CN104744733A - 一种松针粉生物降解塑料及其制备方法 - Google Patents

一种松针粉生物降解塑料及其制备方法 Download PDF

Info

Publication number
CN104744733A
CN104744733A CN201510168885.0A CN201510168885A CN104744733A CN 104744733 A CN104744733 A CN 104744733A CN 201510168885 A CN201510168885 A CN 201510168885A CN 104744733 A CN104744733 A CN 104744733A
Authority
CN
China
Prior art keywords
parts
needle powder
powder
pine
pine needle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510168885.0A
Other languages
English (en)
Inventor
王贵东
宋睿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Ring Macromolecular Material Factory
Original Assignee
Hefei Ring Macromolecular Material Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Ring Macromolecular Material Factory filed Critical Hefei Ring Macromolecular Material Factory
Priority to CN201510168885.0A priority Critical patent/CN104744733A/zh
Publication of CN104744733A publication Critical patent/CN104744733A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种松针粉生物降解塑料，其特征是由下述重量份的原料制得：松针粉10-15，山药粉3-5，魔芋粉3-5，糯米粉10-15，小麦秸秆4-8，亚麻纤维1-2，聚乙烯10-15，明胶1-2，棉籽油3-5，南瓜籽油0.3-0.5，硅烷偶联剂KH-550 1-2，麦芽糖醇1-2，复合助剂10-15。本发明的生物降解塑料降解率高，降解速度快，且具有良好的柔韧性和符合使用要求的强度，还有抗菌、净化空气的辅助效果，能有效减少白色污染，具有较高的环境效益和经济效益。

Description

一种松针粉生物降解塑料及其制备方法
技术领域
本发明涉及塑料技术领域，具体涉及一种松针粉生物降解塑料及其制备方法。
背景技术
随着工业的发展，塑料在生活中得到了广泛的应用，但是随之带来大量固体废弃物，尤其是一次性塑料制品如塑料包装袋、购物袋、塑料餐盒和地膜等各类生活塑料制品使用后被弃置成为固体废物。由于废旧塑料难以自然降解的特性，和有害的处理方法，产生的塑料废弃物留在水体、土地中，形成“白色污染”，使环境恶化，进而威胁人类的生存，成为世界的公害。
为解决塑料废弃物带来的污染问题，可降解塑料成为研究开发的热点。生物降解塑料是在自然环境下通过微生物的生命活动能很快降解的高分子材料。由于生物降解塑料具有良好的降解性，有助于缓解日益严重的塑料垃圾问题，避免对环境产生的污染，带来极高的社会效益和经济效益，市场前景十分广阔。
发明内容
本发明的目的是提供一种松针粉生物降解塑料，降解率高，降解速度快，且具有良好的柔韧性和符合使用要求的强度，环保无害。
本发明是通过以下技术方案实现的：
一种松针粉生物降解塑料，其特征在于，其是由下述重量份的原料制得：
松针粉10-15，山药粉3-5，魔芋粉3-5，糯米粉10-15，小麦秸秆4-8，亚麻纤维1-2，聚乙烯10-15，明胶1-2，棉籽油3-5，南瓜籽油0.3-0.5，硅烷偶联剂KH-550 1-2，麦芽糖醇1-2，复合助剂10-15；
其中复合助剂由下列重量份的原料制成：
环氧大豆油30-40，羊毛脂3-5，油酸酰胺2-4，液体石蜡2-4，蜂蜡1-2，棕榈酸异丙酯0.5-1，单硬脂酸甘油酯0.1-0.2，聚山梨酯-80 0.1-0.2；
其中复合助剂的制备方法是：
先将环氧大豆油与羊毛脂、液体石蜡和棕榈酸异丙酯混合，先常温下高速混合20-30min，再加入单硬脂酸甘油酯和聚山梨酯-80于80-90℃、1000-1200r/min搅拌5-10min，最后加入油酸酰胺和蜂蜡于同样温度下400-600r/min搅拌1-2h，冷却后即得。
一种松针粉生物降解塑料的制备方法，其包括以下步骤：
（1）将松针粉、山药粉、魔芋粉、糯米粉、明胶和麦芽糖醇混合后按固液重量比2：1-1：1加入水，60-80℃搅拌2-4h后干燥，再加入小麦秸秆和亚麻纤维先于100-120℃处理1-2h，再研磨均匀，过100-200目筛，最后加入硅烷偶联剂KH-550、棉籽油和南瓜籽油100-120℃、1000-1500r/min搅拌20-30min；
（2）将聚乙烯与复合助剂混合后先于120-140℃、200-400r/min条件下搅拌20-30min，再加入（1）中得到的混合物料于140-160℃、600-800r/min条件下搅拌0.5-1h；
（3）将步骤（2）得到的混合物料加入双螺杆挤出机，在140-160℃条件下挤出造粒，即得。
本发明的优点是：
以松针粉为主要原料制备生物降解塑料，松针粉具有丰富的营养物质，能提高材料的降解性能，且具有一定的杀菌功效；通过对配方和工艺的改进，使材料相容性强，降解性能好，协同性高，得到的产品降解率高，降解速度快，且具有良好的柔韧性和符合使用要求的强度，还有抗菌、净化空气的辅助效果，生产工艺简单，能有效减少白色污染，具有较高的环境效益和经济效益。
具体实施方式
本发明非限定实施例如下：
一种松针粉生物降解塑料，由下列重量(kg)的组分原料制备而成：
松针粉12，山药粉4，魔芋粉4，糯米粉12，小麦秸秆6，亚麻纤维1.5，聚乙烯12，明胶1.5，棉籽油4，南瓜籽油0.4，硅烷偶联剂KH-550 1.5，麦芽糖醇1.5，复合助剂12；
其中，复合助剂由下列重量（kg）的原料制成：
环氧大豆油35，羊毛脂4，油酸酰胺3，液体石蜡3，蜂蜡1.5，棕榈酸异丙酯0.8，单硬脂酸甘油酯0.15，聚山梨酯-80 0.15；
复合助剂的制备方法：
先将环氧大豆油与羊毛脂、液体石蜡和棕榈酸异丙酯混合，先常温下高速混合30min，再加入单硬脂酸甘油酯和聚山梨酯-80于90℃、1000r/min搅拌5min，最后加入油酸酰胺和蜂蜡于同样温度下600r/min搅拌2h，冷却后即得。
松针粉生物降解塑料的制备方法包括以下步骤：
（1）将松针粉、山药粉、魔芋粉、糯米粉、明胶和麦芽糖醇混合后按固液重量比1：1加入水， 80℃搅拌3h后干燥，再加入小麦秸秆和亚麻纤维先于120℃处理2h，再研磨均匀，过200目筛，最后加入硅烷偶联剂KH-550、棉籽油和南瓜籽油120℃、1500r/min搅拌200min；
（2）将聚乙烯与复合助剂混合后先于140℃、400r/min条件下搅拌30min，再加入（1）中得到的混合物料于160℃、800r/min条件下搅拌0.5h；
（3）将步骤（2）得到的混合物料加入双螺杆挤出机，在140-160℃条件下挤出造粒，即得。
参照GB/T1040-2006对上述得到的塑料进行拉伸性能测试，测得拉伸强度12.7MPa；材料30d生物降解率≥20%。

