CN104817956A - 一种珊瑚弹性涂料及其制备方法 - Google Patents
一种珊瑚弹性涂料及其制备方法 Download PDFInfo
- Publication number
- CN104817956A CN104817956A CN201510154963.1A CN201510154963A CN104817956A CN 104817956 A CN104817956 A CN 104817956A CN 201510154963 A CN201510154963 A CN 201510154963A CN 104817956 A CN104817956 A CN 104817956A
- Authority
- CN
- China
- Prior art keywords
- parts
- coral
- elastic coating
- agent
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种珊瑚弹性涂料,按质量份计包括以下原料:5-180份珊瑚粉、5-180份滑石粉、50-80份硅微粉、120-160份钛白粉、1-5份杀菌剂、5-10份颜料、50-100份助剂、15-25份乙二醇、300-500份乳液、150-200份水。本发明添加了珊瑚粉,使该涂料具有除湿保湿、保温吸音、消臭、吸收空气中毒素及抗菌的效果。
Description
技术领域
本发明属于涂料领域,具体涉及一种珊瑚弹性涂料及其制备方法。
背景技术
弹性建筑涂料是以合成树脂乳液为基料,与颜料、填料及助剂配制而成,施涂一定厚度(干膜厚度大于等于150μm)后,具有弥盖因基材伸缩(运动)产生细小裂纹的有弹性的功能性涂料。弹性涂料不仅具有普通涂料的保护和装饰作用,而且具有防水和遮盖裂缝功能。
随着人们生活水平的提高,人们对室内环境舒适度及安全性的要求越来越高。目前多数室内装修都是用粉刷水泥抹平、石膏批刮、涂料表面处理;采用部分化学原料作为粘合剂再用油漆产品、装饰品、墙面砖等对室内进行装饰,但这些材料大都保温、保湿抗菌性能差,并且易产生对人体有害的物质。
发明内容
针对现有技术的不足,本发明的目的之一在于提供一种珊瑚弹性涂料,在涂料中添加珊瑚粉,该涂料具有除湿保湿、保温吸音、消臭、吸收空气中毒素及抗菌的效果。
为达此目的,本发明采用以下技术方案:
一种珊瑚弹性涂料,按质量份计包括以下原料:
优选地,一种珊瑚弹性涂料,按质量份计包括以下原料:
本发明的珊瑚粉由天然化石珊瑚制备得到,化石珊瑚有很好的除菌抗菌的功效,可以有效吸附大肠杆菌、金黄色葡萄球菌等菌类及毒素,可以有效预防细菌的繁殖和毒素的传播;珊瑚粉有无数细孔,夏天可有效除湿、冬天有效保湿;可以有效去除室内的臭味;并且吸音效果良好;另外珊瑚粉取自天然化石珊瑚,原料用起来安全、放心。
滑石具有润滑性、抗黏、助流、耐火性、抗酸性、绝缘性、熔点高、化学 性不活泼、遮盖力良好、柔软、光泽度好、吸附力强等优良的物理、化学特性,在涂料中的应用主要体现为:在涂料中,滑石粉作为填料,可起到骨架作用,降低制造成本同时提高涂料的漆膜硬度。主要增加产品形状的稳定,增加张力强度、剪切强度、绕曲强度、压力强度;降低变形、伸长率;白度高、粒度均匀分散性强等特点。
硅微粉是无毒、无味、无污染的无机非金属材料,是由天然石英或熔融石英经破碎、球磨、浮选、酸洗提纯、高纯水处理等多道工艺加工而成的微粉。硅微粉用于涂料中能减少涂料中树脂和分散剂的使用量。不仅能起到填充增容,增稠消光等作用,还能提高油漆细度、流平性能,漆膜硬度,耐电弧绝缘。
涂料用杀菌剂没有统一的界定,通常特指作为一种类似涂料助剂的成份有效防止微生物的污染来提高产品的防腐、防锈、防霉等性能,从而得到高质量耐保存的产品。杀菌剂在涂料中只需极少的添加量,但其特殊的功效却是必不可少的。例如:以环氧树脂为主要基材的水性涂料,加入杀菌剂能够在降低涂料配方成本的同时保证涂料的最佳性能,同时具有分散、增稠、调节pH值,不变色,抗微生物等多方面优越性能。在油漆中加入杀菌剂,则在此油漆的储存期间内,杀菌剂就可以起到保护油漆不被可分解原材料的溶液或分散体破坏的作用。
