CN104559947B - 一种环保防腐蚀有机酸型防冻液 - Google Patents
一种环保防腐蚀有机酸型防冻液 Download PDFInfo
- Publication number
- CN104559947B CN104559947B CN201510050027.6A CN201510050027A CN104559947B CN 104559947 B CN104559947 B CN 104559947B CN 201510050027 A CN201510050027 A CN 201510050027A CN 104559947 B CN104559947 B CN 104559947B
- Authority
- CN
- China
- Prior art keywords
- icing fluid
- environment
- parts
- organic acid
- corrosion inhibiter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种环保防腐蚀有机酸型防冻液,属于防冻液技术领域,其中各组分的重量份为醇类物质35~70份、缓蚀剂0.1~0.5份、表面活性剂0.1~1份、稳定剂0.1~1份、pH缓蚀剂0.1~0.5份、染料0.001~0.001份、去离子水30~65份;该防冻液沸点高,冰点低,防腐蚀能优越,质量稳定,能够长期保存和使用,且不含胺类、硝酸盐、磷酸盐等对环境和人体有害的物质,绿色环保,对环境友好。
Description
技术领域
本发明涉及一种防冻液,具体涉及一种环保防腐蚀有机酸型防冻液,属于防冻液技术领域。
背景技术
防冻液(又称冷却液、不冻液)是内燃机循环冷却系统的冷却介质,具有冬天防冻、夏天防沸、全年防水垢、防腐蚀等优点。我国自20世纪 80年代开始研发汽车防冻液,相比国外一些发达国家,起步较迟。防冻剂主要分为盐类和醇类两大类,因为盐类防冻剂容易腐蚀冷却系统并且引发板结现象,对发动机的使用造成十分严重的影响,因此人们对防冻剂的选择主要为醇类而不是盐类。
目前我国汽车发动机防冻液产品仍以无机型为主,多数腐蚀抑制剂配方中含有诸如亚硝酸盐、胺盐、硼砂等无机盐缓蚀剂,如专利CN201410004822.7(一种汽车发动机防冻液)、CN201310114991.1(新型耐腐蚀汽车防冻液)、CN201410292513.4(一种汽车防冻液及其制备方法)公开的防冻液配方中含有硼砂或胺类。这类缓蚀剂尽管价格便宜,但对环境及人体有害,尤其是胺类和亚硝酸盐反应生成的亚硝酸胺有致癌性,使其在某些国家或地区的应用受到限制。且硼酸盐能够腐蚀铝金属化部件,其腐蚀生成物将散热器堵塞,对铝金属部件的防腐不利,不能满足现代汽车发展的需求。汽车发动机防冻液是发动机冷却系统不可缺少的冷却散热介质。随着汽车发动机技术的发展及人们环保意识的提高,对环保型发动机防冻液的需求在逐年递增。因此根据汽车发动机防冻液的发展方向和我国国情,研制一种性能优良、价格适中的环保型发动机防冻液具有良好的经济和社会效益。
近年来在高级防冻冷却液中使用较多的是有机酸配方,有机酸缓蚀剂的消耗就比常规的缓蚀剂缓慢许多,主要是利用有机酸活性吸附的物理性质来体现它的缓蚀作用,另外,有机酸型汽车防冻液对环境的保护功能非常显著,使用以后能够利用微生物的降解作用保护并绿化环境,因此,在国际上有机酸型汽车防冻液的应用得到了显著的发展。我国近年来也出现了许多有关有机酸型防冻冷却液的研究:CN201110053527.7公开了一种汽车发动机防冻液,防冻液包含葵二酸、己二酸等有机酸,但是该专利对锌、铝金属部件的防腐效果欠佳;CN200910024033.9公开的一种发动机防冻液,组分含有钼酸钠和异辛酸、葵二酸,它是在常规无机型和全有机型发动机防冻液技术的基础上,采用以有机物为主,无机物为辅的新型配方,有机酸采用一元酸和二元酸复合,以便达到长效目的,但是钼酸钠属于有毒物质,会对人体造成一定程度的伤害,欧洲已经开始限制钼酸盐的使用,且异辛酸有臭味,因此防冻液有异味。对于一种对环境绿色友好,而且又具有优良防腐功能的蚀有机酸型防冻液,市场还没有类似产品,技术还尚属空白。
