product of the present invention is outside the feature with wool products such as softness, fluffy, warming, gloss is soft, there is again the advantage such as ANTIPILLING, crease-resistant well-pressed, quick-drying uvioresistant simultaneously, compared with traditional cotton class knit fabric, be especially applicable to the exploitation of clothing knitted product in high-grade cotton class.
As preferably, described Final finishing is included in the agent of polyether-modified polyphosphazene polymer siloxane finishing and passes through with speed of a motor vehicle 30-35m/min.
As preferably, the twist >900T/m of described blended yarn, fineness >60s;
Blended yarn after described dyeing is woven into the bird's eye tissue fabric of two sides different structure by described knitting step, controls the density PA >=75 file/5cm of knit fabric; PB >=80 line/5cm.
By controlling fabric braided parameter, the gas permeability of fabric, warmth retention property and whole style can be improved.
As preferably, described weaving process carries out jacquard weave after being also included in described Final finishing, and described jacquard weave comprises first time loose formula ovens dry, cut pile, the loose formula of second time are dried, the flower pattern half tone of making chromatography.
By jacquard process, Pima cotton and the flax blended spinning extremely refreshing concavo-convex jacquard knitting fabric of type can be prepared.
As preferably, the bake out temperature that the first time pine formula in described jacquard weave step is dried is 130-140 DEG C, and drying time is 5-9min; The bake out temperature that the loose formula of second time is dried is 70-90 DEG C, and drying time is 15-22min; Described cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone of described making chromatography comprises the flower pattern half tone making chromatography of 100-120 order twine.
As preferably, described weaving process carries out bamboo vinegar process after being also included in knitting step, described bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20-40min in bamboo vinegar treatment fluid tossa being immersed in 40-50 DEG C, the process of secondary bamboo vinegar is 10-30min in secondary bamboo vinegar treatment fluid tossa being immersed in 55-80 DEG C, a described bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20-30g/L, described secondary bamboo vinegar treatment fluid is the bamboo vinegar of weight ratio 1:0.1-0.2:60-100, the mixed solution of ethylenediamine tetra-acetic acid and water composition.
As preferably, described blended yarn Tone-on-Tone Dyeing carries out chromatography after being included in dispersion pad-dry-cure dyeing, and described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography.
As preferably, described dispersion pad-dry-cure dyeing is two baths dyeing, first pads DISPERSE DYES dye liquor at 175 DEG C-180 DEG C, then carries out drying, wax baking, reduction cleaning, washes, soaps, washes, dries; Pad reducing dye dye liquor again, then carry out reduction cleaning, washing, oxidation, wash, soap, wash, dry, pad chlorine again and wash promoting agent, oven dry, described DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R.
As preferably; the concrete grammar of described dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 40%-65%; then dry 30 seconds-60 seconds at 60 DEG C-80 DEG C, bake 45 seconds-60 seconds at 100 DEG C-120 DEG C, then adopt concentration to be that the caustic soda of 25-30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning; carry out successively again washing, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then concentration is adopted to be that the caustic soda of 25-30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying.
Detailed description of the invention
Embodiment one
70wt% wool, 30wt%SRN fiber blend combine, pre-drawing, and bar is also rolled up, combing, winder, and dead twist makes blended yarn;
Blended yarn Tone-on-Tone Dyeing: comprise step successively: one side is singed, boil drift, sizing, mercerising, dispersion pad-dry-cure dyeing and chromatography; One side singeing specifically gas singeing, two burner fronts singe twice, speed of a motor vehicle 80m/min be included in dispersion pad-dry-cure dyeing after carry out, chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography;
Chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 40%; then dry 30 seconds at 60 DEG C; 45 seconds are baked at 100 DEG C; adopt concentration to be that the caustic soda of 25g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 85 DEG C of temperature 45 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%, then concentration is adopted to be that the caustic soda of 25g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of temperature 45 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R; Knitting: the fabric blended yarn after dyeing being weaved two sides different structure at the complete shaping Computerized flat knitting machine of MACH-2; The density PA of fabric is 75 files/5cm; PB is 80 lines/5cm;
Final finishing: pass through with speed of a motor vehicle 30m/min, to fabric Final finishing at hyperbranched polyether amino modified polysiloxane finishing agent;
Jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 130 DEG C, and drying time is 5min; The bake out temperature that the loose formula of second time is dried is 70 DEG C, and drying time is 15min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 100 order twines.
