CN104744009A - 一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法 - Google Patents
一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法 Download PDFInfo
- Publication number
- CN104744009A CN104744009A CN201410011025.1A CN201410011025A CN104744009A CN 104744009 A CN104744009 A CN 104744009A CN 201410011025 A CN201410011025 A CN 201410011025A CN 104744009 A CN104744009 A CN 104744009A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- mixing
- batch mixing
- mixed
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是以氧化镁为主要凝胶材料,工业和城市废渣为填料,硫酸镁水溶液为调和剂,添加工业胶水、改性剂和短纤维为增强材料制成的复合混合浆料混入蛋白复合泡沫调和、浇注成型,经过养护制得的轻质混凝土制品。作为强化轻质复合保温外墙板,各种保温模块以及砌块的复合材料,经测试表明其抗压强度,面密度以及抗弯破坏承载、导热系数低、防火性能强等优点。在制备的过程大量使用各类工业废渣和建筑垃圾,是理想的节能环保建筑材料。本发明的改性硫柠镁为主体凝胶材料的制品具有热膨胀性低、不易弯曲、变形、开裂、抗水性能佳、不返潮、不返卤、不泛霜、优良的不燃性、抗冻融、很高的抗渗性和耐磨性。
Description
技术领域本发明属于一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法,特别涉及一种利用各类工业废渣作主要原材填料的建筑板材和砌块。
背景技术目前,用于建筑使用的发泡混凝土墙板和砌块种类繁多,但普遍存在强度不足,防火、隔音、防水性能不佳等缺点。由于使用氯氧镁、硫铝酸盐等快干凝胶材料的配方及其使用方法等原因都导致了板材存在很多的缺陷,如:板材在后期普遍存在出现强度丢失、返卤、返霜、翘曲变形以及耐水性能差现象等。由于各类工业废渣对于环境的污染越来越严重,使用大量的工业废渣成为建材产业中的当务之急,由于各类工业废渣在本发明的掺入量大和掺入品种多,给当前的环境污染治理做出的贡献较大。
发明内容本发明的目的主要是提供一种强化轻质复合墙板以及大量使用工业废渣综合利用的方法。该墙板和砌块的制备大量使用城市及工业废渣、废料,具有成本低、废物利用、重量轻、防火、隔热等特点。由于使用大量废料为减少环境影响和自然资源的破坏以及土地保护有较大的作用。
本发明的一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法,其特征在于,包括如下重量份的组份:氧化镁110-80份,波尔浓度25-30度硫酸镁水溶液90-110份,柠檬酸0.1-10份,工业废渣22-40份,短纤维0.1-0.6份,调性剂10-25份,108工业胶1.0-2.0份,以上所述混合浆料体积混入以上混合浆料体积2.2-5.6倍的复合性蛋白泡沫。
制造所述一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法,其特征于,生产步骤如下:1)首先选取上述重量份数比的氧化镁粉放入搅拌容器备用;
2)选取上述重量份数比的工业废渣放入搅拌容器内;
3)选取上述重量份数比的调性剂放入搅拌容器内;以上干料进行混合备用;
4)选取上述重量比份数硫酸镁水溶液放入另外搅拌容器备用,加入所述柠檬酸,加入所述份数比的短纤维,加入所述份数比的108胶进行搅拌混合;
5)将上述4容器中的液体混料倒入上述3容器干料进行高速搅拌混合,混料搅拌时间不能低于5min,形成粘稠状的混料备用;
6)将上述5的混料通过自动混料机进行上料,在混料机中与通过发泡机发泡的泡沫经过混料机进行充分混合形成泡沫混料;
7)将上述粘稠状混料通过管道输送到成型模具中,约240分钟固化成型,脱模即为成品。
具体实施方式
下面将结合本发明实施例,对本发明作进一步详细说明。
实施例一:
