CN104711862A - Functional finishing technology of qualification badge/shoulder badge silk ribbon - Google Patents
Functional finishing technology of qualification badge/shoulder badge silk ribbon Download PDFInfo
- Publication number
- CN104711862A CN104711862A CN201510157369.8A CN201510157369A CN104711862A CN 104711862 A CN104711862 A CN 104711862A CN 201510157369 A CN201510157369 A CN 201510157369A CN 104711862 A CN104711862 A CN 104711862A
- Authority
- CN
- China
- Prior art keywords
- silk thread
- silk
- finishing
- ribbon
- epaulet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a functional finishing technology of a qualification badge/shoulder badge silk ribbon, which is mainly used for solving the problems that after the existing technology is used for finishing, the width shrinkage rate is inconsistent, and the chromatic aberration cannot meet the requirement. The technology comprises a silk thread finishing working procedure and a braiding working procedure which are carried out sequentially, wherein the silk thread finishing working procedure comprises a silk thread small sample finishing process and a silk thread bulk sample finishing process which are sequentially carried out; the silk thread bulk sample finishing process is regulated according to the hue of the silk thread small sample after being finished. According to the invention, the silk thread bulk sample process is carried out according to the proportion of corresponding substances in a hue regulating finishing liquid of the silk thread small sample after being finished, so that the hue is improved so as to meet the requirement. According to the traditional technology, braiding is carried out firstly, and then finishing is carried out, and after finishing, the width shrinkage rate is inconsistent. According to the invention, a silk thread is finished, and is braided after finishing, namely, finishing is carried out firstly, and braiding is carried out afterwards, and the problem of width shrinkage of the silk ribbon is prevented.
Description
Technical field
The present invention relates to the functional finish process of a kind of Seniority chapter/epaulet silk ribbon.
Background technology
Viscose is one of fiber species that textiles is conventional, it is the cellulose fibre produced for raw material with cotton fiber or other natural fabrics, there is smooth nice and cool, ventilative, the antistatic and characteristic such as lucuriant in design that dyes, so be widely used for makeing assorted embroidery yarn, Seniority chapter silk ribbon, epaulet silk ribbon etc.At present, the silk ribbon of various Seniority chapter, epaulet is all completed through operations such as reactive dyeing, winder, warping and ribbons by the viscose of 60D, 120D, 250D, 300D.
But because viscose fracture strength is less than cotton fiber, elongation at break is larger than cotton, hydroscopicity is also large than cotton, the fracture strength of hygrometric state and extension at break are about the half of dry state, and the inclusion force rate of viscose is poor, also have viscose initial modulus lower, just easily distortion under Smaller load, elastic recovery capability is poor, and this just causes viscose fabric and is drying or drying rear easily distortion, poor dimensional stability.Seniority chapter, epaulet are being exposed to the weather and are not easily being washed after staining, if when washing a little friction will fluff, so be necessary to carry out waterproof, grease proofing, easy decontamination and antibacterial finish to the silk ribbon of Seniority chapter, epaulet.
Traditional three-prevention finishing, is organized that thing completes mainly with web state modes such as padding, dry, cure greatly, and concrete technological process is: weave-dye-pad-dry-cure-shape.Here three-prevention finishing refers to waterproof, grease proofing and antifouling.
First, because the silk ribbon of Seniority chapter, epaulet is different owing to there is stress between silk thread in ribbon process, thus no matter cause silk ribbon be that the mode such as to flood, pad is when carrying out functional treatment, all can not ensure the unanimously stressed of silk ribbon day part, can not ensure that the door width shrinkage factor of silk ribbon is consistent like this, even if when ribbon, we add the amount of contraction that bandwidth reservation arranges, and can not reach the error of silk ribbon finished product requirement upper and lower 2%.
Secondly, various textiles mostly adopts fluorine-containing three-proof finishing agent in three-prevention finishing process, and this finishing agent is p+, after having arranged, form and aspect obfuscation, color ligh modification etc. in various degree can be brought to textiles, be difficult to reach aberration upper and lower 5% requirement.
Summary of the invention
For the problems referred to above, the invention provides the functional finish process of a kind of Seniority chapter/epaulet silk ribbon, the inconsistent and aberration of door width shrinkage factor occurs after existing technique arranges can not meet the requirements of problem to solve.
For achieving the above object, the functional finish process of Seniority chapter of the present invention/epaulet silk ribbon, comprise the silk thread arranging process and ribbon operation that perform successively, wherein silk thread arranging process comprises the silk thread sample arrangement process and silk thread full-page proof arrangement process that perform successively, and the form and aspect after being organized according to silk thread sample arrange process to silk thread full-page proof and adjust.
The present invention adopts and first carries out silk thread sample and arrange process, according to the proportioning of respective substance in the adjustment of color dressing liquid of the silk thread sample after being organized, then carries out silk thread full-page proof process, thus improves form and aspect, make it reach requirement.This technique adopts the mode of sample adjustment to solve the problem affecting form and aspect lightness, changes of shade because of functional treatment.Traditional technique first carries out ribbon, after arrange, a problem that width shrinkage factor is inconsistent can be there is after arrangement.And the present invention arranges silk thread, carry out ribbon work after having arranged, namely first arrange, rear ribbon, avoid the width shrink problem of silk ribbon.
