CN104845475A - Metal quartz sand hard drawing board - Google Patents
Metal quartz sand hard drawing board Download PDFInfo
- Publication number
- CN104845475A CN104845475A CN201510261124.XA CN201510261124A CN104845475A CN 104845475 A CN104845475 A CN 104845475A CN 201510261124 A CN201510261124 A CN 201510261124A CN 104845475 A CN104845475 A CN 104845475A
- Authority
- CN
- China
- Prior art keywords
- parts
- drawing board
- coating
- middle layer
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a metal quartz sand hard drawing board. A gypsum board is used as the base material, and the drawing board is prepared by the following steps of (1) manufacturing paste of the bottom layer; (2) manufacturing paste of the middle layer; (3) manufacturing coating of the surface layer; sequentially spraying the paste of each layer to the base material through a spraying machine, so as to prepare the metal quartz sand hard drawing board. The metal quartz sand hard drawing board has the advantages that the water-resistant property and weather-resistant property are excellent, the coating has grinding feel, the firmness and hardness are good, and the stereo feel is strong; the coating is thick, the easiness in cracking is avoided, the coating can be ground to any thickness; the spraying effect is good by using the spraying process.
Description
Technical field
The present invention relates to a kind of art painting apparatus, especially relate to a kind of employing and repeatedly apply obtained metal stone sand hard drawing board.
Background technology
Gypsum material thing is cheap beautiful, is the extraordinary coating material of drawing board, but gypsum drawing board is long placed in easily jaundice, cracking and distortion, affects preservation and the collection of work of fine arts, and gypsum material lacks texture, and flintiness and stereoscopic sensation are not strong.
Summary of the invention
For the above-mentioned defect that existing gypsum drawing board exists, the invention provides a kind of metal stone sand hard drawing board.Drawing board of the present invention has excellent water tolerance and weathering resistance, coating tool frosted texture, firmness and flintiness good, stereoscopic sensation is strong, and thick painting is not easy to crack, and can polish to any thickness, and supporting leaching coating process showering is effective.
Technical scheme of the present invention is as follows:
Metal stone sand hard drawing board, take plasterboard as base material, the preparation section of described drawing board is as follows:
(1) base pastes is made: by deionized water 245 ~ 255 parts, defoamer 1 ~ 2 part, with pure-acrylic emulsion 145 ~ 155 parts, under the rotating speed of 1800 ~ 2000 turns/min, stirs 10 minutes, be uniformly dispersed, obtained base pastes;
(2) middle layer slurry is made: mixed with 340 ~ 360 parts of deionized waters by 90 ~ 110 parts of organic amines, add 4 ~ 6 parts of dispersion agents and 5 ~ 9 parts of thickening materials, under the rotating speed of 1800 ~ 2000 turns/min, stir 10 minutes, be uniformly dispersed, obtained middle layer slurry; Described organic amine is AMP-95, and the believable Chemical trade company limited of Yixing City provides; Described dispersion agent is selected from the safe Chemicals of break, model NXZ; Described thickening material is selected from Shanghai Shi Cheng Chemical Co., Ltd. product, model TT935;
(3) surface coating material is made: in 295 ~ 305 parts of deionized waters, add 245 ~ 255 parts of texture quartz sands and 290 ~ 310 parts of hot-melt adhesive powders, stir, add defoamer 1 ~ 2 part, under the rotating speed of 2500 ~ 3500 turns/min, stir, obtained surface coating material; The particle diameter of described quartz sand is 200 orders;
(4) leaching coating process is adopted by base pastes showering obtained for step (1) in substrate surface, and dry;
(5) substrate surface that the middle layer slurry that step (2) is obtained sprays after processing through step (4) is carried out drying, ensure viscosity and the thickness of coating;
(6) surface coating material that step (3) is obtained is sprayed at the substrate surface after step (5) process, then dry and obtain metal stone sand hard drawing board finished product.
Leaching coating process described in step (4), (5), (6) adopts curtain coater to carry out, and it drenches the pressing creation of curtain film by surge pump, and thickness is 0.3-1mm, and showering transfer rate is 60 ~ 80m/min.
The technique effect that the present invention is useful is:
1, drawing board of the present invention, is coating auxiliary material with pure acrylic latex, dispersion agent, thickening material, organic amine, quartz sand etc., adopts the technique of three road coatings, two road dryings, improve the original shortcoming of gypsum, make drawing board coating have water tolerance and weathering resistance, be long placed in non-yellowing, do not ftracture, indeformable.
