CN104629624A - Water-based single-component air-drying paint and preparation technique thereof - Google Patents
Water-based single-component air-drying paint and preparation technique thereof Download PDFInfo
- Publication number
- CN104629624A CN104629624A CN201410850301.3A CN201410850301A CN104629624A CN 104629624 A CN104629624 A CN 104629624A CN 201410850301 A CN201410850301 A CN 201410850301A CN 104629624 A CN104629624 A CN 104629624A
- Authority
- CN
- China
- Prior art keywords
- water
- drying
- paint
- air
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based single-component air-drying paint with simple technique and favorable use effect and a preparation technique thereof. The water-based single-component air-drying paint is prepared from the following raw materials: 50% of water-based resin, 10% of pigment, 3% of zinc phosphate, 0.2% of bentonite, 0.2% of gas-phase silicon dioxide, 16.5% of deionized water, 0.1% of leveling agent and the balance of clear water. The preparation technique comprises the following steps: mixing, dispersing uniformly by high-speed stirring, grinding until the particle size is less than 15 mu m, filtering and packaging. The core technique lies in the water-based air-drying paint prepared from the pigment, zinc phosphate, deionized water and assistants. The film forming matter acrylic acid component in the water-based paint solves the problems of water solubility and dryness; the epoxy component enhances the adhesion and water resistance; the polyurethane component enhances the physiochemical properties of the film forming material; the phosphate can form a complex with metals; and thus, the water-based paint solves the problems of high susceptibility to the temperature and humidity in the room-temperature air-drying process of the domestic and foreign water-based room-temperature air-drying paints.
Description
Technical field
The present invention relates to a kind of formula of self-drying paint, the formula of the water-based mono-component self-drying paint that especially a kind of technique is simple, result of use is good and preparation technology thereof.
Background technology
Require that temperature is higher than 5 DEG C at present during waterborne normal-temperature self-drying paint construction both at home and abroad, humidity, not higher than 85, uses limitation stronger.
Summary of the invention
For solving the problem, based on above-mentioned background, the invention provides formula and the preparation technology thereof of a kind of water-based mono-component self-drying paint that a kind of technique is simple, result of use is good, its raw material form and per-cent as follows: water-base resin 50%, pigment 10%, zinc phosphate 3%, wilkinite 0.2%, aerosil 0.2%, deionized water 16.5%, 0.1 flow agent, clear water surplus.
Its preparation technology is as follows: mixing, and high-speed stirring is uniformly dispersed, and is ground to and is less than 15um, filters, packaging.
The core technology of this patent is with the addition of: the aqueous self-drying paint that pigment, zinc phosphate, deionized water, auxiliary agent are made, in this kind of sealing wax, filmogen vinylformic acid composition solves water-soluble and dryness, epoxy composition increases sticking power and water tolerance, urethane composition increases the physicochemical property of film forming matter, phosphoric acid ester can form complex compound with metal, when therefore solving domestic and international waterborne normal-temperature self-drying paint dry during this sealing wax normal temperature self-drying, by the problem that temperature and humidity affects.
Embodiment
The formula of a kind of water-based mono-component self-drying paint that a kind of technique is simple, result of use is good and preparation technology thereof, its raw material form and per-cent as follows: water-base resin 50%, pigment 10%, zinc phosphate 3%, wilkinite 0.2%, aerosil 0.2%, deionized water 16.5%, 0.1 flow agent, clear water surplus.
Its preparation technology is as follows: mixing, and high-speed stirring is uniformly dispersed, and is ground to and is less than 15um, filters, packaging.
The core technology of this patent is with the addition of: the aqueous self-drying paint that pigment, zinc phosphate, deionized water, auxiliary agent are made, in this kind of sealing wax, filmogen vinylformic acid composition solves water-soluble and dryness, epoxy composition increases sticking power and water tolerance, urethane composition increases the physicochemical property of film forming matter, phosphoric acid ester can form complex compound with metal, when therefore solving domestic and international waterborne normal-temperature self-drying paint dry during this sealing wax normal temperature self-drying, by the problem that temperature and humidity affects.
Embodiment recited above is only be described the preferred embodiment of the present invention; not scope of the present invention is limited; do not departing under the present invention designs spiritual prerequisite; the various distortion that the common engineering technical personnel in this area make technical solution of the present invention and improvement, all should fall in protection domain that claims of the present invention determine.
Claims (2)
1. the formula of water-based mono-component self-drying paint and a preparation technology thereof, is characterized in that, its raw material form and per-cent as follows: water-base resin 50%, pigment 10%, zinc phosphate 3%, wilkinite 0.2%, aerosil 0.2%, deionized water 16.5%, 0.1 flow agent, clear water surplus.
2. the formula of a kind of water-based mono-component self-drying paint according to claim 1 and preparation technology thereof, it is characterized in that, its preparation technology is as follows: mixing, and high-speed stirring is uniformly dispersed, and is ground to and is less than 15um, filters, packaging.