CN104762818A - One-side-coated anti-flame moisture-permeable waterproof cloth and preparation process thereof - Google Patents
One-side-coated anti-flame moisture-permeable waterproof cloth and preparation process thereof Download PDFInfo
- Publication number
- CN104762818A CN104762818A CN201510154069.4A CN201510154069A CN104762818A CN 104762818 A CN104762818 A CN 104762818A CN 201510154069 A CN201510154069 A CN 201510154069A CN 104762818 A CN104762818 A CN 104762818A
- Authority
- CN
- China
- Prior art keywords
- coating
- waterproof cloth
- superfine powder
- fire
- core buffer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides one-side-coated anti-flame moisture-permeable waterproof cloth and a preparation process thereof. The waterproof cloth comprises a polyamide fabric as base cloth, wherein a printing layer is arranged on the base cloth and is coated with a waterproof layer, and the waterproof layer is coated with a hemp stem core ultrafine powder modified polyurethane coating. According to the one-side-coated anti-flame moisture-permeable waterproof cloth and the special preparation process, the carbon-black-containing conductive fiber polyamide fabric is taken as the base cloth, and a nylon special washable waterproof agent and a hemp stem core ultrafine powder modified polyurethane coating material are utilized, so that the waterproof cloth has a water-resisting and moisture-permeating function; furthermore, the one-side-coated anti-flame moisture-permeable waterproof cloth integrates inflaming retardance, ultraviolet ray resistance, static electricity resistance, heat aging resistance, low-temperature staining resistance, acid resistance, alkali resistance and sea water resistance, and can be applied to a main engine plant and an air force station.
Description
Technical field
The present invention relates to industrial cloth field, particularly about the fire-retardant moisture-inhibiting waterproof cloth of one side coating and preparation technology thereof.
Background technology
At present, the fire-retardant moisture-inhibiting waterproof cloth of one side coating is generally mainly used in outdoor tent cloth, car and boat harbour waterproof covering cloth, but the waterproof cloth that will apply to main engine plants and station, the military region then exists a difficult problem for waterproof not moisture-inhibiting, but also the function of incompatible fire-retardant, uvioresistant and electrostatic.
Summary of the invention
For solving above-mentioned prior art problem, the invention provides the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating, it possesses the function of Waterproof Breathable, but also the function of compatible fire-retardant, uvioresistant, antistatic, heat-proof aging, low temperature resistant anti-being stained with property, acidproof, alkaline-resisting, sea water resistance, main engine plants and station, the military region can be applied to.
For achieving the above object, the present invention is achieved through the following technical solutions:
The fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating, comprising POLYAMIDE FABRIC is base cloth, and described base cloth is provided with printed layer, and described printed layer is coated with watertight composition, described watertight composition is coated with Chinese Kenaf Core Buffer superfine powder modified polyurethane coating.
As preferably, described POLYAMIDE FABRIC is the high-strength POLYAMIDE FABRIC of 420D × 420D, its through close be 188/cm, filling density is 160/cm.
As preferably, in described POLYAMIDE FABRIC, every 0.5 ~ 1cm radial direction is containing 1 carbon black conductive fiber, reaches permanent anti-static function.
As preferably, described printed layer is plain net camouflage printing layer.
As preferably, the waterproofing agent in described watertight composition is the special washable waterproofing agent of nylon, and its consumption is 5 ~ 15g/m
2.
As preferably, described Chinese Kenaf Core Buffer superfine powder polyurethane coating comprises Chinese Kenaf Core Buffer superfine powder polyurethane coating bottom glue-line and Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue-line successively.
As preferably, described Chinese Kenaf Core Buffer superfine powder polyurethane coating is the Chinese Kenaf Core Buffer superfine powder polyurethane coating adding fire retardant.
Another object of the present invention is to the preparation technology providing the fire-retardant moisture-inhibiting waterproof cloth of above-mentioned one side coating, the technical scheme taked is: the preparation technology of the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating, comprises the steps:
1) according to required decalcomania, silk-screen half tone is made;
2) by ready POLYAMIDE FABRIC, with neatly, evenly, be in an orderly manner laid on printing table by hair to positive and negative;
3) the silk-screen half tone made is covered on fabric, bottoming is starched blade coating on decalcomania;
4) to through step 3) POLYAMIDE FABRIC in decalcomania adopt concentrator to carry out camouflage printing;
5) after printing technology completes, carry out washable WATER REPELLENT TREATMENT with waterproofing agent to printed fabric, then dry under the high temperature of 210 ~ 230 DEG C, preferable temperature is 220 DEG C, dries waterproofing agent at this temperature, and the waterproof effect of the cloth obtained is best;
6) after drying, Chinese Kenaf Core Buffer superfine powder polyurethane coating primer is coated on watertight composition, with calender, under the high temperature of 210 ~ 230 DEG C, press polish is once, coating is carried out again with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue, once, finally last coating procedure is carried out with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue again with calender press polish under the high temperature of 210 ~ 230 DEG C after coating.
