CN108754785A - A kind of high resiliency Comfortable fabric and its processing technology - Google Patents

A kind of high resiliency Comfortable fabric and its processing technology Download PDF

Info

Publication number
CN108754785A
CN108754785A CN201810658846.2A CN201810658846A CN108754785A CN 108754785 A CN108754785 A CN 108754785A CN 201810658846 A CN201810658846 A CN 201810658846A CN 108754785 A CN108754785 A CN 108754785A
Authority
CN
China
Prior art keywords
weft
warp
high resiliency
polynosic
copper ammonia
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810658846.2A
Other languages
Chinese (zh)
Inventor
仝进峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Textile Industry Association
Original Assignee
Nantong Textile Industry Association
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Textile Industry Association filed Critical Nantong Textile Industry Association
Priority to CN201810658846.2A priority Critical patent/CN108754785A/en
Priority to PCT/CN2018/097869 priority patent/WO2020000565A1/en
Publication of CN108754785A publication Critical patent/CN108754785A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of high resiliency Comfortable fabrics, it is mutually woven by warp and weft, the warp is by polynosic, copper ammonia fiber and spandex is blended forms, the weft is by copper ammonia fiber, polynosic blending woven forms, polynosic in the warp, and copper ammonia fiber and spandex blending rate are 2:3:2, the blending rate of copper ammonia fiber in the weft, polynosic is 1:1.A kind of disclosed high resiliency Comfortable fabric, has soft, and gloss is soft, and elasticity is high, there is silky touch, and good hygroscopicity, wearability is high, and humidity absorption and release is strong, salubrious anlistatig advantage.

Description

A kind of high resiliency Comfortable fabric and its processing technology
Technical field
The invention patent relates to a kind of fabrics, and in particular to a kind of high resiliency Comfortable fabric and its processing technology.
Background technology
With the increasingly raising of people's living standard, requirement of the people to the comfort level of clothing, heat-insulating property, elasticity is also got over Come higher, currently, underwear in the market generally uses common cotton or viscose glue class or fine blended yarn weaved fabric, but human metabolism produces Raw grease, moisture, are distributing moisture by epidermis always.There are the defects of highlight for fine blended yarn weaved fabric, after being fabricated to clothes Easily cause dry skin, frictional static, pilling, sulks or poor air permeability, water imbibition difference and easily reels off raw silk from cocoons when washing, flexibility Difference, poor flexibility, durability is poor, and comfort is poor, and this fabric cannot meet the requirement of people.
Invention content
The purpose of invention:The purpose of the present invention is to provide a kind of high resiliency Comfortable fabrics.
The technical solution adopted by the present invention:A kind of high resiliency Comfortable fabric is mutually woven by warp and weft, described Warp is by polynosic, copper ammonia fiber and spandex is blended forms, the weft by copper ammonia fiber, polynosic blending woven and At polynosic in the warp, copper ammonia fiber and spandex blending rate are 2:3:2, copper ammonia fiber in the weft is rich The blending rate of strong fiber is 1:1.
The warp and weft use plain weave or twill weave.
A kind of high resiliency Comfortable fabric processing technology, specifically comprises the following steps:
A, simultaneously process is handed over:By polynosic, copper ammonia fiber and spandex are sent into doubling winder and carry out yarn friendship and formed to mix simultaneously warp, By copper ammonia fiber, polynosic, which is sent into doubling winder, to carry out yarn friendship and forms mixed and weft;
B, winding procedure:Warp simultaneously will be mixed in step a and weft is sent into bobbin-winding machine and carries out winder, while controlling groove drum linear speed Degree is 1150 ~ 1200m/min, and rolling density is 0.32 ~ 0.38 g/cm3
C, warping process:Section warping is carried out to the yarn of winder in step b using warping machine, controls the speed of beaming of warping machine For 340 ~ 360 mm/min, rolling density is 0.5 ~ 0.6 g/cm3
D, weaving process:It is weaved using rapier loom, wherein warp thread and weft yarn is sent into according to preset ratio, wherein weaving speed Degree is 150~200r/min, and opening time is 300 ~ 320 °;
E, finishing process:The step d former cloths weaved are tested, then the villus on burning-off cloth cover, is re-fed into sizing It is carried out shaping in machine, makes into cloth and meet the requirements, then carry out perching, packed.
Groove drum linear velocity is 1180m/min in the step b, and rolling density is 0.37 g/cm3
Whole diameter speed is 350 mm/min, rolling density 0.55g/cm in the step c3
Manufacturing speed is 160r/min in the step d, and opening time is 320 °.
Perching speed is 18-20m/min in the step e.
Advantageous effect:A kind of high resiliency Comfortable fabric has soft, and gloss is soft, and elasticity is high, there is silky touch, moisture absorption Property it is good, wearability is high, and humidity absorption and release is strong, salubrious anlistatig advantage.
Specific implementation mode
The technology contents of the present invention are described in detail with reference to specific embodiment:
A kind of disclosed high resiliency Comfortable fabric, is mutually woven, the warp is by rich and powerful by warp and weft Fiber, copper ammonia fiber and spandex is blended forms, by copper ammonia fiber, polynosic blending woven forms the weft, described Polynosic in warp, copper ammonia fiber and spandex blending rate are 2:3:2, copper ammonia fiber in the weft, polynosic Blending rate is 1:1.
Wherein, the warp and weft use plain weave or twill weave.
A kind of high resiliency Comfortable fabric processing technology, specifically comprises the following steps:
A, simultaneously process is handed over:By polynosic, copper ammonia fiber and spandex are sent into doubling winder and carry out yarn friendship and formed to mix simultaneously warp, By copper ammonia fiber, polynosic, which is sent into doubling winder, to carry out yarn friendship and forms mixed and weft;
B, winding procedure:Warp simultaneously will be mixed in step a and weft is sent into bobbin-winding machine and carries out winder, while controlling groove drum linear speed Degree is 1150 ~ 1200m/min, and rolling density is 0.32 ~ 0.38 g/cm3
C, warping process:Section warping is carried out to the yarn of winder in step b using warping machine, controls the speed of beaming of warping machine For 340 ~ 360 mm/min, rolling density is 0.5 ~ 0.6 g/cm3
D, weaving process:It is weaved using rapier loom, wherein warp thread and weft yarn is sent into according to preset ratio, wherein weaving speed Degree is 150~200r/min, and opening time is 300 ~ 320 °;
E, finishing process:The step d former cloths weaved are tested, then the villus on burning-off cloth cover, is re-fed into sizing It is carried out shaping in machine, makes into cloth and meet the requirements, then carry out perching, packed.
Groove drum linear velocity is 1180m/min in the step b, and rolling density is 0.37 g/cm3
Whole diameter speed is 350 mm/min, rolling density 0.55g/cm in the step c3
Manufacturing speed is 160r/min in the step d, and opening time is 320 °.
Perching speed is 18-20m/min in the step e.
The above is only a preferred embodiment of the present invention, it should be pointed out that:For the ordinary skill people of the art For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered It is considered as protection scope of the present invention.

