CN104804537A - Low-temperature curing silk-screen printing ink for polypropylene materials - Google Patents
Low-temperature curing silk-screen printing ink for polypropylene materials Download PDFInfo
- Publication number
- CN104804537A CN104804537A CN201510196436.7A CN201510196436A CN104804537A CN 104804537 A CN104804537 A CN 104804537A CN 201510196436 A CN201510196436 A CN 201510196436A CN 104804537 A CN104804537 A CN 104804537A
- Authority
- CN
- China
- Prior art keywords
- parts
- screen printing
- polypropylene
- material ink
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses low-temperature curing silk-screen printing ink for polypropylene materials. The silk-screen printing ink comprises the following constituents: 20 to 30 parts of modified polypropylene resin, 10 to 20 parts of chlorinated polyalkene, 1 to 10 parts of an adhesion promoter, 2 to 8 parts of isopropanol, 3 to 9 parts of organic pigment, 2 to 7 parts of a wetting agent, 5 to 10 parts of a defoamer, 5 to 15 parts of fillers, and 25 to 35 parts of a dissolvent. The silk-screen printing ink has good adhesive force on the surface of processed or partially not processed polypropylene materials, is good in coating gloss, high in curing speed, low in curing temperature and good in continuous printing property, does not draw silk, and is clear in printed patterns and strong in stereoscopic sensation.
Description
Technical field
The present invention relates to ink area, particularly relate to a kind of low-temperature curing polypropylene material ink for screen printing.
Background technology
Acrylic plastering has that relative hardness is high, proportion is little, tensile strength is high, the transparency is good, anti-stress cracking and good, the resistance to heat deflection temperature (HDT) of chemical resistance high and there is fabulous injection moulding performance, can arbitrarily stretch and directed, can with the advantage such as other material blending and modifying, have a wide range of applications in people's daily life.
In printing industry, polypropylene everyday articles, packing bag, medicine equipment goods, industrial woven product etc. are all the important stock materials of a class.
But acrylic plastering polarity is low, degree of crystallization is high, and surface energy is low, and stereoregularity is high, natural cohesive force is large.Adopt general ink for screen printing, its sticking power is poor, therefore silk-screen again after conventional complex acid mixed solution etching, surface grinding or plasma treatment, and need main equipment, treatment process is dangerous, contaminate environment.And polyacrylic heat-drawn wire only has 110 DEG C, and the solidification value of common ink is all more than 130 DEG C, toast under such high temperatures, acrylic plastering can deform, and therefore develops the polypropylene material ink for screen printing with low-temperature curing performance significant.
Summary of the invention
The object of the invention is to overcome the deficiency that above-mentioned prior art exists, provide that a kind of sticking power is good, curing speed is fast, glossiness is good, the polypropylene material ink for screen printing of low-temperature curable.
For achieving the above object, the present invention is achieved by the following technical solutions:
A kind of low-temperature curing polypropylene material ink for screen printing, meter comprises following component by weight: modified polypropylene resin 20 ~ 30 parts, chlorinated polyolefin resin 10 ~ 20 parts, adhesion promoter 1 ~ 10 part, Virahol 2 ~ 8 parts, pigment dyestuff 3 ~ 9 parts, wetting agent 2 ~ 7 parts, defoamer 5 ~ 10 parts, filler 5 ~ 15 parts, solvent 25 ~ 35 parts.
Preferably, described modified polypropylene resin is at least one in chlorinated polypropylene, organic-silicon-modified acrylic resin.
Preferably, described adhesion promoter is vinyl chloride-vinyl acetate resin.
Preferably, described wetting agent is at least one in alkyl-sulphate, sulfonate, lipid acid, polyoxyethylene aliphatic alcohol ether.
Preferably, described defoamer is at least one in polypropylene glycerol aether, polyoxypropylene, polyoxyethylene glycerol ether, polydimethylsiloxane.
Preferably, at least one in described solvent ethylene glycol, butylacetate, ethyl acetate.
Beneficial effect of the present invention:
Low-temperature curing polypropylene material ink for screen printing prepared by the present invention, all have good sticking power on treated and part untreated polypropylene material surface, coating gloss is good, curing speed is fast, low, the continuous print of solidification value is good, not wire drawing, printed patterns is clear, and stereoscopic sensation is strong.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
A kind of low-temperature curing polypropylene material ink for screen printing, meter comprises following component by weight: modified polypropylene resin 20 ~ 30 parts, chlorinated polyolefin resin 10 ~ 20 parts, adhesion promoter 1 ~ 10 part, Virahol 2 ~ 8 parts, pigment dyestuff 3 ~ 9 parts, wetting agent 2 ~ 7 parts, defoamer 5 ~ 10 parts, filler 5 ~ 15 parts, solvent 25 ~ 35 parts.
