CN104845650B - 控制焦炭m10指标的炼焦配煤方法 - Google Patents

控制焦炭m10指标的炼焦配煤方法 Download PDF

Info

Publication number
CN104845650B
CN104845650B CN201510265619.XA CN201510265619A CN104845650B CN 104845650 B CN104845650 B CN 104845650B CN 201510265619 A CN201510265619 A CN 201510265619A CN 104845650 B CN104845650 B CN 104845650B
Authority
CN
China
Prior art keywords
coal
coke
rich
coking
bottle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510265619.XA
Other languages
English (en)
Other versions
CN104845650A (zh
Inventor
宋子逵
薛改凤
王元生
陈鹏
张雪红
鲍俊芳
项茹
詹立志
陈细涛
任玉明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Iron and Steel Co Ltd
Original Assignee
Wuhan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Iron and Steel Co Ltd filed Critical Wuhan Iron and Steel Co Ltd
Priority to CN201510265619.XA priority Critical patent/CN104845650B/zh
Publication of CN104845650A publication Critical patent/CN104845650A/zh
Application granted granted Critical
Publication of CN104845650B publication Critical patent/CN104845650B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种控制焦炭M10指标的炼焦配煤方法，该方法中各单种煤的配比按重量百分比为：气煤：10～15％，气肥煤：0～10％，肥煤10～15％，1/3焦煤：20～30％；焦煤：40～50％，瘦煤：5～10％。其中，气肥煤与肥煤之和≤20％，气肥煤与挥发分在34％以上的肥煤之和≤15％。本发明根据强黏结性煤种的不同性质，在气煤配用比例较高时，选择性的调整参与配煤的煤种及配比，通过控制低变质程度、高挥发分煤种的总量，在保证配合煤具有一定黏结性的情况下，减少焦饼中心大气孔结构的生成，从而达到控制焦炭M10的目的。

