CN104761196A - Grave protective material - Google Patents
Grave protective material Download PDFInfo
- Publication number
- CN104761196A CN104761196A CN201510112279.7A CN201510112279A CN104761196A CN 104761196 A CN104761196 A CN 104761196A CN 201510112279 A CN201510112279 A CN 201510112279A CN 104761196 A CN104761196 A CN 104761196A
- Authority
- CN
- China
- Prior art keywords
- parts
- grave
- powder
- vanilla
- cloves
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A grave protective material is composed of following materials: 15-25 parts of calcium hydroxide, 20-25 parts of kaolin, 5-10 parts of calcium carbonate, 8-12 parts of activated carbon, 10-20 parts of fluorinated resin, 3-7 parts of dichlorobenzene, 4-8 parts of realgar, 2-5 parts of cloves, 2-5 parts of agastache rugosa, 3-7 parts of vanilla and 3-6 parts of cinnamon. In the grave protective material, the calcium hydroxide has effects of worm killing, sterilization and environment purification; the kaolin is added for following a custom called "jie di qi" (means being close to earth) of burial in the ground in Southern costumers; the calcium carbonate is used for insulating water; the activated carbon is used for purifying air; the fluorinated resin has the effects of cleaning and insulating water; the dichlorobenzene or camphor is used for worm dispelling and sterilization; the realgar can dispel worms and snakes; the cloves can purifying environmental air; the agastache rugosa is used in worm killing and sterilization; the vanilla is a natural perfume; the cinnamon can gathering earth qi. The raw materials are easy to obtain. The grave protective material is low in cost, has effects of insulating water, resisting dampness, corrosion and pests, dispelling ants and snakes, can protective coffin or bone ash box well, and can achieve the effects by means of the rest drying materials even that the grave protective material itself is soaked by water or damped.
Description
Technical field
The present invention relates to funeral and interment articles for use field, particularly a kind of grave protection material.
Background technology
The Chinese nation is one and payes attention to traditional nationality, along with the development of funeral profession, although adopt cremation at present more, but people still wish that bone ash can burial brings peace to the deceased, therefore, no matter be bone ash or coffin, prevent moist rotten under the dark clammy condition in underground can be remained on, damage by worms, just seem particularly important.And prior art many employings common dessicant and pure chemistry water proof material, common dessicant is cannot water proof, just invalid after inhaling full water; Chemical water proof product on the market, without the effect of expelling parasite ant snake, not only has peculiar smell, is corrosive, also work the mischief to human body simultaneously, therefore, provides a kind of nontoxic, and the grave protection material of Be very effective just seems particularly necessary.
Summary of the invention
For solving above-mentioned prior art Problems existing, the object of the present invention is to provide a kind of grave protection material, it can play water proof, moistureproof, anticorrosion, favorable moth-proof, drives ant, drives snake, the well object of protection coffin or cinerary casket.
For achieving the above object, technical scheme of the present invention is:
A kind of grave protection material, is made up of following material:
Calcium hydroxide 15-25 part;
Kaolin 20-25 part;
Calcium carbonate 5-10 part;
Activated carbon 8-12 part;
Fluoride resin 10-20 part;
Dichlorobenzene 3-7 part;
Realgar 4-8 part;
Cloves 2-5 part;
Ageratum 2-5 part;
Vanilla 3-7 part;
Chinese cassia tree 3-6 part.
Further, described grave protection material, is made up of following material:
20 parts, calcium hydroxide;
Kaolin 23 parts;
7 parts, calcium carbonate;
Activated carbon 10 parts;
Fluoride resin 15 parts;
Dichlorobenzene 4 parts;
Realgar 5 parts;
Cloves 4 parts;
Ageratum 4 parts;
Vanilla 4 parts;
Chinese cassia tree 4 parts.
Further, described dichlorobenzene is replaced by camphor.
Further, the water content of described cloves, wrinkled giant hyssop, vanilla, Chinese cassia tree is less than 8%.
