CN105218119A - 一种再生铁沟浇注料 - Google Patents

一种再生铁沟浇注料 Download PDF

Info

Publication number
CN105218119A
CN105218119A CN201510717501.6A CN201510717501A CN105218119A CN 105218119 A CN105218119 A CN 105218119A CN 201510717501 A CN201510717501 A CN 201510717501A CN 105218119 A CN105218119 A CN 105218119A
Authority
CN
China
Prior art keywords
parts
component
pig iron
iron pouring
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510717501.6A
Other languages
English (en)
Inventor
佘云锋
佘成其
吴建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGXING FURNACE MATERIAL Co Ltd
Original Assignee
CHANGXING FURNACE MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGXING FURNACE MATERIAL Co Ltd filed Critical CHANGXING FURNACE MATERIAL Co Ltd
Priority to CN201510717501.6A priority Critical patent/CN105218119A/zh
Publication of CN105218119A publication Critical patent/CN105218119A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种再生铁沟浇注料，利用廉价的主要成分为刚玉，高铝矾土和碳素材料的滑板磨削废料制造出成本低的铁沟浇注料，显著降低了铁沟料的显气孔率，提高体积密度和抗折强度，增强了抗渣性能，铁沟浇注料中复合硅溶胶-聚丙烯酸钠作为结合剂使铁沟料在高温时形成大量形态各异的网状莫来石晶体，网状分错在结构中，提高了高温抗折强度，增强铁沟料的常温耐压强度，提高了施工性能，其性能和现用的铁沟料持平，但价格仅仅为它的85％，符合清洁生产和循环经济的发展要求。

Description

一种再生铁沟浇注料
【技术领域】
本发明涉及金属冶炼的技术领域，特别是一种再生铁沟浇注料的技术领域。
【背景技术】
高炉出铁沟是引导高温铁水和熔渣并使之充分分离的通道，其所使用耐材的寿命，直接影响高炉的正常生产。目前出铁沟组织疏松、抗氧化查、通铁量低，出铁沟三天一小修，五天一大修，重复修钩次数多，工人劳动强度大，出铁沟使用时间短。经常影响高炉正点出铁，给高炉生产带来不便。随着高炉强化冶炼和高炉操作技术的不断进步，高炉利用系数和出铁次数不断增多，出铁沟耐火材料的使用条件日益苛刻。对出铁沟用材料安全使用、长寿的要求越来越高。相应的铁沟浇注料的成本也急剧增加。
近年来，随着钢铁行业的持续低迷，各钢铁企业降低成本的压力剧增，耐火材料也成为钢铁行业将本增效的重要环节。另外，许多耐火企业每年的滑板生产中会产生大量的滑板磨削废料，随意堆放造成了资源的浪费与环境的破坏。
【发明内容】
本发明的目的就是解决现有技术中的问题，提出一种再生铁沟浇注料，利用廉价的滑板磨削废料制造出成本低的铁沟浇注料，有效的提高了铁沟浇注料的体积密度和抗折强度，增强了抗渣性能，增强铁沟浇注料料的常温耐压强度，提高了施工性能，符合清洁生产和循环经济的发展要求。
为实现上述目的，本发明提出了一种再生铁沟浇注料，包括以下组分且各组分的质量比例为：
所述滑板磨削废料为颗粒＜0.125mm的细粉，所述滑板磨削废料的主要成分为刚玉，高铝矾土和碳素材料。
作为优选，所述红柱石原料为颗粒＜0.085mm的细粉，所述红柱石原料的纯度大于90％。
作为优选，所述碳化硅原料为颗粒＜0.095mm的细粉，所述碳化硅原料的纯度大于95％。
作为优选，所述抗氧化剂为碳化硼，所述碳化硼原料的纯度大于90％。
作为优选，所述复合微粉包括以下组分且各组分的质量比例为：氧化铝微粉：40～50份；氧化硅微粉：50～60份。
作为优选，所述复合结合剂包括以下组分且各组分的质量比例为：硅溶胶：35～40份；聚丙烯酸钠：50～60份；填充料：10～20份。
作为优选，所述分散剂包括以下组分且各组分的质量比例为：聚羧酸：30～40份；聚乙二醇：60～70份。
作为优选，各组分的质量比例为：滑板磨削废料：60份；红柱石：10份；碳化硅：11份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：10份；复合结合剂：12份；分散剂：1份。
作为优选，各组分的质量比例为：滑板磨削废料：65份；红柱石：15份；碳化硅：12份；抗氧化剂：6份；聚丙烯纤维：1份；复合微粉：14份；复合结合剂：11份；分散剂：1份。
作为优选，各组分的质量比例为：滑板磨削废料：70份；红柱石：17份；碳化硅：12份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：16份；复合结合剂：14份；分散剂：2份。
本发明的有益效果：本发明利用廉价的主要成分为刚玉，高铝矾土和碳素材料的滑板磨削废料制造出成本低的铁沟浇注料，铁沟浇注料加入滑板磨削废料，可以填充间隙，显著降低了铁沟料的显气孔率，提高体积密度和抗折强度，增强了抗渣性能，铁沟浇注料中复合硅溶胶-聚丙烯酸钠作为结合剂使铁沟料在高温时形成大量形态各异的网状莫来石晶体，网状分错在结构中，提高了高温抗折强度；另一方面聚丙烯酸钠可以起到减水剂的作用，增强铁沟料的常温耐压强度，提高了施工性能。本发明在重钢在2500m3高炉上使用，通铁量达到了15万吨以上，其性能和现用的铁沟料持平，但价格仅仅为它的85％，符合清洁生产和循环经济的发展要求。未来国内25％的滑板磨削废料将通过此项技术得到综合利用，前景看好。
本发明的特征及优点将通过实施例进行详细说明。
【具体实施方式】
本发明一种再生铁沟浇注料，包括以下组分且各组分的质量比例为：
所述滑板磨削废料为颗粒＜0.125mm的细粉，所述滑板磨削废料的主要成分为刚玉，高铝矾土和碳素材料。
所述红柱石原料为颗粒＜0.085mm的细粉，所述红柱石原料的纯度大于90％。
所述碳化硅原料为颗粒＜0.095mm的细粉，所述碳化硅原料的纯度大于95％。
所述抗氧化剂为碳化硼，所述碳化硼原料的纯度大于90％。
所述复合微粉包括以下组分且各组分的质量比例为：氧化铝微粉：40～50份；氧化硅微粉：50～60份。
所述复合结合剂包括以下组分且各组分的质量比例为：硅溶胶：35～40份；聚丙烯酸钠：50～60份；填充料：10～20份。
所述分散剂包括以下组分且各组分的质量比例为：聚羧酸：30～40份；聚乙二醇：60～70份。
实施例一：滑板磨削废料：60份；红柱石：10份；碳化硅：11份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：10份；复合结合剂：12份；分散剂：1份。
实施例二：滑板磨削废料：65份；红柱石：15份；碳化硅：12份；抗氧化剂：6份；聚丙烯纤维：1份；复合微粉：14份；复合结合剂：11份；分散剂：1份。
实施例三：滑板磨削废料：70份；红柱石：17份；碳化硅：12份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：16份；复合结合剂：14份；分散剂：2份。
本发明利用廉价的主要成分为刚玉，高铝矾土和碳素材料的滑板磨削废料制造出成本低的铁沟浇注料，铁沟浇注料加入滑板磨削废料，可以填充间隙，显著降低了铁沟料的显气孔率，提高体积密度和抗折强度，增强了抗渣性能，铁沟浇注料中复合硅溶胶-聚丙烯酸钠作为结合剂使铁沟料在高温时形成大量形态各异的网状莫来石晶体，网状分错在结构中，提高了高温抗折强度；另一方面聚丙烯酸钠可以起到减水剂的作用，增强铁沟料的常温耐压强度，提高了施工性能。本发明在重钢在2500m3高炉上使用，通铁量达到了15万吨以上，其性能和现用的铁沟料持平，但价格仅仅为它的85％，符合清洁生产和循环经济的发展要求。未来国内25％的滑板磨削废料将通过此项技术得到综合利用，前景看好。
上述实施例是对本发明的说明，不是对本发明的限定，任何对本发明简单变换后的方案均属于本发明的保护范围。