Claims (7)

1. a kind of high resiliency Comfortable fabric is mutually woven by warp and weft, it is characterised in that:The warp is by rich and powerful fibre Dimension, copper ammonia fiber and spandex is blended forms, the weft is formed by copper ammonia fiber, polynosic blending woven, the warp Polynosic in line, copper ammonia fiber and spandex blending rate are 2:3:2, copper ammonia fiber in the weft, polynosic it is mixed Spinning ratio is 1:1.
2. a kind of high resiliency Comfortable fabric according to claim 1, it is characterised in that:The warp and weft use plain weave Or twill weave.
3. a kind of high resiliency Comfortable fabric processing technology, it is characterised in that:Specifically comprise the following steps:
A, simultaneously process is handed over:By polynosic, copper ammonia fiber and spandex are sent into doubling winder and carry out yarn friendship and formed to mix simultaneously warp, By copper ammonia fiber, polynosic, which is sent into doubling winder, to carry out yarn friendship and forms mixed and weft;
B, winding procedure:Warp simultaneously will be mixed in step a and weft is sent into bobbin-winding machine and carries out winder, while controlling groove drum linear speed Degree is 1150 ~ 1200m/min, and rolling density is 0.32 ~ 0.38 g/cm3
C, warping process:Section warping is carried out to the yarn of winder in step b using warping machine, controls the speed of beaming of warping machine For 340 ~ 360 mm/min, rolling density is 0.5 ~ 0.6 g/cm3
D, weaving process:It is weaved using rapier loom, wherein warp thread and weft yarn is sent into according to preset ratio, wherein weaving speed Degree is 150~200r/min, and opening time is 300 ~ 320 °;
E, finishing process:The step d former cloths weaved are tested, then the villus on burning-off cloth cover, is re-fed into sizing It is carried out shaping in machine, makes into cloth and meet the requirements, then carry out perching, packed.
4. a kind of high resiliency Comfortable fabric processing technology according to claim 3, it is characterised in that:The step b bracket grooves Cylinder linear velocity is 1180m/min, and rolling density is 0.37 g/cm3
5. a kind of high resiliency Comfortable fabric processing technology according to claim 3, it is characterised in that:It is whole in the step c Diameter speed is 350 mm/min, rolling density 0.55g/cm3
6. a kind of high resiliency Comfortable fabric processing technology according to claim 3, it is characterised in that:It is made in the step d It is 160r/min to make speed, and opening time is 320 °.
7. a kind of high resiliency Comfortable fabric processing technology according to claim 3, it is characterised in that:It is tested in the step e Cloth speed is 18-20m/min.
CN201810658846.2A 2018-06-25 2018-06-25 A kind of high resiliency Comfortable fabric and its processing technology Pending CN108754785A (en)