Description

控制焦炭M10指标的炼焦配煤方法
技术领域
本发明属于炼焦配煤技术领域，具体涉及一种控制焦炭M10指标的炼焦配煤方法
背景技术
作为高炉内的燃料、骨架和还原剂，焦炭是高炉运行不可或缺的原燃料。随着高炉大型化、强化冶炼和富氧喷吹技术的发展，高炉对焦炭质量要求越来越高，侧重点也在发生着变化。从最开始的追求冷态强度 (抗碎强度M40，耐磨强度M10)到中期的追求热态性能(反应性CRI，反应后强度CSR)。但是随着焦炭反应后强度的不断提高，其对高炉顺行稳定性的提升已经到了一个瓶颈，而在这样一个环境下，冷态强度中的耐磨强度M10由于其直接影响着高炉内料柱的透气性，对高炉焦比和利用系数的影响就显得更加重要了。
在现如今钢铁市场下滑的环境下，各大钢企都在不断的压缩生产配煤成本，低价的劣质煤种所占的比例越来越高，这类劣质煤种势必会影响焦炭的M10指标。例如，气煤即对焦炭M10具有劣化影响作用，这是因为，一方面气煤是弱黏结性煤，配入后会降低配合煤的黏结性，导致配合煤成焦后焦粉增多，M10劣化；二是气煤挥发分较高，当比例配入较高时，可能会引起焦饼中心生成较大气孔，孔壁较薄，从而导致耐磨性降低，M10劣化。因此若能在劣质煤配比较高的情况下，优化控制焦炭M10，则既能降低配煤成本，又能改善高炉透气性，降低燃料比，对整个钢企的可持续发展有重要意义。
发明内容
本发明的目的在于提供一种在气煤配比达到10～15％情况下，稳定控制焦炭耐磨强度(干熄焦M10≤6.0％，湿熄焦M10≤7.0％)的配煤方法，以保证在配煤成本较低的情况下，保障焦炭质量。
为实现上述目的，本发明采用的技术方案包括气煤、气肥煤、肥煤、 1/3焦煤、焦煤和瘦煤。
各单种煤的配比按重量百分比为：
气煤：10～15％，气肥煤：0～10％，肥煤10～15％，1/3焦煤：20～ 30％；焦煤：40～50％，瘦煤：5～10％。
其中，气肥煤与肥煤之和≤20％，气肥煤与挥发分在34％以上的肥煤之和≤15％。
进一步地，各单种煤的配比按重量百分比为：
气煤：10～12％，气肥煤：5～9％，肥煤10～12％，1/3焦煤：25～ 28％；焦煤：40～43％，瘦煤：6～8％。
气煤作为弱黏结性煤，配入后会降低配合煤黏结性，从而劣化M10。为提高焦炭的耐磨强度，通常的办法是在提高气煤比例的同时提高强黏结性煤种比例，以调整配合煤黏结性。但本发明的发明人经过长期的研究发现，单纯的增加强黏结性煤种配比并不能较好地解决上述技术问题，还应该根据强黏结性煤种的不同性质，选择性的调整。当气煤比例在10～15％时，高挥发分的气肥煤比例应控制在10％以内，若同时配用了挥发分在34％以上的肥煤时，气肥煤+该类肥煤之和应在15％以内，且气肥煤与肥煤的总量不能超过20％。因此，本发明通过控制低变质程度、高挥发分煤种(气煤、气肥煤、高挥发分肥煤)的总量，在保证配合煤具有一定黏结性的情况下，减少焦饼中心大气孔结构的生成，从而达到控制焦炭M10的目的。
具体实施方式
以下结合具体实施方式对本发明作进一步详细的说明。
本发明的炼焦配煤方法按以下步骤进行：
(1)取用气煤、气肥煤、肥煤、1/3焦煤、焦煤和瘦煤，其中挥发分大于≥34％的肥煤命名为肥煤1#，挥发分小于34％的肥煤命名为肥煤 2#。
(2)按如下配煤方案进行配煤炼焦。
方案 气煤 气肥煤 肥煤1# 肥煤2# 1/3焦煤 焦煤 瘦煤
1 10 10 10 0 20 40 10
2 10 10 5 5 20 40 10
3 10 10 0 10 20 40 10
4 15 6 9 0 20 42 8
5 15 6 0 9 20 42 8
6 10 10 15 0 20 40 5
7 10 10 0 15 20 40 5
(3)对7个配煤方案所得的焦炭(湿熄焦)进行M10检测分析：
方案 M10/％
1 9.49
2 6.98
3 6.24
4 6.78
5 6.59
6 10.13
7 9.87
由焦炭M10数据可知，方案1中虽然气肥煤与肥煤配比之和满足≤ 20％的条件，但该方案中气肥煤与肥煤1#配比之和＞15％，因此不能有效提高焦炭耐磨强度，所得焦炭M10＞7.0％；方案2～5中，气肥煤和肥煤配比之和≤20％，且气肥煤和肥煤1#配比之和≤15％，故能有效提高焦炭耐磨强度，所得焦炭M10均低于7.0％。方案6、7中，气肥煤与肥煤配比之和超过20％，因此不论气肥煤与挥发分≥34％的肥煤之和是否满足≤15％的条件，均不能有效提高焦炭耐磨强度，所得焦炭M10均大于7.0％。
因此按本发明方法中所述的通过对气肥煤、肥煤配比以及高、低挥发分肥煤配比的控制，可以有效起到控制焦炭M10的作用。
本发明的发明人还进行了干熄焦配煤炼焦实验，所得焦炭的M10均在6.0％以下。

Claims (1)

1.一种控制焦炭M10指标的炼焦配煤方法，其特征在于：该方法中各单种煤的配比按重量百分比为：
气煤：15％；气肥煤：6％，肥煤9％，1/3焦煤：20％；焦煤：42％，瘦煤：8％；
其中，肥煤的挥发分在34％以上。
CN201510265619.XA 2015-05-22 2015-05-22 控制焦炭m10指标的炼焦配煤方法 Active CN104845650B (zh)