Further, the preparation method of described grave protection material comprises the steps:
Step one, above-mentioned raw materials proportionally to be got all the ready, by calcium hydroxide, kaolin, calcium carbonate, activated carbon, fluoride resin, mixing, added in shredder by mixed raw material afterwards and be finely ground to powder, fineness is not more than 100 μm, for subsequent use;
Step 2, by cloves, ageratum, vanilla, Chinese cassia tree, adds in shredder and is finely ground to powder, and granularity is not more than 80 μm, for subsequent use;
Step 3, step one and step 2 gained powder are placed in thermostat container separately dry, step one powder bake out temperature is 230-420 DEG C, and after drying, water content is not more than 6%, and step 2 powder bake out temperature is 80-120 DEG C, and after drying, water content is not more than 6%;
Step 4, step 3 is dried after all powder and realgar be mixed together and stir, obtain grave protection material of the present invention.
Relative to prior art, beneficial effect of the present invention is:
Calcium hydroxide desinsection in grave protection material of the present invention, sterilization, environment purification, kaolin in order to satisfied southern client grave must ground connection gas custom and add, calcium carbonate is used for water proof, activated carbon is used for purifying air, fluoride resin plays the effect of clear water water proof, dichlorobenzene or camphor are used for sterilization, expelling parasite, realgar expelling parasite snake, cloves energy cleaning ambient air, ageratum disinfection and deinsectization, vanilla natural perfume, Chinese cassia tree gathers ground vapour, existing cinerary casket is wooden mostly, marble, stone and ceramic material, time has been grown and all can seep water, and bone ash can go bad after contacting water, go rotten smelly, also bad to offspring, so moisture can be cut off completely with his this medicinal powder, grave protection material raw material of the present invention is easy to get, cost is low, water proof can be played simultaneously, moistureproof, anticorrosion, favorable moth-proof, drive ant, drive snake, the object of good protection coffin or cinerary casket, even and if material immersion itself is moist, the material of residue drying can play a role equally.
Embodiment
Below in conjunction with embodiment, technical solution of the present invention is described in further detail:
Embodiment 1: a kind of grave protection material, is made up of following material:
15 parts, calcium hydroxide;
Kaolin 25 parts;
5 parts, calcium carbonate;
Activated carbon 12 parts;
Fluoride resin 10 parts;
Dichlorobenzene 7 parts;
Realgar 4 parts;
Cloves 5 parts;
Ageratum 2 parts;
Vanilla 7 parts;
Chinese cassia tree 3 parts.
The preparation method of described grave protection material comprises the steps:
Step one, above-mentioned raw materials proportionally to be got all the ready, by calcium hydroxide, kaolin, calcium carbonate, activated carbon, fluoride resin, mixing, added in shredder by mixed raw material afterwards and be finely ground to powder, fineness is not more than 100 μm, for subsequent use;
Step 2, by cloves, ageratum, vanilla, Chinese cassia tree, adds in shredder and is finely ground to powder, and granularity is not more than 80 μm, for subsequent use;
Step 3, step one and step 2 gained powder are placed in thermostat container separately dry, step one powder bake out temperature is 230-420 DEG C, and after drying, water content is not more than 6%, and step 2 powder bake out temperature is 80-120 DEG C, and after drying, water content is not more than 6%;
Step 4, step 3 is dried after all powder and realgar be mixed together and stir, obtain grave protection material of the present invention.
Embodiment 2:
A kind of grave protection material, is made up of following material:
20 parts, calcium hydroxide;
Kaolin 23 parts;
7 parts, calcium carbonate;
Activated carbon 10 parts;
Fluoride resin 15 parts;
Camphor 4 parts;
Realgar 5 parts;
Cloves 4 parts;
Ageratum 4 parts;
Vanilla 4 parts;
Chinese cassia tree 4 parts.
The preparation method of described grave protection material comprises the steps:
Step one, above-mentioned raw materials proportionally to be got all the ready, by calcium hydroxide, kaolin, calcium carbonate, activated carbon, fluoride resin, mixing, added in shredder by mixed raw material afterwards and be finely ground to powder, fineness is not more than 100 μm, for subsequent use;
Step 2, by cloves, ageratum, vanilla, Chinese cassia tree, adds in shredder and is finely ground to powder, and granularity is not more than 80 μm, for subsequent use;
Step 3, step one and step 2 gained powder are placed in thermostat container separately dry, step one powder bake out temperature is 230-420 DEG C, and after drying, water content is not more than 6%, and step 2 powder bake out temperature is 80-120 DEG C, and after drying, water content is not more than 6%;
Step 4, step 3 is dried after all powder and realgar be mixed together and stir, obtain grave protection material of the present invention.
