CN104650516A - 丙烯酸酯橡胶的硫化工艺 - Google Patents
丙烯酸酯橡胶的硫化工艺 Download PDFInfo
- Publication number
- CN104650516A CN104650516A CN201310578788.XA CN201310578788A CN104650516A CN 104650516 A CN104650516 A CN 104650516A CN 201310578788 A CN201310578788 A CN 201310578788A CN 104650516 A CN104650516 A CN 104650516A
- Authority
- CN
- China
- Prior art keywords
- rubber
- acrylic ester
- sulfuration
- carbon black
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种丙烯酸酯橡胶的硫化工艺，它包括以下步骤：一、将生胶放入双辊开炼机中进行生胶压合，加入二甲基硅油、硬脂酸、防老剂和炭黑，将炭黑混入生胶，加入硫磺，在双辊上打三角包5次，薄通3次，下料，出片，过水，冷风吹干；二、将混炼胶放置24h，用平板硫化机在175℃下硫化2h，然后放在老化箱中在165℃-175℃下老化3-4h。本发明提供的丙烯酸酯橡胶的硫化工艺，操作简单，所得丙烯酸酯橡胶性能与国外先进产品性能相接近。
Description
技术领域
本发明涉及一种橡胶的硫化工艺，具体涉及一种丙烯酸酯橡胶的硫化工艺。
背景技术
丙烯酸酯橡胶是以丙烯酸酯为主单体经共聚而成的弹性体，具有许多优异的特点，如耐热、耐老化、耐油、耐臭氧、抗紫外线等。被广泛应用于各种高温、耐油环境中，成为近年来汽车工业着重开发推广的一种密封材料，尤其是要求在耐高温耐油环境下使用的密封件。丙烯酸酯橡胶的硫化是影响其综合性能的重要工序。
发明内容
本发明的目的在于，提供一种丙烯酸酯橡胶的硫化工艺，操作简单，所得丙烯酸酯橡胶性能与国外先进产品性能相接近。
所述丙烯酸酯橡胶的硫化工艺，它包括以下步骤：
一、将生胶放入双辊开炼机中进行生胶压合，加入二甲基硅油、硬脂酸、防老剂和炭黑，将炭黑混入生胶，加入硫磺，在双辊上打三角包5次，薄通3次，下料，出片，过水，冷风吹干；
二、将混炼胶放置24h，用平板硫化机在175℃下硫化2h，然后放在老化箱中在165℃-175℃下老化3-4h。
本发明提供的丙烯酸酯橡胶的硫化工艺，其有益效果在于，操作简单，所得丙烯酸酯橡胶性能与国外先进产品性能相接近。
具体实施方式
下面结合一个实施例，对本发明提供的丙烯酸酯橡胶的硫化工艺进行详细的说明。
实施例
一、将生胶放入双辊开炼机中进行生胶压合，加入二甲基硅油、硬脂酸、防老剂和炭黑，将炭黑混入生胶，加入硫磺，在双辊上打三角包5次，薄通3次，下料，出片，过水，冷风吹干；
二、将混炼胶放置24h，用平板硫化机在175℃下硫化2h，然后放在老化箱中在165℃下老化4h。
Claims (1)
1.一种丙烯酸酯橡胶的硫化工艺，其特征在于：它包括以下步骤：
一、将生胶放入双辊开炼机中进行生胶压合，加入二甲基硅油、硬脂酸、防老剂和炭黑，将炭黑混入生胶，加入硫磺，在双辊上打三角包5次，薄通3次，下料，出片，过水，冷风吹干；
二、将混炼胶放置24h，用平板硫化机在175℃下硫化2h，然后放在老化箱中在165℃-175℃下老化3-4h。