CN104744963A - Terrace and construction method thereof - Google Patents
Terrace and construction method thereof Download PDFInfo
- Publication number
- CN104744963A CN104744963A CN201510168555.1A CN201510168555A CN104744963A CN 104744963 A CN104744963 A CN 104744963A CN 201510168555 A CN201510168555 A CN 201510168555A CN 104744963 A CN104744963 A CN 104744963A
- Authority
- CN
- China
- Prior art keywords
- parts
- terrace
- plastics
- toner
- wood chip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a terrace and a construction method thereof, and belongs to the research field of terraces. The invention provides a terrace for overcoming the problem that the exiting terrace material cannot be directly applied to a swimming pool. The terrace is prepared from the following components in parts by weight: 25-30 parts of sawdust, 30-40 parts of plastic, 10-20 parts of polyacrylate, 10-15 parts of butyl acetate, 3-5 parts of corundum powder, 3-5 parts of butadiene rubber, 5-10 parts of hydrogenated silicon oil, 1-3 parts of plasticizer, 0.2-0.3 part of preservative, 3-5 parts of diethylene triamine and 2-4 parts of toner. The terrace provided by the invention is used for reducing possible risks of hard bottom and side walls of the swimming pool on users, reinforcing the adaptability of the inner walls of the swimming pool on impact caused by water, non-water and different water temperatures and enhancing the adaptability of the swimming pool, so that the terrace is conducive to popularization and application.
Description
Technical field
The invention belongs to the research field of terrace.
Background technology
Present swimming pool all uses ceramic tile to lay at the bottom of pond and pond sidewall, and it also exists to lay and bothers, easily leaks, easily comes off and the single drawback of color.Existing floor material, owing to itself having excellent anti-skidding, wear-resisting, characteristic that the life-span is long, is therefore widely used in the regions such as open deck, mill floor, parking lot.Also there is precedent terrace technology being applied to swimming pool, but often occur swimming bottom surface, bay wall pond cracking, leak and phenomenon that metope comes off.Analysis is because the environment for use of swimming pool and outdoor environment for use very different, therefore existing floor material cannot be directly applied to swimming pool.
Summary of the invention
The present invention is directed to the problem that existing floor material cannot directly apply to swimming pool, a kind of terrace and constructional method are provided, can solve the problem preferably.
Described object is achieved by the following scheme:
A kind of terrace, be prepared from by following ratio of weight and number, wood chip 25-30 part, plastics 30-40 part, polyacrylic ester 10-20 part, N-BUTYL ACETATE 10-15 part, lapis amiridis 3-5 part, cis-1,4-polybutadiene rubber 3-5 part, hydrogenation silicone oil 5-10 part, softening agent 1-3 part, sanitas 0.2-0.3, diethylenetriamine 3-5 part, toner 2-4 part.
Described wood chip is that wood adds the sawdust, the wood shavings powder that stay man-hour, and size is 10-50 order.
Described plastics are long 5-10 centimetre, the rectangular strip of wide 1-3 centimetre, thick 0.1-0.3 centimetre.
Preferred version 1:
Be prepared from by following ratio of weight and number, wood chip 25 parts, 35 parts, plastics, polyacrylic ester 10 parts, N-BUTYL ACETATE 15 parts, lapis amiridis 3 parts, cis-1,4-polybutadiene rubber 5 parts, hydrogenation silicone oil 7 parts, 1 part, softening agent, sanitas 0.3, diethylenetriamine 3 parts, toner 4 parts.
Preferred version 2:
Be prepared from by following ratio of weight and number, wood chip 20 parts, 40 parts, plastics, polyacrylic ester 20 parts, N-BUTYL ACETATE 13 parts, lapis amiridis 5 parts, cis-1,4-polybutadiene rubber 3 parts, hydrogenation silicone oil 5 parts, 2 parts, softening agent, sanitas 0.2, diethylenetriamine 4 parts, toner 4 parts.
