CN104804845A - Raw silk soft and anti-wear cutting fluid - Google Patents
Raw silk soft and anti-wear cutting fluid Download PDFInfo
- Publication number
- CN104804845A CN104804845A CN201510149888.XA CN201510149888A CN104804845A CN 104804845 A CN104804845 A CN 104804845A CN 201510149888 A CN201510149888 A CN 201510149888A CN 104804845 A CN104804845 A CN 104804845A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw silk
- cutting fluid
- minute
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a raw silk soft and anti-wear cutting fluid which comprises the following raw materials by weight: 4 to 6 parts of sodium molybdate, 0.5 to 1 part of laurocapram, 0.1 to 0.2 part of aluminum ammonium sulfate, 0.6 to 2 parts of diazolidinyl urea, 0.1 to 0.2 part of ricinus oil polyoxyethylene ether, 0.7 to 1 part of 2,6-butylated hydroxytoluene, 5 to 7 parts of acetylated lanolin, 3 to 4 parts of polylactic acid, 16 to 20 parts of dimethyl sulfoxide, 4 to 5 parts of raw silk, 20 to 30 parts of triethanolamine borate, 1 to 2 parts of sodium dodecyl sulfonate, and 200 to 300 parts of deionized water. A fibroin lubricating liquid (an intermediate product of the raw silk soft and anti-wear cutting fluid) takes natural silk as a main material, thereby being nontoxic, free of pollution, and high in lubricity; triethanolamine borate, which is excellent in extreme pressure lubricity, rust-proof, anti-bacterial, capable of sterilizing and the like, is mixed with the fibroin lubricating liquid to obtain a liquid mixture; the liquid mixture is modified with polylactic acid. Therefore, the fracture strength and wettability of a blend membrane can be improved.
Description
Technical field
The present invention relates generally to cutting fluid field, particularly relates to the soft wear-resistant cutting fluid of a kind of raw silk.
Background technology
Cutting fluid is that one is used in metal cutting, the mill course of processing, be used for the industrial type fluid of Cooling and Lubricator cutter and workpiece, cutting fluid is formed through the cooperation of science compound by multiple super strong functional auxiliary agent, possesses good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature simultaneously.Overcome the easily difficult dilution in smelly, winter in summer of traditional soap base emulsion, rust-proof effect difference defect, lathe paint is also had no adverse effects, be applicable to ferrous metal cutting and mill processing, belong to leading current abrasive product.
For reducing metal because of the loss brought of wearing and tearing in the course of processing, the performance requriements of each manufacturing enterprise to metal working fluid is more and more higher; Simultaneously; due to the attention of Environmental protection; propose the requirement such as cleaner production, energy-saving and emission-reduction; impel metal working fluid towards environmental protection, energy-conservation, efficient future development. fully synthetic cutting fluid has the advantages such as clean environment firendly, resource are wide, easy preparation, is the prior development direction of metal working fluid from now on.
Summary of the invention
The object of the invention is just to provide the soft wear-resistant cutting fluid of a kind of raw silk.
The present invention is achieved by the following technical solutions:
The soft wear-resistant cutting fluid of a kind of raw silk, it is made up of the raw material of following weight parts:
Sodium orthomolybdate 4-6, laurocapram 0.5-1, exsiccated ammonium alum 0.1-0.2, two Imidurea 0.6-2, castor oil polyoxyethylene ether 0.1-0.2,2,6 ditertiary butyl p cresol 0.7-1, Modulan 5-7, poly(lactic acid) 3-4, dimethyl sulfoxide (DMSO) 16-20, raw silk 4-5, Triethanolamine borate 20-30, sodium laurylsulfonate 1-2, deionized water 200-300.
A preparation method for the soft wear-resistant cutting fluid of raw silk, comprises the following steps:
(1) poly(lactic acid) is joined in dimethyl sulfoxide (DMSO), obtain PLA solution;
(2) above-mentioned raw silk is joined in the sodium carbonate solution of its weight 90-100 0.4-0.6wt% doubly, heat-insulation soaking 60-80 minute at 98-100 DEG C, filter, dry, wear into fine powder, mix with sodium laurylsulfonate, add the 85-90% of above-mentioned deionized water weight, stir, obtain fibroin lubricating fluid;
(3) Triethanolamine borate is heated to 80-90 DEG C, add PLA solution, fibroin lubricating fluid, magnetic stirring apparatus stirs 3-4 minute, adds Modulan, insulated and stirred 2-3 minute at 40-45 DEG C, obtains extreme pressure lubricating liquid;
(4) castor oil polyoxyethylene ether is joined in remaining deionized water, stir, add Sodium orthomolybdate, obtain rust protection liquid;
(5) mixed with rust protection liquid by above-mentioned extreme pressure lubricating liquid, be heated to 60-70 DEG C, 80-100 rev/min of dispersed with stirring 20-30 minute, add each raw material of residue, 600-1000 rev/min of dispersed with stirring 30-40 minute, obtains described cutting fluid.