1)将110份氧化镁粉、30份粉煤灰、10份调性剂加入搅拌机搅拌使其均匀,制成氧化镁粉粉煤灰混料。
2)取12份硫酸镁在小型池中或容器内加入16份水搅拌溶解制成硫酸镁水溶液,加入5份柠檬酸,然后加入0.5份的短纤维和1.0份的108工业胶进行充分均匀搅拌制成混液。
3)在放有氧化镁粉和粉煤灰混料的搅拌机中加入硫酸镁混合溶液进行高速混合时间5-10min,充分搅拌混合制成粘稠状混合浆料。
4)以上浆料通过发泡混合机与混合机里的3.5倍复合性蛋白泡沫进行充分混合获得泡沫混合浆料,泡经控制在0.3-1.0mm之间。
5)以上泡沫混浆通过管道注入到砌块模具,经初凝养护脱模制成砌块。
6)以上泡沫混料投入墙板平模2-3mm,布入一层玻纤网。
7)将带有两面燕尾槽的聚苯保温板放入模内压实定位。
8)再将混合泡沫浆料注入放入聚苯保温板的模具2-3mm的混料层再布一层玻纤网抹平。
9)将平模的复合料块经过初凝养护脱模形成复合墙体。
实施例二
1)将100份氧化镁粉、30份铁矿渣、5份硅灰、5份调性剂加入搅拌机搅拌使其均匀,制成氧化镁粉铁矿渣混料。
2)取16份硫酸镁粉在小型池中或容器内加入23份水搅拌溶解制成硫酸镁水溶液,加入3份柠檬酸,然后加入0.2份的短纤维和0.8份的108工业胶进行充分均匀搅拌制成混液。
3)在放有氧化镁粉和铁矿渣混料的搅拌机中加入硫酸镁混合溶液进行高速混合时间5-10min,充分搅拌混合制成粘稠状混合浆料。
4)以上浆料通过发泡混合机与混合机里的3.5倍复合性蛋白泡沫进行充分混合获得泡沫混合浆料,泡经控制在0.3-1.0mm之间。
5)以上泡沫混浆通过管道注入到砌块模具,经初凝养护脱模制成砌块。
6)以上泡沫混料投入墙板平模2-3mm,布入一层玻纤网。
7)将带有两面燕尾槽的聚苯保温板放入模内压实定位。
8)再将混合泡沫浆料注入放入聚苯保温板的模具2-3mm的混料层再布一层玻纤网抹平。
9)将平模的复合料块经过初凝养护脱模形成复合墙体。
实施例三
1)将110份氧化镁粉、20份白泥、10份粉煤灰、6份调性剂加入搅拌机搅拌使其均匀,制成氧化镁粉白泥混料。
2)取14份硫酸镁粉在小型池中或容器内加入22份水搅拌溶解制成硫酸镁水溶液,加入2份柠檬酸,然后加入0.2份的短纤维和0.8份的108工业胶进行充分均匀搅拌制成混液。
10)在放有氧化镁粉和粉煤灰混料的搅拌机中加入硫酸镁混合溶液进行高速混合时间5-10min,充分搅拌混合制成粘稠状混合浆料。
11)以上浆料通过发泡混合机与混合机里的3.5倍复合性蛋白泡沫进行充分混合获得泡沫混合浆料,泡经控制在0.3-1.0mm之间。
12)以上泡沫混浆通过管道注入到砌块模具,经初凝养护脱模制成砌块。
13)以上泡沫混料投入墙板平模2-3mm,布入一层玻纤网。
14)将带有两面燕尾槽的聚苯保温板放入模内压实定位。
15)再将混合泡沫浆料注入放入聚苯保温板的模具2-3mm的混料层再布一层玻纤网抹平。
将平模的复合料块经过初凝养护脱模形成复合墙体。
Claims (6)
1.一种改性硫柠氧镁材料制备轻质复合墙板及砌块的方法,其特征在于,包括如下重量份的组份:
氧化镁粉110-80份,波尔浓度25-30度硫酸镁水溶液90-110份,工业废渣22-40份,柠檬酸0.1-10份,短纤维0.1-0.6份,调性剂10-25份,108工业胶1.0-2.0份,以上所述混合浆料体积混入以上混合浆料体积4.2-5.6倍的复合性蛋白泡沫。
2.根据权利要求1所述的工业废渣为粉煤灰、铁矿渣、金矿渣、碱渣、铝渣、建筑垃圾中的一种或者以上几种的混合。
3.根据权利要求1或2所述工业废渣是选用120-200目粉。
4.根据权利要求1所述的调性剂是硅灰、磷酸、三氯化铁、多聚磷酸钠的一种或者多种混合。
5.根据权利要求1所述的混入泡沫为复合性蛋白泡沫。
6.一种用于上述强化轻质复合墙板或砌块生产工艺方法是:
1)首先选取上述重量份数比的氧化镁粉放入搅拌容器备用;
2)选取上述重量份数比的工业废渣放入搅拌容器内;
3)选取上述重量份数比的调性剂放入搅拌容器内;以上干料进行混合备用;
4)选取上述重量比份数硫酸镁水溶液放入另外搅拌容器备用,加入所述份数柠檬酸,加入所述份数比的短纤维,加入所述份数比的108胶进行搅拌混合;
5)将上述4容器中的液体混料倒入上述3容器干料进行搅拌混合,形成粘稠状的混料备用;
6)将上述5的混料通过自动混料机进行上料,在混料机中与通过发泡机发泡的泡沫经过混料机进行充分混合形成泡沫混料;
7)将上述粘稠状混料通过管道输送到成型模具中,约240分钟固化成型,脱模即为成品。