CN104588572B - 一种离心铸造用涂料及其制备方法 - Google Patents
一种离心铸造用涂料及其制备方法 Download PDFInfo
- Publication number
- CN104588572B CN104588572B CN201410838554.9A CN201410838554A CN104588572B CN 104588572 B CN104588572 B CN 104588572B CN 201410838554 A CN201410838554 A CN 201410838554A CN 104588572 B CN104588572 B CN 104588572B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- centrifugal casting
- preparation
- rectorite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种离心铸造用涂料,由下述重量份数的原料制成:累托石1~5份、羧甲基纤维素钠0.1~0.7份、石英粉和50~60份、十二烷基硫酸铵0.01~0.5份、水40~45份。本发明的涂料配方简单、成本低廉、制造工艺简单,并且结合离心铸造工艺可以制备出符合行业要求的铸入式气缸套。
Description
技术领域
本发明属于发动机用铸入式气缸套生产技术领域,具体涉及一种离心铸造用涂料及其制备方法。
背景技术
采用金属型离心铸造技术来生产外壁铸造直接成型的气缸套时,涂料是关键;现有气缸套用涂料主要为普通的保温涂料,其主要作用为降低毛坯在铸造过程中的冷却速度,保证毛坯的金相组织及内在质量,保护模具,所铸造的毛坯外径无法满足注入式气缸套的使用要求;而现有的能满足生产气缸套生产要求的涂料多是配方复杂、价格昂贵、使用条件较为苛刻,从而提升了气缸套的制造成本。
发明内容
本发明的目的是提供一种成本低廉、配方简单、制造工艺简单的离心铸造用涂料及其制备方法。
为实现上述发明目的,本发明采用的技术方案是,一种离心铸造用涂料,由下述重量份数的原料制成:累托石1~5份、羧甲基纤维素钠0.1~0.7份、石英粉50~60份、十二烷基硫酸铵0.01~0.5份、水40~45份。
所述离心铸造用涂料的制备方法,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵
搅拌均匀。
本发明中的涂料中各成分的作用是:累托石、羧甲基纤维素钠为悬浮剂,以水载体,以石英粉为骨料,十二烷基硫酸铵为活性剂。
本发明中的涂料配合离心铸造工艺,可以在铸管表面生成毛刺。
本发明产生的有益效果是,本发明的涂料配方简单、成本低廉、制造工艺简单,并且结合离心铸造工艺可以制备出符合行业要求的铸入式气缸套。
附图说明
图1为实施例1中制备的铸入式气缸套外径表面结构示意图。
具体实施方式
实施例1
一种离心铸造用涂料,由下述重量份数的原料制成:累托石3份、羧甲基纤维素钠0.4份、石英粉55份、十二烷基硫酸铵0.3份、水43份。
所述离心铸造用涂料的制备方法,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵搅拌均匀即得涂料。
涂料的应用
本实施例中制备得到的涂料用于铸入式气缸套的制备工艺,包括以下步骤:包括以下步骤:①将铁液熔炼到1500℃开始出炉,铁液中各成分重量百分比如下:C 3.2%、S 0.05%、Si 2.5%、P 0.7%、Mn 0.7%、Cr 0.3%、Cu 0.4%,余量为铁;②离心铸造:将配置好的涂料加入压力涂料罐中,压力调整为0.4MPa;启动离心铸管机,转速设定为1500r/min,将模具的温度加热到300℃,然后涂料喷管开始向模具内壁喷洒配好的涂料,喷洒的涂料的厚度为0.8mm,涂料在模具内壁上受热,涂料受热产生蒸汽迅速在涂料中形成均匀空腔,继而涂料表面产生破裂,气体溢出涂料层,最终在涂料层中形成空腔;将温度为1480-1550℃的铁液转入到浇铸包中,同时加入铁液质量0.8%的孕育剂进行孕育,除去铁液表面浮渣即可浇注入模具中,铁液在离心力作用下注入到空腔中,冷却结晶后在毛坯上形成毛刺。所述孕育剂为硅铁。
表面处理:将离心铸造制得的毛坯经过清砂处理即得到产品。
如图1所示,实施例1中制备的铸入式气缸套1外径表面均匀分布有毛刺2;毛刺2高度在0.3-0.4mm,平均密度70个/平方厘米;毛刺为蘑菇状,缸套硬度97HRB,金相显微组织为A型石墨95%,细片状珠光体基体。
实施例2
一种离心铸造用涂料,由下述重量份数的原料制成:累托石1份、羧甲基纤维素钠0.1份、石英粉50份、十二烷基硫酸铵0.01份、水40份。
所述离心铸造用涂料的制备方法,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵搅拌均匀即得涂料。
实施例3
一种离心铸造用涂料,由下述重量份数的原料制成:累托石5份、羧甲基纤维素钠0.7份、石英粉60份、十二烷基硫酸铵0.5份、水45份。
所述离心铸造用涂料的制备方法,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵搅拌均匀即得涂料。
实施例4
一种离心铸造用涂料,由下述重量份数的原料制成:累托石2份、羧甲基纤维素钠0.3份、石英粉53份、十二烷基硫酸铵0.1份、水42份。
所述离心铸造用涂料的制备方法,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵搅拌均匀即得涂料。
Claims (2)
1.一种离心铸造用涂料,其特征在于,由下述重量份数的原料制成:累托石1~5份、羧甲基纤维素钠0.1~0.7份、石英粉50~60份、十二烷基硫酸铵0.01~0.5份、水40~45份。
2. 如权利要求1所述离心铸造用涂料的制备方法,其特征在于,包括以下步骤:按所述重量份数取累托石、羧甲基纤维素钠、水,混合,搅拌均匀;然后加入石英粉,搅拌均匀;最后加入十二烷基硫酸铵搅拌均匀。