Embodiment two
60wt% wool, 40wt%SRN fiber blend combine, pre-drawing, and bar is also rolled up, combing, winder, and dead twist makes blended yarn;
Blended yarn Tone-on-Tone Dyeing: comprise step successively: one side is singed, boil drift, sizing, mercerising, dispersion pad-dry-cure dyeing and chromatography; One side singeing specifically gas singeing, two burner fronts singe twice, speed of a motor vehicle 85m/min be included in dispersion pad-dry-cure dyeing after carry out, chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography;
Chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 65%; then dry 60 seconds at 80 DEG C; 60 seconds are baked at 120 DEG C; adopt concentration to be that the caustic soda of 30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 95 DEG C of temperature 60 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 65%, then concentration is adopted to be that the caustic soda of 30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 95 DEG C of temperature 60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R;
Knitting: the fabric blended yarn after dyeing being weaved two sides different structure at the complete shaping Computerized flat knitting machine of MACH-2; The density PA85 file/5cm of fabric; PB90 line/5cm;
Final finishing: pass through with speed of a motor vehicle 35m/min, to fabric Final finishing at hyperbranched polyether amino modified polysiloxane finishing agent;
Jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 140 DEG C, and drying time is 9min; The bake out temperature that the loose formula of second time is dried is 90 DEG C, and drying time is 22min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 120 order twines.
Embodiment three
80wt% wool, 20wt%SRN fiber blend combine, pre-drawing, and bar is also rolled up, combing, winder, and dead twist makes blended yarn;
Blended yarn Tone-on-Tone Dyeing: comprise step successively: turn over cloth, one side is singed, boil drift, sizing, mercerising, dispersion pad-dry-cure dyeing and chromatography; One side singeing specifically gas singeing, two burner fronts singe twice, speed of a motor vehicle 82m/min be included in dispersion pad-dry-cure dyeing after carry out, chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography;
Chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography; The concrete grammar of dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor; four leachings one are adopted to roll mode; pick-up 55%; then dry 50 seconds at 70 DEG C; 50 seconds are baked at 110 DEG C; adopt concentration to be that the caustic soda of 28g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, then carry out successively washing, adopt basic soap lotion DF-5 soap at 90 DEG C of temperature 50 seconds, washing, to dry, a bath terminates; Then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 48%, then concentration is adopted to be that the caustic soda of 28g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 90 DEG C of temperature 50 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying;
DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R;
Turn over cloth requirement unanimously positive and negative, margin to seam is straight, requires flat, straight, neat, firm, and pin is close at 50-65 pin/15cm, and both sides are encrypted to 7-9 pin/cm, prevents from dyeing and printing process, produce wrinkle bar, skew of weft, crimping;
Knitting: the fabric blended yarn after dyeing being weaved two sides different structure at the complete shaping Computerized flat knitting machine of MACH-2; The density PA88 file/5cm of fabric; PB88 line/5cm;
Final finishing: pass through with speed of a motor vehicle 33m/min, to fabric Final finishing at hyperbranched polyether amino modified polysiloxane finishing agent;
Jacquard weave: the flower pattern half tone of first time loose formula oven dry, cut pile, the oven dry of second time loose formula, making chromatography: the bake out temperature that loose formula is dried for the first time is 135 DEG C, and drying time is 6min; The bake out temperature that the loose formula of second time is dried is 80 DEG C, and drying time is 15-22min; Cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone making chromatography comprises the flower pattern half tone making chromatography of 110 order twines.
Embodiment four
With embodiment one, bamboo vinegar process is carried out after being also included in weaving step unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20min in bamboo vinegar treatment fluid tossa being immersed in 40 DEG C, the process of secondary bamboo vinegar is 10min in secondary bamboo vinegar treatment fluid tossa being immersed in 55 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.1:60, ethylenediamine tetra-acetic acid and water composition.