Low-temperature curing polypropylene material ink for screen printing prepared by the present invention, has the advantages such as sticking power is good, curing speed is fast, glossiness is good, low-temperature curable.
Embodiment 1
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: chlorinated polypropylene 30 parts, chlorinated polyolefin resin 10 parts, vinyl chloride-vinyl acetate resin 1 part, Virahol 8 parts, pigment dyestuff 9 parts, alkyl-sulphate 7 parts, polypropylene glycerol aether 10 parts, filler 5 parts, ethylene glycol 35 parts.
Embodiment 2
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: organic-silicon-modified acrylic resin 20 parts, chlorinated polyolefin resin 20 parts, vinyl chloride-vinyl acetate resin 10 parts, Virahol 2 parts, pigment dyestuff 3 parts, 2 parts, sulfonate, polyoxypropylene 5 parts, filler 15 parts, butylacetate 25 parts.
Embodiment 3
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: chlorinated polypropylene 25 parts, chlorinated polyolefin resin 15 parts, vinyl chloride-vinyl acetate resin 5 parts, Virahol 6 parts, pigment dyestuff 6 parts, lipid acid 4, polyoxyethylene glycerol ether 7 parts, filler 10 parts, ethyl acetate 30 parts.
Embodiment 4
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: organic-silicon-modified acrylic resin 22 parts, chlorinated polyolefin resin 11 parts, vinyl chloride-vinyl acetate resin 2 parts, Virahol 3 parts, pigment dyestuff 4 parts, polyoxyethylene aliphatic alcohol ether 4 parts, polydimethylsiloxane 6 parts, filler 7 parts, butylacetate 28 parts.
Embodiment 5
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: chlorinated polypropylene 28 parts, chlorinated polyolefin resin 18 parts, vinyl chloride-vinyl acetate resin 9 parts, Virahol 7 parts, pigment dyestuff 8 parts, 6 parts, sulfonate, polyoxypropylene 9 parts, filler 13 parts, ethyl acetate 33 parts.
Embodiment 6
Low-temperature curing polypropylene material ink for screen printing of the present invention, meter comprises following component by weight: organic-silicon-modified acrylic resin 20 parts, chlorinated polyolefin resin 18 parts, vinyl chloride-vinyl acetate resin 6 parts, Virahol 4 parts, pigment dyestuff 3 parts, alkyl-sulphate 2 parts, polypropylene glycerol aether 10 parts, filler 9 parts, ethylene glycol 30 parts.
Performance test
Basic mechanical design feature of the present invention is as shown in table 1:
Table 1
As seen from Table 1, low-temperature curing polypropylene material ink for screen printing prepared by the present invention, has the advantages such as sticking power is good, curing speed is fast, glossiness is good, low-temperature curable.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (6)
1. a low-temperature curing polypropylene material ink for screen printing, it is characterized in that, meter comprises following component by weight: modified polypropylene resin 20 ~ 30 parts, chlorinated polyolefin resin 10 ~ 20 parts, adhesion promoter 1 ~ 10 part, Virahol 2 ~ 8 parts, pigment dyestuff 3 ~ 9 parts, wetting agent 2 ~ 7 parts, defoamer 5 ~ 10 parts, filler 5 ~ 15 parts, solvent 25 ~ 35 parts.
2. polypropylene material ink for screen printing according to claim 1, is characterized in that: described modified polypropylene resin is at least one in chlorinated polypropylene, organic-silicon-modified acrylic resin.
3. polypropylene material ink for screen printing according to claim 1, is characterized in that: described adhesion promoter is vinyl chloride-vinyl acetate resin.
4. polypropylene material ink for screen printing according to claim 1, is characterized in that: described wetting agent is at least one in alkyl-sulphate, sulfonate, lipid acid, polyoxyethylene aliphatic alcohol ether.
5. polypropylene material ink for screen printing according to claim 1, is characterized in that: described defoamer is at least one in polypropylene glycerol aether, polyoxypropylene, polyoxyethylene glycerol ether, polydimethylsiloxane.
6. polypropylene material ink for screen printing according to claim 1, is characterized in that: at least one in described solvent ethylene glycol, butylacetate, ethyl acetate.