CN104651742A - 一种用于金属门窗的高强度防腐不锈钢及其加工工艺 - Google Patents
一种用于金属门窗的高强度防腐不锈钢及其加工工艺 Download PDFInfo
- Publication number
- CN104651742A CN104651742A CN201510065940.3A CN201510065940A CN104651742A CN 104651742 A CN104651742 A CN 104651742A CN 201510065940 A CN201510065940 A CN 201510065940A CN 104651742 A CN104651742 A CN 104651742A
- Authority
- CN
- China
- Prior art keywords
- cooled
- stainless steel
- cooling
- parts
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例 | 抗拉强度,MPa | 屈服强度,MPa | 延伸率,% | 厚度方向断面收缩率,% | -20℃夏比冲击功,J | CLR, % | CTR, % | CSR,% | SSC |
实施例1 | 347 | 214 | 33 | 60.0 | 225 | 0 | 0 | 0 | 无裂纹 |
实施例2 | 327 | 299 | 36 | 60.7 | 206 | 0 | 0 | 0 | 无裂纹 |
实施例3 | 372 | 235 | 39.5 | 70.0 | 232 | 0 | 0 | 0 | 无裂纹 |
Claims (8)