Embodiment five
With embodiment two, bamboo vinegar process is carried out after being also included in weaving step unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 40min in bamboo vinegar treatment fluid tossa being immersed in 50 DEG C, the process of secondary bamboo vinegar is 30min in secondary bamboo vinegar treatment fluid tossa being immersed in 80 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 30g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.2:100, ethylenediamine tetra-acetic acid and water composition.
Embodiment six
With embodiment two, bamboo vinegar process is carried out after being also included in weaving step unlike weaving process, bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 30min in bamboo vinegar treatment fluid tossa being immersed in 45 DEG C, the process of secondary bamboo vinegar is 20min in secondary bamboo vinegar treatment fluid tossa being immersed in 60 DEG C, a bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 25g/L, and secondary bamboo vinegar treatment fluid is the mixed solution of the bamboo vinegar of weight ratio 1:0.12:80, ethylenediamine tetra-acetic acid and water composition.
Comparative example one
With embodiment one, combine unlike by 90wt% wool, 10wt%SRN fiber blend, pre-drawing, bar is also rolled up, combing, winder, and dead twist makes blended yarn; The twist 800T/m of obtained blended yarn, fineness 50s.
Comparative example two
With embodiment two, weave at SES series import Computerized flat knitting machine unlike by the blended yarn after dyeing, control the density PA 60 files/5cm of knit fabric; PB 70 lines/5cm; The finishing agent that Final finishing adopts is antistatic additive SN, does not comprise one side and singe and chromatography in blended yarn Tone-on-Tone Dyeing.
In two steps, the first step is evaluation feel style to hand feel evaluation, comprises softness, fluffy, warming, ANTIPILLING, the crease-resistant performance such as well-pressed; Second step is rating, and feel grading is divided into 5 grades, and 1 grade the poorest, and 5 grades best, and evaluation result is averaged.
The bamboo charcoal fibre face fabric performance comparison of table 3 embodiment and comparative example
After testing, the embodiment of the present invention one-embodiment six product ANTIPILLING grade >=3; Warming rate (%) >=30;
Content of formaldehyde :≤75ppm; Color fastness to water: >=3 grades; Color fastness to washing: >=3 grades; Colour fastness to rubbing (unlubricated friction): >=3 grades, colour fastness to rubbing (wet and rub): >=2-3 level, ecological criteria meets GB18401.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this description, as long as but be all subject to the protection of Patent Law in right of the present invention.
Claims (9)
1. environment-friendly type wool and a SRN fiber blend jacquard weave thermal protection knitted fabric, is characterized in that: the weaving process of described knit fabric comprises:
60-80wt% wool, 20-40wt%SRN fiber blend combine, pre-drawing, and bar is also rolled up, combing, winder, and dead twist makes blended yarn;
Blended yarn Tone-on-Tone Dyeing: comprise step successively: one side is singed, boil drift, sizing, mercerising, dispersion pad-dry-cure dyeing and chromatography; Described one side singeing specifically gas singeing, two burner fronts singe twice, speed of a motor vehicle 80-85m/min be included in dispersion pad-dry-cure dyeing after carry out, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography;
Knitting: the fabric blended yarn after described dyeing being weaved two sides different structure at the complete shaping Computerized flat knitting machine of MACH-2;
Final finishing: hyperbranched polyether amino modified polysiloxane finishing agent is to fabric Final finishing.
2. a kind of environment-friendly type wool according to claim 1 and SRN fiber blend jacquard weave thermal protection knitted fabric, is characterized in that: described Final finishing is included in the agent of polyether-modified polyphosphazene polymer siloxane finishing and passes through with speed of a motor vehicle 30-35m/min.
3. a kind of environment-friendly type wool according to claim 2 and SRN fiber blend jacquard weave thermal protection knitted fabric, is characterized in that: the twist >900T/m of described blended yarn, fineness >60s;
Blended yarn after described dyeing is woven into the bird's eye tissue fabric of two sides different structure by described knitting step, controls the density PA >=75 file/5cm of knit fabric; PB >=80 line/5cm.
