CN104629442A

CN104629442A - Formula of chocolate-color wheat straw dye and production method thereof

Info

Publication number: CN104629442A
Application number: CN201310551074.XA
Authority: CN
Inventors: 马文侠
Original assignee: Harbin Arts and Crafts Co Ltd
Current assignee: Harbin Arts and Crafts Co Ltd
Priority date: 2013-11-10
Filing date: 2013-11-10
Publication date: 2015-05-20

Abstract

The invention discloses a formula of chocolate-color wheat straw dye and a production method thereof. The dye is mainly composed of beet root, an antimony ion solution, black flower, alum, an iron ion compound solution, and mineral water. The main procedure of dyed wheat straw production comprises the following steps: material choosing, material cutting, drying, soaking, boiling, mixing, precipitating, dyeing, and finishing. The dye is prepared from pure natural plants, is natural, pollution-free, green, and environment-friendly, and does not have any side or toxic effect to human body.

Description

A kind of formula and production method preparing chocolate wheat straw dye

technical field:

the present invention relates to a kind of vegetable dye, particularly relates to a kind of formula and the production method of preparing chocolate wheat straw dye

background technology:

in prior art, the method that the main raw material Wheat Straw making straw patchwork dyes chocolate is had a variety of, but most dyestuff is chemical dye, the chocolate dyed is impure, easily fade, not only not environmentally, some dyes even can produce toxic gas in the process of dye system, threatens the health of human body.

thus, make field at straw patchwork and lack a kind of vegetable dye Wheat Straw being dyed different colours, particularly Wheat Straw is dyed the natural plant dyestuff of chocolate, not only color is pure for the chocolate Wheat Straw that it dyes, and the straw patchwork made with its material is bright and new beautiful, not easily fades, and environmental protection, works give out plant fragrance for a long time, have the physical and mental health of easy people, and what degree was different solves other poisonous and harmful chemical dye in dye process processed to the prestige evil that people's health causes.

summary of the invention:

the object of the present invention is to provide a kind of pure natural, pollution-free, environmental protection, a kind of formula and the production method preparing chocolate wheat straw dye be mixed with natural plant that the person is had no side effect.

the object of the present invention is achieved like this.It is that the raw material of being joined by following weight is made, beet tails 10-30 part, antimony ion solution 10-30 part, black colored 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

the formula optimization weight proportion scope preparing chocolate wheat straw dye of the present invention is, wherein the weight proportion of various raw material is beet tails 10-25 part, antimony ion solution 10-25 part, black colored 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

the optimum weight ratio range preparing chocolate wheat straw dye of the present invention is that wherein the weight proportion of various raw material is: beet tails 15 parts, antimony ion solution 15 parts, black spend 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

above-mentioned each component is made the production method of chocolate wheat straw dye of the present invention, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the beet tails, antimony ion solution, black flower, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material beet tails selected, black flower are cut into bulk; C, oven dry, the beet tails of the shape that is cut into small pieces, black colored raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, add antimony ion solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure chocolate cellulose solution; H, dyeing, the temperature of 100 liters of pure chocolate cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb chocolate cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to chocolate Wheat Straw finished product at room temperature.

production method advantage of the present invention is: 1, select raw material, scientific formulation, color is pure; 2, do not add sanitas in product, industrial chemicals, pure natural, to human body without any injury, the straw patchwork works made with its raw material not only distribute Scent, and anticorrosive; 3 raw material sources are extensive, add process line short, the easy processing and manufacturing of product.

Embodiment

below in conjunction with specific embodiment, the present invention is further illustrated:

embodiment 1:

the formulation weight ratio range preparing chocolate wheat straw dye of the present invention is: beet tails 10-30 part, antimony ion solution 10-30 part, black colored 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

embodiment 2:

the formula optimization weight proportion scope preparing chocolate wheat straw dye of the present invention is: beet tails 10-25 part, antimony ion solution 10-25 part, black colored 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

embodiment 3:

the formula optimum weight ratio range preparing chocolate wheat straw dye of the present invention is: wherein the weight proportion of various raw material is, beet tails 15 parts, antimony ion solution 15 parts, black spend 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

above-mentioned each component is made the production method of chocolate wheat straw dye of the present invention, technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the beet tails, antimony ion solution, black flower, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material beet tails selected, black flower are cut into bulk; C, oven dry, the beet tails of the shape that is cut into small pieces, black colored raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, add antimony ion solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure chocolate cellulose solution; H, dyeing, the temperature of 100 liters of pure chocolate cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb chocolate cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to chocolate Wheat Straw finished product at room temperature.

Claims

1. prepare the formula of chocolate wheat straw dye for one kind, it is characterized in that: it is made up of the raw material of following weight proportioning, beet tails 10-30 part, antimony ion solution 10-30 part, black colored 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

2. prepare the formula of chocolate wheat straw dye for one kind, it is characterized in that: wherein the weight proportion of various raw material is, beet tails 10-25 part, antimony ion solution 10-25 part, black colored 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

3. prepare a formula for chocolate wheat straw dye, it is characterized in that: wherein the weight proportion of various raw material is, beet tails 15 parts, antimony ion solution 15 parts, black spend 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

4. a kind of production method preparing chocolate wheat straw dye formula according to claim 1-3, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the beet tails, antimony ion solution, black flower, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material beet tails selected, black flower are cut into bulk; C, oven dry, the beet tails of the shape that is cut into small pieces, black colored raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, add antimony ion solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure chocolate cellulose solution; H, dyeing, the temperature of 100 liters of pure chocolate cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb chocolate cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to chocolate Wheat Straw finished product at room temperature.