CN104665527B - 纤维毯制造工艺 - Google Patents

纤维毯制造工艺 Download PDF

Info

Publication number
CN104665527B
CN104665527B CN201510045587.2A CN201510045587A CN104665527B CN 104665527 B CN104665527 B CN 104665527B CN 201510045587 A CN201510045587 A CN 201510045587A CN 104665527 B CN104665527 B CN 104665527B
Authority
CN
China
Prior art keywords
density
web layer
machine
tapetum fibrosum
finished product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510045587.2A
Other languages
English (en)
Other versions
CN104665527A (zh
Inventor
王俊杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou City Xin Auto Parts Co ltd
Original Assignee
Liuzhou City Person Of Outstanding Talent Auto Parts Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou City Person Of Outstanding Talent Auto Parts Manufacturing Co Ltd filed Critical Liuzhou City Person Of Outstanding Talent Auto Parts Manufacturing Co Ltd
Priority to CN201510045587.2A priority Critical patent/CN104665527B/zh
Publication of CN104665527A publication Critical patent/CN104665527A/zh
Application granted granted Critical
Publication of CN104665527B publication Critical patent/CN104665527B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种纤维毯制造工艺，包括从下至上依次设置的第一高密纤维层、混合纤维毡和第二高密纤维层，工艺步骤如下：将高密度PET纤维由喂棉机送入梳理机进行梳理，形成高密度纤维网；将该高密度纤维网输送给铺棉机，铺叠形成高密纤维层；将高密纤维层在针刺机上进行针刺加固，将再生纤维、涤纶纤维和高密度PET纤维混合均匀，得到混合纤维；将混合纤维由喂棉机送入梳理机进行梳理；将该混合纤维网输送给铺棉机，铺叠形成混合纤维毡；将混合纤维毡在针刺机上进行针刺加固，从下至上依次铺设第一高密纤维层、混合纤维毡和第二高密纤维层，在针刺机上进行针刺加固；本发明涉及的这种纤维毯制造工艺，质地均密，隔音良好。

Description

纤维毯制造工艺
技术领域
本发明涉及一种纤维毯制造工艺，属于纺织制造技术领域。
背景技术
人们日常使用纤维毯除了美观大方，还可以起到隔音的效果，如何制造出质地更好，更容易清洗和使隔音效果更好的纤维毯为本发明要研究的课题。
发明内容
本发明的目的是提供一种纤维毯制造工艺，质地均密，隔音良好。
为了解决上述问题，本发明采用的技术方案是：一种纤维毯制造工艺，纤维毯包括从下至上依次设置的第一高密纤维层、混合纤维毡和第二高密纤维层，包括以下工艺步骤：
（1）第一高密纤维层的制备：将高密度PET纤维（密度大于1.4g/cm3）由喂棉机送入梳理机进行梳理，形成高密度纤维网；将该高密度纤维网输送给铺棉机，铺叠形成高密纤维层；将高密纤维层在针刺机上进行针刺加固，针刺速度为200～300转/分钟；
（2）混合纤维毡的制备：将再生纤维、涤纶纤维和高密度PET纤维按重量比40～60:20～30:20～30混合均匀，得到混合纤维；将混合纤维由喂棉机送入梳理机进行梳理，形成混合纤维网；将该混合纤维网输送给铺棉机，铺叠形成混合纤维毡；将混合纤维毡在针刺机上进行针刺加固，针刺速度为400～800转/分钟；
（3）从下至上依次铺设第一高密纤维层、混合纤维毡和第二高密纤维层，在针刺机上进行针刺加固，针刺速度为1000～1200转/分钟，得到纤维毯半成品；
（4）将经步骤（3）针刺加固后的纤维毯半成品置于成型模具内进行模压成型：首先上模抽真空，抽真空时间为10～20秒，压力为0.01～0.02MPa，在抽真空的同时通入高温蒸汽；保持真空度，继续通入高温蒸汽进行加热成型，蒸汽压力为0.6～2MPa，蒸汽温度为105～115℃，加热成型的压力为5～10MPa，成型时间为40～60秒；
（5）冷却：将经步骤（4）处理后的纤维毯半成品放入冷却治具，在常温下进行冷却定型，冷却时间为30～45秒；
（6）将经步骤（5）冷却后的纤维毯半成品切割成所需的外形尺寸，并在半成品上进行冲断加工得到所需要的孔，即得到所述的纤维毯成品。
所述高密纤维层的密度为200～250g/m2，所述混合纤维毡的密度为900～1800g/m2。
所述步骤（1）中，喂棉机的速度为20～30Hz，梳理机道夫的速度为350～450转/分钟，铺棉机往复频度为4～10Hz；所述步骤（2）中，喂棉机的速度为20～40Hz，梳理机道夫的速度为350～600转/分钟，铺棉机往复频度为4～20Hz。
所述步骤（6）中，纤维毯半成品采用水刀切割机进行切割，切割压力为40000～60000psi，切割气压为0.5～0.8MPa；纤维毯半成品采用冲断加工孔时，冲断压力为5～10MPa，冲断时间为3～10秒。
具体实施方式
一种纤维毯制造工艺，纤维毯包括从下至上依次设置的第一高密纤维层、混合纤维毡和第二高密纤维层，包括以下工艺步骤：
（1）第一高密纤维层的制备：将高密度PET纤维由喂棉机送入梳理机进行梳理，形成高密度纤维网；将该高密度纤维网输送给铺棉机，铺叠形成高密纤维层；将高密纤维层在针刺机上进行针刺加固，针刺速度为200～300转/分钟；
（2）混合纤维毡的制备：将再生纤维、涤纶纤维和高密度PET纤维按重量比40～60:20～30:20～30混合均匀，得到混合纤维；将混合纤维由喂棉机送入梳理机进行梳理，形成混合纤维网；将该混合纤维网输送给铺棉机，铺叠形成混合纤维毡；将混合纤维毡在针刺机上进行针刺加固，针刺速度为400～800转/分钟；
（3）从下至上依次铺设第一高密纤维层、混合纤维毡和第二高密纤维层，在针刺机上进行针刺加固，针刺速度为1000～1200转/分钟，得到纤维毯半成品；
（4）将经步骤（3）针刺加固后的纤维毯半成品置于成型模具内进行模压成型：首先上模抽真空，抽真空时间为10～20秒，压力为0.01～0.02MPa，在抽真空的同时通入高温蒸汽；保持真空度，继续通入高温蒸汽进行加热成型，蒸汽压力为0.6～2MPa，蒸汽温度为105～115℃，加热成型的压力为5～10MPa，成型时间为40～60秒；
（5）冷却：将经步骤（4）处理后的纤维毯半成品放入冷却治具，在常温下进行冷却定型，冷却时间为30～45秒；
（6）将经步骤（5）冷却后的纤维毯半成品切割成所需的外形尺寸，并在半成品上进行冲断加工得到所需要的孔，即得到所述的纤维毯成品。

