CN104672924A - Scrap rubber-modified asphalt - Google Patents
Scrap rubber-modified asphalt Download PDFInfo
- Publication number
- CN104672924A CN104672924A CN201310638552.0A CN201310638552A CN104672924A CN 104672924 A CN104672924 A CN 104672924A CN 201310638552 A CN201310638552 A CN 201310638552A CN 104672924 A CN104672924 A CN 104672924A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- activator
- coal tar
- modifying asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides scrap rubber-modified asphalt, which comprises rubber powder, matrix asphalt, a rubber activating agent, a rubber renewable reducing agent, coal tar and an emulsifier. The scrap rubber-modified asphalt is capable of effectively improving the properties such as low-temperature crack resistance, high-temperature stability performance, ageing resistance and elasticity of the asphalt.
Description
Technical field
The invention belongs to resource recycling and asphalt material technical field, be specifically related to a kind of pitch utilizing waste and old modified rubber.
Background technology
The current existing modifying asphalt major part of China adopts physically modified technological method, realizes the modification of polymkeric substance to pitch, as heated and stirred, shearing, colloidal mill etc.Although the method for physically modified can make the performance of pitch make moderate progress, over-all properties is not still fundamentally improved, and only exists to adsorb partially, mix between polymkeric substance and pitch, and and non-fully dissolve.This system belongs to thermodynamic unstable system, the separation between two-phase very easily occurs, causes segregation phenomenon; When the modified bitumen product of in-situ processing is once external force fails, polymkeric substance will be separated and float on surface aggregation from pitch, forms the coarse epidermis of larger particles.Therefore the production of physically modified pitch carries out at the construction field (site), and existing producing now spreads, and product not easily stores, and cannot reach industrialization and produce.
And the whole world has millions of tons waste tire rubber to produce every year, quantity is so huge, how to carry out effective process to it and has become human society question of common concern.The recovery process technology of domestic and international junked tire mainly contains the methods such as the original shape transformation of the way, thermo-cracking, tyre rebuilding, burning.Junked tire can directly utilize by original shape transformation of the way method, but utilization is limited; Pyrolysis method can prepare oil fuel, carbon black etc., but technical sophistication, cost is high, easily causes secondary pollution; The power consumption of tyre rebuilding method less, pollution-free, but investment is large, and technical requirements is high; Although combustion method is simple, release obnoxious flavour, secondary pollution is serious.These methods have recycled a part of junked tire to a certain extent, but the damaged tire limited amount of process, along with the fast development of automotive industry, is unable to catch up with the quantity that junked tire produces gradually, therefore, need to find more effective, a large amount of approach utilizing junked tire.
Summary of the invention
The object of the present invention is to provide a kind of pitch received discarded rubber for tire and prepare modified rubber, namely discarded rubber for tire can be carried out recycling, the use properties of pitch can be improved again.Several lower technical scheme of concrete employing:
A kind of waste rubber modifying asphalt, comprises rubber powder and matrix pitch, also comprises rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent.
Waste rubber modifying asphalt provided by the invention, described rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts: 10 ~ 20 parts of rubber powders, 50 ~ 80 parts of matrix pitches, 0.5 ~ 3 part of rubber activator, 0.5 ~ 3 part of rubber regeneration reductive agent, 6 ~ 12 parts of coal tar, 2 ~ 5 parts of emulsifying agents.
Waste rubber modifying asphalt provided by the invention, described rubber activator is ferrous sulfate, Iron nitrate or iron protochloride.
Waste rubber modifying asphalt provided by the invention, described rubber regeneration reductive agent is PTC-R.
In preferred embodiments of the present invention, described rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts: 18 parts of rubber powders, 80 parts of matrix pitches, 1 part of rubber activator, 1.5 parts of rubber regeneration reductive agents, 10 parts of coal tar, 4 parts of emulsifying agents.
In preferred embodiments of the present invention, described rubber activator is ferrous sulfate.
Rubber powder of the present invention is by waste tire rubber cleaning, seasoning, and preliminary broken rear removal metal and fiber foreign material, conducting powder is broken.
Discarded tyre rubber powder effectively can improve the performances such as the crack resistance at low-temperature of pitch, high temperature stability performance, ageing resistance and elasticity.The road surface adopting height provided by the invention anti-ageing property rubber asphalt to lay is more durable than plain asphalt road surface, and the crackle of generation is few, and weathering resistance is better, and chance severe cold weather is also not-easy-to-freeze.
Embodiment
The following examples can make the present invention of those of ordinary skill in the art's comprehend, but do not limit the present invention in any way.
Embodiment 1
Waste rubber modifying asphalt provided by the invention, described rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts:
Above-mentioned raw materials is mixed, in 200 DEG C of reaction 3 ~ 5h, obtains rubber modified asphalt.
Embodiment 2
Waste rubber modifying asphalt provided by the invention, described rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts:
Above-mentioned raw materials is mixed, in 200 DEG C of reaction 3 ~ 5h, obtains rubber modified asphalt.
Embodiment 3
Waste rubber modifying asphalt provided by the invention, described rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts:
Above-mentioned raw materials is mixed, in 200 DEG C of reaction 3 ~ 5h, obtains rubber modified asphalt.
Claims (4)
1. a waste rubber modifying asphalt, comprises rubber powder and matrix pitch, it is characterized in that: also comprise rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent.
2. modifying asphalt according to claim 1, it is characterized in that rubber powder, matrix pitch, rubber activator, rubber regeneration reductive agent, coal tar and emulsifying agent are prepared according to following mass parts: 10 ~ 20 parts of rubber powders, 50 ~ 80 parts of matrix pitches, 0.5 ~ 3 part of rubber activator, 0.5 ~ 3 part of rubber regeneration reductive agent, 6 ~ 12 parts of coal tar, 2 ~ 5 parts of emulsifying agents.
3. modifying asphalt according to claim 1 and 2, is characterized in that: described rubber activator is ferrous sulfate, Iron nitrate or iron protochloride.
4. modifying asphalt according to claim 1 and 2, is characterized in that: described rubber regeneration reductive agent is PTC-R.