CN104830109A - Water-based anticorrosive paint for engineering machinery - Google Patents
Water-based anticorrosive paint for engineering machinery Download PDFInfo
- Publication number
- CN104830109A CN104830109A CN201510235369.5A CN201510235369A CN104830109A CN 104830109 A CN104830109 A CN 104830109A CN 201510235369 A CN201510235369 A CN 201510235369A CN 104830109 A CN104830109 A CN 104830109A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- anticorrosive paint
- engineering machinery
- based anticorrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based anticorrosive paint for engineering machinery, which is prepared by the following components in parts by weight: 20-30 parts of deionized water, 8-15 parts of amino resin, 4-8 parts of film-forming resin, 1-3 parts of neutralizer, 2-4 parts of anti-settling agent, 3-10 parts of acrylonitrile, 4-6 parts of methyl acetate and 6-10 parts of vanadium diboride. The water-based anticorrosive paint for engineering machinery has favorable corrosion resistance, and has the advantages of long anticorrosive time, favorable physiochemical properties and favorable corrosion resistance.
Description
Technical field
The present invention relates to coating, especially, relate to a kind of engineering machinery water-based anticorrosive paint.
Background technology
Along with improving constantly of people's Environmental awareness, the development of modern science and technology, water-based anticorrosive paint, with water as solvent, saves ample resources; And more environmental protection, reduce and poison the dirt dye With of air, water-based anticorrosive paint only adopts a small amount of hypotoxicity alcohol ether organic solvent, improves operating environmental condition, pollutes saving resource Be very effective to reduction.Water-based anticorrosive paint directly can apply construction in wet structure and wet environment; Strong to material coating adhesion, surperficial adaptability is good.
Summary of the invention
The object of the invention is to provide a kind of engineering machinery water-based anticorrosive paint, and poor to solve antiseptic property in prior art, the anticorrosion time is short, the problem of physicochemical property and poor corrosion resistance.
For achieving the above object, the invention provides a kind of engineering machinery water-based anticorrosive paint, wherein, this coating is made up of the composition of following weight part:
Deionized water 20-30 part;
Aminoresin 8-15 part;
Film-forming resin 4-8 part;
Neutralizing agent 1-3 part;
Anti-settling agent 2-4 part;
Vinyl cyanide 3-10 part;
Methyl acetate 4-6 part; And
Vanadium diboride 6-10 part.
Further, the invention provides a kind of engineering machinery water-based anticorrosive paint, wherein, this coating is made up of the composition of following weight part: deionized water 20 parts; 10 parts, aminoresin; Film-forming resin 5 parts; Neutralizing agent 1 part; Anti-settling agent 2.5 parts; Vinyl cyanide 5 parts; Methyl acetate 4 parts; Vanadium diboride 7 parts.
Further, the invention provides a kind of engineering machinery water-based anticorrosive paint, wherein, this coating is made up of the composition of following weight part: deionized water 28 parts; 14 parts, aminoresin; Film-forming resin 7 parts; Neutralizing agent 2.5 parts; Anti-settling agent 4 parts; Vinyl cyanide 8 parts; Methyl acetate 6 parts; Vanadium diboride 10 parts.
The present invention has following beneficial effect: engineering machinery water-based anticorrosive paint provided by the invention has good antiseptic property, and the anticorrosion time is long, possesses good physicochemical property and corrosion resistance nature.
Embodiment
A kind of engineering machinery water-based anticorrosive paint that this preferred embodiment provides, its specific implementation process is as follows:
The invention provides a kind of engineering machinery water-based anticorrosive paint, wherein, this coating is made up of the composition of following weight part:
Deionized water 20-30 part;
Aminoresin 8-15 part;
Film-forming resin 4-8 part;
Neutralizing agent 1-3 part;
Anti-settling agent 2-4 part;
Vinyl cyanide 3-10 part;
Methyl acetate 4-6 part; And
Vanadium diboride 6-10 part.
Embodiment 1:
Wherein, this coating is made up of the composition of following weight part: deionized water 20 parts; 10 parts, aminoresin; Film-forming resin 5 parts; Neutralizing agent 1 part; Anti-settling agent 2.5 parts; Vinyl cyanide 5 parts; Methyl acetate 4 parts; Vanadium diboride 7 parts.
Embodiment 2:
Wherein, this coating is made up of the composition of following weight part: deionized water 28 parts; 14 parts, aminoresin; Film-forming resin 7 parts; Neutralizing agent 2.5 parts; Anti-settling agent 4 parts; Vinyl cyanide 8 parts; Methyl acetate 6 parts; Vanadium diboride 10 parts.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
Engineering machinery water-based anticorrosive paint provided by the invention has good antiseptic property, and the anticorrosion time is long, possesses good physicochemical property and corrosion resistance nature.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. an engineering machinery water-based anticorrosive paint, is characterized in that, this coating is made up of the composition of following weight part:
Deionized water 20-30 part;
Aminoresin 8-15 part;
Film-forming resin 4-8 part;
Neutralizing agent 1-3 part;
Anti-settling agent 2-4 part;
Vinyl cyanide 3-10 part;
Methyl acetate 4-6 part; And
Vanadium diboride 6-10 part.
2. engineering machinery water-based anticorrosive paint according to claim 1, is characterized in that: this coating is made up of the composition of following weight part: deionized water 20 parts; 10 parts, aminoresin; Film-forming resin 5 parts; Neutralizing agent 1 part; Anti-settling agent 2.5 parts; Vinyl cyanide 5 parts; Methyl acetate 4 parts; Vanadium diboride 7 parts.
3. engineering machinery water-based anticorrosive paint according to claim 1, is characterized in that: this coating is made up of the composition of following weight part: deionized water 28 parts; 14 parts, aminoresin; Film-forming resin 7 parts; Neutralizing agent 2.5 parts; Anti-settling agent 4 parts; Vinyl cyanide 8 parts; Methyl acetate 6 parts; Vanadium diboride 10 parts.