Claims (10)

1.一种再生铁沟浇注料，其特征在于：包括以下组分且各组分的质量比例为：
所述滑板磨削废料为颗粒＜0.125mm的细粉，所述滑板磨削废料的主要成分为刚玉，高铝矾土和碳素材料。
2.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述红柱石原料为颗粒＜0.085mm的细粉，所述红柱石原料的纯度大于90％。
3.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述碳化硅原料为颗粒＜0.095mm的细粉，所述碳化硅原料的纯度大于95％。
4.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述抗氧化剂为碳化硼，所述碳化硼原料的纯度大于90％。
5.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述复合微粉包括以下组分且各组分的质量比例为：氧化铝微粉：40～50份；氧化硅微粉：50～60份。
6.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述复合结合剂包括以下组分且各组分的质量比例为：硅溶胶：35～40份；聚丙烯酸钠：50～60份；填充料：10～20份。
7.如权利要求1所述的一种再生铁沟浇注料，其特征在于：所述分散剂包括以下组分且各组分的质量比例为：聚羧酸：30～40份；聚乙二醇：60～70份。
8.如权利要求1所述的一种再生铁沟浇注料，其特征在于：包括以下组分且各组分的质量比例为：滑板磨削废料：60份；红柱石：10份；碳化硅：11份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：10份；复合结合剂：12份；分散剂：1份。
9.如权利要求1所述的一种再生铁沟浇注料，其特征在于：包括以下组分且各组分的分数比例为：滑板磨削废料：65份；红柱石：15份；碳化硅：12份；抗氧化剂：6份；聚丙烯纤维：1份；复合微粉：14份；复合结合剂：11份；分散剂：1份。
10.如权利要求1所述的一种再生铁沟浇注料，其特征在于：包括以下组分且各组分的分数比例为：滑板磨削废料：70份；红柱石：17份；碳化硅：12份；抗氧化剂：5份；聚丙烯纤维：1份；复合微粉：16份；复合结合剂：14份；分散剂：2份。
CN201510717501.6A 2015-10-29 2015-10-29 一种再生铁沟浇注料 Pending CN105218119A (zh)