CN104826444A - Fiber modified antibacterial activated carbon diatomite air purifier and preparation method thereof - Google Patents
Fiber modified antibacterial activated carbon diatomite air purifier and preparation method thereof Download PDFInfo
- Publication number
- CN104826444A CN104826444A CN201510191577.XA CN201510191577A CN104826444A CN 104826444 A CN104826444 A CN 104826444A CN 201510191577 A CN201510191577 A CN 201510191577A CN 104826444 A CN104826444 A CN 104826444A
- Authority
- CN
- China
- Prior art keywords
- parts
- activated carbon
- diatomite
- air purifier
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fiber modified antibacterial activated carbon diatomite air purifier which is characterized by comprising the following raw materials by weight: 98-105 parts of coconut shell activated carbon, 35-39 parts of diatomite, 3-5 parts of magnet powder, 3-4 parts of soybean fiber, 3-5 parts of bamboo fiber, 2-3 parts of sodium metabisulfite, 3-5 parts of organic silicon resin, 1-2 parts of cuprous oxide, 3-4 parts of polyacrylamide, 7-9 parts of silicon carbide, 4-6 parts of boron nitride, 2-3 parts of Arabic gum, 3-5 parts of titanium dioxide, 4-6 parts of an adsorption aid, and right amount of water; the bamboo fiber and the soybean fiber are added into the activated carbon, the porosity and specific surface area are increased, the fiber modified antibacterial activated carbon diatomite air purifier has natural antibacterial ingredients, and is antibacterial and deodorizing; by addition of the adsorption aid, the fiber modified antibacterial activated carbon diatomite air purifier is specially porous, the air and air purifier contact time can be extended; by addition of the magnet powder, the cuprous oxide, the silicon carbide, and the like, desulfurization efficiency is high, and the fiber modified antibacterial activated carbon diatomite air purifier is safe, non-toxic, and suitable for using in industries, household, automobiles, and the like.
Description
Technical field
The present invention relates to a kind of desulphurized aetivated carbon and preparation method thereof, particularly a kind of bacteriostatic activated carbon diatomite air purifying preparation and preparation method thereof of fibre modification.
Background technology
Bamboo fibre is exactly a kind of cellulose fibre extracted from the bamboo of self-sow, is the fifth-largest natural fiber after cotton, fiber crops, hair, silk.Bamboo fibre have good gas permeability, moment the characteristic such as water imbibition, stronger wearability and good dyeability, have again simultaneously natural antibacterial, antibacterial, except mite, deodorization and anti-ultraviolet function.Because have a kind of unique material inside bamboo, this material is named as " bamboo a kind of jade ", has natural antibacterial, anti-mite, deodorization, insect protected function.
Soybean fiber belongs to aftergrowth azelon, be the soybean meal pressed the oil be raw material, utilize biotechnology, extract the globulin in dregs of beans, by adding functional aid, with the high polymer such as itrile group, hydroxyl grafting, copolymerization, blended, make certain density protein spinning solution, change protein steric structure, form through wet spinning.It has the soft feel as cashmere, the sub dued lustre as silk, the premium properties such as cotton warmth retention property and good skin-friendly, also has obvious bacteria resistance function.
Active carbon with high specific surface area has loose structure, can adsorb various organic matter and inorganic matter, and having the advantages that adsorption capacity is large, adsorption rate is fast, is a kind of high-efficiency adsorbent of high-quality, is widely used in the every field such as food industry, chemical industry and environmental protection.
Summary of the invention
Bacteriostatic activated carbon diatomite air purifying preparation that the object of this invention is to provide a kind of fibre modification and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A bacteriostatic activated carbon diatomite air purifying preparation for fibre modification, is made up of the raw material of following weight portion: cocoanut active charcoal 98-105, diatomite 35-39, magnet powder 3-5, fibre and soya 3-4, bamboo fibre 3-5, sodium pyrosulfite 2-3, organic siliconresin 3-5, cuprous oxide 1-2, polyacrylamide 3-4, carborundum 7-9, boron nitride 4-6, Arabic gum 2-3, titanium dioxide 3-5, adsorption aid 4-6, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion: deer natural pond soil 1.5-2.5, aluminum sulfate 1.5-2.5, sodium carbonate 2-3, kaolin 12-14, aluminium oxide 2-3, titanium dioxide 2-3, tea seed episperm 8-10, lotus pod 13-15; Preparation method is by tea seed episperm, lotus pod dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except the soil of deer natural pond, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, 80-100 order powder is ground into after taking out cooling, 1.5-2 hour is soaked with the acetum of 50%-60%, filter, get filter residue add deer natural pond soil, 1.5-2 times amount pure water grinding 40-50 minute slurry.
The bacteriostatic activated carbon diatomite air purifying preparation of a kind of fibre modification of the present invention, be made up of following concrete steps:
(1) fibre and soya, bamboo fibre are toasted 1.5-2.5 hour under the condition of 95 DEG C-105 DEG C, be ground into 80-100 object dried powder and cocoanut active charcoal, diatomite together put into ball mill ball milling 1.5-2.5 hour, cross 150-200 mesh sieve after ball milling, obtain mixed-powder stand-by;
(2) add appropriate water by magnet powder, cuprous oxide, carborundum, boron nitride, titanium dioxide, constantly stir and make slurry, then add all the other residual components except adsorption aid, stir, be heated to 75 DEG C-85 DEG C, insulation grinding 1.5-2 hour, obtains mixed slurry stand-by;
(3) mixed-powder, mixed slurry, adsorption aid are stirred mutually, then concentrate drying, to send in comminutor granulation and get final product.
