CN104782592A - 一种复合多层柔韧鱼线 - Google Patents
一种复合多层柔韧鱼线 Download PDFInfo
- Publication number
- CN104782592A CN104782592A CN201510133622.6A CN201510133622A CN104782592A CN 104782592 A CN104782592 A CN 104782592A CN 201510133622 A CN201510133622 A CN 201510133622A CN 104782592 A CN104782592 A CN 104782592A
- Authority
- CN
- China
- Prior art keywords
- layer
- coating
- fishing line
- coating layer
- composite multi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及渔具生产加工技术领域,具体涉及一种复合多层柔韧鱼线,其包含尼龙层、切水涂层、柔韧涂层、抗拉防老化涂层,其中尼龙层的外侧涂覆有切水涂层、切水涂层的外侧涂覆有柔韧涂层、每层均有特定组分按一定配比混合制成,经本发明合成的鱼线各涂层相互作用,紧密连接,能同时保证有较强的承受力、耐磨和柔韧性,切水度好,能快速传达渔汛,不会出现绕丝现象,在一定承受范围内不会断丝,承受力相对于现有同种类的鱼线来讲有较大的提升。
Description
技术领域
本发明涉及渔具生产加工技术领域,具体涉及一种复合多层柔韧鱼线。
背景技术
鱼线是钓鱼工具之一,可以分为“线”和“丝”两种,线是用两股或两股以上的单纱或丝一次或多次合并加捻而成,而丝则是独此一根,钓丝的制作方法,通常是将原料熔融后,从特制的喷丝孔中挤压出来,经冷却、牵伸、卷绕等加工后制成。这样制得的鱼线为透明状,伸长率较小且具有较强的拉力,特别适于做鱼线使用,现有技术中鱼线一般分成尼龙线、塑料线、钢丝线、编织线、合成线5大种类,目前鱼线多为单丝合成,每种鱼线均具各自的缺点,不能满足市场多元化的需求。
发明内容
本发明的目的在于提供一种复合多层柔韧鱼线。
本发明采用的技术方案为:一种复合多层柔韧鱼线,其包含以下各层:
尼龙层、切水涂层、柔韧涂层、抗拉防老化涂层,其中尼龙层的外侧涂覆有切水涂层、切水涂层的外侧涂覆有柔韧涂层;
其中,尼龙层由以下组份的原料按特定的比例混合制成:
尼龙50%60%
聚酰胺树脂5%-8%
硬脂酸锌10%-12%
脂肪醇聚氧乙烯醚2%-4%
大豆纤维1%-3%
石英纤维18%-25%;
其中,切水涂层由以下组份的原料按特定的比例混合制成:
高密度聚乙烯65%-70%
衣康酸5%-8%
十二羟基硬脂酸3%-6%
丙烯酸树脂10%-12%
减水剂1%-2%
环氧硬脂酸辛酯2%-8%;
其中,柔韧涂层由以下组份的原料按特定的比例混合制成:
PE树脂65%-70%
硬脂酸钡1%-2%
二甲基硅油8%-10%
苎麻纤维15%-20%
羟乙基纤维素3%-5%。
本发明的有益效果在于,经本发明合成的鱼线各涂层相互作用,紧密连接,能同时保证有较强的承受力、耐磨和柔韧性,切水度好,能快速传达渔汛,不会出现绕丝现象,在一定承受范围内不会断丝,承受力相对于现有同种类的鱼线来讲有较大的提升。
具体实施方式
一种复合多层柔韧鱼线,其包含以下各层:
尼龙层、切水涂层、柔韧涂层、抗拉防老化涂层,其中尼龙层的外侧涂覆有切水涂层、切水涂层的外侧涂覆有柔韧涂层;
其中,尼龙层由以下组份的原料按特定的比例混合制成:
尼龙50%60%
聚酰胺树脂5%-8%
硬脂酸锌10%-12%
脂肪醇聚氧乙烯醚2%-4%
大豆纤维1%-3%
石英纤维18%-25%;
其中,切水涂层由以下组份的原料按特定的比例混合制成:
高密度聚乙烯65%-70%
衣康酸5%-8%
十二羟基硬脂酸3%-6%
丙烯酸树脂10%-12%
减水剂1%-2%
环氧硬脂酸辛酯2%-8%
其中,柔韧涂层由以下组份的原料按特定的比例混合制成:
PE树脂65%-70%
硬脂酸钡1%-2%
二甲基硅油8%-10%
苎麻纤维15%-20%
羟乙基纤维素3%-5%
经本发明制作出的鱼线在不同直径相对的拉力值如下:
直径为0.128mm时,拉力值为3.08kg
直径为0.148mm时,拉力值为3.68kg
直径为0.165mm时,拉力值为4.12kg
直径为0.181mm时,拉力值为5.56kg
直径为0.203mm时,拉力值为7.08kg
直径为0.234mm时,拉力值为8.68kg。
Claims (1)
1.一种复合多层柔韧鱼线,其特征在于,其包含以下各层:
尼龙层、切水涂层、柔韧涂层、抗拉防老化涂层,其中尼龙层的外侧涂覆有切水涂层、切水涂层的外侧涂覆有柔韧涂层;
其中,尼龙层由以下组份的原料按特定的比例混合制成:
尼龙50%60%
聚酰胺树脂5%-8%
硬脂酸锌10%-12%
脂肪醇聚氧乙烯醚2%-4%
大豆纤维1%-3%
石英纤维18%-25%;
其中,切水涂层由以下组份的原料按特定的比例混合制成:
高密度聚乙烯65%-70%
衣康酸5%-8%
十二羟基硬脂酸3%-6%
丙烯酸树脂10%-12%
减水剂1%-2%
环氧硬脂酸辛酯2%-8%;
其中,柔韧涂层由以下组份的原料按特定的比例混合制成:
PE树脂65%-70%
硬脂酸钡1%-2%
二甲基硅油8%-10%
苎麻纤维15%-20%
羟乙基纤维素3%-5%。