CN104588572A - 一种离心铸造用涂料及其制备方法 - Google Patents

一种离心铸造用涂料及其制备方法 Download PDF

Info

Publication number
CN104588572A
CN104588572A CN201410838554.9A CN201410838554A CN104588572A CN 104588572 A CN104588572 A CN 104588572A CN 201410838554 A CN201410838554 A CN 201410838554A CN 104588572 A CN104588572 A CN 104588572A
Authority
CN
China
Prior art keywords
coating
parts
centrifugal casting
preparation
rectorite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410838554.9A
Other languages
English (en)
Other versions
CN104588572B (zh
Inventor
侯起飞
邹悟会
高广东
刘治军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Province Zynp Corp
ZYNP Corp
Original Assignee
ZYNP Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZYNP Corp filed Critical ZYNP Corp
Priority to CN201410838554.9A priority Critical patent/CN104588572B/zh
Publication of CN104588572A publication Critical patent/CN104588572A/zh
Application granted granted Critical
Publication of CN104588572B publication Critical patent/CN104588572B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种离心铸造用涂料，由下述重量份数的原料制成：累托石1～5份、羧甲基纤维素钠0.1～0.7份、石英粉和50～60份、十二烷基硫酸铵0.01～0.5份、水40～45份。本发明的涂料配方简单、成本低廉、制造工艺简单，并且结合离心铸造工艺可以制备出符合行业要求的铸入式气缸套。

Description

一种离心铸造用涂料及其制备方法
技术领域
本发明属于发动机用铸入式气缸套生产技术领域，具体涉及一种离心铸造用涂料及其制备方法。
背景技术
采用金属型离心铸造技术来生产外壁铸造直接成型的气缸套时，涂料是关键；现有气缸套用涂料主要为普通的保温涂料，其主要作用为降低毛坯在铸造过程中的冷却速度，保证毛坯的金相组织及内在质量，保护模具，所铸造的毛坯外径无法满足注入式气缸套的使用要求；而现有的能满足生产气缸套生产要求的涂料多是配方复杂、价格昂贵、使用条件较为苛刻，从而提升了气缸套的制造成本。
发明内容
本发明的目的是提供一种成本低廉、配方简单、制造工艺简单的离心铸造用涂料及其制备方法。
为实现上述发明目的，本发明采用的技术方案是，一种离心铸造用涂料，由下述重量份数的原料制成：累托石1～5份、羧甲基纤维素钠0.1～0.7份、石英粉50～60份、十二烷基硫酸铵0.01～0.5份、水40～45份。
 所述离心铸造用涂料的制备方法，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵
搅拌均匀。
本发明中的涂料中各成分的作用是：累托石、羧甲基纤维素钠为悬浮剂，以水载体，以石英粉为骨料，十二烷基硫酸铵为活性剂。
 本发明中的涂料配合离心铸造工艺，可以在铸管表面生成毛刺。
本发明产生的有益效果是，本发明的涂料配方简单、成本低廉、制造工艺简单，并且结合离心铸造工艺可以制备出符合行业要求的铸入式气缸套。
附图说明
图1为实施例1中制备的铸入式气缸套外径表面结构示意图。
具体实施方式
实施例1
一种离心铸造用涂料，由下述重量份数的原料制成：累托石3份、羧甲基纤维素钠0.4份、石英粉55份、十二烷基硫酸铵0.3份、水43份。
所述离心铸造用涂料的制备方法，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵搅拌均匀即得涂料。
涂料的应用
本实施例中制备得到的涂料用于铸入式气缸套的制备工艺，包括以下步骤：包括以下步骤：①将铁液熔炼到1500℃开始出炉，铁液中各成分重量百分比如下：C 3.2%、S 0.05%、Si 2.5%、P 0.7%、Mn 0.7%、Cr 0.3%、Cu 0.4%，余量为铁；②离心铸造：将配置好的涂料加入压力涂料罐中，压力调整为0.4MPa；启动离心铸管机，转速设定为1500r/min，将模具的温度加热到300℃，然后涂料喷管开始向模具内壁喷洒配好的涂料，喷洒的涂料的厚度为0.8mm，涂料在模具内壁上受热，涂料受热产生蒸汽迅速在涂料中形成均匀空腔，继而涂料表面产生破裂，气体溢出涂料层，最终在涂料层中形成空腔；将温度为1480-1550℃的铁液转入到浇铸包中，同时加入铁液质量0.8%的孕育剂进行孕育，除去铁液表面浮渣即可浇注入模具中，铁液在离心力作用下注入到空腔中，冷却结晶后在毛坯上形成毛刺。所述孕育剂为硅铁。
表面处理：将离心铸造制得的毛坯经过清砂处理即得到产品。
如图1所示，实施例1中制备的铸入式气缸套1外径表面均匀分布有毛刺2；毛刺2高度在0.3-0.4mm，平均密度70个/平方厘米；毛刺为蘑菇状，缸套硬度97HRB，金相显微组织为A型石墨95%，细片状珠光体基体。
实施例2
一种离心铸造用涂料，由下述重量份数的原料制成：累托石1份、羧甲基纤维素钠0.1份、石英粉50份、十二烷基硫酸铵0.01份、水40份。
所述离心铸造用涂料的制备方法，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵搅拌均匀即得涂料。
 实施例3
一种离心铸造用涂料，由下述重量份数的原料制成：累托石5份、羧甲基纤维素钠0.7份、石英粉60份、十二烷基硫酸铵0.5份、水45份。
所述离心铸造用涂料的制备方法，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵搅拌均匀即得涂料。
实施例4
一种离心铸造用涂料，由下述重量份数的原料制成：累托石2份、羧甲基纤维素钠0.3份、石英粉53份、十二烷基硫酸铵0.1份、水42份。
所述离心铸造用涂料的制备方法，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵搅拌均匀即得涂料。

Claims (2)

1.一种离心铸造用涂料，其特征在于，由下述重量份数的原料制成：累托石1～5份、羧甲基纤维素钠0.1～0.7份、石英粉50～60份、十二烷基硫酸铵0.01～0.5份、水40～45份。
2. 如权利要求1所述离心铸造用涂料的制备方法，其特征在于，包括以下步骤：按所述重量份数取累托石、羧甲基纤维素钠、水，混合，搅拌均匀；然后加入石英粉，搅拌均匀；最后加入十二烷基硫酸铵搅拌均匀。
CN201410838554.9A 2014-12-30 2014-12-30 一种离心铸造用涂料及其制备方法 Active CN104588572B (zh)