CN104746214A - Silky fabric and processing technique thereof - Google Patents
Silky fabric and processing technique thereof Download PDFInfo
- Publication number
- CN104746214A CN104746214A CN201510192309.XA CN201510192309A CN104746214A CN 104746214 A CN104746214 A CN 104746214A CN 201510192309 A CN201510192309 A CN 201510192309A CN 104746214 A CN104746214 A CN 104746214A
- Authority
- CN
- China
- Prior art keywords
- warp
- sliding surface
- surface material
- speed
- parallel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a silky fabric. The silky fabric is formed by mutually weaving warps and wefts, wherein the wraps are formed by blending bombyx mori silk fibers and cotton fibers; the wefts are formed by blending and weaving spandex fibers and viscose; the bending ratio of the cotton fibers to the bombyx mori silk fibers is 1: 2; the blending ratio of the spandex fibers to the viscose is 1: 2. The silky fabric is soft and smooth in touch, light, thin, breathable, and good in dropping performance, and is a high-level fabric.
Description
Technical field
Patent of the present invention relates to a kind of fabric, is specifically related to a kind of silk sliding surface material and processing technology thereof.
Background technology
Along with the development of science and technology, the textile fabric meeting the different needs of people emerges in an endless stream, and to satisfy the demands of consumers, plays a part more and more important in daily life.
Summary of the invention
The object of invention: the object of the present invention is to provide a kind of silk sliding surface material, feel is soft and smooth, frivolous ventilative, hanging from above property is good.
The technical solution used in the present invention: a kind of silk sliding surface material, mutually woven by warp and parallel and form, described warp is formed by mulberry silk fiber and cotton fiber blending, described parallel is woven by spandex fibre and viscose fiber blending and forms, in described warp, the blending rate of cotton fiber and mulberry silk fiber is 1:2, and in described parallel, the blending rate of spandex fibre and viscose is 1:2.
Described warp and parallel adopt plain weave or twill weave.
A kind of silk sliding surface material processing technology, specifically comprises the steps:
A, to hand over and operation: cotton fiber and mulberry silk fiber are sent in doubling winder and carried out yarn friendship and form mixed and warp, spandex fibre and viscose are sent in doubling winder and carried out yarn friendship and form mixed and parallel;
B, winding procedure: will mix in step a in warp also and parallel feeding bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, and rolling density is 0.32 ~ 0.37 g/cm
3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm
3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160 ~ 200r/min, and opening time is 300 ~ 320 °;
E, dyeing: the fabric weaved is carried out overflow dyeing, the weight ratio controlling fabric and water is 1: 5 ~ 20,90 DEG C ~ 100 DEG C are progressively warming up to the speed of 1 DEG C/min under the condition of 50 DEG C ~ 70 DEG C, insulation 50 ~ 80mins, then carries out the clear water washing of fixation and 1 ~ 2 time to fabric;
F, finishing process: former cloth steps d weaved is tested, the fine hair then on burning-off cloth cover, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packaging.
In described step b, groove drum linear velocity is 1000m/min, and rolling density is 0.35 g/cm
3.
In described step c, whole footpath speed is 340 mm/min, and rolling density is 0.52g/cm
3.
In described steps d, manufacturing speed is 180r/min, and opening time is 300 °.
In described step f, perching speed is 18-20m/min.
Beneficial effect: disclosed a kind of silk sliding surface material, adopts this natural animal protein fiber of mulberry silk as warp thread, makes fabric smooth pliable, be rich in gloss, have sensation cool in summer and warm in winter, during friction, have unique " scroop " phenomenon, there is good extensibility, good heat resistance.
Detailed description of the invention
Below in conjunction with specific embodiment, technology contents of the present invention is described in detail:
Disclosed a kind of silk sliding surface material, mutually woven by warp and parallel and form, described warp is formed by mulberry silk fiber and cotton fiber blending, described parallel is woven by spandex fibre and viscose fiber blending and forms, in described warp, the blending rate of cotton fiber and mulberry silk fiber is 1:2, and in described parallel, the blending rate of spandex fibre and viscose is 1:2.
Wherein, described warp and parallel adopt plain weave or twill weave.
