CN104629407A

CN104629407A - Formula and production method for preparation of orange red wheat straw dye

Info

Publication number: CN104629407A
Application number: CN201310545555.XA
Authority: CN
Inventors: 马文侠
Original assignee: Harbin Arts and Crafts Co Ltd
Current assignee: Harbin Arts and Crafts Co Ltd
Priority date: 2013-11-07
Filing date: 2013-11-07
Publication date: 2015-05-20

Abstract

Provided are a formula and a production method for preparation of an orange red wheat straw dye; clove twigs, dandelion toots, alum, a ferric ion compound solution and mineral water are taken as main raw materials, and the production method comprises the main technological process of material selection, material cutting, drying, soaking, hot boiling, mixing, precipitating, dyeing, and obtaining the finished product. The formula and the production method for preparation of the orange red wheat straw dye which is pure natural, pollution-free, green and environmentally friendly, has no toxic or side effects on human bodies and is prepared from pure natural plants are provided.

Description

A kind of formula and production method preparing orange red wheat straw dye

technical field:

the present invention relates to a kind of vegetable dye, particularly relates to a kind of formula and the production method of preparing orange red wheat straw dye

background technology:

in prior art, the main raw material Wheat Straw making straw patchwork is dyed orange-red method to be had a variety of, but most dyestuff is chemical dye, what dye is orange red impure, easily fade, not only not environmentally, some dyes even can produce toxic gas in the process of dye system, threatens the health of human body.

thus, make field at straw patchwork and lack a kind of vegetable dye Wheat Straw being dyed different colours, particularly Wheat Straw is dyed orange-red natural plant dyestuff, not only color is pure for the orange red Wheat Straw that it dyes, and the straw patchwork made with its material is bright and new beautiful, not easily fades, and environmental protection, works give out plant fragrance for a long time, have the physical and mental health of easy people, and what degree was different solves other poisonous and harmful chemical dye in dye process processed to the prestige evil that people's health causes.

summary of the invention:

the object of the present invention is to provide a kind of pure natural, pollution-free, environmental protection, a kind of formula and the production method preparing orange red wheat straw dye be mixed with natural plant that the person is had no side effect

the object of the present invention is achieved like this.It is that the raw material of being joined by following weight is made, cloves branch 10-30 part, Radix Taraxaci 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

the formula optimization weight proportion scope of the orange red wheat straw dye of preparation the present invention is that wherein the weight proportion of various raw material is cloves branch 10-25 part, Radix Taraxaci 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

the optimum weight ratio range of the orange red wheat straw dye of preparation the present invention is that wherein the weight proportion of various raw material is: 15 parts, cloves branch, Radix Taraxaci 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

above-mentioned each component is made the production method of the orange red wheat straw dye of the present invention, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the cloves branch, Radix Taraxaci, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material cloves branch selected, Radix Taraxaci are cut into bulk; C, oven dry, the cloves branch of the shape that is cut into small pieces, Radix Taraxaci raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure orange red cellulose solution; H, dyeing, the temperature of 100 liters of pure orange red cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb orange red cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to orange red Wheat Straw finished product at room temperature.

production method advantage of the present invention is: 1, select raw material, scientific formulation, color is pure; 2, do not add sanitas in product, industrial chemicals, pure natural, to human body without any injury, the straw patchwork works made with its raw material not only distribute Scent, and anticorrosive; 3 raw material sources are extensive, add process line short, the easy processing and manufacturing of product.

Embodiment

below in conjunction with specific embodiment, the present invention is further illustrated:

embodiment 1:

the formulation weight ratio range of the orange red wheat straw dye of preparation the present invention is: cloves branch 10-30 part, Radix Taraxaci 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

embodiment 2:

the formula optimization weight proportion scope of the orange red wheat straw dye of preparation the present invention is: cloves branch 10-25 part, Radix Taraxaci 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

embodiment 3:

the formula optimum weight ratio range of the orange red wheat straw dye of preparation the present invention is: wherein the weight proportion of various raw material is, 15 parts, cloves branch, Radix Taraxaci 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

above-mentioned each component is made the production method of the orange red wheat straw dye of the present invention, technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the cloves branch, Radix Taraxaci, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material cloves branch selected, Radix Taraxaci are cut into bulk; C, oven dry, the cloves branch of the shape that is cut into small pieces, Radix Taraxaci raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure orange red cellulose solution; H, dyeing, the temperature of 100 liters of pure orange red cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb orange red cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to orange red Wheat Straw finished product at room temperature.

Claims

1. prepare the formula of orange red wheat straw dye for one kind, it is characterized in that: it is made up of the raw material of following weight proportioning, cloves branch 10-30 part, Radix Taraxaci 10-30 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 30-80 part.

2. prepare a formula for orange red wheat straw dye, it is characterized in that: wherein the weight proportion of various raw material is, cloves branch 10-25 part, Radix Taraxaci 10-25 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 30-70 part.

3. prepare a formula for orange red wheat straw dye, it is characterized in that: wherein the weight proportion of various raw material is, 15 parts, cloves branch, Radix Taraxaci 15 parts, alum 8 parts, ferric ion compounds solution 8 parts, mineral water 65 parts.

4. a kind of production method preparing orange red wheat straw dye formula according to claim 1-3, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat are boiled, mix, precipitate, dye, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select the cloves branch, Radix Taraxaci, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, the raw material cloves branch selected, Radix Taraxaci are cut into bulk; C, oven dry, the cloves branch of the shape that is cut into small pieces, Radix Taraxaci raw material are placed in stoving oven mummification, temperature controls at 100-120 DEG C, 30 minutes time, makes raw materials evaporate moisture content, sterilizing; D, immersion, the raw material after drying is placed in the storage tank that mineral water is housed and soaks, temperature is 20 DEG C, room, time 2-4 hour; E, heat are boiled, pulled out from water by the raw material steeped, and are put into pottery interior heat and boil, 6 hours time, cook pigment solution; F, mixing, invaded in 20% ferric ion compounds solution by pigment solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool for mixing solutions to 20 DEG C, be settled out pure orange red cellulose solution; H, dyeing, the temperature of 100 liters of pure orange red cellulose solutions is raised to more than 80 DEG C gradually, soaked wherein by Wheat Straw after sterilization, desulfurization, boiling process, constant temperature leaves standstill 12-14 hour, and Wheat Straw stirs by period up and down, Wheat Straw is made fully to absorb orange red cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution adding alum powder, soak 3-6 hour, pull out after making the abundant fixation of Wheat Straw, drench dry, be slowly dried to orange red Wheat Straw finished product at room temperature.