CN104845222A - 一种pet用色母粒及其制备方法 - Google Patents
一种pet用色母粒及其制备方法 Download PDFInfo
- Publication number
- CN104845222A CN104845222A CN201410780360.8A CN201410780360A CN104845222A CN 104845222 A CN104845222 A CN 104845222A CN 201410780360 A CN201410780360 A CN 201410780360A CN 104845222 A CN104845222 A CN 104845222A
- Authority
- CN
- China
- Prior art keywords
- pet
- masterbatch
- pet masterbatch
- photostabilizer
- masterbatch according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种PET用色母粒及其制备方法。本发明的一种PET用色母粒,其组分按质量百分数配比为:PET树脂15%~50%、着色剂20%~40%、增容剂8%~15%、光稳定剂2%~10%、碳酸钙5%~40%、硬脂酸钠0.1%~1%、超细TAS-2A粉0.5%~3%。本发明的有益效果是,本发明具有高浓度、高分散、强着色、无污染和使用方便等特点,在生产PET添加10%~30%质量分数时,将具有良好的着色性能和加工性能,而且还明显提高了力学性能和耐热、耐老化性能,降低了成本,提高了生产效率,有利于工业化生产与推广应用。
Description
技术领域
本发明涉及高分子材料技术领域,具体地说是一种PET用色母粒及其制备方法。
背景技术
聚对苯二甲酸乙二醇酯(PET)是一种结晶性聚合物,由于它具有优异的机械强度、电绝缘性、耐热性和耐化学品性,已被广泛应用于纤维、薄膜、工程塑料等领域。尤其是,PET以其高强度、尺寸稳定、耐化学腐蚀等优异的性能, 在服装、地毯及装饰织物方面具有非常广泛的用途。近年来,随着色母粒生产技术的长足发展,PET色母粒的发展也很快。色母粒着色具有分散性好、无污染和使用方便等优点,克服了采用色粉直接着色存在的色点、色差和生产环境污染的问题。
发明内容
本发明的目的在于提供一种浓度高、着色力强、耐热耐光性好和使用方便的PET用色母粒及其制备方法。
本发明解决其技术问题所采用的技术方案是:一种PET用色母粒,其组分按质量百分数配比为:PET树脂15%~50%、着色剂20%~40%、增容剂8%~15%、光稳定剂2%~10%、碳酸钙5%~40%、硬脂酸钠0.1%~1%、超细TAS-2A粉0.5%~3%。
所述PET树脂为聚对苯二甲酸乙二醇酯。
所述着色剂为无机颜料或有机颜料,所述无机颜料选自钛白粉、炭黑、氧化铁红、铅铬黄、铁蓝中的一种,所述有机颜料选自大红粉、偶淡黄、酞菁蓝、喹吖啶酮中的一种。
所述增容剂为苯乙烯-马来酸酐共聚物。
所述光稳定剂为质量比1:1的受阻胺类高分子量光稳定剂GW-944Z与GW-622的复配物。
所述碳酸钙为表面经过铝钛复合偶联剂改性处理、且粒径小于5μm的重质碳酸钙粒子。
上述的一种PET用色母粒的制备方法为:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于230℃~280℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明。
本发明的有益效果是,本发明具有高浓度、高分散、强着色、无污染和使用方便等特点,在生产PET添加10%~30%质量分数时,将具有良好的着色性能和加工性能,而且还明显提高了力学性能和耐热、耐老化性能,降低了成本,提高了生产效率,有利于工业化生产与推广应用。
具体实施方式
下面结合具体实施例来进一步说明本发明的技术方案。
实施例1:
一种PET用色母粒,其组分按质量百分数配比为:PET树脂34%、氧化铁红30%、苯乙烯-马来酸酐共聚物12%、光稳定剂6%、碳酸钙15%、硬脂酸钠0.5%、超细TAS-2A粉2.5%,所述光稳定剂为质量比1:1的受阻胺类高分子量光稳定剂GW-944Z与GW-622的复配物,所述碳酸钙为表面经过铝钛复合偶联剂改性处理、且粒径小于5μm的重质碳酸钙粒子。
制备方法:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于230℃~280℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明的一种PET用色母粒。
实施例2:
一种PET用色母粒,其组分按质量百分数配比为:PET树脂32%、酞菁蓝20%、苯乙烯-马来酸酐共聚物10%、光稳定剂5%、碳酸钙30%、硬脂酸钠0.5%、超细TAS-2A粉2.5%,所述光稳定剂为质量比1:1的受阻胺类高分子量光稳定剂GW-944Z与GW-622的复配物,所述碳酸钙为表面经过铝钛复合偶联剂改性处理、且粒径小于5μm的重质碳酸钙粒子。
制备方法:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于230℃~280℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明的一种PET用色母粒。
Claims (6)
1.一种PET用色母粒,其特征在于,其组分按质量百分数配比为:PET树脂15%~50%、着色剂20%~40%、增容剂8%~15%、光稳定剂2%~10%、碳酸钙5%~40%、硬脂酸钠0.1%~1%、超细TAS-2A粉0.5%~3%。
2.根据权利要求1所述的一种PET用色母粒,其特征在于,所述着色剂为无机颜料或有机颜料,所述无机颜料选自钛白粉、炭黑、氧化铁红、铅铬黄、铁蓝中的一种,所述有机颜料选自大红粉、偶淡黄、酞菁蓝、喹吖啶酮中的一种。
3.根据权利要求1所述的一种PET用色母粒,其特征在于,所述增容剂为苯乙烯-马来酸酐共聚物。
4.根据权利要求1所述的一种PET用色母粒,其特征在于,所述光稳定剂为质量比1:1的受阻胺类高分子量光稳定剂GW-944Z与GW-622的复配物。
5.根据权利要求1所述的一种PET用色母粒,其特征在于,所述碳酸钙为表面经过铝钛复合偶联剂改性处理、且粒径小于5μm的重质碳酸钙粒子。
6.根据权利要求1所述的一种PET用色母粒的制备方法,其特征在于,包括以下步骤:按重量配比称取各组分,并分别加入料筒温度在80℃~120℃的高速混合器中,使一起搅拌3~15分钟,待混合均匀后出料加入双螺杆挤出机中,于230℃~280℃温度下经过熔融混炼后挤出造粒,然后进行干燥、包装,即得本发明。