Preferred version 3:
Be prepared from by following ratio of weight and number, wood chip 30 parts, 30 parts, plastics, polyacrylic ester 15 parts, N-BUTYL ACETATE 10 parts, lapis amiridis 4 parts, cis-1,4-polybutadiene rubber 4 parts, hydrogenation silicone oil 10 parts, 3 parts, softening agent, sanitas 0.25, diethylenetriamine 5 parts, toner 3 parts.
Constructional method: polyacrylic ester, N-BUTYL ACETATE, cis-1,4-polybutadiene rubber, hydrogenation silicone oil, diethylenetriamine are diluted rear and softening agent, sanitas, lapis amiridis, wood chip, plastics, toner mixing and stirring by (1) according to a conventional method; (2) with terrace preparation of construction, mixture is smeared evenly on swimming pool bottom and sidewall; (3) tie with shredder.
The present invention effectively utilizes the expansion characteristics of wood chip, is applied in floor material, can improve terrace density, increases water resistance, is applied to can increase leakproof characteristic in swimming pool; The present invention adds plastic components in floor material, and plastics are set to long 5-10 centimetre, the rectangular strip of wide 1-3 centimetre, thick 0.1-0.3 centimetre, the favorable elasticity that such plastics have self can increase the snappiness of swimming pool bottom and sidewall greatly, both reduced at the bottom of hard pond, risk that sidewall may cause user to injure, in turn enhance the impact that swimming pool inwall adapts to have water, anhydrous and different water temperatures bring pool wall, enhance the conformability of swimming pool, be beneficial to and apply.
Embodiment
Elaborate the preferred embodiment of the present invention below.
embodiment 1:
A kind of terrace, be prepared from by following ratio of weight and number, wood chip 25-30 part, plastics 30-40 part, polyacrylic ester 10-20 part, N-BUTYL ACETATE 10-15 part, lapis amiridis 3-5 part, cis-1,4-polybutadiene rubber 3-5 part, hydrogenation silicone oil 5-10 part, softening agent 1-3 part, sanitas 0.2-0.3, diethylenetriamine 3-5 part, toner 2-4 part.Described wood chip is that wood adds the sawdust, the wood shavings powder that stay man-hour, and size is 10-50 order.Described plastics are long 5-10 centimetre, the rectangular strip of wide 1-3 centimetre, thick 0.1-0.3 centimetre.
embodiment 2:
Be prepared from by following ratio of weight and number, wood chip 25 parts, 35 parts, plastics, polyacrylic ester 10 parts, N-BUTYL ACETATE 15 parts, lapis amiridis 3 parts, cis-1,4-polybutadiene rubber 5 parts, hydrogenation silicone oil 7 parts, 1 part, softening agent, sanitas 0.3, diethylenetriamine 3 parts, toner 4 parts.Described wood chip is that wood adds the sawdust stayed man-hour, and size is 40 orders.Described plastics are long 10 centimetres, wide 2 centimetres, thick 0.1 centimetre rectangular strip.
Constructional method, polyacrylic ester, N-BUTYL ACETATE, cis-1,4-polybutadiene rubber, hydrogenation silicone oil, diethylenetriamine are diluted rear and softening agent, sanitas, lapis amiridis, wood chip, plastics, toner mixing and stirring by (1) according to a conventional method; (2) with terrace preparation of construction, mixture is smeared evenly on swimming pool bottom and sidewall; (3) tie with shredder.