氨基硅油乳液易溶于水,水溶液极其稳定,配伍性好,无破乳和漂油现象,不粘不黄变。具有吸附性、相容性及易乳化性。用作纤维后整理剂,可与纤维表面的活性基发生相互作用,提高亲水性和耐洗性,赋予织物滑糯、柔软、防皱、穿着舒适等特性,是棉、麻、丝绸、毛纺品等天然纤维及聚酯、尼龙、腈纶、等几乎所有纤维的最重要的柔软助剂,优选地,乳液为8040氨基硅油。
乙二醇能将涂料中的成膜物质溶解或分散为均匀的液态,另外还可以作为 防冻剂。
为了改善涂料的性能通常需要添加各种类型的助剂,其中助剂包括分散剂、润湿剂、消泡剂、成膜助剂、流平剂、增稠剂和多功能助剂。
分散剂是一种在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂,可均一分散并且难溶于液体的无机、有机颜料的固体颗粒,同时也能防止固体颗粒的沉降和凝聚,形成安定悬浮液所需的药剂。在涂料中使用颜料分散剂,可增加涂膜的光泽,改善流平性,提高涂料的着色和遮盖力,防止浮色、沉降,提高生产效率和涂料的贮存稳定性。膨润土和有机膨润土、金属皂、加氢蓖麻油等增稠剂可起颜料分散剂的作用。各种表面活性剂、低分子量的聚氧化乙烯(聚环氧乙烷)、低粘度甲基硅油、卵磷脂及其衍生物等也常使用,优选地,分散剂采用分散剂LXE。
润湿剂能使固体物料更易被水浸湿的物质。通过降低其表面张力或界面张力,使水能展开在固体物料表面上,或透入其表面,而把固体物料润湿。在涂料中,润湿剂不仅可以降低水的表面张力,便于更好的分散体系的粉料,同时便于基材的润湿;而且对乳液有一定的保护作用,可以提高乳液的机械稳定性和化学稳定性,优选地,润湿剂采用润湿剂486。
使用消泡剂是用来避免气泡的形成或将已形成的气泡尽快消除,确保产品质量。在建筑涂料生产中,由于配方中有乳化剂、分散剂和增稠剂等助剂的存在,不仅会产生大量的气泡,而且还能稳定气泡,致使建筑涂料中出现大量气泡。在成膜过程中,若气泡不能消失,则会造成涂膜缩孔、针眼等弊病。因此,添加消泡剂来消除这些气泡,才能取得满意的效果,优选地,采用消泡剂NXZ。
涂料成膜助剂又称聚结助剂,能促进乳胶粒子塑性流动和弹性变形,改善聚结性能,使涂料能在较广泛施工温度范围内成膜。目前市场上成膜助剂种类繁多,可以选用十二碳醇酯、丙二醇苯醚(PPH)、各种酯类、醚醇类化合物等。
流平剂有助于形成光滑涂饰面的物质。能够提高涂料表面张力的物质一般都有流平剂的作用。工业上已使用的流平剂主要有三种:(1)改性聚二甲基硅氧烷型;(2)相容性受限制的长链树脂型流平剂;(3)以高沸点溶剂为主要成分的流平剂。工业上已使用的流平剂有含氟表面活性剂、聚丙烯酸酯类和聚乙烯醇缩丁醛等多种系列,优选地,流平剂采用流平剂728。
增稠剂能够提高涂料粘度、降低其流动性的物质。使用增稠剂的重要目的是减轻涂饰时的流淌现象。涂料用的增稠剂主要有以下几类:①白炭黑;②膨润土和有机膨润土(用阳离子性有机物处理的膨润土);③经表面处理的活性碳酸钙微粒;④加氢蓖麻油;⑤金属皂,如硬脂酸钙、硬脂酸铝、硬脂酸锌等;⑥聚合的植物油及脂肪酸二聚体与多元醇所成的酯。优选地,增稠剂采用增稠剂HA。另外,纤维素在涂料中的作用在于具有良好的增稠、悬浮、分散、乳化、粘合、成膜、保护水分和提供保护胶体等,纤维素可以选自木质纤维素、羟丙基纤维素、羧甲基纤维素、钠苯丙乳液、聚阴离子纤维素、聚乙烯醇丙二醇、聚丙烯酸钠乙基纤维素、羟乙基纤维素等。优选地,纤维素为羟乙基纤维素三万。
多功能助剂AMP-95含有5%的水份-2-氨基-2-甲基-1-丙醇,是目前少数具有低分子量和高碱性的工业胺之一。AMP-95可以作为各种类型乳胶漆的多功能助剂,在配方中用AMP-95作为强力共分散剂可以防止颜料再凝聚。同时,多功能助剂AMP-95对漆层的所有性能贡献出显著的优越性。
本发明的目的之二在于提供一种珊瑚弹性涂料的制备方法,包括如下步骤: 按质量份计,称取150-200份水、15-25份乙二醇、5-180份珊瑚粉、5-180份滑石粉、50-80份硅微粉、120-160份钛白粉搅拌混合,边搅拌边加入1-5份杀菌剂、50-100份助剂,混合均匀后加300-500份乳液,搅拌均匀后加入5-10份颜料上色,得到所述珊瑚弹性涂料。
