CN104690384A - Vacuum brazing technological process of plate fin type aluminum alloy radiator - Google Patents
Vacuum brazing technological process of plate fin type aluminum alloy radiator Download PDFInfo
- Publication number
- CN104690384A CN104690384A CN201310646760.5A CN201310646760A CN104690384A CN 104690384 A CN104690384 A CN 104690384A CN 201310646760 A CN201310646760 A CN 201310646760A CN 104690384 A CN104690384 A CN 104690384A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- vacuum brazing
- clean
- radiator
- alloy radiator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a vacuum brazing technological process, in particular to a vacuum brazing technological process of a plate fin type aluminum alloy radiator. The process comprises the steps of preparation of raw materials, cleaning, assembly, brazing, inspection, drying and cleaning. The process is simple; the produced aluminum alloy radiator has the advantages of compact structure, good stability, high strength, uniform and compact welding line, firmness, beauty, good tightness, less proneness to product corrosion and high pass percent; and the vacuum brazing technological process produces the plate fin type aluminum alloy radiator with high strength and high performance.
Description
Technical field
The present invention relates to a kind of vacuum brazing technique flow process, especially a kind of vacuum brazing technique flow process of plate wing aluminum alloy radiator.
Background technology
Plate wing aluminum alloy radiator has captured increasing market with its good heat dispersion, high strength, advanced free of contamination production method.The traditional manufacturing process of plate wing aluminum alloy radiator is salt bath brazing, the cleaning more complicated of product surface residual flux after its soldering, is difficult to thoroughly clean up, and residual villaumite can corrode product surface, reduces the reliability of product.
Summary of the invention
The present invention is intended to solve the problem, and provides a kind of vacuum brazing technique flow process of plate wing aluminum alloy radiator, and it pollutes less, product easy cleaning, and its technical scheme adopted is as follows:
A vacuum brazing technique flow process for plate wing aluminum alloy radiator, is characterized in that, the step of the vacuum brazing technique flow process of described plate wing aluminum alloy radiator is followed successively by:
A) raw material prepares: strip of paper used for sealing, fin adopt AA3003 aluminium alloy, and dividing plate adopts 4343/3003/4343 duplex coating aluminium alloy, and side guard plate adopts 4343/3003 single covering grass plantation;
B) clean: surface clean is carried out to unit parts, the greasy dirt, oxide skin etc. of removing material surface;
C) assemble: each unit parts are superposed successively, after closed assembly, puts fixture; ;
D) soldering: the product after closed assembly is put into vacuum brazing furnace brazing, brazing temperature 600-620 DEG C, vacuum (3-5) × 10
-3pa;
E) check: product complete for soldering is put into the compressed air that water passes into 0.25-0.35MPa, and pressurize 2min does not reveal;
F) dry: the water first drying up spreader surface with air cannon, then radiator is sent into chain type drying oven and dry, bake out temperature 70-85 DEG C;
G) clean: the impurity of product surface is removed, keep product surface to clean.
Tool of the present invention has the following advantages: its technological process is simple, the aluminium alloy heat radiator compact conformation produced, good stability, intensity are high, even weld densification, firmly attractive in appearance, good airproof performance, product is not easily corroded, qualification rate is high, is a kind of vacuum brazing technique flow process of producing high strength, high-performance plate wing aluminum alloy radiator.
Accompanying drawing explanation
Fig. 1: production technological process of the present invention;
Detailed description of the invention
Below in conjunction with accompanying drawing and example, the invention will be further described:
As shown in Figure 1, a kind of vacuum brazing technique flow process of plate wing aluminum alloy radiator, is characterized in that, the step of the vacuum brazing technique flow process of described plate wing aluminum alloy radiator is followed successively by:
A) raw material prepares: strip of paper used for sealing, fin adopt AA3003 aluminium alloy, and dividing plate adopts 4343/3003/4343 duplex coating aluminium alloy, and side guard plate adopts 4343/3003 single covering grass plantation;
B) clean: surface clean is carried out to unit parts, the greasy dirt, oxide skin etc. of removing material surface;
C) assemble: each unit parts are superposed successively, after closed assembly, puts fixture; ;
D) soldering: the product after closed assembly is put into vacuum brazing furnace brazing, brazing temperature 600-620 DEG C, vacuum (3-5) × 10
-3pa;
E) check: product complete for soldering is put into the compressed air that water passes into 0.25-0.35MPa, and pressurize 2min does not reveal;
F) dry: the water first drying up spreader surface with air cannon, then radiator is sent into chain type drying oven and dry, bake out temperature 70-85 DEG C;
G) clean: the impurity of product surface is removed, keep product surface to clean.
Describe the present invention by way of example above, but the invention is not restricted to above-mentioned specific embodiment, all any changes of doing based on the present invention or modification all belong to the scope of protection of present invention.
Claims (1)
1. a vacuum brazing technique flow process for plate wing aluminum alloy radiator, is characterized in that, the step of the vacuum brazing technique flow process of described plate wing aluminum alloy radiator is followed successively by:
A) raw material prepares: strip of paper used for sealing, fin adopt AA3003 aluminium alloy, and dividing plate adopts 4343/3003/4343 duplex coating aluminium alloy, and side guard plate adopts 4343/3003 single covering grass plantation;
B) clean: surface clean is carried out to unit parts, the greasy dirt, oxide skin etc. of removing material surface;
C) assemble: each unit parts are superposed successively, after closed assembly, puts fixture; ;
D) soldering: the product after closed assembly is put into vacuum brazing furnace brazing, brazing temperature 600-620 DEG C, vacuum (3-5) × 10
-3pa;
E) check: product complete for soldering is put into the compressed air that water passes into 0.25-0.35MPa, and pressurize 2min does not reveal;
F) dry: the water first drying up spreader surface with air cannon, then radiator is sent into chain type drying oven and dry, bake out temperature 70-85 DEG C;
G) clean: the impurity of product surface is removed, keep product surface to clean.