Test proves, at the bottom of the swimming pool sidewall adopting scheme described in the present embodiment to obtain and pond, use within 3 years, absolutely not leak, cracking phenomena, its flexility reaches diameter 40 millimeters and does not rupture.
embodiment 3:
Be prepared from by following ratio of weight and number, wood chip 20 parts, 40 parts, plastics, polyacrylic ester 20 parts, N-BUTYL ACETATE 13 parts, lapis amiridis 5 parts, cis-1,4-polybutadiene rubber 3 parts, hydrogenation silicone oil 5 parts, 2 parts, softening agent, sanitas 0.2, diethylenetriamine 4 parts, toner 4 parts.Test proves, at the bottom of the swimming pool sidewall adopting scheme described in the present embodiment to obtain and pond, use within 3 years, absolutely not leak, cracking phenomena, its flexility reaches diameter 38 millimeters and does not rupture.
embodiment 4:
Be prepared from by following ratio of weight and number, wood chip 30 parts, 30 parts, plastics, polyacrylic ester 15 parts, N-BUTYL ACETATE 10 parts, lapis amiridis 4 parts, cis-1,4-polybutadiene rubber 4 parts, hydrogenation silicone oil 10 parts, 3 parts, softening agent, sanitas 0.25, diethylenetriamine 5 parts, toner 3 parts.Test proves, at the bottom of the swimming pool sidewall adopting scheme described in the present embodiment to obtain and pond, use within 3 years, absolutely not leak, cracking phenomena, its flexility reaches diameter 43 millimeters and does not rupture.
Present embodiment does not just limit its protection domain to the exemplary illustration of this patent; those skilled in the art can also carry out local to it and change; as long as no the spirit exceeding this patent, be all considered as the equivalent replacement to this patent, all within the protection domain of this patent.
Claims (7)
1. a terrace, it is characterized in that: be prepared from by following ratio of weight and number, wood chip 25-30 part, plastics 30-40 part, polyacrylic ester 10-20 part, N-BUTYL ACETATE 10-15 part, lapis amiridis 3-5 part, cis-1,4-polybutadiene rubber 3-5 part, hydrogenation silicone oil 5-10 part, softening agent 1-3 part, sanitas 0.2-0.3, diethylenetriamine 3-5 part, toner 2-4 part.
2. terrace according to claim 1, is characterized in that: described wood chip is that wood adds the sawdust, the wood shavings powder that stay man-hour, and size is 10-50 order.
3. terrace according to claim 1, is characterized in that: described plastics are long 5-10 centimetre, the rectangular strip of wide 1-3 centimetre, thick 0.1-0.3 centimetre.
4. the terrace according to claim 1,2 or 3, it is characterized in that: be prepared from by following ratio of weight and number, wood chip 25 parts, 35 parts, plastics, polyacrylic ester 10 parts, N-BUTYL ACETATE 15 parts, lapis amiridis 3 parts, cis-1,4-polybutadiene rubber 5 parts, hydrogenation silicone oil 7 parts, 1 part, softening agent, sanitas 0.3, diethylenetriamine 3 parts, toner 4 parts.
5. the terrace according to claim 1,2 or 3, it is characterized in that: be prepared from by following ratio of weight and number, wood chip 20 parts, 40 parts, plastics, polyacrylic ester 20 parts, N-BUTYL ACETATE 13 parts, lapis amiridis 5 parts, cis-1,4-polybutadiene rubber 3 parts, hydrogenation silicone oil 5 parts, 2 parts, softening agent, sanitas 0.2, diethylenetriamine 4 parts, toner 4 parts.
6. the terrace according to claim 1,2 or 3, it is characterized in that: be prepared from by following ratio of weight and number, wood chip 30 parts, 30 parts, plastics, polyacrylic ester 15 parts, N-BUTYL ACETATE 10 parts, lapis amiridis 4 parts, cis-1,4-polybutadiene rubber 4 parts, hydrogenation silicone oil 10 parts, 3 parts, softening agent, sanitas 0.25, diethylenetriamine 5 parts, toner 3 parts.
7. a constructional method for terrace described in claim 1,2 or 3, is characterized in that: polyacrylic ester, N-BUTYL ACETATE, cis-1,4-polybutadiene rubber, hydrogenation silicone oil, diethylenetriamine are diluted rear and softening agent, sanitas, lapis amiridis, wood chip, plastics, toner mixing and stirring by (1) according to a conventional method; (2) with terrace preparation of construction, mixture is smeared evenly on swimming pool bottom and sidewall; (3) tie with shredder.