Claims (2)

1.一种松针粉生物降解塑料，其特征在于，其是由下述重量份的原料制得：
松针粉10-15，山药粉3-5，魔芋粉3-5，糯米粉10-15，小麦秸秆4-8，亚麻纤维1-2，聚乙烯10-15，明胶1-2，棉籽油3-5，南瓜籽油0.3-0.5，硅烷偶联剂KH-550 1-2，麦芽糖醇1-2，复合助剂10-15；
所述复合助剂由下列重量份的原料制成：
环氧大豆油30-40，羊毛脂3-5，油酸酰胺2-4，液体石蜡2-4，蜂蜡1-2，棕榈酸异丙酯0.5-1，单硬脂酸甘油酯0.1-0.2，聚山梨酯-80 0.1-0.2；
所述复合助剂的制备方法是：
先将环氧大豆油与羊毛脂、液体石蜡和棕榈酸异丙酯混合，先常温下高速混合20-30min，再加入单硬脂酸甘油酯和聚山梨酯-80于80-90℃、1000-1200r/min搅拌5-10min，最后加入油酸酰胺和蜂蜡于同样温度下400-600r/min搅拌1-2h，冷却后即得。
2.根据权利要求1所述的一种松针粉生物降解塑料的制备方法，其特征在于，包括以下步骤：
（1）将松针粉、山药粉、魔芋粉、糯米粉、明胶和麦芽糖醇混合后按固液重量比2：1-1：1加入水，60-80℃搅拌2-4h后干燥，再加入小麦秸秆和亚麻纤维先于100-120℃处理1-2h，再研磨均匀，过100-200目筛，最后加入硅烷偶联剂KH-550、棉籽油和南瓜籽油100-120℃、1000-1500r/min搅拌20-30min；
（2）将聚乙烯与复合助剂混合后先于120-140℃、200-400r/min条件下搅拌20-30min，再加入（1）中得到的混合物料于140-160℃、600-800r/min条件下搅拌0.5-1h；
（3）将步骤（2）得到的混合物料加入双螺杆挤出机，在140-160℃条件下挤出造粒，即得。
CN201510168885.0A 2015-04-10 2015-04-10 一种松针粉生物降解塑料及其制备方法 Pending CN104744733A (zh)