CN104762687A - 一种碳素鱼线的加工方法 - Google Patents
一种碳素鱼线的加工方法 Download PDFInfo
- Publication number
- CN104762687A CN104762687A CN201510140241.0A CN201510140241A CN104762687A CN 104762687 A CN104762687 A CN 104762687A CN 201510140241 A CN201510140241 A CN 201510140241A CN 104762687 A CN104762687 A CN 104762687A
- Authority
- CN
- China
- Prior art keywords
- fishing line
- mixed material
- add
- minute
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及渔具生产加工技术领域，具体涉及一种碳素鱼线的加工方法，其由尼龙、竹炭、丙烯酸树脂、玻璃纤维、氧化铁、单季铵盐、聚四氢呋喃多元醇、亚磷酸酯抗氧剂经过混合制成，本发明各原料配比合理，混合制成的浆料作为鱼线生产所用，生产出的鱼线弹性好，具有较强的耐磨性，质地柔软，更容易与线盘融合，降低缠线和卷线的几率，比重可达到1.85-1.92，下沉速度较快，吸水性只有0.005-0.006，延展性仅为15%-20%。
Description
技术领域
本发明涉及渔具生产加工技术领域，具体涉及一种碳素鱼线的加工方法。
背景技术
鱼线是钓鱼工具之一，可以分为“线”和“丝”两种，线是用两股或两股以上的单纱或丝一次或多次合并加捻而成，而丝则是独此一根，钓丝的制作方法，通常是将原料熔融后，从特制的喷丝孔中挤压出来，经冷却、牵伸、卷绕等加工后制成。这样制得的鱼线为透明状，伸长率较小且具有较强的拉力，特别适于做鱼线使用，现有技术中鱼线一般分成尼龙线、碳素线、钢丝线、编织线、合成线5大种类，其中碳塑线在制造过程中加入碳素，使其较耐磨，而且其比重大于水的一般比重，故其切水性较佳，但其存在质地较硬，展性较差的缺点。
发明内容
为改善现有技术中碳素鱼线存在的缺点，本发明提供一种碳素鱼线的加工方法。
本发明采用的技术方案为：一种碳素鱼线的加工方法，其由以下步骤制成：
a、将尼龙在320℃-350℃的温度下加热融化，保持融化温度不变，加入竹炭在300kpa-320kpa的压力下反应2-4小时，得到第一混合物料；
b、将第一混合物料温度降低至130-145℃，加入玻璃纤维，在压力为350kpa-400kpa的压力下搅拌反应6-8分钟，得到第二混合物料；
c、将第二混合物料的温度加热至160-175℃，加入氧化铁和二甲基硅油，在转速为600-650转/分钟的搅拌速率下搅拌反应30-35分钟，得到第三混合物料；
d、待第三混合物料的温度降至120-135℃时，加入单季铵盐搅拌10-15分钟，最后升温至330-345℃时，加入亚磷酸酯抗氧剂、聚四氢呋喃多元醇、丙烯酸树脂搅拌反应3-5分钟，得到鱼线浆液原料；
e、将鱼线浆料原液加入挤压机内挤压成型，过10-12℃的水浴冷却即可。
本发明通过合理控制原料反应条件得到混合制成的浆料作为鱼线生产所用，生产出的鱼线弹性好，具有较强的耐磨性，质地柔软，更容易与线盘融合，降低缠线和卷线的几率，比重可达到1.85-1.92，下沉速度较快，吸水性只有0.005-0.006，延展性仅为15%-20%。
具体实施方式
实施例1：
取：尼龙60份、竹炭10份、丙烯酸树脂20份、玻璃纤维0.5份、氧化铁0.2份、二甲基硅油0.3-0.5份、单季铵盐0.2份、聚四氢呋喃多元醇0.3份、亚磷酸酯抗氧剂0.5份。
将尼龙在320℃-350℃的温度下加热融化，放置在密封保温反应容器内，加入竹炭在300kpa-320kpa的压力下反应2-4小时后，得到第一反应物，对第一反应物进行降温处理，待第一反应物的温度降低至130-145℃时，加入玻璃纤维，在压力为350kpa-400kpa的压力下搅拌反应6-8分钟，得到第二反应物，将第二反应物的温度加热至160-175℃时，向第二反应物中加入氧化铁和二甲基硅油，在转速为600-650转/分钟的搅拌速率下搅拌反应30-35分钟得到第三反应物，对第三反应物进行降温处理，待第三反应物的温度降至120-135℃时，加入单季铵盐搅拌10-15分钟得到第四反应物，最后将第四反应物升温至330-345℃，加入亚磷酸酯抗氧剂、聚四氢呋喃多元醇、丙烯酸树脂搅拌反应3-5分钟，得到浆液原料，将鱼线浆料原液加入挤压机内挤压成型，过10-12℃的水浴冷却即可。
Claims (1)
1.一种碳素鱼线的加工方法，其特征在于：其由以下步骤制成：
a、将尼龙在320℃-350℃的温度下加热融化，保持融化温度不变，加入竹炭在300kpa-320kpa的压力下反应2-4小时，得到第一混合物料；
b、将第一混合物料温度降低至130-145℃，加入玻璃纤维，在压力为350kpa-400kpa的压力下搅拌反应6-8分钟，得到第二混合物料；
c、将第二混合物料的温度加热至160-175℃，加入氧化铁和二甲基硅油，在转速为600-650转/分钟的搅拌速率下搅拌反应30-35分钟，得到第三混合物料；
d、待第三混合物料的温度降至120-135℃时，加入单季铵盐搅拌10-15分钟，最后升温至330-345℃时，加入亚磷酸酯抗氧剂、聚四氢呋喃多元醇、丙烯酸树脂搅拌反应3-5分钟，得到鱼线浆液原料；
e、将鱼线浆料原液加入挤压机内挤压成型，过10-12℃的水浴冷却即可。