Accompanying drawing explanation
Fig. 1 is the flow chart of the functional finish process of Seniority chapter of the present invention/epaulet silk ribbon;
Detailed description of the invention
Below in conjunction with Figure of description, the present invention will be further described.
Function in functional treatment in the present invention refers to waterproof, grease proofing, easy decontamination and antibacterial, also can become four anti-arrangements.
The invention provides the functional finish process of a kind of Seniority chapter/epaulet silk ribbon, this technique comprises the silk thread arranging process and ribbon operation that perform successively, wherein silk thread arranging process comprises the silk thread sample arrangement process and silk thread full-page proof arrangement process that perform successively, and the form and aspect after being organized according to silk thread sample arrange process to silk thread full-page proof and adjust.
The present invention adopts and first carries out silk thread sample and arrange process, according to the proportioning of respective substance in the adjustment of color dressing liquid of the silk thread sample after being organized, then carries out silk thread full-page proof process, thus improves form and aspect, make it reach requirement.This technique adopts the mode of sample adjustment to solve the problem affecting form and aspect lightness, changes of shade because of functional treatment.
Traditional technique first carries out ribbon, after arrange, a problem that width shrinkage factor is inconsistent can be there is after arrangement.And the present invention arranges silk thread, carry out ribbon work after having arranged, namely first arrange, rear ribbon, avoid the width shrink problem of silk ribbon.
In the present invention, silk thread sample and silk thread full-page proof amount can set as required, and such as, silk thread sample in described silk thread sample arrangement process is 5-15g, and the silk thread full-page proof in described silk thread full-page proof arrangement process is greater than 15g.
Further, described silk thread sample arrange process and silk thread ocean arrange process include perform successively twisted yarn dyeing, dipping, dehydration, dry and cure process.
In above-mentioned impregnation process, add texcote nanometer finishing agent, softener, described finishing agent and softener mix.The amount of wherein said texcote nanometer finishing agent is 40g/l.In described impregnation process, dipping temperature can be 40 DEG C, and dip time can be 30min.
In described drying and processing, bake out temperature can be 120 DEG C, and drying time can be 5min; Cure stoving temperature in operation can be 170 DEG C described, the time of curing can be 5min.
Texcote nanometer finishing agent is also referred to as Deco nanometer finishing agent, fabric after this finishing agent arranges, has according to water, refuses oil, refuses dirt, fungi-proofing, deodorization, the effect such as ventilative, and the intimate avirulence of finishing agent itself, non-stimulated to skin, eyes, environmental protection.
Visible, the fabric that this technique obtains has:
(1) good water proofing property spot effect;
(2) oil stain can not enter fibrous inside easily, and oil stain is more easily wiped;
(3) dust and spot are not easy to stain very much, and are easily shaked off and wipe off;
(4) repeatedly washing function still maintains;
(5) there is fungistatic effect.
Above; be only preferred embodiment of the present invention, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should define with claim is as the criterion.
Claims (8)
1. a functional finish process for Seniority chapter/epaulet silk ribbon, is characterized in that, comprises the following steps performed successively:
1.1 silk thread arranging processes;
Described silk thread arranging process comprises:
Silk thread sample arranges process;
Adjust according to the form and aspect after silk thread sample is organized;
Silk thread full-page proof arranges process;
1.2 ribbon operations.
2. the functional finish process of Seniority chapter according to claim 1/epaulet silk ribbon, is characterized in that: described silk thread sample arrange process and silk thread ocean arrange process include perform successively twisted yarn dyeing, dipping, dehydration, dry, cure process.
3. the functional finish process of Seniority chapter according to claim 2/epaulet silk ribbon, is characterized in that: the softener adding texcote nanometer finishing agent and mix with described finishing agent in described impregnation process.
4. the functional finish process of Seniority chapter according to claim 3/epaulet silk ribbon, is characterized in that: the amount of described texcote nanometer finishing agent is 40g/l.
5. the functional finish process of Seniority chapter according to claim 1/epaulet silk ribbon, is characterized in that: the silk thread sample in described silk thread sample arrangement process is 5-15g, and the silk thread full-page proof in described silk thread full-page proof arrangement process is greater than 15g.
6. the functional finish process of Seniority chapter according to claim 2/epaulet silk ribbon, is characterized in that: in described impregnation process, dipping temperature is 40 DEG C, and dip time is 30min.
7. the functional finish process of Seniority chapter according to claim 2/epaulet silk ribbon, is characterized in that: in described drying and processing, bake out temperature is 120 DEG C, and drying time is 5min.
8. the functional finish process of Seniority chapter according to claim 2/epaulet silk ribbon, is characterized in that: to cure stoving temperature in operation be 170 DEG C described, and the time of curing is 5min.