与现有技术相比,本发明的有益效果为:一种珊瑚弹性涂料,按质量份计包括以下原料:5-180份珊瑚粉、5-180份滑石粉、50-80份硅微粉、120-160份钛白粉、1-5份杀菌剂、5-10份颜料、50-100份助剂、15-25份乙二醇、300-500份乳液、150-200份水。本发明添加了珊瑚粉,使该涂料具有除湿保湿、保温吸音、消臭、吸收空气中毒素及抗菌的效果。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
如无具体说明,本发明的各种原料均可市售购得,或根据本领域的常规方法制备得到。
实施例1
按质量份计,称取180份水、20份乙二醇、150份珊瑚粉、150份滑石粉、60份硅微粉、140份钛白粉搅拌混合,边搅拌边加入1份杀菌剂LXZ、4份分散剂LXE、2份润湿剂486、2份消泡剂NXZ、1.2份多功能助剂AMP-95、2份膨润土、32份成膜助剂、2份流平剂728、6份增稠剂HA,混合均匀后加400份8040氨基硅油乳液,搅拌均匀后加入8份颜料上色,得到珊瑚弹性中涂涂料,性能及检测见表1。
实施例2
按质量份计,称取150份水、15份乙二醇、50份珊瑚粉、60份滑石粉、50 份硅微粉、120份钛白粉搅拌混合,边搅拌边加入2份杀菌剂LXZ、5份分散剂LXE、4份润湿剂486、3份消泡剂NXZ、2份多功能助剂AMP-95、5份膨润土、25份成膜助剂、6份流平剂728、5份增稠剂HA,混合均匀后加300份8040氨基硅油乳液,搅拌均匀后加入5份颜料上色,得到珊瑚弹性底漆涂料,性能及检测见表1。
实施例3
按质量份计,称取160份水、20份乙二醇、100份珊瑚粉、100份滑石粉、70份硅微粉、130份钛白粉搅拌混合,边搅拌边加入4份杀菌剂LXZ、8份分散剂LXE、2份润湿剂486、7份消泡剂NXZ、5份多功能助剂AMP-95、8份膨润土、15份成膜助剂、8份流平剂728、3份增稠剂HA,混合均匀后加400份8040氨基硅油乳液,搅拌均匀后加入8份颜料上色,得到珊瑚弹性中涂拉毛涂料,性能及检测见表1。
实施例4
按质量份计,称取170份水、16份乙二醇、165份珊瑚粉、130份滑石粉、60份硅微粉、120份钛白粉搅拌混合,边搅拌边加入4份杀菌剂LXZ、6份分散剂LXE、3份润湿剂486、4份消泡剂NXZ、5份多功能助剂AMP-95、10份膨润土、10份成膜助剂、10份流平剂728、5份增稠剂HA,混合均匀后加350份8040氨基硅油乳液,搅拌均匀后加入5份颜料上色,得到珊瑚弹性面涂涂料,性能及检测见表1。
实施例5
按质量份计,称取170份水、16份乙二醇、165份珊瑚粉、130份滑石粉、60份硅微粉、120份钛白粉搅拌混合,边搅拌边加入4份杀菌剂LXZ、6份分散剂LXE、3份润湿剂486、4份消泡剂NXZ、5份多功能助剂AMP-95、10份 膨润土、10份成膜助剂、10份流平剂728、5份增稠剂HA,混合均匀后加350份8040氨基硅油乳液,搅拌均匀后加入10份颜料上色,得到珊瑚弹性面涂涂料,性能及检测见表1。
实施例6
按质量份计,称取185份水、20份乙二醇、50份珊瑚粉、60份滑石粉、60份硅微粉、140份钛白粉搅拌混合,边搅拌边加入3份杀菌剂LXZ、6份分散剂LXE、5份润湿剂486、4份消泡剂NXZ、5份多功能助剂AMP-95、5份膨润土、10份成膜助剂、8份流平剂728、2份增稠剂HA,混合均匀后加400份8040氨基硅油乳液,搅拌均匀后加入5份颜料上色,得到珊瑚弹性中涂拉毛涂料,性能及检测见表1。
实施例7
按质量份计,称取155份水、18份乙二醇、50份珊瑚粉、100份滑石粉、100份硅微粉、150份钛白粉搅拌混合,边搅拌边加入5份杀菌剂LXZ、5份分散剂LXE、5份润湿剂486、6份消泡剂NXZ、5份多功能助剂AMP-95、5份膨润土、10份成膜助剂、8份流平剂728、8份增稠剂HA,混合均匀后加350份8040氨基硅油乳液,搅拌均匀后加入6份颜料上色,得到珊瑚弹性外墙涂料,性能及检测见表1。
实施例8