发明内容
本发明的目的是提供一种环保防腐蚀有机酸型防冻液,该防冻液沸点高,冰点低,防腐蚀能优越,质量稳定,能够长期保存和使用;且不含胺类、硝酸盐、磷酸盐等对环境和人体有害的物质,绿色环保,对环境友好。
为了解决上述问题,本发明所采用的技术方案是:
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
醇类物质35~70份、缓蚀剂0.1~0.5份、表面活性剂0.1~1份、稳定剂0.1~1份、pH缓蚀剂0.1~0.5份、染料0.001~0.001份、去离子水30~65份;
所述的醇类物质为乙二醇;
所述的缓蚀剂为有机一元羧酸与有机二元羧酸复配,其中一元羧酸为月桂酸,二元酸为癸二酸,两者的质量比为1:1~1:3;
所述的表面活性剂为吐温20或吐温40或吐温60;
所述的稳定剂为苯并三氮唑;
所述的pH缓蚀剂为碳酸钾。
本发明相对于现有技术的有益效果是:
(1)本发明提供的防冻液沸点高,冰点低,防腐蚀能优越,质量稳定,能够长期保存和使用;
(2)本发明提供的防冻液,不含胺类、硝酸盐、磷酸盐,也没有含有目前使用较普遍的钼酸盐等对环境和人体有害的物质,绿色环保,对环境友好,符合汽车发动机防冻液的发展方向和我国国情,经济和社会效益看好;
(3)本发明利用脂肪酸和二元酸复配作为防冻液的缓蚀剂,能有效抑制金属的腐蚀,
且由于缓蚀剂作用过程不需要成膜,消耗量很少,从而保证防冻剂的质量,延长使用时间。
具体实施方式
下面通过实施例对本发明做进一步详细说明,这些实施例仅用来说明本发明,并不限制本发明的范围。
实施例1
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
乙二醇35份、缓蚀剂0.1份(月桂酸和癸二酸的质量比为1:1)、吐温20 0.1份、苯并三氮唑0.1份、碳酸钾0.1份、染料0.001份、去离子水30份。
实施例2
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
乙二醇70份、缓蚀剂0.5份(月桂酸和癸二酸的质量比为1:3)、吐温40 1份、苯并三氮唑1份、碳酸钾0.5份、染料0.001份、去离子水65份。
实施例3
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
乙二醇50份、缓蚀剂0.3份(月桂酸和癸二酸的质量比为1:2)、吐温60 0.5份、苯并三氮唑0.5份、碳酸钾0.3份、染料0.0051份、去离子水45份。
实施例4
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
乙二醇40份、缓蚀剂0.2份(月桂酸和癸二酸的质量比为1:1.2)、吐温60 0.2份、苯并三氮唑0.2份、碳酸钾0.1份、染料0.0035份、去离子水35份。
实施例5
一种环保防腐蚀有机酸型防冻液,各组分的重量份为:
乙二醇65份、缓蚀剂0.4份(月桂酸和癸二酸的质量比为1:2.6)、吐温60 0.7份、苯并三氮唑0.65份、碳酸钾0.42份、染料0.0078份、去离子水60份。
实施例6
对实施例1的环保防腐蚀有机酸型防冻液进行玻璃器皿腐蚀试验,结果如表1所示,结果显示:防冻液各方面性能均符合行业标准SH/T0521-99,具有冰点低、沸点高、防腐蚀性好、泡沫倾向性小等优点。
表1 玻璃器皿腐蚀试验结果
Claims (1)
1.一种环保防腐蚀有机酸型防冻液,其特征在于:各组分的重量份为:
醇类物质35~70份、缓蚀剂0.1~0.5份、表面活性剂0.1~1份、稳定剂0.1~1份、pH缓蚀剂0.1~0.5份、染料0.001份、去离子水30~65份;
其中,所述的醇类物质为乙二醇;
所述的缓蚀剂为有机一元羧酸与有机二元羧酸复配,其中一元羧酸为月桂酸,二元酸为癸二酸,两者的质量比为1:1~1:3;
所述的表面活性剂为吐温20或吐温40或吐温60;
所述的稳定剂为苯并三氮唑;
所述的pH缓蚀剂为碳酸钾。