Claims (1)

1.一种纤维毯制造工艺，其特征是，纤维毯包括从下至上依次设置的第一高密纤维层、混合纤维毡和第二高密纤维层，包括以下工艺步骤：
（1）第一高密纤维层的制备：将高密度PET纤维由喂棉机送入梳理机进行梳理，形成高密度纤维网；将该高密度纤维网输送给铺棉机，铺叠形成高密纤维层；将高密纤维层在针刺机上进行针刺加固，针刺速度为200～300转/分钟；
（2）混合纤维毡的制备：将再生纤维、涤纶纤维和高密度PET纤维按重量比40～60:20～30:20～30混合均匀，得到混合纤维；将混合纤维由喂棉机送入梳理机进行梳理，形成混合纤维网；将该混合纤维网输送给铺棉机，铺叠形成混合纤维毡；将混合纤维毡在针刺机上进行针刺加固，针刺速度为400～800转/分钟；
（3）从下至上依次铺设第一高密纤维层、混合纤维毡和第二高密纤维层，在针刺机上进行针刺加固，针刺速度为1000～1200转/分钟，得到纤维毯半成品；
（4）将经步骤（3）针刺加固后的纤维毯半成品置于成型模具内进行模压成型：首先上模抽真空，抽真空时间为10～20秒，压力为0.01～0.02MPa，在抽真空的同时通入高温蒸汽；保持真空度，继续通入高温蒸汽进行加热成型，蒸汽压力为0.6～2MPa，蒸汽温度为105～115℃，加热成型的压力为5～10MPa，成型时间为40～60秒；
（5）冷却：将经步骤（4）处理后的纤维毯半成品放入冷却治具，在常温下进行冷却定型，冷却时间为30～45秒；
（6）将经步骤（5）冷却后的纤维毯半成品切割成所需的外形尺寸，并在半成品上进行冲断加工得到所需要的孔，即得到纤维毯成品。
CN201510045587.2A 2015-01-29 2015-01-29 纤维毯制造工艺 Expired - Fee Related CN104665527B (zh)