CN104593554A - 一种绿色环保淬火剂及其制备方法 - Google Patents
一种绿色环保淬火剂及其制备方法 Download PDFInfo
- Publication number
- CN104593554A CN104593554A CN201510011060.8A CN201510011060A CN104593554A CN 104593554 A CN104593554 A CN 104593554A CN 201510011060 A CN201510011060 A CN 201510011060A CN 104593554 A CN104593554 A CN 104593554A
- Authority
- CN
- China
- Prior art keywords
- sodium
- parts
- add
- stir
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种绿色环保淬火剂,其特征是由下述重量份的原料制得:魔芋胶1-2,黄原胶1-2,马铃薯淀粉3-5,柠檬酸1-2,黄腐酸0.05-0.1,山梨醇0.5-1,辛酸/癸酸甘油三酯0.3-0.5,椰油酰甘氨酸钠0.5-1,聚丙烯酸钠0.5-1,酒石酸钾钠0.3-0.5,氯化钠3-5,助剂3-5,水70-80。本发明的淬火剂冷却性能好,能有效减少工件的淬火变形,避免淬裂;性质稳定、无异味、带出量小、不易变质,且无毒无害,绿色环保,节能减排,符合环保产业政策的要求。
Description
技术领域
本发明涉及热处理技术,具体涉及一种绿色环保淬火剂及其制备方法。
背景技术
淬火是将金属工件加热到相变温度以上,保温后在淬火介质中急剧冷却得到马氏体组织的过程。通过淬火工艺,能达到提高或调整工件的硬度以及耐磨性等目的。在这个过程中对淬火介质(淬火剂)的要求是应避免工件变形和开裂;淬火剂易于清洗,不污染以及腐蚀工件表面;性能稳定,耐高温、耐老化、不容易变质;便于配制、运输和储存,使用安全;原材料易得,成本低廉。
通常,淬火剂按组成分为油基型和水基型两大类。油基型淬火剂目前较为通用,其缺点是油品冷却速度慢,淬火效果差且易燃等,同时由于油价较高,并且对环境有一定负面影响,其局限性较为明显。而水基型淬火剂具有安全,环保,使用寿命长,使用成本低等优点,逐渐成为热处理行业的首选淬火介质。然而水基型淬火剂还有水冷却速度快,容易导致工件开裂等局限性,需要通过调整淬火剂的组成成分来克服以上问题。
发明内容
本发明的目的是提供一种绿色环保淬火剂。
本发明是通过以下技术方案实现的:
一种绿色环保淬火剂,其特征在于,其是由下述重量份的原料制得:
魔芋胶1-2,黄原胶1-2,马铃薯淀粉3-5,柠檬酸1-2,黄腐酸0.05-0.1,山梨醇0.5-1,辛酸/癸酸甘油三酯0.3-0.5,椰油酰甘氨酸钠0.5-1,聚丙烯酸钠0.5-1,酒石酸钾钠0.3-0.5,氯化钠3-5,助剂3-5,水70-80;
其中助剂由下列重量份的原料制成:
鲜猪骨粉15-20,月桂酰肌氨酸钠1-2,十二烷基葡糖苷1-2,山梨醇酐单油酸酯0.5-1,乙二胺四乙酸钠1-2,葡萄糖酸钠3-5,柠檬酸钠2-4,甲基异噻唑啉酮0.3-0.5,维生素C磷酸酯镁0.5-1;
助剂的制备方法是:
先按固液重量比1:6-1:5向鲜猪骨粉中加入8-10%的醋酸溶液,再加入月桂酰肌氨酸钠、十二烷基葡糖苷和山梨醇酐单油酸酯搅拌均匀并于60-80℃保温8-12h,将pH调至6-7后过滤,再按固液重量比1:8-1:10向滤液中加入活性白土,40-60℃搅拌4-8h,过滤后向滤液中加入其余原料,充分搅拌至溶解完全,即得。
一种绿色环保淬火剂的制备方法,其特征在于,包括以下步骤:
(1)将魔芋胶、黄原胶、柠檬酸和马铃薯淀粉共同加入1/3-1/2量的水,60-80℃、400-600r/min搅拌1-2h,冷却后过滤,向滤液中加入椰油酰甘氨酸钠200-500r/min搅拌5-10min,再加入辛酸/癸酸甘油三酯50-60℃搅拌15-30min,得A组分;