Advantage of the present invention is:
Fibroin lubricating fluid of the present invention take silk as major ingredient, nontoxic pollution-free, oilness is high, the extreme boundary lubrication of Triethanolamine borate is good, and has the functions such as antirust, antibacterial, virus killing concurrently, mixes with silk fibroin solution, and adopt polylactic acid modified, breaking tenacity and the wettability of blend film can be improved, more stable lubricant film layer can be generated on the surface at frictional metal, effectively raise extreme pressure anti-wear and reactive behavior.
The Modulan that the present invention adds can the flexibility of modification cutting fluid, better promotes the effect of extreme-pressure anti-wear.
Embodiment
Embodiment 1:
The soft wear-resistant cutting fluid of a kind of raw silk, it is made up of the raw material of following weight parts:
Sodium orthomolybdate 6, laurocapram 0.5, exsiccated ammonium alum 0.2, two Imidurea 0.6, castor oil polyoxyethylene ether 0.2,2,6 ditertiary butyl p cresol 0.7, Modulan 7, poly(lactic acid) 4, dimethyl sulfoxide (DMSO) 20, raw silk 5, Triethanolamine borate 30, sodium laurylsulfonate 1, deionized water 300.
A preparation method for the soft wear-resistant cutting fluid of raw silk, comprises the following steps:
(1) poly(lactic acid) is joined in dimethyl sulfoxide (DMSO), obtain PLA solution;
(2) above-mentioned raw silk is joined in the sodium carbonate solution of 0.6wt% of its weight 100 times, heat-insulation soaking 60 minutes at 100 DEG C, filter, dry, wear into fine powder, mix with sodium laurylsulfonate, add 90% of above-mentioned deionized water weight, stir, obtain fibroin lubricating fluid;
(3) Triethanolamine borate is heated to 90 DEG C, adds PLA solution, fibroin lubricating fluid, magnetic stirring apparatus stirs 3 minutes, and add Modulan, at 45 DEG C, insulated and stirred 3 minutes, obtains extreme pressure lubricating liquid;
(4) castor oil polyoxyethylene ether is joined in remaining deionized water, stir, add Sodium orthomolybdate, obtain rust protection liquid;
(5) mixed with rust protection liquid by above-mentioned extreme pressure lubricating liquid, be heated to 70 DEG C, 100 revs/min of dispersed with stirring 30 minutes, add each raw material of residue, 1000 revs/min of dispersed with stirring 40 minutes, obtain described cutting fluid.
Performance test:
Claims (2)
1. the soft wear-resistant cutting fluid of raw silk, is characterized in that what it was made up of the raw material of following weight parts:
Sodium orthomolybdate 4-6, laurocapram 0.5-1, exsiccated ammonium alum 0.1-0.2, two Imidurea 0.6-2, castor oil polyoxyethylene ether 0.1-0.2,2,6 ditertiary butyl p cresol 0.7-1, Modulan 5-7, poly(lactic acid) 3-4, dimethyl sulfoxide (DMSO) 16-20, raw silk 4-5, Triethanolamine borate 20-30, sodium laurylsulfonate 1-2, deionized water 200-300.
2. a preparation method for the soft wear-resistant cutting fluid of raw silk as claimed in claim 1, is characterized in that comprising the following steps:
(1) poly(lactic acid) is joined in dimethyl sulfoxide (DMSO), obtain PLA solution;
(2) above-mentioned raw silk is joined in the sodium carbonate solution of its weight 90-100 0.4-0.6wt% doubly, heat-insulation soaking 60-80 minute at 98-100 DEG C, filter, dry, wear into fine powder, mix with sodium laurylsulfonate, add the 85-90% of above-mentioned deionized water weight, stir, obtain fibroin lubricating fluid;
(3) Triethanolamine borate is heated to 80-90 DEG C, add PLA solution, fibroin lubricating fluid, magnetic stirring apparatus stirs 3-4 minute, adds Modulan, insulated and stirred 2-3 minute at 40-45 DEG C, obtains extreme pressure lubricating liquid;
(4) castor oil polyoxyethylene ether is joined in remaining deionized water, stir, add Sodium orthomolybdate, obtain rust protection liquid;
(5) mixed with rust protection liquid by above-mentioned extreme pressure lubricating liquid, be heated to 60-70 DEG C, 80-100 rev/min of dispersed with stirring 20-30 minute, add each raw material of residue, 600-1000 rev/min of dispersed with stirring 30-40 minute, obtains described cutting fluid.