CN102485800A - Preparation method of modified biological tar asphalt - Google Patents
Preparation method of modified biological tar asphalt Download PDFInfo
- Publication number
- CN102485800A CN102485800A CN201010576060XA CN201010576060A CN102485800A CN 102485800 A CN102485800 A CN 102485800A CN 201010576060X A CN201010576060X A CN 201010576060XA CN 201010576060 A CN201010576060 A CN 201010576060A CN 102485800 A CN102485800 A CN 102485800A
- Authority
- CN
- China
- Prior art keywords
- biological
- tar
- modified
- asphalt
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an agricultural waste comprehensive utilization technology and specially, relates to a preparation method of modified biological tar asphalt. The preparation method comprises the following steps of 1, a biological asphalt preparation process comprising removing a fraction having a temperature below 220 DEG C of biological tar by normal pressure distillation and collecting a residue, wherein the residue is biological asphalt, 2, a heating process comprising heating the residue so that the residue becomes liquid, and 3, a modifier addition process comprising adding 1 to 3% of a chloroprene rubber latex asphalt modifier into the liquid obtained by the step 2 according to a certain ratio, and heating with uniform stirring to obtain the modified biological tar asphalt. The preparation method realizes effective utilization of biological tar, solves the problems of biological tar secondary pollution in agricultural waste carbon gasification technology utilization, changes waste into valuables, and improves the economic benefit of the agricultural waste carbon gasification technology utilization.
Description
Technical field
The present invention relates to a kind of agricultural wastes comprehensive utilization technique, particularly a kind ofly agricultural wastes are fully utilized the biological tar that produces in the switching process convert biological modified by tar bituminous making method to
Background technology
Biological tar is a kind of important chemical material, and quality is higher than coal tar, its complicated component; Each component content of the biological tar of different starting material gained is different, wherein contains 5~6% the hydro carbons of having an appointment, 2~3% alcohols; 40~60 creosote, a small amount of aldehydes exists with liquid state when being lower than 200 ℃; Pyrolysis takes place in the time of more than 200 ℃, and pyrolysis becomes micro-molecular gas.Pressing in the biological tar distillation cut of normal pressure temperature collection, is the sour water cut below 110 ℃, is light oil distillate in the time of 110~190 ℃, is the creosote cut in the time of more than 190 ℃, also has higher residual the heating up in a steamer of thermal value.The sour water cut that wherein biological tar distillation obtains can be processed with biological acetic acid; Light oil distillate can be used as the floatation frother that fuel or non-ferrous metal ore are used; All the other cuts can further convert biological stopper, biological anti-oxidant, industrial creosote and liquid fuel etc. to, and its residue is that biological pitch can be used for making biological modified by tar bituminous raw material.
In the existing agricultural wastes charcoal gasification system; The method of washing decoking is generally adopted in the separation of combustion gas and purification, and the waste water that is mixed with biological tar and wood vinegar is in a large number entered the farmland, collects utilization and abandons it; Cause soil and water source severe contamination, agroecological environment is done great damage.
How biological tar is effectively utilized; Solve agricultural wastes charcoal gasification technology and utilize in the process, secondary pollution problem turns waste into wealth; Agricultural wastes charcoal gasification technology is applied, promoted the development of agricultural wastes utilization of resources technology to have vital role.
Existing modifying asphalt is to mix rubber, resin, high molecular polymer, levigated rubber powder or other fillers at petroleum pitch, coal-tar pitch or wood tar pitch; Or take to measures such as pitch mild oxidation processing the asphaltic binder that makes the performance of pitch or asphalt be improved and process.Modifying asphalt can improve the road surface resistance to flow, the ability of anti-rut under the high temperature; Improve flexibility and elasticity, the i.e. ability of cracking resistance under the low temperature; Improve the abrasion performance ability and increase the service life.Also do not find the concrete process method of producing modifying asphalt at present with biological tar (the careless tar that is produced with agricultural wastes pyrolysis such as stalks).
Summary of the invention
Main purpose of the present invention is; Overcome in the existing agricultural wastes charcoal gasification technology utilization; The waste water that contains biological tar and wood vinegar is in a large number entered the farmland, and severe contamination soil and water source work the mischief to agroecological environment; Utilize biological tar to make biological modified by tar bituminous making method and provide a kind of, technical problem to be solved be make produced in the agricultural wastes charcoal gasification technology impurity--biological tar is utilized effectively.
Biological modified by tar bituminous making method provided by the present invention is realized by following technical scheme.
A kind of biological modified by tar bituminous making method, comprising following steps:
The method of step 1, usefulness heating is removed the cut of biological tar below 260 ℃, collects its residue--biological pitch;
Step 2, biological pitch is poured in the container with whisking appliance, liquid biological bituminous temperature is kept in 90~110 ℃ of scopes;
Step 3, add the latex bitumen properties-correcting agent of X 050 in proportion, heat while stirring, stirring obtains bio-modification pitch.
