CN104761914A - 炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶 - Google Patents

炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶 Download PDF

Info

Publication number
CN104761914A
CN104761914A CN201510176436.0A CN201510176436A CN104761914A CN 104761914 A CN104761914 A CN 104761914A CN 201510176436 A CN201510176436 A CN 201510176436A CN 104761914 A CN104761914 A CN 104761914A
Authority
CN
China
Prior art keywords
whisker
carbon black
silicone rubber
parts
semi
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510176436.0A
Other languages
English (en)
Inventor
柳培健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510176436.0A priority Critical patent/CN104761914A/zh
Publication of CN104761914A publication Critical patent/CN104761914A/zh
Pending legal-status Critical Current

Abstract

一种炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，涉及橡胶制品技术领域，由以下重量份数的组分组成：甲基乙烯基硅橡胶生胶40-100份、白炭黑10-40份、羟基聚二甲基硅氧烷1-10份、炭黑1-5份、煅烧高岭土微粉1-5份、重稀土0.5-2份、纯碱0.5-2份、海泥2-4份。将甲基乙烯基硅橡胶生胶、白炭黑、羟基聚二甲基硅氧烷，在捏合机中混炼，170℃下加热混合后，向其中加入炭黑，混合均匀配成胶料。本发明组分简单，制备方便，制备的半导电性混炼硅橡胶性能好。

Description

炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶
技术领域
本发明涉及橡胶制品技术领域，具体涉及一种炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶。
背景技术
硅橡胶(英文名称Silicone rubber)，分热硫化型(高温硫化硅胶HTV)、室温硫化型(RTV)，其中室温硫化型又分缩聚反应型和加成反应型。高温硅橡胶主要用于制造各种硅橡胶制品，而室温硅橡胶则主要是作为粘接剂、灌封材料或模具使用。热硫化型用量最大，热硫化型又分甲基硅橡胶、甲基乙烯基硅橡胶、甲基乙烯基苯基硅橡胶，其他还有睛硅橡胶、氟硅橡胶等。在众多的合成橡胶中，硅橡胶是在其中的佼佼者。它具有无味无毒，不怕高温和抵御严寒的特点，在三百摄氏度和零下九十摄氏度时“泰然自若”、“面不改色”，仍不失原有的强度和弹性。硅橡胶还有良好的电绝缘性、耐氧抗老化性、耐光抗老化性以及防霉性、化学稳定性等。迄今，进行固化而成为硅橡胶的硅橡胶组合物已为人们所熟知，利用其耐候性、耐热性、耐寒性、电绝缘性等优异的性质，广泛使用于电气电子零件的封装材料、涂布材料、靠模用等成型材料等。此外，对本来为绝缘材料的硅橡胶组合物赋予导电性而使用也已进行过，但传统方法制备的半导电性混炼硅橡胶性能还不佳。
发明内容
本发明所要解决的技术问题在于提供一种物理、化学性能良好、制备简单的炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶。
本发明所要解决的技术问题采用以下技术方案来实现：
一种炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，由以下重量份数的组分组成，
所述的炭黑为比表面积为1000㎡/g、DBP吸油量为3.40Ml/g的炉法炭黑。
所述的炭黑包覆有金属化合物晶须。
所述的金属化合物晶须为钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须、二氧化钛晶须、钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须或二氧化钛晶须表面上经银镜反应形成银的包覆层，通过蒸着方法形成炭的包覆层或经表面湿式吸附法形成氧化锡、氧化锑包覆层使之具有导电性。
所述金属化合物晶须的晶须纤维的长度10～20um、直径0.2～0.5um、DBP吸油量1.5～2.5Ml/g。
本发明还提供一种炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶的制备方法，其方法步骤如下，
将甲基乙烯基硅橡胶生胶、白炭黑、羟基聚二甲基硅氧烷，在捏合机中混炼，170℃下加热混合后，向其中加入炭黑、煅烧高岭土微粉、重稀土、纯碱、海泥，混合均匀配成胶料。
本发明的有益效果是：本发明组分简单，制备方便，制备的半导电性混炼硅橡胶性能好。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，由以下重量的组分组成，
其中炭黑为比表面积为1000㎡/g、DBP吸油量为3.40Ml/g的炉法炭黑。
在炭黑包覆有金属化合物晶须，金属化合物晶须为钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须、二氧化钛晶须、钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须或二氧化钛晶须表面上经银镜反应形成银的包覆层，通过蒸着方法形成炭的包覆层或经表面湿式吸附法形成氧化锡、氧化锑包覆层使之具有导电性，金属化合物晶须的晶须纤维的长度10～20um、直径0.2～0.5um、DBP吸油量1.5～2.5Ml/g。
本发明还提供一种炭黑与金属化合物晶须并配制半导电性混炼硅橡胶的制备方法，其方法步骤如下，
将甲基乙烯基硅橡胶生胶、白炭黑、羟基聚二甲基硅氧烷，在捏合机中混炼，170℃下加热混合后，向其中加入炭黑、煅烧高岭土微粉、重稀土、纯碱、海泥，混合均匀配成胶料。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (5)

1.炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，其特征在于，由以下重量份数的组分制成：
2.根据权利要求1所述的炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，其特征在于：所述的炭黑为比表面积为1000m2/g、DBP吸油量为3.40ml/g的炉法炭黑。
3.根据权利要求2所述的炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，其特征在于：所述的炭黑包覆有金属化合物晶须。
4.根据权利要求3所述的炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，其特征在于：所述的金属化合物晶须为钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须、二氧化钛晶须、钛酸钾晶须、碳化硅晶须、氧化锌晶须、硼酸铝晶须或二氧化钛晶须表面上经银镜反应形成银的包覆层，通过蒸着方法形成炭的包覆层或经表面湿式吸附法形成氧化锡、氧化锑包覆层使之具有导电性。
5.根据权利要求3所述的炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶，其特征在于：所述金属化合物晶须的晶须纤维的长度10～20um、直径0.2～0.5um、DBP吸油量1.5～2.5ml/g。
CN201510176436.0A 2015-04-14 2015-04-14 炭黑与金属化合物晶须并用配制半导电性混炼硅橡胶 Pending CN104761914A (zh)