As preferably, described POLYAMIDE FABRIC is the high-strength POLYAMIDE FABRIC of 420D × 420D, its through close be 188/cm, filling density is 160/cm, and its every Gram Mass is 162g/m
2.
As preferably, in described POLYAMIDE FABRIC, every 0.5 ~ 1cm radial direction is containing 1 carbon black conductive fiber;
As preferably, described step 5) in waterproofing agent be the special washable waterproofing agent of nylon, its consumption is 5 ~ 15g/m
2.
As preferably, described step 6) described in Chinese Kenaf Core Buffer superfine powder polyurethane coating primer be coated with twice, the consumption of first pass is 5 ~ 10g/m
2, the consumption of second time is 10 ~ 15g/m
2.
As preferably, described step 6) in carry out Chinese Kenaf Core Buffer superfine powder polyurethane coat side gel coating with after Chinese Kenaf Core Buffer superfine powder polyurethane coating bottom gel coating, coating twice, the consumption of first pass is 15 ~ 20g/m
2, the consumption of second time is 15 ~ 20g/m
2.
As preferably, described step 6) in last again with again Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue being carried out last coating procedure, its consumption is 20 ~ 30g/m
2.
As preferably, described step 6) calendering temperature be 220 DEG C.
As preferably, described Chinese Kenaf Core Buffer superfine powder polyurethane coating primer and total consumption of face glue are 80g/m
2.
The fire-retardant moisture-inhibiting waterproof cloth of one side coating of the present invention is to contain carbon black conductive fiber and nylon cloth for base cloth, have employed the special washable waterproofing agent of nylon and Chinese Kenaf Core Buffer superfine powder modified polyurethane coating material, and its distinctive preparation technology, make this waterproof cloth, possesses the function of Waterproof Breathable, but also the function of compatible fire-retardant, uvioresistant, antistatic, heat-proof aging, low temperature resistant anti-being stained with property, acidproof, alkaline-resisting, sea water resistance, main engine plants and station, the military region can be applied to.
Accompanying drawing explanation
Fig. 1 is the structural representation of the fire-retardant moisture-inhibiting waterproof cloth of one side coating of the present invention;
Wherein: 1-contains the POLYAMIDE FABRIC of carbon black conductive fiber, 2-plain net camouflage printing layer, 3-watertight composition, 4-Chinese Kenaf Core Buffer superfine powder modified polyurethane coating primer layer, 5-Chinese Kenaf Core Buffer superfine powder modified polyurethane coating face glue-line.
Detailed description of the invention
Below in conjunction with Figure of description, the fire-retardant moisture-inhibiting waterproof cloth of one side coating of the present invention is described in further detail.
Embodiment 1
The fire-retardant moisture-inhibiting waterproof cloth of one side coating as described in Figure 1, comprise the high-strength every 0.5 ~ 1cm radial direction of 420D × 420D containing 1 carbon black conductive fiber and nylon cloth, its through close be 188/cm, filling density is 160/cm, this high-strength polyamide-fiber nylon cloth is provided with plain net camouflage printing, described plain net camouflage printing is coated with the watertight composition of the special washable waterproofing agent of nylon, the consumption of the special washable waterproofing agent of nylon is 10g/m
2, described watertight composition applies successively Chinese Kenaf Core Buffer superfine powder modified polyurethane coating primer layer and face glue-line.
Embodiment 2
Prepare the fire-retardant moisture-inhibiting waterproof cloth of one side coating, it comprises the steps:
1) according to required decalcomania, silk-screen half tone is made;
2) by ready every 0.55cm radial direction containing 1 carbon black conductive fiber and nylon cloth, with neatly, evenly, be in an orderly manner laid on printing table by hair to positive and negative;
3) the silk-screen half tone made is covered on fabric, bottoming is starched blade coating on decalcomania;
4) to through step 3) POLYAMIDE FABRIC in decalcomania adopt concentrator to carry out camouflage printing;
5), after printing technology completes, carry out washable WATER REPELLENT TREATMENT with the special washable waterproofing agent of nylon to printed fabric, its consumption is 10g/m
2, its consumption is 10g/m
2, then dry under the high temperature of 220 DEG C;
6), after drying, Chinese Kenaf Core Buffer superfine powder polyurethane coating primer to be coated on watertight composition twice, the consumption of first pass primer is 5g/m
2, the consumption of second time primer is 10g/m
2, then use calender press polish under the high temperature of 220 once, then to carry out twice coating with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue, the consumption of first pass face glue is 15g/m
2, the consumption of second time face glue is 20g/m
2, twice later calender under the high temperature of 220 DEG C press polish once, finally carry out last coating procedure with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue again, the consumption of face glue is 30g/m
2.
Described POLYAMIDE FABRIC is the high-strength POLYAMIDE FABRIC of 420D × 420D, its through close be 188/cm, filling density is 160/cm, and its every Gram Mass is 162g/m
2.