(2)将酒石酸钾钠和聚丙烯酸钠共同加入余量的水中,60-80℃搅拌20-40min,得B组分;
(3)将B组分加入反应釜,并于90-95℃条件下向反应釜中加入氯化钠和黄腐酸搅拌直至完全溶解,再将温度降至30-40℃,缓慢加入A组分200-600r/min搅拌20-30min,最后加入其余原料混合均匀,过滤后即得。
本发明的优点是:
本发明的淬火剂冷却性能好,能有效减少工件的淬火变形,避免淬裂;性质稳定、无异味、带出量小、不易变质,且无毒无害,绿色环保,节能减排,符合环保产业政策的要求。
具体实施方式
本发明非限定实施例如下:
一种绿色环保淬火剂,由下列重量(kg)的组分原料制备而成:
魔芋胶1.5,黄原胶1.5,马铃薯淀粉4,柠檬酸1.5,黄腐酸0.08,山梨醇0.8,辛酸/癸酸甘油三酯0.4,椰油酰甘氨酸钠0.8,聚丙烯酸钠0.8,酒石酸钾钠0.4,氯化钠4,助剂4,水75;
其中,助剂由下列重量(kg)的原料制成:
鲜猪骨粉18,月桂酰肌氨酸钠1.5,十二烷基葡糖苷1.5,山梨醇酐单油酸酯0.8,乙二胺四乙酸钠1.5,葡萄糖酸钠4,柠檬酸钠3,甲基异噻唑啉酮0.4,维生素C磷酸酯镁0.8;
助剂的制备方法:
先按固液重量比1:6向鲜猪骨粉中加入10%的醋酸溶液,再加入月桂酰肌氨酸钠、十二烷基葡糖苷和山梨醇酐单油酸酯搅拌均匀并于80℃保温8h,将pH调至6后过滤,再按固液重量比1:8向滤液中加入活性白土,60℃搅拌6h,过滤后向滤液中加入其余原料,充分搅拌至溶解完全,即得。
绿色环保淬火剂的制备方法包括以下步骤:
(1)将魔芋胶、黄原胶、柠檬酸和马铃薯淀粉共同加入1/2量的水,70℃、500r/min搅拌1.5h,冷却后过滤,向滤液中加入椰油酰甘氨酸钠400r/min搅拌5min,再加入辛酸/癸酸甘油三酯60℃搅拌15min,得A组分;
(2)将酒石酸钾钠和聚丙烯酸钠共同加入余量的水中,70℃搅拌30min,得B组分;
(3)将B组分加入反应釜,并于90℃条件下向反应釜中加入氯化钠和黄腐酸搅拌直至完全溶解,再将温度降至40℃,缓慢加入A组分400r/min搅拌20min,最后加入其余原料混合均匀,过滤后即得。
使用本实施例制备得到的淬火剂对42CrMo钢进行淬火,淬火加热温度为850℃,淬火后测量硬度为HRC55,无开裂现象。
Claims (2)
1.一种绿色环保淬火剂,其特征在于,其是由下述重量份的原料制得:
魔芋胶1-2,黄原胶1-2,马铃薯淀粉3-5,柠檬酸1-2,黄腐酸0.05-0.1,山梨醇0.5-1,辛酸/癸酸甘油三酯0.3-0.5,椰油酰甘氨酸钠0.5-1,聚丙烯酸钠0.5-1,酒石酸钾钠0.3-0.5,氯化钠3-5,助剂3-5,水70-80;
所述助剂由下列重量份的原料制成:
鲜猪骨粉15-20,月桂酰肌氨酸钠1-2,十二烷基葡糖苷1-2,山梨醇酐单油酸酯0.5-1,乙二胺四乙酸钠1-2,葡萄糖酸钠3-5,柠檬酸钠2-4,甲基异噻唑啉酮0.3-0.5,维生素C磷酸酯镁0.5-1;
所述助剂的制备方法是:
先按固液重量比1:6-1:5向鲜猪骨粉中加入8-10%的醋酸溶液,再加入月桂酰肌氨酸钠、十二烷基葡糖苷和山梨醇酐单油酸酯搅拌均匀并于60-80℃保温8-12h,将pH调至6-7后过滤,再按固液重量比1:8-1:10向滤液中加入活性白土,40-60℃搅拌4-8h,过滤后向滤液中加入其余原料,充分搅拌至溶解完全,即得。
2.根据权利要求1所述的一种绿色环保淬火剂的制备方法,其特征在于,包括以下步骤:
(1)将魔芋胶、黄原胶、柠檬酸和马铃薯淀粉共同加入1/3-1/2量的水,60-80℃、400-600r/min搅拌1-2h,冷却后过滤,向滤液中加入椰油酰甘氨酸钠200-500r/min搅拌5-10min,再加入辛酸/癸酸甘油三酯50-60℃搅拌15-30min,得A组分;
(2)将酒石酸钾钠和聚丙烯酸钠共同加入余量的水中,60-80℃搅拌20-40min,得B组分;
(3)将B组分加入反应釜,并于90-95℃条件下向反应釜中加入氯化钠和黄腐酸搅拌直至完全溶解,再将温度降至30-40℃,缓慢加入A组分200-600r/min搅拌20-30min,最后加入其余原料混合均匀,过滤后即得。