CN104671727A - 一种防渗水水泥 - Google Patents
一种防渗水水泥 Download PDFInfo
- Publication number
- CN104671727A CN104671727A CN201310629127.5A CN201310629127A CN104671727A CN 104671727 A CN104671727 A CN 104671727A CN 201310629127 A CN201310629127 A CN 201310629127A CN 104671727 A CN104671727 A CN 104671727A
- Authority
- CN
- China
- Prior art keywords
- cement
- water seepage
- fluorine
- seepage prevention
- latex powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防渗水水泥,由以下重量份的原料制成:5-8%的含氟聚丙烯酸酯乳胶粉,氟含量1-3%;2-3%的松香,100-200目;3-5%的硅酸钠;3-5%的氢氧化钙;1-2%的明矾;1-2%的十二烷基磺酸钠;10-15%的硫铝酸盐水泥;余量为硅酸盐水泥。本发明制备成的水泥具有防渗水的功能。
Description
技术领域
本发明属于聚合物水泥材料研究的技术领域,特别涉及一种防渗水水泥。
背景技术
通过微观分析可知水泥在水化过程中将在基体中形成凝胶孔、过渡孔、毛细孔及大孔四类孔。这些孔的总孔率、孔径的分布、孔径的尺寸及形状都将对基体的抗压及抗弯强度造成影响。一般的水泥基复合材料主要是由未水化的水泥熟料颗粒、水泥的水化结晶矿物和凝胶体、水和少量的空气组成,它是一个固-液-气多相多孔体。因此,由普通水泥制成的建筑物,必然会渗水。所以,需要在水泥制品的上层或下层铺设防水层。这样,会增加工程造价,提高施工强度。
近年来,随着材料科学与工程的发展,特种水泥的需求量也在大幅增长,例如,在众多建筑工程中需要防渗水水泥,但目前,市场上提供的具有防渗防水性能优良的水泥,品种较少,而且效果并不理想。
发明内容
本发明针对目前水泥产品在宏观上的很多缺陷,提供一种防渗性能优良的防渗水水泥。
本发明是通过以下方案实现的:
本发明的防渗水水泥,由以下重量份的原料制成:
5-8%的含氟聚丙烯酸酯乳胶粉,氟含量1-3%;
2-3%的松香,100-200目;
3-5%的硅酸钠;
3-5%的氢氧化钙;
1-2%的明矾;
1-2%的十二烷基磺酸钠;
10-15%的硫铝酸盐水泥;
余量为硅酸盐水泥。
制备方法:把各原料粉碎,与硅酸盐水泥混匀即可。
上述本发明采用的含氟聚丙烯酸酯乳胶粉,其制备方法和产品性能与普通的聚丙烯酸酯乳胶粉基本相同,其区别在于聚合单体的部分氢原子由氟原子取代。本发明采用的含氟聚丙烯酸酯乳胶粉,由于含有具有憎水功能的氟原子,提高了防渗水水泥的憎水性能,使水汽不能进入水泥的缝隙中。
本发明的防渗水水泥中,加入一定量的松香,可以充填部分水泥缝隙,减少缝隙率,提高防水性能。
本发明的防渗水水泥中,加入一定量的硅酸钠、氢氧化钙及明矾,可以与硫铝酸盐水泥和硅酸盐水泥,形成交联的网状结构,降低缝隙率,提高防水性能。
本发明的防渗水水泥,加入一定量的十二烷基磺酸钠,可以降低材料的表面张力,增加材料之间的融合能力,减少缝隙度,从而提高防水性能
本发明的防渗水水泥中,加入一定量的硫铝酸盐水泥,可以进一步降低空隙率,提高防水性能。
本发明与现有技术相比,具有防渗性能强,粘结强度高等优点,能显著提高水泥砂浆抗渗压力,并能提高其抗折,抗压强度。
具体实施方式
下面结合实施例对本发明做进一步说明。
实施例1
取5%的氟含量1%的含氟聚丙烯酸酯乳胶粉、2%的100目的松香、3%的硅酸钠、3%的氢氧化钙、1%的明矾、1%的十二烷基磺酸钠、10%的硫铝酸盐水泥与75%的硅酸盐水泥,粉碎,混匀。
实施例2
取7%的氟含量2%含氟聚丙烯酸酯乳胶粉、3%的200目的松香、4%的硅酸钠、4%的氢氧化钙、2%的明矾、2%的十二烷基磺酸钠、13%的硫铝酸盐水泥与65%的硅酸盐水泥,粉碎,混匀。
实施例3
取8%的氟含量3%的含氟聚丙烯酸酯乳胶粉、3%的200目的松香、5%的硅酸钠、5%的氢氧化钙、2%的明矾、2%的十二烷基磺酸钠、15%的硫铝酸盐水泥和60%的硅酸盐水泥,粉碎,混匀。
根据GB18445-2001的标准中方法进行检测。
检测结果汇总如表1:
表 1
实验项目 | 国家标准 | 实施例1 | 实施例2 | 实施例3 |
抗折强度 ,MPa,(7d) | ≥2.80 | 5.72 | 5.81 | 5.92 |
抗折强度,MPa,(28d) | ≥3.50 | 7.88 | 8.07 | 8.17 |
抗压强度,MPa,(7d) | ≥12.0 | 38.4 | 40.2 | 40.7 |
抗压强度,MPa,(28d) | ≥18.0 | 56.3 | 58.7 | 58.9 |
湿基面粘结强度,MPa | ≥1.0 | 1.41 | 1.56 | 1.58 |
抗渗压力,MPa(28d) | ≥1.2 | 1.71 | 1.79 | 1.82 |
渗透压力比(28d)% | ≥300 | 402 | 409 | 414 |
由实验数据可以看出,本发明的防渗水水泥、抗压强度、抗渗压力、与湿基面粘结强度和渗透压力比各指标都明显高于国家标准。
Claims (1)
1. 一种防渗水水泥,其特征在于,由以下重量份的原料制成:
5-8%的含氟聚丙烯酸酯乳胶粉,氟含量1-3%;
2-3%的松香,100-200目;
3-5%的硅酸钠;
3-5%的氢氧化钙;
1-2%的明矾;
1-2%的十二烷基磺酸钠;
10-15%的硫铝酸盐水泥;
余量为硅酸盐水泥。