2, drawing board of the present invention uses the pure-acrylic emulsion of customization macromolecular structure large arch dam, with water Homogeneous phase mixing in proportion, sprays at substrate surface, ensure that the firmness of coating, also not easy to crack when thick coating reaches 3mm, and has good water tolerance; The present invention adds 200 order quartz sands especially, makes coating have frosted texture, improves stereoscopic sensation and the flintiness of drawing board; The low molecule organic amine had no irritating odor with environmental protection replaces ammoniacal liquor to regulate pH, and coating pH value is in neutral, and be conducive to acid-proof anticorrosion, oxidation-resistance is strong.
3, the acrylic polymer coating layer that drawing board of the present invention is special, arbitrarily can polish with thin sand paper, also can not polish direct picture greasepaint and acrylic paints.
4, in drawing board preparation technology of the present invention, coating techniques is adopted to substitute conventional spray paint technology, curtain coater drenches the pressing creation of curtain film by surge pump, thickness is adjustable, can effectively control coating surface tension and speed, reach free of pinholes, change the rough phenomenon of drawing board, improve coatingsurface planeness.
5, drawing board of the present invention is suitable for acrylic paints, casein, oil colour, can directly draw, and also can adopt the thick painting technique of painting.
6, the present invention adopts metal stone sand, spinel powders shape and with metalluster, finally makes drawing board have the effect of band metalluster.
Embodiment
Below in conjunction with embodiment, the present invention is specifically described.
Embodiment 1
Metal stone sand hard drawing board, be base material with plasterboard, preparation section is as follows:
(1) base pastes is made: by deionized water 245 parts, defoamer 1 part, with pure-acrylic emulsion 145 parts, under the rotating speed of 1800 turns/min, stirs 10 minutes, be uniformly dispersed, obtained base pastes;
(2) middle layer slurry is made: mixed with 340 parts of deionized waters by 90 parts of organic amine AMP-95 (the believable Chemical trade company limited of Yixing City), add 4 parts of dispersion agent NXZ (the safe Chemicals of break) and 5 parts of thickening material TT935 (Shanghai Shi Cheng Chemical Co., Ltd. product), under the rotating speed of 2000 turns/min, stir 10 minutes, be uniformly dispersed, obtained middle layer slurry;
(3) surface coating material is made: in 295 parts of deionized waters, add 245 parts of texture quartz sands and 290 parts of hot-melt adhesive powders, stir, add defoamer 1 part, under the rotating speed of 2500 turns/min, stir, obtained surface coating material; The particle diameter of described quartz sand is 200 orders;
(4) leaching coating process is adopted by base pastes showering obtained for step (1) in substrate surface, and dry;
(5) substrate surface that the middle layer slurry that step (2) is obtained sprays after processing through step (4) is carried out drying, ensure viscosity and the thickness of coating;
(6) surface coating material that step (3) is obtained is sprayed at the substrate surface after step (5) process, then dry and obtain metal stone sand hard drawing board finished product.
Leaching coating process described in step (4), (5), (6) adopts curtain coater to carry out, and it drenches the pressing creation of curtain film by surge pump, and thickness is 0.3mm, and showering transfer rate is 80m/min.
Embodiment 2
Metal stone sand hard drawing board, be base material with plasterboard, preparation section is as follows:
(1) base pastes is made: by deionized water 255 parts, defoamer 2 parts, with pure-acrylic emulsion 155 parts, under the rotating speed of 2000 turns/min, stirs 10 minutes, be uniformly dispersed, obtained base pastes;
(2) middle layer slurry is made: mixed with 360 parts of deionized waters by 110 parts of organic amine AMP-95 (the believable Chemical trade company limited of Yixing City), add 6 parts of dispersion agent NXZ (the safe Chemicals of break) and 9 parts of thickening material TT935 (Shanghai Shi Cheng Chemical Co., Ltd. product), under the rotating speed of 1800 turns/min, stir 10 minutes, be uniformly dispersed, obtained middle layer slurry;
(3) surface coating material is made: in 305 parts of deionized waters, add 255 parts of texture quartz sands and 310 parts of hot-melt adhesive powders, stir, add defoamer 2 parts, under the rotating speed of 3000 turns/min, stir, obtained surface coating material; The particle diameter of described quartz sand is 200 orders;
(4) leaching coating process is adopted by base pastes showering obtained for step (1) in substrate surface, and dry;
(5) substrate surface that the middle layer slurry that step (2) is obtained sprays after processing through step (4) is carried out drying, ensure viscosity and the thickness of coating;
(6) surface coating material that step (3) is obtained is sprayed at the substrate surface after step (5) process, then dry and obtain metal stone sand hard drawing board finished product.