Except that above-mentioned essential features, in the practical implementation process, also can further replenish following technology contents.
Described biological modified by tar bituminous making method, wherein the said method with heating of step 1 is in still kettle, to carry out air distillation, or in container, carries out direct heating.
Described biological modified by tar bituminous making method, wherein said air distillation, or direct-fired optimum temps is 220 ℃.
Described biological modified by tar bituminous making method, wherein step 3 is said is to rise the latex bitumen properties-correcting agent that biological pitch adds 1 ± 0.2ml or 2 ± 0.2ml or 3 ± 0.2ml X 050 at each in proportion.
The advantage of invention is:
1, the ability of cracking resistance all is superior to the modifying asphalt produced with wood tar oil or coal tar under biological its plasticity of modified by tar pitch, flowability and the low temperature that the present invention produced.Biological modified by tar pitch satisfies the requirement of (SBS modifying asphalt) and State Standard of the People's Republic of China GB18242-2000 " elastomer modified asphalt waterproof roll ".
2, the present invention effectively utilizes biological tar; Solving agricultural wastes charcoal gasification technology utilizes in the process; The secondary pollution problem of biological tar turns waste into wealth, and improves the economic benefit that agricultural wastes charcoal gasification technology utilizes; Agricultural wastes charcoal gasification technology is applied, promoted the development of agricultural wastes utilization of resources technology to have vital role.
Above-mentioned explanation only is the general introduction of technical scheme of the present invention; Understand technique means of the present invention in order can more to know; And can implement according to the content of specification sheets, and for let of the present invention above-mentioned with other purposes, feature and advantage can be more obviously understandable, below special act preferred embodiment; And conjunction with figs., specify as follows.
Description of drawings
Fig. 1 is the schema of the biological modified by tar bituminous of the present invention making method.
Embodiment
Reach technique means and the effect that predetermined goal of the invention is taked for further setting forth the present invention; Below in conjunction with accompanying drawing and preferred embodiment; To biological its embodiment of modified by tar bituminous making method, characteristic and the effect thereof that proposes according to the present invention, specify as after.
See also shown in Figure 1ly, the biological modified by tar bituminous making method of preferred embodiment of the present invention may further comprise the steps:
A kind of biological modified by tar bituminous making method, comprising following steps:
The method of step 1, usefulness heating is removed the cut of biological tar below 260 ℃, collects its residue--biological pitch;
Step 2, biological pitch is poured in the container with whisking appliance, liquid biological bituminous temperature is kept in 90~110 ℃ of scopes;
Step 3, add the latex bitumen properties-correcting agent of X 050 in proportion, heat while stirring, stirring obtains bio-modification pitch.
The said method with heating of step 1 is in still kettle, to carry out air distillation, or in container, carries out direct heating.
Said air distillation, or direct-fired optimum temps is 220 ℃.
Rapid three said be to rise the latex bitumen properties-correcting agent that biological pitch adds 1 ± 0.2ml or 2 ± 0.2ml or 3 ± 0.2ml X 050 in proportion at each.
The prepared biological modified by tar bituminous performance of the present invention is as shown in table 1.
The biological modified by tar pitch of being produced satisfies the requirement of (SBS modifying asphalt) and State Standard of the People's Republic of China GB18242-2000 " elastomer modified asphalt waterproof roll ".
Biological modified by tar pitch of the present invention can be used for expressway construction.
The above only is preferred embodiment of the present invention, is not the present invention is done any pro forma restriction; Though the present invention discloses as above with preferred embodiment; Yet be not in order to limiting the present invention, anyly be familiar with the professional and technical personnel, in not breaking away from technical scheme scope of the present invention; When the technology contents of above-mentioned announcement capable of using is made a little change or is modified to the equivalent embodiment of equivalent variations; In every case be the content that does not break away from technical scheme of the present invention, to any simple modification, equivalent variations and modification that above embodiment did, all still belong in the scope of technical scheme of the present invention according to technical spirit of the present invention.
Claims (4)
1. biological modified by tar bituminous making method is characterized in that may further comprise the steps:
The method of step 1, usefulness heating is removed the cut of biological tar below 260 ℃, collects its residue--biological pitch;
Step 2, biological pitch is poured in the container with whisking appliance, liquid biological bituminous temperature is kept in 90~110 ℃ of scopes;
Step 3, add the latex bitumen properties-correcting agent of X 050 in proportion, heat while stirring, stirring obtains bio-modification pitch.
2. biological modified by tar bituminous making method according to claim 1 is characterized in that the said method with heating of step 1 is in still kettle, to carry out air distillation, or in container, carries out direct heating.
3. biological modified by tar bituminous making method according to claim 1 it is characterized in that said air distillation, or direct-fired optimum temps is 220 ℃.
4. biological modified by tar bituminous making method according to claim 1, it is characterized in that step 3 said be that each rises the latex bitumen properties-correcting agent that adds 1 ± 0.2ml or 2 ± 0.2ml or 3 ± 0.2ml X 050 in the biological pitch in proportion.