CN104624727A - 一种矫直弯方坯的方法 - Google Patents
一种矫直弯方坯的方法 Download PDFInfo
- Publication number
- CN104624727A CN104624727A CN201410818350.9A CN201410818350A CN104624727A CN 104624727 A CN104624727 A CN 104624727A CN 201410818350 A CN201410818350 A CN 201410818350A CN 104624727 A CN104624727 A CN 104624727A
- Authority
- CN
- China
- Prior art keywords
- billet
- square billet
- bent
- plate
- slab
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种在连铸技术领域应用对弯曲变形的方坯进行矫直的方法,尤其是一种矫直弯方坯的方法。所述的包括以下步骤:1)在弯方坯下方铺一块板坯,板坯的长度大于或等于弯方坯的长度;2)将方坯弯曲面朝上平放在板坯上,在弯方坯上铺一块或一块以上同等长度的板坯;3)板坯开始的温度在7000C以上,自然冷却至少保持压4个小时。本发明操作简单且方便,提高了连铸坯的成坯率,节约了生产成本。
Description
技术领域
本发明涉及一种在连铸技术领域应用对弯曲变形的方坯进行矫直的方法,尤其是一种矫直弯方坯的方法。
背景技术
连铸机翻转冷床是一种具有使铸坯冷却均匀、降温快、并能实现自行矫直的设备。Cr-Mo系列合金冷镦钢铸坯经过连铸机翻转冷床处理后,连铸坯经常会发生镰刀弯的情况,连铸坯弯曲变形往往是其内部结构应力集中导致的,内部结构的金相组织不同,不同金属材料的线性膨胀系数不同,而且金属材料的膨胀系数受温度的影响很大,膨胀系数受温度影响越大,连铸坯相变过程中的体积变化越大,连铸坯弯曲变形越严重。
当在上述技术条件下生产的连铸坯达不到质量要求时,往往需要将连铸坯进行精整,精整即为将达不到质量要求的弯方坯的某部分直接切掉,精整过的方坯轧制后常常因为盘轻不受客户青睐,而且坯料浪费严重,生产成本高。
发明内容
本发明所要解决的技术问题是提供一种矫直弯方坯的方法,所述能够对Cr-Mo系列合金冷镦钢连铸坯的镰刀弯部位进行矫直,以消除内部结构的不平衡应力引起的连铸坯弯曲变形,减少弯曲坯精整切废,降低坯料浪费,节约生产成本,提高用户对盘重的满意度。
为了解决上述技术问题,本发明的技术方案是这样实现的:
一种矫直弯方坯的方法,包括以下步骤:
1)在弯方坯下方铺一块板坯,板坯的长度大于或等于弯方坯的长度;
2)将方坯弯曲面朝上平放在板坯上,在弯方坯上铺一块或一块以上同等长度的板坯;
3)板坯开始的温度在7000C以上,自然冷却至少保持压4个小时。
本发明相比现有技术的有益效果:
本发明操作简单且方便,提高了连铸坯的成坯率,节约了生产成本。具体来说:
(1)连铸坯弯曲率较多,用精整方法处理弯方坯,精整切废量大,坯料浪费严重,生产8炉35CrMo,踢废率5.6%,而使用本发明生产35CrMo,没有踢废率,仅生产1个中包(8炉35CrMo钢)节约成本3.9万元。
(2)使用本发明处理弯方坯后,因精整非定尺坯数量大幅度下降,提高了用户对盘重的满意度。
附图说明
图1是本发明的流程图。
图2是采用本发明进行弯方坯矫直的结构示意图。
具体实施方式
以下结合附图对本发明作进一步地详细描述。
如图1和图2所示,一种矫直弯方坯的方法,包括以下步骤:
1)在弯方坯1下方铺一块板坯3,板坯3的长度大于或等于弯方坯1的长度;
2)将弯方坯1平放在板坯3上,在弯方坯1上铺一块或一块以上同等长度的板坯2;
3)板坯开始的温度在7000C以上,自然冷却至少保持压4个小时。
表1和表2所示为弯曲方坯及精整情况,表3所示为利用本发明处理弯曲方坯的情况。(未标明炉号生产的方坯符合质量要求)
表1 2013年7月16日生产的9炉35CrMo
表2 2013年9月4日生产8炉35CrMo
表3 2013年10月17日生产8炉35CrMo
由表1、表2及表3看出,采用本发明处理弯曲方坯与精整处理弯曲方坯相比有如下优点:矫直弯方坯操作方便,弯曲方坯切废率低,有效地降低了生产成本,提高了经济效益。
综上所述,以上仅为本发明的较佳实施例而已,并非用于限定本发明的保护范围。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (1)
1.一种矫直弯方坯的方法,其特征在于:该方法包括以下步骤:
1)在弯方坯下方铺一块板坯,板坯的长度大于或等于弯方坯的长度;
2)将方坯弯曲面朝上平放在板坯上,在弯方坯上铺一块或一块以上同等长度的板坯;
3)板坯开始的温度在7000C以上,自然冷却至少保持压4个小时。