Leaching coating process described in step (4), (5), (6) adopts curtain coater to carry out, and it drenches the pressing creation of curtain film by surge pump, and thickness is 0.5mm, and showering transfer rate is 70m/min.
Embodiment 3
Metal stone sand hard drawing board, be base material with plasterboard, preparation section is as follows:
(1) base pastes is made: by deionized water 250 parts, defoamer 1.5 parts, with pure-acrylic emulsion 150 parts, under the rotating speed of 2000 turns/min, stirs 10 minutes, be uniformly dispersed, obtained base pastes;
(2) middle layer slurry is made: mixed with 350 parts of deionized waters by 100 parts of organic amine AMP-95 (the believable Chemical trade company limited of Yixing City), add 5 parts of dispersion agent NXZ (the safe Chemicals of break) and 7 parts of thickening material TT935 (Shanghai Shi Cheng Chemical Co., Ltd. product), under the rotating speed of 2000 turns/min, stir 10 minutes, be uniformly dispersed, obtained middle layer slurry;
(3) surface coating material is made: in 300 parts of deionized waters, add 250 parts of texture quartz sands and 300 parts of hot-melt adhesive powders, stir, add defoamer 1.5 parts, under the rotating speed of 3500 turns/min, stir, obtained surface coating material; The particle diameter of described quartz sand is 200 orders;
(4) leaching coating process is adopted by base pastes showering obtained for step (1) in substrate surface, and dry;
(5) substrate surface that the middle layer slurry that step (2) is obtained sprays after processing through step (4) is carried out drying, ensure viscosity and the thickness of coating;
(6) surface coating material that step (3) is obtained is sprayed at the substrate surface after step (5) process, then dry and obtain metal stone sand hard drawing board finished product.
Leaching coating process described in step (4), (5), (6) adopts curtain coater to carry out, and it drenches the pressing creation of curtain film by surge pump, and thickness is 1mm, and showering transfer rate is 60m/min.
The above is only the preferred embodiment of the present invention, the invention is not restricted to above embodiment.Be appreciated that the oher improvements and changes that those skilled in the art directly derive without departing from the spirit and concept in the present invention or associate, all should think and be included within protection scope of the present invention.
Claims (2)
1. metal stone sand hard drawing board is base material with plasterboard, it is characterized in that the preparation section of described drawing board is as follows:
(1) base pastes is made: by deionized water 245 ~ 255 parts, defoamer 1 ~ 2 part, with pure-acrylic emulsion 145 ~ 155 parts, under the rotating speed of 1800 ~ 2000 turns/min, stirs 10 minutes, be uniformly dispersed, obtained base pastes;
(2) middle layer slurry is made: mixed with 340 ~ 360 parts of deionized waters by 90 ~ 110 parts of organic amines, add 4 ~ 6 parts of dispersion agents and 5 ~ 9 parts of thickening materials, under the rotating speed of 1800 ~ 2000 turns/min, stir 10 minutes, be uniformly dispersed, obtained middle layer slurry; Described organic amine is AMP-95, and the believable Chemical trade company limited of Yixing City provides; Described dispersion agent is selected from the safe Chemicals of break, model NXZ; Described thickening material is selected from Shanghai Shi Cheng Chemical Co., Ltd. product, model TT935;
(3) surface coating material is made: in 295 ~ 305 parts of deionized waters, add 245 ~ 255 parts of texture quartz sands and 290 ~ 310 parts of hot-melt adhesive powders, stir, add defoamer 1 ~ 2 part, under the rotating speed of 2500 ~ 3500 turns/min, stir, obtained surface coating material; The particle diameter of described quartz sand is 200 orders;
(4) leaching coating process is adopted by base pastes showering obtained for step (1) in substrate surface, and dry;
(5) substrate surface that the middle layer slurry that step (2) is obtained sprays after processing through step (4) is carried out drying, ensure viscosity and the thickness of coating;
(6) surface coating material that step (3) is obtained is sprayed at the substrate surface after step (5) process, then dry and obtain metal stone sand hard drawing board finished product.
2. metal stone sand hard drawing board according to claim 1, it is characterized in that leaching coating process described in step (4), (5), (6) adopts curtain coater to carry out, it drenches the pressing creation of curtain film by surge pump, thickness is 0.3-1mm, and showering transfer rate is 60 ~ 80m/min.