4. a kind of environment-friendly type wool according to claim 1 and SRN fiber blend jacquard weave thermal protection knitted fabric, it is characterized in that: described weaving process carries out jacquard weave after being also included in described Final finishing, described jacquard weave comprises the flower pattern half tone of first time loose formula oven dry, cut pile, the loose formula oven dry of second time, making chromatography.
5. a kind of environment-friendly type wool according to claim 4 and SRN fiber blend jacquard weave thermal protection knitted fabric, is characterized in that: the bake out temperature that the first time pine formula in described jacquard weave step is dried is 130-140 DEG C, and drying time is 5-9min; The bake out temperature that the loose formula of second time is dried is 70-90 DEG C, and drying time is 15-22min; Described cut pile step comprises the cut pile along hair and more than three times; The flower pattern half tone of described making chromatography comprises the flower pattern half tone making chromatography of 100-120 order twine.
6. a kind of environment-friendly type wool according to claim 3 or 5 and SRN fiber blend jacquard weave thermal protection knitted fabric, it is characterized in that: described weaving process carries out bamboo vinegar process after being also included in knitting step, described bamboo vinegar process comprises a bamboo vinegar process and the process of secondary bamboo vinegar, a bamboo vinegar process is 20-40min in bamboo vinegar treatment fluid tossa being immersed in 40-50 DEG C, the process of secondary bamboo vinegar is 10-30min in secondary bamboo vinegar treatment fluid tossa being immersed in 55-80 DEG C, a described bamboo vinegar treatment fluid is the bamboo vinegar aqueous solution of 20-30g/L, described secondary bamboo vinegar treatment fluid is the bamboo vinegar of weight ratio 1:0.1-0.2:60-100, the mixed solution of ethylenediamine tetra-acetic acid and water composition.
7. a kind of environment-friendly type wool according to claim 6 and SRN fiber blend jacquard weave thermal protection knitted fabric, it is characterized in that: described blended yarn Tone-on-Tone Dyeing carries out chromatography after being included in dispersion pad-dry-cure dyeing, described chromatography adopts REACTIVE DYES or intellectual circle's dyestuff to carry out chromatography.
8. a kind of environment-friendly type wool according to claim 7 and SRN fiber blend jacquard weave thermal protection knitted fabric; it is characterized in that: described dispersion pad-dry-cure dyeing is two bath dyeing; first pad DISPERSE DYES dye liquor at 175 DEG C-180 DEG C, then carry out drying, wax baking, reduction cleaning, wash, soap, wash, dry; Pad reducing dye dye liquor again, then carry out reduction cleaning, washing, oxidation, wash, soap, wash, dry, pad chlorine again and wash promoting agent, oven dry, described DISPERSE DYES is LXF series dyes, ETD is blue, ETD is red, SBL grey at least one, reducing dye is at least one in olive T, blue ARN, red R, black ES-SE, blue RSN, blue CLF, purple 2R.
9. a kind of environment-friendly type wool according to claim 8 and SRN fiber blend jacquard weave thermal protection knitted fabric, it is characterized in that: the concrete grammar of described dispersion pad-dry-cure dyeing is: semi-finished product pad DISPERSE DYES dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then dry 30 seconds-60 seconds at 60 DEG C-80 DEG C, 45 seconds-60 seconds are baked at 100 DEG C-120 DEG C, concentration is adopted to be that the caustic soda of 25-30g/L and sodium hydrosulfite reducing solution carry out reduction cleaning again, wash successively again, basic soap lotion DF-5 is adopted to soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, dry, one bath terminates, then again semi-finished product are padded reducing dye dye liquor, four leachings one are adopted to roll mode, pick-up 40%-65%, then concentration is adopted to be that the caustic soda of 25-30g/ L and sodium hydrosulfite reducing solution carry out reduction cleaning, carry out successively again washing, be oxidized, wash, adopt basic soap lotion DF-5 soap at 85 DEG C of-95 DEG C of temperature 45 seconds-60 seconds, washing, to dry, finally pad chlorine and wash promoting agent RFC-39, then carry out drying.