CN104789056A - Elastic galling middle-coating paint and preparation method thereof - Google Patents
Elastic galling middle-coating paint and preparation method thereof Download PDFInfo
- Publication number
- CN104789056A CN104789056A CN201510228588.0A CN201510228588A CN104789056A CN 104789056 A CN104789056 A CN 104789056A CN 201510228588 A CN201510228588 A CN 201510228588A CN 104789056 A CN104789056 A CN 104789056A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- elastic
- revs
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an elastic galling middle-coating paint which comprises the following components in parts by weight: 60-80 parts of quartz sand, 100-120 parts of styrene-acrylic elastic emulsion, 0.5-0.8 part of defoaming agent, 30-50 parts of tackifying resin, 1-4 parts of coupling agent, 10-20 parts of corn rice flour, 8-12 parts of 6# solvent oil and 10-15 parts of ethylene glycol. The paint prepared according to the specific formula and preparation method has the advantages of favorable adsorptive power, high surface smoothness, high strength and high cracking resistance.
Description
Technical field
The present invention relates to the preparation method of a kind of formulation for coating material and this coating, be specifically related to coating and preparation method thereof in a kind of elastic napping.
Background technology
Coating, is called paint at Chinese tradition.China's coating circle more authoritative " coating process " book is definition like this: " coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating ".
In building external paint, elastic napping coating has concavo-convex texture and texture, can revise body of wall crackle, and finishing effect is given prominence to, and stereoscopic sensation is strong, because receive liking of people.Though current elastic napping coating possesses as above advantage, but still there are some defects, as adsorptive power is poor, intensity is low, and anti-division poor performance, surface flatness is low.
Summary of the invention
In view of this, the object of this invention is to provide coating and preparation method thereof in a kind of elastic napping, make it have the advantage that adsorptive power is good, surface flatness is high, intensity is high and anti-division performance is good.
For achieving the above object, coating in elastic napping of the present invention, comprise following component by weight: quartz sand 60-80 part, phenylpropyl alcohol elastic emulsion 100-120 part, defoamer 0.5-0.8 part, tackifying resin 30-50 part, coupling agent 1-4 part, corn ground rice 10-20 part, 6# solvent oil 8-12 part, ethylene glycol 10-15 part.
Further, described tackifying resin is choose any one kind of them in Gum Rosin, terpine resin and petroleum resin.
Further, described coupling agent is γ-glycidyl ether oxygen propyl trimethoxy silicane (KH-560), γ (methacryloxypropyl)-propyl trimethoxy silicane (KH-570), 3,3,4-isopropyl tri (dioctylphosphato)titanate and 3, one in 3,10-tri-(dioctylphosphato) metatitanic acid second diester.
The preparation method of coating of the present invention, comprises the following steps:
(1) the formula feeding by described is for subsequent use;
(2) described batching is poured in mixing machine, be heated to 70 DEG C-90 DEG C, with the speed blending dispersion 15-20 minutes of 800 revs/min;
(3) pour in shredder by raw material subsequently, with the speed of 300 revs/min grinding 30-40 minutes, cooling, can obtain finished product.
Advantageous Effects of the present invention is: the coating adopting special formulation of the present invention and preparation method's gained, has the advantage that adsorptive power is good, surface flatness is high, intensity is high and anti-division performance is good.
Embodiment
Below in conjunction with embodiment and experimental data, to above-mentioned being described in more detail with other technical characteristic and advantage of the present invention.
embodiment 1
Coating in a kind of elastic napping, comprise following component by weight: quartz sand 60kg, phenylpropyl alcohol elastic emulsion 100kg, defoamer 0.5kg, Gum Rosin 30kg, γ-glycidyl ether oxygen propyl trimethoxy silicane (KH-560) 1kg, corn ground rice 10kg, 6# solvent oil 8kg, ethylene glycol 10kg.
Concrete preparation process is as follows:
(1) the formula feeding by described is for subsequent use;
(2) described batching is poured in mixing machine, be heated to 70 DEG C, with the speed blending dispersion 15 minutes of 800 revs/min;
(3) pour in shredder by raw material subsequently, grind 30 minutes with the speed of 300 revs/min, cooling, can obtain finished product.
embodiment 2
Coating in a kind of elastic napping, comprise following component by weight: quartz sand 70kg, phenylpropyl alcohol elastic emulsion 110kg, defoamer 0.6kg, terpine resin 40kg, γ (methacryloxypropyl)-propyl trimethoxy silicane (KH-570) 3kg, corn ground rice 15kg, 6# solvent oil 10kg, ethylene glycol 12kg.
Concrete preparation process is as follows:
(1) the formula feeding by described is for subsequent use;
(2) described batching is poured in mixing machine, be heated to 80 DEG C, with the speed blending dispersion 18 minutes of 800 revs/min;
(3) pour in shredder by raw material subsequently, grind 35 minutes with the speed of 300 revs/min, cooling, can obtain finished product.
embodiment 3
Coating in a kind of elastic napping, comprises following component: quartz sand 80kg, phenylpropyl alcohol elastic emulsion 120kg by weight, defoamer 0.8kg, petroleum resin 50kg, 3,3,4-isopropyl tri (dioctylphosphato)titanate and 3,3,10-tri-(dioctylphosphato) metatitanic acid second diester 4kg, corn ground rice 20kg, 6# solvent oil 12kg, ethylene glycol 15kg.
Concrete preparation process is as follows:
(1) the formula feeding by described is for subsequent use;
(2) described batching is poured in mixing machine, be heated to 90 DEG C, with the speed blending dispersion 20 minutes of 800 revs/min;
(3) pour in shredder by raw material subsequently, grind 40 minutes with the speed of 300 revs/min, cooling, can obtain finished product.
In above-mentioned three embodiments, the EFKA-2020 defoamer that described defoamer adopts the holy high chemical Science and Technology Ltd. in Guangzhou to produce.
Coating prepared by this special formulation and method, adsorptive power improves 40-60%, and intensity improves 30-38%, and face slickness improves 50-60%, and anti-division performance improves 65-70%.
What finally illustrate is, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (4)
1. coating in an elastic napping, it is characterized in that, comprise following component by weight: quartz sand 60-80 part, phenylpropyl alcohol elastic emulsion 100-120 part, defoamer 0.5-0.8 part, tackifying resin 30-50 part, coupling agent 1-4 part, corn ground rice 10-20 part, 6# solvent oil 8-12 part, ethylene glycol 10-15 part.
2. coating according to claim 1, is characterized in that: described tackifying resin is choose any one kind of them in Gum Rosin, terpine resin and petroleum resin.
3. coating according to claim 1, it is characterized in that: described coupling agent is γ-glycidyl ether oxygen propyl trimethoxy silicane (KH-560), γ (methacryloxypropyl)-propyl trimethoxy silicane (KH-570), 3,3,4-isopropyl tri (dioctylphosphato)titanate and 3, one in 3,10-tri-(dioctylphosphato) metatitanic acid second diester.
4. prepare a method for coating as described in claim 1-3 any one, it is characterized in that, comprise the following steps:
(1) the formula feeding by described is for subsequent use;
(2) described batching is poured in mixing machine, be heated to 70 DEG C-90 DEG C, with the speed blending dispersion 15-20 minutes of 800 revs/min;
(3) pour in shredder by raw material subsequently, with the speed of 300 revs/min grinding 30-40 minutes, cooling, can obtain finished product.