Embodiment 3:
A kind of grave protection material is made up of following material:
15 parts, calcium hydroxide;
Kaolin 25 parts;
5 parts, calcium carbonate;
Activated carbon 12 parts;
Fluoride resin 10 parts;
Dichlorobenzene 7 parts;
Realgar 4 parts;
Cloves 5 parts;
Ageratum 2 parts;
Vanilla 7 parts;
Chinese cassia tree 3 parts.
The preparation method of described grave protection material comprises the steps:
Step one, above-mentioned raw materials proportionally to be got all the ready, by calcium hydroxide, kaolin, calcium carbonate, activated carbon, fluoride resin, mixing, added in shredder by mixed raw material afterwards and be finely ground to powder, fineness is not more than 100 μm, for subsequent use;
Step 2, by cloves, ageratum, vanilla, Chinese cassia tree, adds in shredder and is finely ground to powder, and granularity is not more than 80 μm, for subsequent use;
Step 3, step one and step 2 gained powder are placed in thermostat container separately dry, step one powder bake out temperature is 230-420 DEG C, and after drying, water content is not more than 6%, and step 2 powder bake out temperature is 80-120 DEG C, and after drying, water content is not more than 6%;
Step 4, step 3 is dried after all powder and realgar be mixed together and stir, obtain grave protection material of the present invention.
In actual use, after being mixed in proportion by grave protection material of the present invention, direct spreading is on ground, coffin pit, and the ground of cinerary casket surrounding, and after capping is good, tile one deck again on top.
Test example:
Material in above-described embodiment is added in the experimental ware of a simulation coffin pit environment, this simulation coffin pit surrounding becomes cavity, middle part surrounds and is used for holding inner and outer coffin or cinerary casket, water and mud is filled in its surrounding, by material-paving of the present invention in middle part, the lower survey at simulation coffin pit surrounding and middle part has gap moisture to infiltrate, and the middle part putting into material of the present invention can keep not immersed by moisture for ten months, still can play water proof effect, and medicine remains Powdered.
Meanwhile, after being stacked by protective material of the present invention, in the direct water filling of its surrounding, after material surface of the present invention is moistening, its within continues the water proof that keeps dry, and effect is lasting.
The above, be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any change of expecting without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.
Claims (5)
1. a grave protection material, is characterized in that, is made up of following material:
Calcium hydroxide 15-25 part;
Kaolin 20-25 part;
Calcium carbonate 5-10 part;
Activated carbon 8-12 part;
Fluoride resin 10-20 part;
Dichlorobenzene 3-7 part;
Realgar 4-8 part;
Cloves 2-5 part;
Ageratum 2-5 part;
Vanilla 3-7 part;
Chinese cassia tree 3-6 part.
2. method according to claim 1, is characterized in that, described grave protection material, is made up of following material:
20 parts, calcium hydroxide;
Kaolin 23 parts;
7 parts, calcium carbonate;
Activated carbon 10 parts;
Fluoride resin 15 parts;
Dichlorobenzene 4 parts;
Realgar 5 parts;
Cloves 4 parts;
Ageratum 4 parts;
Vanilla 4 parts;
Chinese cassia tree 4 parts.
3. method according to claim 1 and 2, is characterized in that, described dichlorobenzene is replaced by camphor.
4. method according to claim 1 and 2, is characterized in that, the water content of described cloves, wrinkled giant hyssop, vanilla, Chinese cassia tree is less than 8%.
5. method according to claim 1 and 2, is characterized in that, the preparation method of described grave protection material comprises the steps:
Step one, above-mentioned raw materials proportionally to be got all the ready, by calcium hydroxide, kaolin, calcium carbonate, activated carbon, fluoride resin, mixing, added in shredder by mixed raw material afterwards and be finely ground to powder, fineness is not more than 100 μm, for subsequent use;
Step 2, by cloves, ageratum, vanilla, Chinese cassia tree, adds in shredder and is finely ground to powder, and granularity is not more than 80 μm, for subsequent use;
Step 3, step one and step 2 gained powder are placed in thermostat container separately dry, step one powder bake out temperature is 230-420 DEG C, and after drying, water content is not more than 6%, and step 2 powder bake out temperature is 80-120 DEG C, and after drying, water content is not more than 6%;
Step 4, step 3 is dried after all powder and realgar be mixed together and stir, obtain grave protection material of the present invention.