CN104649693A - 一种真空感应炉衬用耐火材料 - Google Patents

一种真空感应炉衬用耐火材料 Download PDF

Info

Publication number
CN104649693A
CN104649693A CN201510056654.0A CN201510056654A CN104649693A CN 104649693 A CN104649693 A CN 104649693A CN 201510056654 A CN201510056654 A CN 201510056654A CN 104649693 A CN104649693 A CN 104649693A
Authority
CN
China
Prior art keywords
parts
granularity
furnace lining
vacuum induction
induction furnace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510056654.0A
Other languages
English (en)
Inventor
王相丰
裘伟
王维
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Haicheng City Jin Fu Cutting Edge Of A Knife Or A Sword Science And Technology Ltd
Original Assignee
Haicheng City Jin Fu Cutting Edge Of A Knife Or A Sword Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Haicheng City Jin Fu Cutting Edge Of A Knife Or A Sword Science And Technology Ltd filed Critical Haicheng City Jin Fu Cutting Edge Of A Knife Or A Sword Science And Technology Ltd
Priority to CN201510056654.0A priority Critical patent/CN104649693A/zh
Publication of CN104649693A publication Critical patent/CN104649693A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种真空感应炉衬用耐火材料，其成分按重量份配比组成：电熔白刚玉60-80份、电熔镁砂10-25份、ɑ-Al2O3粉5-15份、结合剂3-7份。所述的结合剂为硼酸和染料级氧化铬绿其中一种或两种组合。所述的电熔白刚玉粒度组成以重量份计：6-3mm20-30份，3-1mm15-25份，1-0mm15-25份，200目细粉 5-15份。所述的电熔镁砂粒度组成以重量份计：6-3mm5-15份，3-1mm5-15份，1-0mm5-15份。所述的ɑ-Al2O3粉粒度为325目。本发明一种真空感应炉衬用耐火材料的抗侵蚀能力有显著提升，良好的抗热震性和抗渣性减少了侵蚀坩埚，很大程度的提高抗剥落次数，产品具有质量稳定可靠，性能好，使用寿命长的特点。