A kind of silk sliding surface material processing technology, specifically comprises the steps:
A, to hand over and operation: cotton fiber and mulberry silk fiber are sent in doubling winder and carried out yarn friendship and form mixed and warp, spandex fibre and viscose are sent in doubling winder and carried out yarn friendship and form mixed and parallel;
B, winding procedure: will mix in step a in warp also and parallel feeding bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, and rolling density is 0.32 ~ 0.37 g/cm
3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm
3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160 ~ 200r/min, and opening time is 300 ~ 320 °;
E, dyeing: the fabric weaved is carried out overflow dyeing, the weight ratio controlling fabric and water is 1: 5 ~ 20,90 DEG C ~ 100 DEG C are progressively warming up to the speed of 1 DEG C/min under the condition of 50 DEG C ~ 70 DEG C, insulation 50 ~ 80mins, then carries out the clear water washing of fixation and 1 ~ 2 time to fabric;
F, finishing process: former cloth steps d weaved is tested, the fine hair then on burning-off cloth cover, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packaging.
In described step b, groove drum linear velocity is 1000m/min, and rolling density is 0.35 g/cm
3.
In described step c, whole footpath speed is 340 mm/min, and rolling density is 0.52g/cm
3.
In described steps d, manufacturing speed is 180r/min, and opening time is 300 °.
In described step f, perching speed is 18-20m/min.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (7)
1. a silk sliding surface material, mutually woven by warp and parallel and form, it is characterized in that: described warp is formed by mulberry silk fiber and cotton fiber blending, described parallel is woven by spandex fibre and viscose fiber blending and forms, in described warp, the blending rate of cotton fiber and mulberry silk fiber is 1:2, and in described parallel, the blending rate of spandex fibre and viscose is 1:2.
2. a kind of silk sliding surface material according to claim 1, is characterized in that: described warp and parallel adopt plain weave or twill weave.
3. a silk sliding surface material processing technology, is characterized in that: specifically comprise the steps:
A, to hand over and operation: cotton fiber and mulberry silk fiber are sent in doubling winder and carried out yarn friendship and form mixed and warp, spandex fibre and viscose are sent in doubling winder and carried out yarn friendship and form mixed and parallel;
B, winding procedure: will mix in step a in warp also and parallel feeding bobbin winder and carry out winder, control groove drum linear velocity is 1000 ~ 1100m/min simultaneously, and rolling density is 0.32 ~ 0.37 g/cm
3;
C, warping process: adopt warping machines to carry out section warping to the yarn of winder in step b, the speed of beaming controlling warping machines is 330 ~ 350 mm/min, and rolling density is 0.5 ~ 0.6 g/cm
3;
D, weaving process: adopt Rapier looms to weave, wherein warp thread and weft yarn are sent into according to preset ratio, and wherein weaving speed is 160 ~ 200r/min, and opening time is 300 ~ 320 °;
E, dyeing: the fabric weaved is carried out overflow dyeing, the weight ratio controlling fabric and water is 1: 5 ~ 20,90 DEG C ~ 100 DEG C are progressively warming up to the speed of 1 DEG C/min under the condition of 50 DEG C ~ 70 DEG C, insulation 50 ~ 80mins, then carries out the clear water washing of fixation and 1 ~ 2 time to fabric;
F, finishing process: former cloth steps d weaved is tested, the fine hair then on burning-off cloth cover, then send in setting machine and shape, make into cloth and meet the requirements, then carry out perching, packaging.
4. a kind of silk sliding surface material processing technology according to claim 3, it is characterized in that: in described step b, groove drum linear velocity is 1000m/min, rolling density is 0.35 g/cm
3.
5. a kind of silk sliding surface material processing technology according to claim 3, it is characterized in that: in described step c, whole footpath speed is 340 mm/min, rolling density is 0.52g/cm
3.
6. a kind of silk sliding surface material processing technology according to claim 3, it is characterized in that: in described steps d, manufacturing speed is 180r/min, opening time is 300 °.
7. a kind of silk sliding surface material processing technology according to claim 3, is characterized in that: in described step f, perching speed is 18-20m/min.