Embodiment 3
Prepare the fire-retardant moisture-inhibiting waterproof cloth of one side coating, it comprises the steps:
1) according to required decalcomania, silk-screen half tone is made;
2) by ready every 1cm radial direction containing 1 carbon black conductive fiber and nylon cloth, with neatly, evenly, be in an orderly manner laid on printing table by hair to positive and negative;
3) the silk-screen half tone made is covered on fabric, bottoming is starched blade coating on decalcomania;
4) to through step 3) POLYAMIDE FABRIC in decalcomania adopt concentrator to carry out camouflage printing;
5), after printing technology completes, carry out washable WATER REPELLENT TREATMENT with the special washable waterproofing agent of nylon to printed fabric, its consumption is 15g/m
2, then dry under the high temperature of 230 DEG C;
6), after drying, Chinese Kenaf Core Buffer superfine powder polyurethane coating primer to be coated on watertight composition twice, the consumption of first pass primer is 10g/m
2, the consumption of second time primer is 15g/m
2, then use calender press polish under the high temperature of 230 once, then to carry out twice coating with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue, the consumption of first pass face glue is 15g/m
2, the consumption of second time face glue is 20g/m
2, twice later calender under the high temperature of 230 DEG C press polish once, finally carry out last coating procedure with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue again, the consumption of face glue is 20g/m
2.
Described POLYAMIDE FABRIC is the high-strength POLYAMIDE FABRIC of 420D × 420D, its through close be 188/cm, filling density is 160/cm, and its every Gram Mass is 162g/m
2.
The performance of the fire-retardant moisture-inhibiting waterproof cloth of one side coating that embodiment 2 and embodiment 3 prepare is detected, obtains following result:
Claims (10)
1. the fire-retardant moisture-inhibiting waterproof cloth of one side coating, it is characterized in that comprising POLYAMIDE FABRIC is base cloth, described base cloth is provided with printed layer, and described printed layer is coated with watertight composition, described watertight composition applies Chinese Kenaf Core Buffer superfine powder modified polyurethane coating.
2. the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 1, is characterized in that described POLYAMIDE FABRIC is the high-strength polyamide-fiber nylon cloth of 420D × 420D, its through close be 188/cm, filling density is 160/cm.
3. the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 1, is characterized in that in described POLYAMIDE FABRIC, every 0.5 ~ 1cm radial direction is containing 1 carbon black conductive fiber.
4. the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 1, is characterized in that described printed layer is plain net camouflage printing layer.
5. the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 1, is characterized in that the waterproofing agent in described watertight composition is the special washable waterproofing agent of nylon.
6. the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 1, is characterized in that described Chinese Kenaf Core Buffer superfine powder polyurethane coating comprises Chinese Kenaf Core Buffer superfine powder polyurethane coating bottom glue-line and Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue-line successively.
7. prepare as arbitrary in claim 1 as described in the preparation technology of the fire-retardant moisture-inhibiting waterproof cloth of one side coating, it is characterized in that comprising the steps:
1) according to required decalcomania, silk-screen half tone is made;
2) by ready POLYAMIDE FABRIC, with neatly, evenly, be in an orderly manner laid on printing table by hair to positive and negative;
3) the silk-screen half tone made is covered on fabric, bottoming is starched blade coating on decalcomania;
4) to through step 3) POLYAMIDE FABRIC in decalcomania adopt concentrator to carry out camouflage printing;
5) after printing technology completes, with waterproofing agent, washable WATER REPELLENT TREATMENT is carried out to printed fabric, then dries under the high temperature of 210 ~ 230 DEG C,
6) after drying, Chinese Kenaf Core Buffer superfine powder polyurethane coating primer is coated on watertight composition, with calender, under the high temperature of 210 ~ 230 DEG C, press polish is once, coating is carried out again with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue, once, finally last coating procedure is carried out with Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue again with calender press polish under the high temperature of 210 ~ 230 DEG C after coating.
8. the preparation technology of the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 7, it is characterized in that described POLYAMIDE FABRIC is that 420D × 420D is containing the POLYAMIDE FABRIC of every 0.5 ~ 1cm radial direction containing 1 carbon black conductive fiber, its through close be 188/cm, filling density is 160/cm, and its every Gram Mass is 162g/m
2; Described step 5) in waterproofing agent be the special washable waterproofing agent of nylon, its consumption is 5 ~ 15g/m
2.
9. the preparation technology of the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 7, is characterized in that described step 6) described in Chinese Kenaf Core Buffer superfine powder polyurethane coating primer be coated with twice, the consumption of first pass is 5 ~ 10g/m
2, the consumption of second time is 10 ~ 15g/m
2; Carry out Chinese Kenaf Core Buffer superfine powder polyurethane coat side gel coating after described Chinese Kenaf Core Buffer superfine powder polyurethane coating bottom gel coating, coating twice, the consumption of first pass is 15 ~ 20g/m
2, the consumption of second time is 15 ~ 20g/m
2; Last again with again Chinese Kenaf Core Buffer superfine powder polyurethane coat side glue being carried out last coating procedure, its consumption is 20 ~ 30g/m
2.
10. the preparation technology of the fire-retardant moisture-inhibiting waterproof cloth of a kind of one side coating according to claim 7, is characterized in that total consumption of described Chinese Kenaf Core Buffer superfine powder polyurethane coating primer and face glue is 80g/m
2.