CN104649645A - Coating composition - Google Patents
Coating composition Download PDFInfo
- Publication number
- CN104649645A CN104649645A CN201410260114.XA CN201410260114A CN104649645A CN 104649645 A CN104649645 A CN 104649645A CN 201410260114 A CN201410260114 A CN 201410260114A CN 104649645 A CN104649645 A CN 104649645A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating composition
- fineness
- powder
- meshes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating composition and belongs to the technical field of building materials. The coating composition is prepared from the following raw materials in parts by weight: 51-54 parts of calcium carbide powder having the fineness of 2000-2500 meshes, 25-27 parts of zirconium dioxide powder having the fineness of 2000-2500 meshes, 16-18 parts of photocatalyst active titanium dioxide powder having the fineness of 2000-2500 meshes, 40-45 parts of potassium silicate solution having the modulus of 2.8, 0.6-0.8 part of hydrophobic silicon auxiliary, 18-22 parts of acrylic emulsion and 27-30 parts of hydroxyethyl cellulose. The coating composition has the functions of antibiosis, pollution prevention and deodorization, and also has the effects of removing formaldehyde and purifying the indoor environment.
Description
Technical field
The invention belongs to building material technical field, particularly relate to a kind of coating composition of interior architecture.
Background technology
Coating is a kind of material, and this material can be coated in article surface by different construction technologies, form adhere well, there is some strength, continuously, the solid film of protection or decoration.The film of such formation is referred to as film usually, also known as paint film or coating.
In recent years, along with the raising of people's living standard, people more and more focus on the indoor environmental quality of living, also more and more higher to its requirement.Wherein, due to be generally used for interior architecture coating in be rich in the nutritive ingredient of microorganism growth, the humiture of indoor environment is applicable to microbe survival, mouldy, metachromatism will be there is in its interior architecture surface scribbling coating because of the amount reproduction of microorganism, thus generation peculiar smell, destroying the composition of coating, is that this coating loses its original function.For this reason, someone have studied the coating that some have the function of antibacterial, antifouling, deodorizing, but its effect is not so good.
Summary of the invention
The invention provides a kind of coating composition, this coating composition has the function of good antibacterial, antifouling, deodorizing.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of coating composition, be made up of the raw material of following parts by weight: fineness is 51 parts ~ 54 parts, 2000 order ~ 2500 object carbide of calcium powder, fineness is 2000 order ~ 2500 object Zirconium dioxide powder 25 parts ~ 27 parts, fineness is 2000 order ~ 2500 object photocatalyst activity titania powder 16 parts ~ 18 parts, modulus is the potassium silicate solution 40 parts ~ 45 parts of 2.8, hydrophobic type silicon additive 0.6 part ~ 0.8 part, ACRYLIC EMULSION 18 ~ 22 parts, Natvosol 27 parts ~ 30 parts.
Owing to adopting technique scheme, the beneficial effect that the present invention obtains is:
Coating composition of the present invention not only has function that is antibacterial, antifouling, deodorizing, also has the effect except formaldehyde and decontamination chamber's environment.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only confined to following examples.
Embodiment 1
A kind of coating composition, be made up of the raw material of following weight: fineness is 2000 object carbide of calcium powder 5.1kg, fineness is 2000 object Zirconium dioxide powder 2.7kg, fineness is 2000 object photocatalyst activity titania powder 1.6kg, modulus is the potassium silicate solution 4.5kg of 2.8, hydrophobic type silicon additive 0.06kg, ACRYLIC EMULSION 1.8kg, Natvosol 3.0kg.
The preparation method of this coating composition is: by above-mentioned raw materials weight, by carbide of calcium powder, Zirconium dioxide powder, photocatalyst activity titania powder, mixes and joins in potassium silicate solution, adds hydrophobic type silicon additive wherein, stir, add Walocel MT 20.000PV and ACRYLIC EMULSION again, stir.
The present embodiment coating composition is carried out the effect experimental of formaldehyde clearance, its formaldehyde clearance 90%.
The present embodiment coating composition is coated in animal sliced meat surface as test group, does blank group with allogenic animal sliced meat; Test under test group and blank group being placed in the environment of 25 DEG C ~ 30 DEG C, find that the present embodiment coating composition has significant germ resistance.
Embodiment 2
A kind of coating composition, be made up of the raw material of following weight: fineness is 2200 object carbide of calcium powder 5.4kg, fineness is 2200 object Zirconium dioxide powder 2.5kg, fineness is 2200 object photocatalyst activity titania powder 1.8kg, modulus is the potassium silicate solution 4.0kg of 2.8, hydrophobic type silicon additive 0.08kg, ACRYLIC EMULSION 2.2kg, Natvosol 2.7kg.
The preparation method of this coating composition is: by above-mentioned raw materials weight, by carbide of calcium powder, Zirconium dioxide powder, photocatalyst activity titania powder, mixes and joins in potassium silicate solution, adds hydrophobic type silicon additive wherein, stir, add Walocel MT 20.000PV and ACRYLIC EMULSION again, stir.
The present embodiment coating composition is carried out the effect experimental of formaldehyde clearance, its formaldehyde clearance 95%.
The present embodiment coating composition is coated in animal sliced meat surface as test group, does blank group with allogenic animal sliced meat; Test under test group and blank group being placed in the environment of 25 DEG C ~ 30 DEG C, find that the present embodiment coating composition has significant germ resistance.
Embodiment 3
A kind of coating composition, be made up of the raw material of following weight: fineness is 2500 object carbide of calcium powder 5.3kg, fineness is 2500 object Zirconium dioxide powder 2.6kg, fineness is 2500 object photocatalyst activity titania powder 1.7kg, modulus is the potassium silicate solution 4.3kg of 2.8, hydrophobic type silicon additive 0.07kg, ACRYLIC EMULSION 2.0kg, Natvosol 2.8kg.
The preparation method of this coating composition is: by above-mentioned raw materials weight, by carbide of calcium powder, Zirconium dioxide powder, photocatalyst activity titania powder, mixes and joins in potassium silicate solution, adds hydrophobic type silicon additive wherein, stir, add Walocel MT 20.000PV and ACRYLIC EMULSION again, stir.
The present embodiment coating composition is carried out the effect experimental of formaldehyde clearance, its formaldehyde clearance 92.5%.
The present embodiment coating composition is coated in animal sliced meat surface as test group, does blank group with allogenic animal sliced meat; Test under test group and blank group being placed in the environment of 25 DEG C ~ 30 DEG C, find that the present embodiment coating composition has significant germ resistance.
Claims (1)
1. a coating composition, its feature is made at the raw material by following parts by weight:
Fineness is 51 parts ~ 54 parts, 2000 order ~ 2500 object carbide of calcium powder, fineness is 2000 order ~ 2500 object Zirconium dioxide powder 25 parts ~ 27 parts, fineness is 2000 order ~ 2500 object photocatalyst activity titania powder 16 parts ~ 18 parts, modulus is the potassium silicate solution 40 parts ~ 45 parts of 2.8, hydrophobic type silicon additive 0.6 part ~ 0.8 part, ACRYLIC EMULSION 18 ~ 22 parts, Natvosol 27 parts ~ 30 parts.