Description

一种真空感应炉衬用耐火材料
技术领域
本发明涉及黑色冶金及有色冶金领域，特别涉及一种真空感应炉衬用耐火材料。
背景技术
真空感应炉主要应用于冶炼铜、高温合金和特种合金等。其具有没有空气和炉渣污染，冶炼的合金等纯净，性能水平高、熔炼出的钢和合金气体含量低、金属不易氧化、能准确的调整和控制化学成分、可以使用返回料等特点。目前，国内外所用真空感应炉衬主要有刚玉质炉衬材料、镁砂炉衬、石英砂炉衬、铝矾土炉衬等。其在使用效果上一直不是很理想，使用寿命短、侵蚀坩埚。我国在真空感应炉炉衬的耐材，大多都为进口，一直缺席“真空感应炉炉衬用耐火材料”领域。始终落后于欧洲等发达国家。
发明内容
本发明所要解决的技术问题是提供一种真空感应炉衬用耐火材料，抗侵蚀能力强，使用寿命长，减少侵蚀坩埚。
为实现上述目的，本发明采用以下技术方案实现：
一种真空感应炉衬用耐火材料，其成分按重量份配比组成：电熔白刚玉60-80份、电熔镁砂10-25份、ɑ-Al2O3粉5-15份、结合剂3-7份。
所述的结合剂为硼酸和染料级氧化铬绿其中一种或两种组合。
所述的电熔白刚玉粒度组成以重量份计：6-3mm 20-30份，3-1mm 15-25份，1-0㎜15-25份，200目细粉5-15份。
所述的电熔镁砂粒度组成以重量份计：6-3mm 5-15份，3-1mm 5-15份，1-0㎜5-15份。
所述的ɑ-Al2O3粉粒度为325目。
所述的真空感应炉衬用耐火材料其成品理化指标为：
与现有的技术相比，本发明的有益效果是：
本发明一种真空感应炉衬用耐火材料的抗侵蚀能力有显著提升，良好的抗热震性和抗渣性减少了侵蚀坩埚，很大程度的提高抗剥落次数，产品具有质量稳定可靠，性能好，使用寿命长的特点。
具体实施方式
下面结合实施例对本发明进一步说明：
以下实施例对本发明进行详细描述。这些实施例仅是对本发明的最佳实施方案进行描述，并不对本发明的范围进行限制。
实施例1：
一种真空感应炉衬用耐火材料，其成分按重量份配比组成：优质电熔白刚玉(Al2O3≥99.0％)60份，优质电熔镁砂(MgO≥98.0％)25份，优质ɑ-Al2O3粉(Al2O3≥99.0％)15份。结合剂硼酸4份。
将优质电熔白刚玉加工成粒度6-3mm、3-1mm、1-0㎜的产品，并抽出优质电熔白刚玉部分1-0㎜磨成200目细粉。粒度组成以重量份计：6-3mm 20份、3-1mm 15份、1-0㎜15份，200目细粉10份。
将优质电熔镁砂加工成粒度6-3mm、3-1mm、1-0㎜的产品。粒度组成以重量份计：6-3mm10份、3-1mm 10份、1-0㎜5份。
将优质ɑ-Al2O3加工磨成粒度325目的产品。
然后将上述原料按照配比搅拌混合均匀，最后成品装袋。
实施例2：
一种真空感应炉衬用耐火材料，其成分按重量份配比组成：优质电熔白刚玉(Al2O3≥99.0％)75份，优质电熔镁砂(MgO≥98.0％)20份，优质ɑ-Al2O3粉(Al2O3≥99.0％)5份。结合剂染料级氧化铬绿5份。
将优质电熔白刚玉加工成粒度6-3mm、3-1mm、1-0㎜的产品，并抽出优质电熔白刚玉部分1-0㎜磨成200目细粉。粒度组成以重量份计：6-3mm 25份、3-1mm 20份、1-0㎜20份，200目细粉10份。
将优质电熔镁砂加工成粒度6-3mm、3-1mm、1-0㎜的产品。粒度组成以重量份计：6-3mm10份、3-1mm 5份、1-0㎜5份。
将优质ɑ-Al2O3加工细磨成粒度325目的产品。
然后将上述原料按照配比搅拌混合均匀，最后成品装袋。
实施例3：
一种真空感应炉衬用耐火材料，其成分按重量份配比组成：优质电熔白刚玉(Al2O3≥99.0％)80份，优质电熔镁砂(MgO≥98.0％)10份，优质ɑ-Al2O3粉(Al2O3≥99.0％)10份。结合剂硼酸和染料级氧化铬绿按重量份1:1混合物外加6份。
将优质电熔白刚玉加工成粒度6-3mm、3-1mm、1-0㎜的产品，并抽出优质电熔白刚玉部分1-0㎜磨成200目细粉。粒度组成以重量份计：6-3mm 25份、3-1mm 25份、1-0㎜20份，200目细粉10份。
将优质电熔镁砂加工成粒度6-3mm、3-1mm、1-0㎜的产品。粒度组成以重量份计：6-3mm3份、3-1mm 3份、1-0㎜4份。
将优质ɑ-Al2O3加工细磨成粒度325目的产品。
然后将上述原料按照配比搅拌混合均匀，最后成品装袋。
上述实施例真空感应炉衬用耐火材料其成品理化指标为：

Claims (6)

1.一种真空感应炉衬用耐火材料，其特征在于，其成分按重量份配比组成：电熔白刚玉60-80份、电熔镁砂10-25份、ɑ-Al2O3粉5-15份、结合剂3-7份。
2.根据权利要求1所述的一种真空感应炉衬用耐火材料，其特征在于，所述的结合剂为硼酸和染料级氧化铬绿其中一种或两种组合。
3.根据权利要求1所述的一种真空感应炉衬用耐火材料，其特征在于，所述的电熔白刚玉粒度组成以重量份计：6-3mm 20-30份，3-1mm 15-25份，1-0㎜15-25份，200目细粉5-15份。
4.根据权利要求1所述的一种真空感应炉衬用耐火材料，其特征在于，所述的电熔镁砂粒度组成以重量份计：6-3mm 5-15份，3-1mm 5-15份，1-0㎜5-15份。
5.根据权利要求1所述的一种真空感应炉衬用耐火材料，其特征在于，所述的ɑ-Al2O3粉粒度为325目。
6.根据权利要求1所述的一种真空感应炉衬用耐火材料，其特征在于，所述的真空感应炉衬用耐火材料其成品理化指标为：
CN201510056654.0A 2015-02-03 2015-02-03 一种真空感应炉衬用耐火材料 Pending CN104649693A (zh)