The invention has the beneficial effects as follows: bamboo fibre, fibre and soya add in active carbon by the present invention, add porosity and specific area, and have natural antimicrobial component, bacteriostatic deodorizing; Add adsorption aid, there is special porous, extend gas time of contact with it; Add magnet powder, cuprous oxide, carborundum etc., desulfuration efficiency is high, air purifying preparation of the present invention, safety non-toxic, is applicable to the uses such as industry, family, automobile.
Specific embodiments
Below by instantiation, the present invention is described in detail.
A bacteriostatic activated carbon diatomite air purifying preparation for fibre modification, is made up of the raw material of following weight portion (kilogram): cocoanut active charcoal 98, diatomite 35, magnet powder 3, fibre and soya 3, bamboo fibre 3, sodium pyrosulfite 2, organic siliconresin 3, cuprous oxide 1, polyacrylamide 3, carborundum 7, boron nitride 4, Arabic gum 2, titanium dioxide 3, adsorption aid 4, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion (kilogram): deer natural pond soil 1.5, aluminum sulfate 1.5, sodium carbonate 2, kaolin 12, aluminium oxide 2, titanium dioxide 2, tea seed episperm 8, lotus pod 13; Preparation method is by tea seed episperm, lotus pod dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except the soil of deer natural pond, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, 80-100 order powder is ground into after taking out cooling, 1.5-2 hour is soaked with the acetum of 50%-60%, filter, get filter residue add deer natural pond soil, 1.5-2 times amount pure water grinding 40-50 minute slurry.
The bacteriostatic activated carbon diatomite air purifying preparation of a kind of fibre modification of the present invention, be made up of following concrete steps:
(1) fibre and soya, bamboo fibre are toasted 1.5-2.5 hour under the condition of 95 DEG C-105 DEG C, be ground into 80-100 object dried powder and cocoanut active charcoal, diatomite together put into ball mill ball milling 1.5-2.5 hour, cross 150-200 mesh sieve after ball milling, obtain mixed-powder stand-by;
(2) add appropriate water by magnet powder, cuprous oxide, carborundum, boron nitride, titanium dioxide, constantly stir and make slurry, then add all the other residual components except adsorption aid, stir, be heated to 75 DEG C-85 DEG C, insulation grinding 1.5-2 hour, obtains mixed slurry stand-by;
(3) mixed-powder, mixed slurry, adsorption aid are stirred mutually, then concentrate drying, to send in comminutor granulation and get final product.
Inventive samples important technological parameters is: Sulfur capacity (wt%): >=23.6%, desulfurization precision (ppm) :≤1; Inventive samples is utilized to carry out exhaust-gas treatment, trapping micronic dust efficiency >=99%.
Claims (2)
1. the bacteriostatic activated carbon diatomite air purifying preparation of a fibre modification, it is characterized in that, be made up of the raw material of following weight portion: cocoanut active charcoal 98-105, diatomite 35-39, magnet powder 3-5, fibre and soya 3-4, bamboo fibre 3-5, sodium pyrosulfite 2-3, organic siliconresin 3-5, cuprous oxide 1-2, polyacrylamide 3-4, carborundum 7-9, boron nitride 4-6, Arabic gum 2-3, titanium dioxide 3-5, adsorption aid 4-6, water are appropriate;
Described adsorption aid is made up of the raw material of following weight portion: deer natural pond soil 1.5-2.5, aluminum sulfate 1.5-2.5, sodium carbonate 2-3, kaolin 12-14, aluminium oxide 2-3, titanium dioxide 2-3, tea seed episperm 8-10, lotus pod 13-15; Preparation method is by tea seed episperm, lotus pod dry 1-1.5 hour under 100 DEG C of-120 DEG C of conditions, be ground into 40-60 order powder, then add suitable quantity of water to stir with all the other residual components except the soil of deer natural pond, form purees, then the retort putting into 400 DEG C-500 DEG C carbonizes 2-3 hour, 80-100 order powder is ground into after taking out cooling, 1.5-2 hour is soaked with the acetum of 50%-60%, filter, get filter residue add deer natural pond soil, 1.5-2 times amount pure water grinding 40-50 minute slurry.
2. the bacteriostatic activated carbon diatomite air purifying preparation of a kind of fibre modification according to claim 1, is characterized in that, be made up of following concrete steps:
(1) fibre and soya, bamboo fibre are toasted 1.5-2.5 hour under the condition of 95 DEG C-105 DEG C, be ground into 80-100 object dried powder and cocoanut active charcoal, diatomite together put into ball mill ball milling 1.5-2.5 hour, cross 150-200 mesh sieve after ball milling, obtain mixed-powder stand-by;
(2) add appropriate water by magnet powder, cuprous oxide, carborundum, boron nitride, titanium dioxide, constantly stir and make slurry, then add all the other residual components except adsorption aid, stir, be heated to 75 DEG C-85 DEG C, insulation grinding 1.5-2 hour, obtains mixed slurry stand-by;
(3) mixed-powder, mixed slurry, adsorption aid are stirred mutually, then concentrate drying, to send in comminutor granulation and get final product.