CN104805523A - 一种高性能鱼线加工方法 - Google Patents

一种高性能鱼线加工方法 Download PDF

Info

Publication number
CN104805523A
CN104805523A CN201510133408.0A CN201510133408A CN104805523A CN 104805523 A CN104805523 A CN 104805523A CN 201510133408 A CN201510133408 A CN 201510133408A CN 104805523 A CN104805523 A CN 104805523A
Authority
CN
China
Prior art keywords
extruder
fishing line
sections
nylon
ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510133408.0A
Other languages
English (en)
Inventor
胡文龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHAOHU XIANGYU FISHING GEAR Co Ltd
Original Assignee
CHAOHU XIANGYU FISHING GEAR Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHAOHU XIANGYU FISHING GEAR Co Ltd filed Critical CHAOHU XIANGYU FISHING GEAR Co Ltd
Priority to CN201510133408.0A priority Critical patent/CN104805523A/zh
Publication of CN104805523A publication Critical patent/CN104805523A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高性能鱼线加工方法，包括以下步骤，（1）、将尼龙干燥，（2）、将添加剂干燥，（3）、混合造粒，（4）、挤出成型，（5）、冷却成型；本发明在加工时，在尼龙原料中加入多种助剂，改善了尼龙的加工性能，提高了其耐磨性、防腐性能及拉伸性能，提高加工的效率。

Description

一种高性能鱼线加工方法
技术领域
本发明属于渔具加工领域，具体涉及一种高性能鱼线加工方法。
背景技术
鱼线，是用来将钓具配件连接起来的丝线，主要是用来连接鱼竿和鱼钩。过去的鱼线，多是棉、麻、蚕丝等天然纤维制成，强度不高、透明度不好、柔软度和耐磨性不够。现代鱼线主要是尼龙制成，在强度、透明度和耐磨度等方面有较大提高。由于尼龙类鱼线透明度高、柔软性好、比较耐磨的特点，使尼龙鱼线成为鱼线市场的主力军，占据鱼线市场80%以上的份额。      但是在鱼线生产过程中，往往使用挤出机挤出成型，但是由于尼龙的吸水作用，造成在生产过程中产生气泡，制成的鱼线强度不均匀，影响产品质量。
发明内容
本发明的目的是提供一种高性能鱼线加工方法，提高了渔网的均匀性，也提高了鱼线的耐磨性，也提高了鱼线成品率。
本发明通过以下技术方案实现：
一种高性能鱼线加工方法，包括以下步骤：（1）、将尼龙6在105℃真空条件下干燥20min；（2）、将硫酸铝钾、氯磺化聚乙烯、纳米二氧化钛、轻质碳酸钙干燥；（3）、将尼龙6、十二烷基苯磺酸钠、氯磺化聚乙烯、纳米氧化银、轻质碳酸钙、纳米氧化铝粉末按重量比85:0.8:3.2:2.5:1.2:1.7的比例混合，使用单螺杆挤出机挤出，造粒，挤出机长径比30:1，挤出机采用4段加热方式，4段温度分别为240℃、240℃、243℃、245℃；（4）、将步骤（3）造粒好的原料使用长径比为25:1的挤出机挤出成型，挤出机端部设有纺丝模具，挤出机采用5段加热方式，挤出机5段温度分别为237℃、239℃、240℃、242℃、244℃，模具温度为109℃，螺杆与机筒间隙为0.18mm；（5）、挤出成型后，在110℃下冷却液的中牵引拉伸10s，拉伸强度为87.5kg/mm2，冷却液为松节油、四氯化碳、四丁基三溴化铵按重量比60:50:0.2的比例混合制成，处理完成后冷却卷绕。
本发明的有益效果：本发明在加工时，在尼龙原料中加入多种助剂，通过个中助剂的比例配比和各原料的协同作用，使尼龙鱼线的性能大大提升，改善了尼龙的加工性能，提高了其耐磨性、防腐性能及拉伸性能，加入碳酸钙和纳米氧化铝可以降低鱼线的弹性，而且采用2步挤出方法，使各原料充分混合，在较高的温度下挤出，挤出效率高，而且挤出的鱼线粗细均匀、质量好，而且不产生气泡，鱼线加工的成品率提高20%以上；在挤出成型后，在冷却液中拉伸后可以使鱼线的强度更均匀，而且在冷却液中处理可以防止鱼线脆性增加，影响鱼线使用，本发明方法处理可以直径0.1mm尼龙单丝拉伸强度提升35%以上。
具体实施方式
一种高性能鱼线加工方法，包括以下步骤：（1）、将尼龙6在105℃真空条件下干燥20min；（2）、将硫酸铝钾、氯磺化聚乙烯、纳米二氧化钛、轻质碳酸钙干燥；（3）、将尼龙6、十二烷基苯磺酸钠、氯磺化聚乙烯、纳米氧化银、轻质碳酸钙、纳米氧化铝粉末按重量比85:0.8:3.2:2.5:1.2:1.7的比例混合，使用单螺杆挤出机挤出，造粒，挤出机长径比30:1，挤出机采用4段加热方式，4段温度分别为240℃、240℃、243℃、245℃；（4）、将步骤（3）造粒好的原料使用长径比为25:1的挤出机挤出成型，挤出机端部设有纺丝模具，挤出机采用5段加热方式，挤出机5段温度分别为237℃、239℃、240℃、242℃、244℃，模具温度为109℃，螺杆与机筒间隙为0.18mm；（5）、挤出成型后，在110℃下冷却液的中牵引拉伸10s，拉伸强度为87.5kg/mm2，冷却液为松节油、四氯化碳、四丁基三溴化铵按重量比60:50:0.2的比例混合制成，处理完成后冷却卷绕。

Claims (1)

1.一种高性能鱼线加工方法，其特征在于，包括以下步骤：（1）、将尼龙6在105℃真空条件下干燥20min；（2）、将硫酸铝钾、氯磺化聚乙烯、纳米二氧化钛、轻质碳酸钙干燥；（3）、将尼龙6、十二烷基苯磺酸钠、氯磺化聚乙烯、纳米氧化银、轻质碳酸钙、纳米氧化铝粉末按重量比85:0.8:3.2:2.5:1.2:1.7的比例混合，使用单螺杆挤出机挤出，造粒，挤出机长径比30:1，挤出机采用4段加热方式，4段温度分别为240℃、240℃、243℃、245℃；（4）、将步骤（3）造粒好的原料使用长径比为25:1的挤出机挤出成型，挤出机端部设有纺丝模具，挤出机采用5段加热方式，挤出机5段温度分别为237℃、239℃、240℃、242℃、244℃，模具温度为109℃，螺杆与机筒间隙为0.18mm；（5）、挤出成型后，在110℃下冷却液的中牵引拉伸10s，拉伸强度为87.5kg/mm2，冷却液为松节油、四氯化碳、四丁基三溴化铵按重量比60:50:0.2的比例混合制成，处理完成后冷却卷绕。
CN201510133408.0A 2015-03-26 2015-03-26 一种高性能鱼线加工方法 Pending CN104805523A (zh)