按质量份计,称取155份水、18份乙二醇、50份珊瑚粉、100份滑石粉、100份硅微粉、150份钛白粉搅拌混合,边搅拌边加入5份杀菌剂LXZ、5份分散剂LXE、5份润湿剂486、6份消泡剂NXZ、5份多功能助剂AMP-95、5份膨润土、10份成膜助剂、8份流平剂728、8份增稠剂HA,混合均匀后加350份8040氨基硅油乳液,搅拌均匀后加入9份颜料上色,得到珊瑚弹性外墙涂料, 性能及检测见表1。
表1
实施例 | 颜色 | 粘度(cps) | 温度(℃) | 细度(um) | 容器中状态 | 施工性 |
实施例1 | 灰色 | 51.6 | 14 | 40 | 搅拌后均匀无结块 | 良好 |
实施例2 | 透明 | 13.05 | 17 | 40 | 搅拌后均匀无结块 | 良好 |
实施例3 | 浅灰 | 8.2 | 29 | 45 | 搅拌后均匀无结块 | 良好 |
实施例4 | 浅白 | 16.4 | 21 | 35 | 搅拌后均匀无结块 | 良好 |
实施例5 | 米黄 | 16.4 | 21 | 35 | 搅拌后均匀无结块 | 良好 |
实施例6 | 浅灰 | 8.3 | 25 | 40 | 搅拌后均匀无结块 | 良好 |
实施例7 | 白 | 21.6 | 15 | 40 | 搅拌后均匀无结块 | 良好 |
实施例8 | 米黄 | 21.6 | 15 | 40 | 搅拌后均匀无结块 | 良好 |
实施例9
按质量份计,称取160份水、20份乙二醇、100份滑石粉、70份硅微粉、130份钛白粉搅拌混合,调节珊瑚粉的用量,具体见表2,边搅拌边加入4份杀菌剂LXZ、8份分散剂LXE、2份润湿剂486、7份消泡剂NXZ、5份多功能助剂AMP-95、8份膨润土、15份成膜助剂、8份流平剂728、3份增稠剂HA,混合均匀后加400份8040氨基硅油乳液,搅拌均匀后加入8份颜料上色,制备不同珊瑚粉含量的涂料。在培养皿中加入金黄色葡萄球菌(用蒸馏水稀释到15倍),放入生化培养箱中培养48h,取出培养基后抽取一滴培养液到制作好的涂料漆膜上培养12h,显微镜下观察细菌数目,实验结果见表2。
表2
涂料中珊瑚粉含量 | 0 | 5份 | 20份 | 60份 | 100份 | 150份 | 180份 |
[0051]
细菌数目(百万个) | 10 | 9.2 | 8.6 | 7.4 | 6.8 | 6.1 | 5.7 |
由表2可以看出,随着涂料中珊瑚粉含量的增加,金黄色葡萄球菌的数目减少,说明涂料中珊瑚粉有很好的杀菌作用。
以上实施例仅用来说明本发明的详细方法,本发明并不局限于上述详细方法,即不意味着本发明必须依赖上述详细方法才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种珊瑚弹性涂料,其特征在于,按质量份计包括以下原料:
2.根据权利要求1所述的一种珊瑚弹性涂料,其特征在于,按质量份计包括以下原料:
3.根据权利要求1所述的一种珊瑚弹性涂料,其特征在于,所述珊瑚粉为化石珊瑚粉,由天然化石珊瑚制备得到。
4.根据权利要求1所述的一种珊瑚弹性涂料,其特征在于,所述助剂包括分散剂、润湿剂、消泡剂、成膜助剂、流平剂、增稠剂和多功能助剂。
5.根据权利要求1所述的一种珊瑚弹性涂料,其特征在于,所述乳液为8040氨基硅油。
6.根据权利要求4所述的一种珊瑚弹性涂料,其特征在于,所述多功能助剂为多功能助剂AMP-95。
7.根据权利要求4所述的一种珊瑚弹性涂料,其特征在于,所述分散剂为分散剂LXE。
8.根据权利要求4所述的一种珊瑚弹性涂料,其特征在于,所述润湿剂为润湿剂486。
9.根据权利要求4所述的一种珊瑚弹性涂料,其特征在于,所述消泡剂为消泡剂NXZ;
优选地,所述流平剂为流平剂728;
优选地,所述增稠剂为增稠剂HA。
10.如权利要求1所述的一种珊瑚弹性涂料的制备方法,其特征在于,包括如下步骤:按质量份计,称取150-200份水、15-25份乙二醇、5-180份珊瑚粉、5-180份滑石粉、50-80份硅微粉、120-160份钛白粉搅拌混合,边搅拌边加入1-5份杀菌剂、50-100份助剂,混合均匀后加300-500份乳液,搅拌均匀后加入5-10份颜料上色,得到所述珊瑚弹性涂料。